O processo sol-gel: uma visão físico-química

The aim of this work was to revise the main concepts involved in the physical-chemistry of the sol-gel process. First, the preparation and its influence on the gel's structure are focalized; the sol-gel transition is revised under the thermodynamics of crytical phenomena point of view and by considering the kinetic models of aggregation. Second, the experimental methods usually used to characterize the sol-gel transition are discussed.

Catalysis and temperature dependence on the formation of ZnO nanoparticles and of zinc acetate derivatives prepared by the sol-gel route

The chemical and structural nature of powders prepared from the zinc acetate-derived precursor using the sol-gel route is discussed. The influence of the synthesis temperature and of the hydrolytic catalyst on the structural features of the powder is focused on the basis of X-ray powder diffraction (XRPD) and extended X-ray absorption fine structure (EXAFS) measurements and complemented with density and thermoanalysis (TG-DTA) results. EXAFS and XRPD results show that no-washed nanoparticulate powders are composed of a mixture of ZnO (wurtzite), zinc acetate, and zinc hydroxyacetate. The latter has a layered structure typical of hydroxy double salts (HDS). The main component of no-washed powders is always unreacted zinc acetate solid but the relative amount of the zinc-based compounds depends on the nature of the hydrolytic catalyst, hydrolysis ratio, and of synthesis temperature. According to the proportion of the three zinc-based compounds, three families of powders could be distinguished. The amount of ZnO nanoparticles (1.6 +/- 0.6 nm) decreases as the synthesis temperature increases, as the hydrolysis ratio decreases, or by changing from basic to acid catalysis. This finding suggests that the formation of zinc compounds is controlled by the equilibrium between hydrolysis-condensation and complexation-reprecipitation reactions.

Influence of age on the behavior of dental pulp of dog teeth after capping with an adhesive system or calcium hydroxide

This study evaluated histomorphologically the influence of chronological age of the dog on the dental pulp-healing process after capping with the All Bond 2 system or with calcium hydroxide paste. The animals were divided according to age into young and adult groups. Class 5-type cavities were prepared, and the pulp was submitted to an exposure of a diameter of 0.5 mm. The pulp of the teeth was then protected with the adhesive system or with a calcium hydroxide paste. Sixty days after treatment, the results obtained with the adhesive system in the young group were significantly better than those in the adult group. With calcium hydroxide, the results were similar for both groups. The pulp treated with calcium hydroxide exhibited a complete hard tissue bridge and a pulp without inflammatory reaction, a fact not observed when the adhesive system was used. In conclusion, the chronological age of the pulp influenced the comparative results only for the adhesive system (P = 0.1), and the total results were better with calcium hydroxide than with the All Bond 2 system (P = 0.01).

Small-angle X-ray scattering study of gelation and aging of Eu3+-doped sol-gel-derived siloxane-poly(oxyethylene) nanocomposites

The aggregation, gelation, and aging of urea-cross-linked siloxane-poly(oxyethylene) nanohybrids [(U600)-n] containing two different amounts of europium triflate initially dissolved in an ethanol-water mixture were investigated by in situ small-angle X-ray scattering (SAXS). For both low (n = [O]/[Eu] = 80) and high (n = 25) europium contents, the SAXS intensity was attributed to the formation of siloxane clusters of about 8-11 Angstrom in size. Siloxane cluster formation and growth is a rapid process in hybrids with low Eu contents and slow in Eu-rich hybrids. An additional contribution to the scattering intensity at very low angles was attributed to the formation of a coarse structure level. At this secondary level, the structure can be described as a set of dense domains containing siloxane clusters embedded in a depleted matrix composed of unfolded polymer chains and solvent. By fitting a theoretical function for this model to the experimental SAXS curves, relevant structural parameters were determined as functions of time during the sol-gel transition and gel aging. For hybrids with low europium contents (n = 80), the size of the siloxane clusters remains essentially invariant, whereas the dense segregation domains progressively grow. In hybrids with high doping contents (n = 25), the preponderant structure variation during the first stages of the sol-gel transformation is the slow growth of siloxane clusters. For these hybrids, the segregation of siloxane clusters forming dense domains occurs only during advanced stages of the process.

Characterization of the porosity developed in a new titania-alumina catalyst support prepared by the sol gel route

Titanium oxide (TiO2) is a good candidate for support of hydrotreating catalysts but has the disadvantage of presenting a low surface area and a poor thermal stability when compared with Al2O3. A mixed TiO2-Al2O3 support was proposed as an alternative that is expected to be free from these drawbacks. The variation during firing of the nanoporous texture of supports composed of TiO2-Al2O3, TiO2 and Al2O3 was studied by small angle X-ray scattering (SAXS). The supports were prepared by the sol-gel route using Ti and Al isopropoxides. We have particularly analyzed the effects of acid and basic hydrolysis on the nanostructural features of catalyst supports fired at different temperatures. The nanopore radius distribution functions were determined from SAXS results assuming a simple model of spherical nanopores embedded in a homogeneous solid matrix. The modal pore radius in both pure TiO2 and pure Al2O3 supports grows from 1.3 to 2.2 nm as the firing temperature increases from 673 to 973 K. on the other hand, the modal pore radius in the mixed TiO2-Al2O3 support remains below 1.2 nm over the same range of firing temperatures. These results demonstrate the good thermal stability of the nanoporous texture of mixed TiO2-Al2O3 supports.

