Effect of different surface treatments on the repair bond strength of indirect composites

Purpose: To evaluate the tensile bond strength of indirect composites repaired with different surface treatments and direct composites. Methods: 180 specimens were prepared with Targis, belleGlass HP and Sculpture indirect composites, light-activated and post-cured according to the manufacturers` recommendations. The specimens were stored in distilled water for 24 hours at 37 degrees C. The bonding surfaces were prepared with air abrasion, hydrofluoric acid or hydrofluoric acid followed by a neutralizing solution. All the treated surfaces were subject to the application of a silane and a bonding agent before the repair procedures with Tetric Ceram and Tetric Flow for the Targis specimens, Herculite XRV and Revolution for the belleGlass HP specimens and Sculp-It and Flow-It for Sculpture specimens. The tensile bond strength tests were carried out using a universal testing machine at cross-head speed of 0.5 mm/minute. The type of fracture was observed under a light microscope at x40 magnification. Data were analyzed by a two-way ANOVA and Tukey`s post-hoc tests (P<0.05). Results: Targis showed a statistically higher repair bond strength than belleGlass HP and Sculpture, which were not significantly different from each other. Air abrasion increased the repair bond strength of belleGlass HP and Sculpture. For Targis, all the surface treatments resulted in similar repair bond strength. The different viscosity of repair composites did not affect the repair of indirect composites. Fractured surfaces showed mostly adhesive failures, mainly with hydrofluoric acid treatment.

Influence of differently oriented dentin surfaces and the regional variation of specimens on adhesive layer thickness and bond strength

Statement of the Problem: Adhesive systems can spread differently onto a substrate and, consequently, influence bonding. Purpose: The purpose of this study was to evaluate the effect of differently oriented dentin surfaces and the regional variation of specimens on adhesive layer thickness and microtensile bond strength (MTBS). Materials and Methods: Twenty-four molars were sectioned mesiodistally to expose flat buccal and lingual halves. Standardized drop volumes of adhesive systems (Single Bond [SB] and Prime & Bond 2.1 [PB2.1]) were applied to dentin according to the manufacturer`s instructions. Teeth halves were randomly divided into groups: 1A-SB/parallel to gravity; 1B-SB/perpendicular to gravity; 2A-PB2.1/parallel to gravity; and 2B-PB2.1/perpendicular to gravity. The bonded assemblies were stored in 37 degrees C distilled water for 24 hours and then sectioned to obtain dentin sticks (0.8 mm(2)). The adhesive layer thickness was determined in a light microscope (x200), and after 48 hours the specimens were subjected to MTBS test. Data were analyzed by one-way and two-way analysis of variance and Student-Newman-Keuls tests. Results: Mean values (MPa +/- SD) of MTBS were: 39.1 +/- 12.9 (1A); 32.9 +/- 12.4 (1B); 52.9 +/- 15.2 (2A); and 52.3 +/- 16.5 (2B). The adhesive systems` thicknesses (mu m +/- SD) were: 11.2 +/- 2.9 (1A); 18.1 +/- 7.3 (1B); 4.2 +/- 1.8 (2A); and 3.9 +/- 1.3 (2B). No correlation between bond strength and adhesive layer thickness for both SB and PB2.1 (r = -0.224, p = 0.112 and r = 0.099, p = 0.491, respectively) was observed. Conclusions: The differently oriented dentin surfaces and the regional variation of specimens on the adhesive layer thickness are material-dependent. These variables do not influence the adhesive systems` bond strength to dentin. CLINICAL SIGNIFICANCE Adhesive systems have different viscosities and spread differently onto a substrate, influencing the bond strength and also the adhesive layer thickness. Adhesive thickness does not influence dentin bond strength, but it may impair adequate solvent evaporation, polymer conversion, and may also determine water sorption and adhesive degradation over time. In the literature, many studies have shown that the adhesive layer is a permeable membrane and can fail over timebecause ofits continuous plasticizing and degradation when in contact with water. Therefore, avoiding thick adhesive layers may minimize these problems and provide long-term success for adhesive restorations.

