Synthesis of barium fluoride nanoparticles from microemulsion

The cetyltrimethylammonium bromide (CTAB)/2-octanol/water microemulsion system was used to synthesize barium fluoride nanoparticles. X-ray powder diffraction (XRD) analysis showed that the products were single phase. The results of scanning electron microscopy and calculations using the Scherrer equation from the line widths of the XRD have been used to estimate the average particle sizes of the powder products. The results showed that the nanoparticle size was affected by water content and surfactant (CTAB) concentration. As water content decreases from 14.2 to 9.47% (w/w), the particle size decreases from 75 to 40 rim. In addition, increasing the reaction times from 5 to 120 min increases the particle size from 75 to 150 rim, and increasing the amount of surfactant decreases the size of the particle. Luminescence spectra of the BaF2:Ce nanoparticles are also discussed.

Gold nanoparticles as fine tuners of electrochemical properties of the electrode/solution interface

Recently, a novel approach for preparing SERS and SPR substrates was developed, which indicates a potential application in tailoring the interfacial structure of an electrode surface. In this study, (3-mercaptopropyl)trimethoxysilane (MPTMS) was selected as a polymeric adhesive layer, and a low concentration of colloid Au solution was used to achieve a more accurate control over interface morphology at nanoscale dimensions due to slow self-assembling kinetics of gold nanoparticle's. Subsequent seeding growth of these MPTMS-supported submonolayers of gold nanoparticles in Au3+/NH2OH aqueous solution enlarges particle size and eventually results in the generation of conductive gold films (similar to previous (3-aminopropyl)trimethoxysilane-supported gold films). Such tunable interface structure was evaluated by atomic force microscopy (AFM). Also, ac impedance spectroscopy (ACIS) and cyclic voltammograms were performed to evaluate electrochemical properties of the as-prepared interfaces by using Fe(CN)(6) (3-/4-) couples as a probe. Furthermore, relevant theories of microarray electrodes were introduced into this study to explain the highly tunable electrochemical properties of the as-prepared interfaces. As a result, it is concluded that the electrochemical properties toward Fe(CN)(6) (3-/4-) couples are highly dependent on the active nanoelectrode (nanoparticles) area fraction and nanoparticles are fine-tuners of interfacial properties because the number density. (numbers/unit area) and size of nanoparticles are highly tunable by self-assembling and seeding growth time scale control. This is in agreement with the theoretical expectations for a microarray electrode if a single nanoparticle tethered to a blocking SAM is taken as a nanoelectrode and 2-D nanoparticle assemblies are taken as nanoelectrode arrays.

Colloid chemical approach to nanoelectrode ensembles with highly controllable active area fraction

A novel "bottom-up" approach to highly controllable nanoelectrode ensembles (NEEs) has been developed using colloidal nanoparticle self-assembly techniques. Ibis solution-based strategy allows flexible control over nanoelectrode size, shape, and interspacing of the as-prepared NEEs. Atomic force microscopy (AFM) was proved to be a powerful tool to monitor the NEE topography, which yields parameters that can be used to calculate the fractional nanoelectrode area of the NEEs. AFM, ac impedance, and cyclic voltammetry studies demonstrate that most of nanoelectrodes on the NEEs (at least by 9-min self-assembly) are not diffusionally isolated under conventional ac frequency range and scan rates. As a result, the NEEs behave as "nanoelectrode-patch" assemblies. Besides, the as-prepared NEEs by different self-assembling times show an adjustable sensitivity to heterogeneous electron-transfer kinetics, which may be helpful to sensor applications. Like these NEEs constructed by other techniques, the present NEEs prepared by chemical self-assembly also exhibit the enhancement of electroanalytical detection limit consistent with NEE theory prediction.

Preparation of CeO2 nanopartides hydrosol

CeO2 nanoparticles hydrosol was synthesized by colloidal chemical method. The optimum experiment conditions for the preparation of CeO2 nanoparticles hydrosol were discussed. The effects of pH values, the reactant concentration and temperature on peptization process were studied. TEM photos showed that the CeO2 nanoparticles were spherical in shape and the size was about 3nm. Particle size distribution was in narrow range, and no agglomerates were observed. ED images indicated that the CeO2 nanoparticles were polycrystalline structure, and some of CeO2 were monocrystal particles.

