Preparation of new glass systems by the polymeric precursor method for dental applications

Glass ionomer cements (GICs) are largely employed in Dentistry for several applications, such as luting cements for the attachment of crowns, bridges, and orthodontic brackets as well as restorative materials. The development of new glass systems is very important in Dentistry to improve of the mechanical properties and chemical stability. The aim of this study is the preparation of two glass systems containing niobium in their compositions for use as GICs. Glass systems based on the composition SiO2,Al2O3-Nb2O5-CaO were prepared by chemical route at 700degreesC. The XRD and DTA results confirmed that the prepared materials are glasses. The structures of the obtained glasses were compared to commercial material using FTIR, Al-27 and Si-29 MAS-NMR. The analysis of FTIR and MAS-NMR spectra indicated that the systems developed and commercial material are formed by SiO4 and AlO4 linked tetrahedra. These structures are essential to get the set time control and to have cements. These results encourage further applications of the experimental glasses in the formation of GICs. (C) 2004 Elsevier B.V. All rights reserved.

Evaluation of the Spreading of Isolated Bacterias from Dental Consulting-Room using RAPD Technique

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Accuracy of Mechanical Torque Devices for Implants Used in Brazilian Dental Offices

The purpose of this study was to determine the accuracy of mechanical torque devices in delivering target torque values in dental offices in Salvador, Brazil. A team of researchers visited 16 dental offices, and the clinicians applied torque values (20 and 32 Ncm) to electronic torque controllers. Five repetitions were completed at each torque value and data were collected. When 20 Ncm of torque was used, 62.5% of measured values were accurate (within 10% of the target value). For 32 Ncm, however, only 37.5% of these values were achieved. Several of the tested mechanical torque devices were inaccurate. Int J Prosthodont 2011;24:38-39.

Periosteum-Derived Cells as an Alternative to Bone Marrow Cells for Bone Tissue Engineering Around Dental Implants. A Histomorphometric Study in Beagle Dogs

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Evaluation of dental pulp repair using low level laser therapy (688 nm and 785 nm) morphologic study in capuchin monkeys

The aim of this study was to evaluate the hypothesis that low-level laser therapy (LLLT) 688 nm and 785 nm accelerate dentin barrier formation and repair process after traumatic pulp exposure. The sample consisted of 45 premolars of capuchin monkeys (Cebus apella) with pulp exposure Class V cavities. All premolars were treated with calcium hydroxide (Ca(OH)(2)), divided in groups of 15 teeth each, and analyzed on 7(th), 25(th), and 60(th) day. Group GI - only Ca(OH)(2), GIF- laser 688 nm, and GIII - laser 785 nm. Laser beam was used in single and punctual dose with the parameters: continuous, 688 nm and 785 nm wavelength, tip's area of 0.00785 cm(2), power 50 mW, application time 20 s, dose 255 J/cm(2), energy 2 J. Teeth were capped with Ca(OH)(2), Ca(OH)(2) cement and restored with amalgam. All groups presented pulp repair. on 25(th) day the thickness of the formed dentin barrier was different between the groups GI and GII (p < 0.05) and between groups GI and GIII (p < 0.01). on 60(th) day there was difference between GI and GIII (p < 0.01). It may be concluded that, LLLT 688 nm and 785 nm accelerated dentin barrier formation and consequently pulp repair process, with best results using infrared laser 785 nm. (c) 2009 by Astro Ltd. Published exclusively by WLLEY-VCH Verlag GmbH & Co. KGaA