Evaluation of proximal caries in images resulting from different modes of radiographic digitalization

Objective: The aim of this study was to evaluate the performances of observers in diagnosing proximal caries in digital images obtained from digital bitewing radiographs using two scanners and four digital cameras in Joint Photographic Experts Group (JPEG) and tagged image file format (TIFF) files, and comparing them with the original conventional radiographs. Method: In total, 56 extracted teeth were radiographed with Kodak Insight film (Eastman Kodak, Rochester, NY) in a Kaycor Yoshida X-ray device (Kaycor X-707;Yoshida Dental Manufacturing Co., Tokyo, Japan) operating at 70 kV and 7 mA with an exposure time of 0.40 s. The radiographs were obtained and scanned by CanonScan D646U (Canon USA Inc., Newport News, VA) and Genius ColorPage HR7X (KYE Systems Corp. America, Doral, FL) scanners, and by Canon Powershot G2 (Canon USA Inc.), Canon RebelXT (Canon USA Inc.), Nikon Coolpix 8700 (Nikon Inc., Melville, NY), and Nikon D70s (Nikon Inc.) digital cameras in JPEG and TIFF formats. Three observers evaluated the images. The teeth were then observed under the microscope in polarized light for the verification of the presence and depth of the carious lesions. Results: The probability of no diagnosis ranged from 1.34% (Insight film) to 52.83% (CanonScan/JPEG). The sensitivity ranged from 0.24 (Canon RebelXT/JPEG) to 0.53 (Insight film), the specificity ranged from 0.93 (Nikon Coolpix/JPEG, Canon Powershot/TIFF, Canon RebelXT/JPEG and TIFF) to 0.97 (CanonScan/TIFF and JPEG) and the accuracy ranged from 0.82 (Canon RebelXT/JPEG) to 0.91 (CanonScan/JPEG). Conclusion: The carious lesion diagnosis did not change in either of the file formats (JPEG and TIFF) in which the images were saved for any of the equipment used. Only the CanonScan scanner did not have adequate performance in radiography digitalization for caries diagnosis and it is not recommended for this purpose. Dentomaxillofacial Radiology (2011) 40, 338-343. doi: 10.1259/dmfr/67185962

Audiology in Brazil

The profession of audiology took root in Brazil nearly a half a century ago and has since blossomed into a flourishing, well-developed field. Currently, audiologists in Brazil work at private institutions, including private medical practices and dedicated speech and hearing clinics. They are also employed in a wide array of public institutions, including community clinics, elementary schools, colleges, and universities. In both the private sector and health clinics, audiologists perform diagnostic evaluations of auditory and vestibular disorders, select and fit hearing aids, and provide aural rehabilitation. At the public level, they assist with workers` health programs, dispense hearing aids, and aural rehabilitation. There is always room to grow, however, and the future of audiology in Brazil holds both challenges and opportunity. The following article will sketch the development of audiology training and practice in Brazil, provide a picture of how the field stands today, and summarize the unique challenges which the profession faces in this large and diverse nation.

An electron microscopic study of nickel sulfide inclusions in toughened glass

It has been known since the early sixties that nickel sulfide inclusions cause spontaneous fracture of toughened (thermally tempered) glass, but despite the considerable amount of work done on this problem in the last four decades, failures still occur in the field with regularity. In this study we have classified (by viewing through a 60x optical microscope) inclusions into two groups, which are classic and atypical nickel sulfides. The classics look like the nickel sulfide inclusions found at the initiation-of-fracture of windows that have broken spontaneously. We have compared the structure and composition of the atypical inclusions with the structure and composition of the classics. All of the classic and atypical nickel sulfide inclusions studied in this work were found to have a composition in the range of Ni52S48 to Ni48S52. Inclusions on the nickel rich side of stoichiometric NiS were found to be two-phase assemblies, and inclusions on the sulphur rich side of NiS were single phase. It had been proposed that the atypicals were passive, and of a different composition to the classics. However, we found that the difference between passive and dangerous nickel sulfide inclusions was not a difference in composition but rather a difference in the type of material in the internal pore space. The passive's had carbon char in their internal pore space, whereas the pore space of dangerous inclusions contained Na2O. The presence of Na2O and carbon char with the inclusions indicates that the formation of the inclusions results from a reaction of a nickel-rich phase with sodium sulphate and carbon. (C) 2001 Kluwer Academic Publishers.

