Multilayer assemblies of colloidal ZnS doped with silver and polyelectrolytes based on electrostatic interaction

Multilayer assemblies of silver doped ZnS colloid and polycation were fabricated by a self-assembly technique exploiting electrostatic interaction. UV/Vis spectra showed the uniform deposition process and X-ray photoemission spectroscopy (XPS) confirmed the coexistence of silver. It was found that the emission spectra of the silver doped ZnS colloid red-shifted to 528 nm comparing with undoped ZnS colloid. However, the most important finding was that the luminescence intensity of doped ZnS assembled in films was much stronger than that of undoped ZnS in films and that of doped ZnS in the spin-casting film. The mechanism of the enhancement luminescence was discussed. (C) 1998 Elsevier Science S.A. All rights reserved.

自然界中ZnS-CdS完全类质同象系列的发现和初步研究

过去认为在自然界中的Cd只能有限替代ZnS中的Zn。但是，近几年笔者在研究贵州牛角塘镉锌矿床时，经电子探针、扫描电镜和透射电镜等多种方法的研究，发现锌硫化物中的Cd主要以类质同象存在，其含量可从0．8％增至37．93％；镉硫化物中的Zn同样主要以类质同象存在，其含量为2．43％～38．64％。锌硫化物与镉硫化物成渐变的过渡关系，并且Zn与Cd成很好的负相关关系，相关系数达0．99以上，形成ZnS-CdS的完全类质同象系列。这一发现无论在矿物学，还是在地球化学和矿床学上都具有重要的理论意义和实用价值。

Preparation and a time-resolved fluoroimmunoassay application of new europium fluorescent nanoparticles

New silica-based europium fluorescent nanoparticles having surface amino groups were prepared by a covalent binding-copolymerization technique. In the nanoparticles, the fluorescent Eu3+ chelate molecules were covalently bound to silicon atoms to protect the nanoparticles from dye leaking in bio-applications. The amino groups on the surface of nanoparticles made the surface modification and bioconjugation of nanoparticles easier. The nanoparticles were characterized and developed as a new type of fluorescence probe for a highly sensitive time-resolved fluoroimmunoassay (TR-FIA) of human hepatitis B surface antigen (HBsAg).

Size-controllable synthesis of monodispersed SnO2 nanoparticles and application in electrocatalysts

Size-controllable tin oxide nanoparticles are prepared by heating ethylene glycol solutions containing SnCl2 at atmospheric pressure. The particles were characterized by means of transmission electron microscopic (TEM), X-ray diffraction (XRD) studies. TEM micrographs show that the obtained material are spherical nanoparticles, the size and size distribution of which depends on the initial experimental conditions of pH value, reaction time, water concentration, and tin precursor concentration. The XRD pattern result shows that the obtained powder is SnO2 with tetragonal crystalline structure. On the basis of UV/vis and FTIR characterization, the formation mechanism of SnO2 nanoparticles is deduced. Moreover, the SnO2 nanoparticles were employed to synthesize carbon-supported PtSnO2 catalyst, and it exhibits surprisingly high promoting catalytic activity for ethanol electrooxidation.

Factors influencing the catalytic activity of SBA-15-supported copper nanoparticles in CO oxidation

Copper nanoparticles were deposited onto mesoporous SBA-15 support via two different routes: post-grafting method and incipient wet impregnation method. Both XRD and TEM reveal that the post-grafting can make Cu particles very small in size and highly dispersed into channels of SBA-15, while the impregnation method mainly forms large Cu particles on the external surface of SBA-15. TPR experiments show that CuO species formed by the post-grafting method is more reducible than that prepared by the impregnation method. The catalytic activity tests for CO oxidation manifests that the sample prepared by the post-grafting method has a much higher activity than that prepared by the impregnation method, with a lowering of 50 degrees C for T-50, showing a strong dependence of catalytic activity on the size and dispersion of Cu particles. Besides the preparation procedure, other factors including calcination temperature, reduction treatment, copper loading as well as the feed composition, have an important effect on the catalytic activity. The best performance was obtained when the catalyst was calcined at 500 degrees C and reduced at 550 degrees C. The calcination and reduction treatment at high temperature have been found to be necessary to completely remove the organic residue and to generate active metallic copper particles. (c) 2005 Elsevier B.V. All rights reserved.