Study of structural surface modified tin oxide membrane prepared by sol-gel route sintered at 400 degrees C

This work describes the chemical modification by Tiron(R) molecules of the surface of SnO2 nanoparticles used to prepare nanoporous membranes. Samples prepared with Tiron(R) content between 1 and 20 wt% and fired at 400 C were characterised by X-Ray Powder Diffraction (XRPD), Extended X-ray Absorption Fine Structure (EXAFS), N-2 adsorption isotherms analysis and permeation experiments. XRPD and EXAFS results show a continuous reduction of crystallite size by increasing the Tiron(R) contents until 7.5 wt%. The control exercised by Tiron(R) modifying agent in crystallite growth allows the fine tuning of the average pore size that can be screened from 0.4 to 4 nm as the amount of grafted molecules decreases from 10 to 0 wt%. In consequence, the membrane cut-off can be screened from 1500 to 3500 g.mol(-1).

In situ UV-vis and EXAFS studies of ZnO quantum-sized nanocrystals and Zn-HDS formations from sol-gel route

We have pointed Out that. zinc-based particles obtained from zinc acetate sol-gel route is a mixture of quantum-sized ZnO nanoparticles, zinc acetate, and zinc hydroxide double salt (Zn-HDS). Aiming the knowledge of the mechanisms involved in the formation of ZnO and Zn-HDS phases, the thermohydrolysis of ethanolic zinc acetate solutions induced by lithium hydroxide ([LiOH]/[Zn2+] = 0.1) or water ([H2O]/[Zn2+] = 0.05) addition was investigated at different isothermal temperatures (40, 50, 60 and 70 degrees C) by in situ measurements of turbidity, UV-vis absorption spectra and extended X-ray absorption fine structures (EXAFS). Only the growth of ZnO nanoparticles was observed in sol prepared with LiOH, while a two-step process was observed in that prepared with water addition, leading the fast growth of Zn-HDS and the formation of ZnO nanoparticles at advanced stage. A mechanism of dissolution/reprecipitation governed by the water/ethanol proportion is proposed to account for relative amount of ZnO. (c) 2007 Elsevier Ltd. All rights reserved.

Functionalized silica synthesized by sol-gel process

This work considers some aspects of the chemistry involved in the preparation and description of silicon oxide functionalized by sol-gel process. In this work we studied the synthesis and measured the properties of silicon oxide functionalized with 3-chloropropyl, through a sol-gel process. Thermogravimetic analysis, infrared spectra, and elemental analyses were measured. The samples were prepared in the following proportions of tetraethylorthosilicate (TEOS): 3-chloropropyl trimethoxisilane molar ratio: 1:0, 1:1, 2:1, 3:1 and 4:1. The thermogravimetric data for the resulting materials established the 'minimum formulae' 2:0, 3:1, 4.1, 7:1 and 11:1, respectively. As expected, the relative amount of water is inversely proportional to the presence of propyl groups. Infrared data show Si-C and -CH2-vibration modes at 1250 to 1280 and 2920 to 2940 cm(-1), respectively. Thermogravimetric data and infrared spectra showed that inorganic polymers contained organic polymers. (C) 1999 Elsevier B.V. B.V. All rights reserved.

Synthesis of hybrid silicates containing porphyrins incorporated by a sol-gel process and their properties

Porphyrin was incorporated in a silicate network, via a covalent bond, by grafting a functional group with 3-aminopropyltriethoxysilane, using a sol-gel process. We have carried out the synthesis and measured the absorption spectra, nuclear magnetic resonance spectra, infrared (IR) spectra, luminescence spectra and lifetime of these hybrid silicates, porphyrinosilicas. These samples contained the following free-base porphyrins: meso-tetrakis-p-chlorobenzoylporphyrin, meso-tetrakis-2,6-dichloro-3-chlorosulfonylphenylporphyrin. The obtained porphyrinosilicas have similar absorption and luminescence spectra to the free base porphyrins in solution. IR spectra confirm the formation of monomeric species. Lifetime measurement for porphyrinosilica reveals that 32% +/- 2% of porphyrin is covalently bonded to the silica network. (C) 1999 Elsevier B.V. B.V. All rights reserved.

Electron scattering and effects of sources of light on photoconductivity of SnO2 coatings prepared by sol-gel

Electro-optical properties of sol-gel derived 2 mol% antimony or niobium doped tin dioxide films have been measured. The electron density has been calculated considering all the relevant scattering mechanisms and experimental conductivity data measured in the range -197 to 25 degrees C. The results support the hypothesis that both ionised impurity scattering and grain boundary scattering have comparable effects in the resistivity of coatings, for free electron density congruent to 5 x 10(18) cm(-3). We have measured variation of photoconductivity excitation with wavelength using xenon and deuterium lamp as light sources. Results show that the main band in the photoconductivity spectrum is dependent on the spectral light source emission, the excitation peak reaching 5 eV (deuterium lamp). This band is due to the recombination process involving oxygen species and photogenerated electron-hole pairs. (C) 1999 Elsevier B.V. B.V. All rights reserved.