A nanometre-scale non-periodic structural variation in high temperature superconducting ceramics and the implications for properties

Non-periodic structural variation has been found in the high T-c cuprates, YBa2Cu3O7-x and Hg0.67Pb0.33Ba2Ca2Cu3O8+delta, by image analysis of high resolution transmission electron microscope (HRTEM) images. We use two methods for analysis of the HRTEM images. The first method is a means for measuring the bending of lattice fringes at twin planes. The second method is a low-pass filter technique which enhances information contained by diffuse-scattered electrons and reveals what appears to be an interference effect between domains of differing lattice parameter in the top and bottom of the thin foil. We believe that these methods of image analysis could be usefully applied to the many thousands of HRTEM images that have been collected by other workers in the high temperature superconductor field. This work provides direct structural evidence for phase separation in high T-c cuprates, and gives support to recent stripes models that have been proposed to explain various angle resolved photoelectron spectroscopy and nuclear magnetic resonance data. We believe that the structural variation is a response to an opening of an electronic solubility gap where holes are not uniformly distributed in the material but are confined to metallic stripes. Optimum doping may occur as a consequence of the diffuse boundaries between stripes which arise from spinodal decomposition. Theoretical ideas about the high T-c cuprates which treat the cuprates as homogeneous may need to be modified in order to take account of this type of structural variation.

Fatigue and damage accumulation of veneer porcelain pressed on Y-TZP

Objectives: This study compared the reliability and fracture patterns of zirconia cores veneered with pressable porcelain submitted to either axial or off-axis sliding contact fatigue. Methods: Forty-two Y-TZP plates (12 mm x 12 mm x 0.5 mm) veneered with pressable porcelain (12 mm x 12 mm x 1.2 mm) and adhesively luted to water aged composite resin blocks (12 mm x 12 mm x 4 mm) were stored in water at least 7 days prior to testing. Profiles for step-stress fatigue (ratio 3:2:1) were determined from single load to fracture tests (n = 3). Fatigue loading was delivered on specimen either on axial (n = 18) or off-axis 30 degrees angulation (n = 18) to simulate posterior tooth cusp inclination creating a 0.7 mm slide. Single load and fatigue tests utilized a 6.25 mm diameter WC indenter. Specimens were inspected by means of polarized-light microscope and SEM. Use level probability Weibull curves were plotted with 2-sided 90% confidence bounds (CB) and reliability for missions of 50,000 cycles at 200 N (90% CB) were calculated. Results: The calculated Weibull Beta was 3.34 and 2.47 for axial and off-axis groups, respectively, indicating that fatigue accelerated failure in both loading modes. The reliability data for a mission of 50,000 cycles at 200 N load with 90% CB indicates no difference between loading groups. Deep penetrating cone cracks reaching the core-veneer interface were observed in both groups. Partial cones due to the sliding component were observed along with the cone cracking for the off-axis group. No Y-TZP core fractures were observed. Conclusions: Reliability was not significantly different between axial and off-axis mouth-motion fatigued pressed over Y-TZP cores, but incorporation of sliding resulted in more aggressive damage on the veneer. (C) 2009 Elsevier Ltd. All rights reserved.