Tensile modulus of polymer nanocomposites

Based on Takayanagi's two-phase model, a three-phase model including the matrix, interfacial region, and fillers is proposed to calculate the tensile modulus of polymer nanocomposites (E-c). In this model, fillers (sphere-, cylinder- or plate-shape) are randomly distributed in a matrix. If the particulate size is in the range of nanometers, the interfacial region will play an important role in the modulus of the composites. Important system parameters include the dispersed particle size (t), shape, thickness of the interfacial region (tau), particulate-to-matrix modulus ratio (E-d/E-m), and a parameter (k) describing a linear gradient change in modulus between the matrix and the surface of particle on the modulus of nanocomposites (E-c). The effects of these parameters are discussed using theoretical calculation and nylon 6/montmorillonite nanocomposite experiments. The former three factors exhibit dominant influence on E-c At a fixed volume fraction of the dispersed phase, smaller particles provide an increasing modulus for the resulting composite, as compared to the larger one because the interfacial region greatly affects E-c. Moreover, since the size of fillers is in the scale of micrometers, the influence of interfacial region is neglected and the deduced equation is reduced to Takayanagi's model. The curves predicted by the three-phase model are in good agreement with experimental results. The percolation concept and theory are also applied to analyze and interpret the experimental results.

Reactive reinforcement of the interface of poly(ether sulfone)/poly(phenylene sulfide) polymer blend by PMR-POI

The effect of polymerization of monomer reactant-polyimide (POI) as the interfacial agent on the interface characteristics, morphology features, and crystallization of poly(ether sulfone)/poly(phenylene sulfide) (PES/PPS) blends were investigated using a scanning electron microscope, FTIR, WAXD, and XPS surface analysis. It was found that the interfacial adhesion was enhanced, the particle size of the dispersed phase was reduced, and the miscibility between PES and PPS was improved by the addition of POI. It was also found that POI was an effective nucleation agent of the crystallization for PPS.

Preparation of Pt/C catalyst with solid phase reaction method

The PVC catalyst was prepared with solid phase reaction method (Pt/C(S)) for the first time. Its performances were compared with that prepared by the traditional liquid phase reaction method. The results demonstrate that the electrocatalytic activity of PVC catalyst with solid phase reaction method for methanol oxidation is higher than that with liquid phase reaction method. XRD and TEM measurements indicate that the Pt/C(S) possesses low crystalline extent and small particle size.

Preparation and characteristics of polyimide-TiO2 nanocomposite film

A sol-gel approach has been developed to prepare polyimide-TiO2, hybrid films fi om soluble polyimides and a modified titanium precursor. The rate of the hydrolysis reaction of titanium alkoxide can be controlled by using acetic acid as a modifier. FTIR and XPS indicated that TiO2, particles were well distributed in polyimide matrixes with particle size small per than 60 nm. Polyimide hybrid films having the TiO2, component less than or equal to 10% exhibited high thermal stability, high optical transparency and good mechanical properties and possessed higher dielectric constants than correspondingly polyimides. (C) 2000 Society of Chemical Industry.

A new preparation of zinc sulfide nanoparticles by solid-state method at low temperature

A novel solid-state method of the preparation of zinc sulfide nanoparticles is reported. By solid-state reaction of zinc acetate and thioacetamide at low temperature, zinc sulfide nanoparticles of different sizes were prepared. The temperature of preparation varied from room temperature to 300 degrees C. The particles were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), differential thermal analysis (DTA), and photoluminescence spectrum. X-ray diffraction patterns revealed that the particles exhibited pure zinc-blende crystal structure and that particle size increased with increasing temperature. The TEM micrograph showed that the mean particle size was about 40 nm for the sample heated at 100 degrees C. A blue shift was observed in the photoluminescence emission spectrum. A possible mechanism of the reaction corresponding to our observation is proposed, (C) 2000 Elsevier Science Ltd. All rights reserved.

