Preparation of zinc sodium polyphosphates glasses from coacervates precursors. Characterisation of the obtained glasses, and their applications

A soft chemistry route is described to obtain glasses in the P2O5-Na2O-ZnO-H2O. It is based on the addition of zinc salts to coacervates prepared from sodium polyphosphate. The processing of these coacervates leads to polyphosphate glasses with the same properties as those of glasses prepared in the classical way. So far, little work has been implemented in this system using 'coacervate route'. However, it makes an attractive method for coating and joining processes on the industrial scale. As the anion associated to zinc may take part in the adhesion mechanism, coacervate formation has been studied using zinc chloride, nitrate and sulphate as starting materials. The physical properties of the glasses obtained by this method are reported and potential applications of zinc and silver coacervate are described. (C) 2002 Academie des sciences / Editions scientifiques et medicales Elsevier SAS.

Thermal properties of fluoride glasses and their gel precursors

Xerogels were prepared from zirconium, barium, aluminum, lanthanum and lithium acetates, corresponding to a Li containing ZBLA composition. The study of their thermal properties (DSC, TG/DTG, FT-IR) showed that they might be used as chemically stable precursors in the preparation of fluoride glasses. Hydrofluoric acid in solution was chosen as a mild fluorinating agent. This newly proposed technique of fluorinating allowed to obtain high quality ZBLALi glass which presents the advantage of higher thermal stability and homogeneity in comparison with the glass obtained using individual commercial fluorides.

Effect of salt nature on structure and ionic conductivity of sodium-doped siloxane-PPO ormolytes

Siloxane-polyoxypropylene (PPO) hybrids obtained by the sol-gel process and containing short polymer chain have been doped with different sodium salts NaX (X = ClO4, BF4 or I). The effect of the counter-ion (X) on the chemical environment of the sodium ions and on the ionic conductivity of these hybrids was investigated by Na-23 NMR, small angle X-ray scattering (SAXS), complex impedance, Raman spectroscopy and differential scanning calorimetry (DSC). Results reveal that the different sodium salts have essentially the same effect on the nanoscopic structure of the hybrids. The formation of immobile Na+ cations involved in NaCl-like species could be minimized by using a low amount of HCl as hydrolytic catalyst. The differences in the ionic conductivity of hybrids doped with different sodium salts were correlated with the proportion of Na ions solvated by ether-type oxygen of the polymeric chains and by the carboxyl oxygen located in the urea groups of the PPO chain extremities. (c) 2005 Elsevier Ltd. All rights reserved.

Influence of fluoride dentifrice on brushing abrasion of eroded human enamel: An in situ/ex vivo study

This in situ/ex vivo study assessed the effect of fluoride dentifrice on eroded enamel subjected to brushing abrasion. In a crossover study performed in 2 phases, 10 volunteers wore acrylic palatal appliances, each containing 3 human enamel blocks. Dentifrice was used to brush the volunteers' teeth and the specimens subjected to abrasion. In phases A and B the dentifrices used had the same formulation, except for the absence or presence of fluoride, respectively. The blocks were subjected to erosion by immersion of the appliances in a cola drink for 5 min, 4 times a day. Then the blocks were brushed, and the appliance was replaced into the mouth. Enamel alterations were determined using profilometry and percentage change in surface microhardness (%SMHC) tests. The data were tested using the paired t test. The mean wear values (+/- SD, mu m) were: group A 6.84 +/- 1.72 and group B 5.38 +/- 1.21 (p = 0.04). The mean %SMHC values (+/- SD) were: group A 54.6 +/- 16.2 and group B 45.7 +/- 6.8 (p = 0.04). Fluoride dentifrice had a protective effect on eroded enamel subjected to brushing abrasion. Copyright (c) 2007 S. Karger AG, Basel.

Improvement of the chemical resistance of zirconium fluoride glasses coated with a Tiron (R) modified tin oxide layer prepared by the sol-gel process

In order to improve the chemical resistance of zirconium fluoride glass a protective transparent SnO2 layer was deposited by the solgel dip-coating process in the presence of Tiron (R) as particle surface modifier agent. After water immersion for different periods of time, both coated and non-coated fluoride glasses were analyzed by scanning electron microscopy, mass loss evaluation, infrared spectroscopy and X-ray photoelectron spectroscopy. In contrast to the effects occurring for non-coated glass, where the surface undergoes a rapid selective dissolution of the most soluble species, the results for the SnO2-coated glass showed that the filling of the film nanopores by dissolved glass material results in a hermetic barrier protecting the glass surface. The selective glass dissolution was confirmed by liquid chromatography measurements of the etching solution after each exposure time. (c) 2006 Elsevier B.V. All rights reserved.

SOLIDS COATED WITH SODIUM TETRACHLOROPALLADATE - SORBENTS FOR REDUCED SULFUR-COMPOUNDS IN AIR

A study of the preconcentration of tioethers in air by means of the passage of gas flow on solid sorbents coated with sodium tetrachloropalladate was undertaken with the aim of achieving chemical fixation. This fixation presented high specificity and blocked the migration of the sorbed compound through the other active sites. The species obtained were selectively dissolved in organic solvents, resulting in the sulfur reduced compound concentration in the organic phase, which could be determined spectrophotometrically.

In vitro evaluation of the effectiveness of acidic fluoride dentifrices

This study evaluated the effectiveness of acidic low-fluoride dentifrices compared to conventional neutral dentifrices. Enamel blocks were submitted to pH cycling and treatment with slurries of dentifrices containing 0, 275, 412, 550 and 1,100 mu g F/g (pH 4.5 or 7.0), and also a commercial dentifrice (1,100 mu g F/g) and a commercial children's dentifrice (500 mu g F/ g). Variations in surface microhardness and in the mineral content in enamel after pH cycling were calculated. Enamel blocks treated with acidic dentifrices exhibited less mineral loss compared to neutral dentifrices (ANOVA; p < 0.05). The acidic dentifrices with 412 and 550 mu g F/g had the same effectiveness as the neutral 1,100-mu g F/g dentifrice and commercial 1,100-mu g F/g dentifrice. Copyright (c) 2007 S. Karger AG, Basel