The influence of storage condition and duration on the resistance to fracture of different fiber post systems

Purpose: To evaluate the effects of storage condition and duration on the resistance to fracture of different fiber post systems (and to morphologically assess the post structure before and after storage. Methods: Three types of fiber posts (DT Light Post, GC Post, FRC Postect Plus) were divided in different groups (n=12) according to the storage condition (dry at 37 degrees C; saline water at 37 degrees C; mineral oil at 37 degrees C and storage inside the roots of extracted human teeth immersed in saline water at 37 degrees C and duration (6, 12 months). A universal testing machine loading at a 90 degrees angle was employed for the three-point bending test. The test was carried out until fracture of the post. A 3-way ANOVA and Tukey`s test (alpha= 0.05) were used to compare the effect of the experimental factors on the fracture strength. Two posts of each group were observed before and after the storage using a scanning electron microscope. Results: Storage condition and post type had a significant effect on post fracture strength (P< 0.05). The interaction between these factors was significant (P< 0.05). Water storage significantly decreased the fracture strength, regardless of the post type and the storage duration. Storage inside roots, in oil, and at dry conditions did not significantly affect post fracture strength. SEM micrographs revealed voids between fibers and resin matrix for posts stored in water. Posts stored under the other conditions showed a compact matrix without porosities. (Am J Dent 2009;22:366-370).

Post space debridement in oval-shaped canals: The use of a new ultrasonic tip with oval section

This study evaluates the effect on post space debridement in oval-shaped canals of an experimental ultrasonic tip with oval section (Satelec) compared with a circular ultrasonic tip (KaVo). Thirty teeth with an oval-shaped canal were endodontically treated and obturated and then randomly divided into 3 groups (n = 10) according to the procedure used for post space debridement: Satelec tip, Largo #2 drill + KaVo file, and Largo #2 drill + water. Debris and dentin tubules were evaluated by assigning scores to scanning electron microscope post spaces images; lower scores corresponded to fewer debris and higher number of open tubules. The Satelec group showed significantly lower debris and open tubules scores than KaVo group (p < .05) and control group (p < .05), which differed significantly between each other (p < .05). Also the debris and open tubules scores in different post space regions differed significantly among the experimental groups (p < .001). The oval ultrasonic tip resulted in a better post space debridement than a circular ultrasonic tip in oval-shaped canals.

Microtensile vs Microshear Bond Strength of All-in-One Adhesives to Unground Enamel

Purpose To determine the bond strength to unground enamel of all in one adhesives in comparison with an etch and rinse system and to compare the reliability of microtensile and microshear methods in providing such measurements Materials and Methods The bonding procedure was performed on enamel of 64 extracted molars The tested all in one adhesives were Bond Force (Tokuyama), AdheSE One (Ivoclar Vivadent) and Xeno V (Dentsply) Prime&Bond NT (Dentsply) served as control Microtensile specimens were obtained from 4 teeth per group Twelve teeth per group were used for microshear testing Microtensile specimens that failed prior to testing were included in statistical calculations, they were assigned the lowest value measured in the respective group Failure modes were observed under light microscope and classified (cohesive within substrates, adhesive mixed) Statistically significant differences in bond strength were assessed among the adhesives within each testing method and between microshear and microtensile data for each adhesive Failure mode distributions were compared using the chi square test Results All in-one adhesives had similar microshear and microtensile bond strengths In both testing methods, the etch and rinse system achieved the strongest bond For all adhesives significantly higher bond strengths were measured with the microshear test In microtensile testing specimens bonded with the etch and rinse adhesive exhibited a significantly different distribution of failure modes The coefficients of variation were extremely high for microtensile bond strength data, particularly of all in one adhesives Conclusion The adhesive potential to intact enamel of recently introduced all in-one adhesives was inferior to that of an etch and rinse system When testing bond strength to enamel of all in one adhesives, microshear testing may be a more accurate method than microtensile

Influence of Antiplatelet Drugs in the Pathogenesis of Experimental Periodontitis and Periodontal Repair in Rats