Brittle-tough transition in PP/EPDM blends: effects of interparticle distance and tensile deformation speed

The toughness of polypropylene (PP)/ethylene-propylene-diene monomer rubber (EPDM) blends containing various EPDM contents as a function of the tensile speed was studied. The toughness of the blends was determined from the tensile fracture energy of the side-edge notched samples. A sharp brittle-tough transition was observed in the fracture energy versus interparticle distance (ID) curves when the crosshead speed < 102.4 mm/min. It was observed that the brittle-ductile transition of PP/EPDM blend occurred either by reducing ID or by decreasing the tensile speed. The correlation between the critical interparticle distance and tensile deformation rate was compared with that between the critical interparticle distance and temperature for PP/EPDM blends. (C) 2000 Elsevier Science Ltd. All rights reserved.

Electrochemical synthesis of Ag nanoparticles on functional carbon surfaces

In this paper, we present a new method of fabricating metal nanoparticles on carbon substrates through molecular design. Scanning tunneling microscopy measurements show that the electrochemically synthesized Ag nanoparticles are homogeneously dispersed on the modified highly oriented pyrolytic graphite (HOPG) surface with a narrow particle size distribution. Moreover, the size and number density of Ag nanoparticles on the grafted HOPG surface can be easily changed through control of the experimental conditions. (C) 2001 Elsevier Science B.V. All rights reserved.

Tremolite-reinforced nylon 66 composites: Mechanical and rheological properties

The reinforcement effect of an acicular inorganic filler, tremolite, on nylon 66 was studied. The mechanical properties of tremolite-filled nylon 66 composites and the effect of the filler particle size on them were obtained. The dynamic mechanical properties and rheological properties of the composites were measured. Two treatments, silane and unsaturated polyester, were used to improve the interface between tremolite and the nylon matrix. The morphologies of the composites were investigated using SEM. (C) 1998 John Wiley & Sons, Inc.

Toughening of nylon with epoxidised ethylene propylene diene rubber

Blends of nylon-6 and epoxidised ethylene propylene diene (eEPDM) rubber were prepared through reactive mixing. It is found that the toughness of nylon-6 can be much improved by this method, and that the particle size of eEPDM is much smaller than that of unexpoxidised EPDM (uEPDM) rubber in a nylon-6 matrix. This indicates that the epoxy group in eEPDM could react with a nylon-6 end group to form a graft copolymer which could act as an interfacial compatibiliser between the nylon-6 and the eEPDM rubber dispersed phase. (C) 1998 Elsevier Science Ltd. All rights reserved.

Preparation of highly dispersed gold microparticles and their electrocatalytic activity for the oxidation of formaldehyde

The electrochemical preparation of highly dispersed Au microparticles on the surfaces of glassy carbon (GC) electrodes and their electrocatalytic activities for the oxidation of formaldehyde were studied. It was found that the reduction of Au3+ to Au is controlled by diffusion and the formation mechanism of Au microparticles on the GC surfaces corresponds to an instantaneous nucleation and diffusion-controlled three dimensional growth process. The particle size is about 80-90 nm in diameter after the electrochemical ageing treatment. These highly dispersed Au microparticles have high surface areas and exhibit better electrocatalytic activity than that of bulk-form Au toward the electrochemical oxidation of formaldehyde in alkaline media.

Synthesis and properties of cerium oxide nanometer powders by pyrolysis of amorphous citrate

CeO2 nanometer powders of different sizes were prepared at low temperature by pyrolysis of amorphous citrate. XRD patterns show that CeO2 is cubic in structure, space group O-h(5)-F-M3M. TEM indicates that the prepared CeO2 is spherical in shape, and the particle size distribution is in narrow range. It was found that calcination temperature is a more important factor affecting the crystallite size of CeO2 than calcining time, the smaller the particle, the bigger the crystal lattice distortion, the worse the crystal growth. Solubility test of CeO2 in nitric acid reveals that the surface activity of CeO2 decreases with the increasing particle sizes. IR spectra analysis shows that the absorption of Ce-O bond is shifted to higher energy with the decrease of CeO2 particle sizes.