Background: Platelets contain an array of biologic mediators that can modulate inflammation and repair processes including proinflammatory mediators and growth factors. Previous studies have shown that periodontitis and periodontal repair are associated with platelet activation. We hypothesized that drug-induced platelet inactivation may interfere in the processes of inflammation and repair in experimental periodontitis in rats by suppressing the release of biologic mediators from platelets to the site of injury. Methods: To measure the effects on periodontitis, ligatures were placed around first molars, and aspirin (Asp, 30 mg/kg) or clopidogrel (Clo, 75 mg/kg) was given intragastrically once daily for 15 days. Interleukin-6 (IL-6), tumor necrosis factor-a (TNF-alpha), and thromboxane A(2) levels were measured by enzyme-linked immunosorbent assay. To evaluate the effects of antiplatelet drugs on periodontal repair, ligatures were removed after 15 days of periodontitis induction, and Asp or Clo were administered beginning the following day for 15 days. Periodontal repair was assessed by microcomputed tomography. Results: On periodontitis phase, Asp and Clo significantly reduced levels of TNF-alpha and II-6 (P < 0.05), but only Asp decreased thromboxane A(2) (P < 0.05). Asp and Clo decreased inflammatory infiltration; however, this reduction was more pronounced with Clo treatment (P < 0.05). Histometric analysis showed that Asp and Clo impaired alveolar bone resorption. During the repair phase and after removal of the ligatures, microcomputed tomography analysis demonstrated that treatment with Asp and Clo did not impair alveolar bone repair. Conclusion: Systemic administration of Asp and Clo attenuates the inflammation associated with periodontitis without affecting the repair process when stimulus is removed. J Periodontol 2011;82:767-777.

Evaluation of physicochemical properties of four root canal sealers

P>Aim To assess the physicochemical properties and the surface morphology of AH Plus, GuttaFlow, RoekoSeal and Activ GP root canal sealers. Methodology Five samples of each material were evaluated for setting time, dimensional alteration, solubility and radiopacity tests, according to ANSI/ADA Specification 57. A total of 50 mL of deionized distilled water from the solubility tests were used to measure the metal solubility by atomic absorption spectrometry. The morphologies of the external surface and the cross-section of the samples were analysed by means of a scanning electron microscope (SEM). Statistical analysis was performed by using one-way anova and post hoc Tukey-Kramer tests with the null hypothesis set as 5%. Results AH Plus had the longest setting time (580.6 +/- 3.05 min) (P < 0.05). Activ GP did not have a mean value on the radiopacity and solubility tests (1.31 +/- 0.35 mm and 11.8 +/- 0.43%, respectively) in accordance with ANSI/ADA, being significantly different from the other materials (P < 0.05), which had mean values for these tests in accordance with the ADA`s requirements. GuttaFlow was the only sealer that conformed to the Specification 57 concerning the dimensional alteration test (0.44 +/- 0.16%) (P < 0.05). The spectrometry test revealed significant Ca2+, K+, Zn2+ ion release from Activ GP sealer (32.57 +/- 5.0, 1.57 +/- 0.22 and 8.20 +/- 1.74 mu g mL-1, respectively). In SEM analysis, the loss of matrix was evident and the filler particles were more distinguishable in all groups. Conclusions The setting time of all sealers was in accordance with ANSI/ADA`s requirements. Activ GP did not fulfill ANSI/ADA`s protocols regarding radiopacity, dimensional alteration and solubility. GuttaFlow was the only sealer that conformed to the Specification 57 in all tests. SEM analysis revealed that the surfaces of all sealers had micromorphological changes after the solubility test.

Influence of the irradiation distance and the use of cooling to increase enamel-acid resistance with Er:YAG laser

Objectives: The aim of this study was to assess the influence of irradiation distance and the use of cooling in the Er:YAG laser efficacy in preventing enamel demineralization. Methods: 84 enamel blocks were randomly assigned to seven groups (n = 12): G1: control group - no treatment, G2-G7: experimental groups treated with Er:YAG laser (80 mJ/2 Hz) at different irradiation distances with or without cooling: G2: 4 mm/2 mL; G3: 4 mm/no cooling; G4: 8 mm/2 mL; G5: 8 mm/no cooling; G6: 16 mm/2 mL; G7: 16 mm/no cooling. The samples were submitted to an in vitro pH cycles for 14 days. Next, the specimens were sectioned in sections of 80-100 mu m in thickness and the demineralization patterns of prepared slices were assessed using a polarized light microscope. Three samples from each group were analyzed with scanning electronic microscopy. Analysis of variance and the Fisher test were performed for the statistical analysis of the data obtained from the caries-lesion-depth measurements (CLDM) (alpha = 5%). Results: The control group (CLDM = 0.67 mm) was statistically different from group 2 (CLDM = 0.42 mm), which presented a smaller lesion depth, and group 6 (0.91 mm), which presented a greater lesion depth. The results of groups 3 (CLDM = 0.74 mm), 4 (CLDM = 0.70 mm), 5 (CLDM = 0.67 mm) and 7 (CLDM = 0.89 mm) presented statistical similarity. The scanning electronic microscopy analysis showed ablation areas in the samples from groups 4, 5, 6 and 7, and a slightly demineralized area in group 2. Conclusions: It was possible to conclude that Er:YAG laser was efficient in preventing enamel demineralization at a 4-mm irradiation distance using cooling. (C) 2010 Elsevier Ltd. All rights reserved.

Composite filling removal with erbium:yttrium-aluminum-garnet laser: morphological analyses

Considering the increase in esthetic restorative materials and need for improvement in unsatisfactory restoration substitution with minimal inadvertent removal of healthy tissues, this study assessed the efficacy of erbium:yttrium-aluminum-garnet (Er:YAG) laser for composite resin removal and the influence of pulse repetition rate on the morphological analyses of the cavity by scanning electron microscope. Composite resin fillings were placed in cavities (1.0 mm deep) prepared in bovine teeth, and the 75 specimens were randomly assigned to five groups according to the technique used for composite filling removal (high-speed diamond bur, group I, as a control, and Er:YAG laser, 250 mJ output energy and 80 J/cm(2) energy density, using different pulse repetition rates: group II, 2 Hz; group III, 4 Hz; group IV, 6 Hz; group V, 10 Hz). After the removal, the specimens were split in the middle, and we analyzed the surrounding and deep walls to check for the presence of restorative material. The estimation was qualitative. The surfaces were examined with a scanning electron microscope. The results revealed that the experimental groups presented bigger amounts of remaining restorative material. The scanning electron microscopy (SEM) analyses showed irregularities of the resultant cavities of the experimental groups that increased proportionally with increase in repetition rate.

A comparative study of physicochemical properties of AH Plus, Epiphany, and Epiphany SE root canal sealers

P>Aim To assess the physicochemical properties and the surface morphology of AH Plus, Epiphany, and Epiphany SE root canal sealers. Methodology Five samples of each material were employed for each test according to ANSI/ADA specification 57. The samples were assigned to four groups: (i) AH Plus; (ii) Epiphany; (iii) Epiphany + Thinning Resin; (iv) Epiphany SE. The distilled water used during the solubility test was submitted to spectrometry to verify the release of calcium ions. The morphologies of the external surface and the cross-section of the samples were analysed by means of a scanning electron microscope (SEM). Statistical analysis was performed by using One-Way anova and post hoc Tukey-Kramer tests with the null hypothesis set as 5%. Results Setting time, flow and radiopacity results were in accordance with ANSI/ADA requirements whereas the dimensional change of all sealers and solubility of Epiphany did not fulfil ANSI/ADA protocols. AH Plus and Epiphany SE were similar in terms of flow, radiopacity, solubility and dimensional change. The spectrometry test revealed significant calcium ion release from Epiphany with and without the thinning resin. SEM analysis revealed essentially a homogeneous surface with compact layer and some rough areas. Conclusions Setting time, flow, and radiopacity tests conformed to ANSI/ADA standardization. The dimensional change in all groups and the solubility of Epiphany were greater than values considered acceptable, with higher amounts of calcium ion release. Epiphany SE revealed more organized, compacted, and homogeneous polymers in a reduced resin matrix when compared with the other groups.