Enhanced electrical property of nanostructured Sb-doped SnO2 thin film processed by soft chemical method

The effect of the Sb addition on the microstructural and electrical conductivity of the SnO2 thin film was studied in this work. Experimental results show that the Sb addition allowed to control the grain size and electrical conductivity of the SnO2 thin film, resulting in a nanostructured material. The nanostructured Sb-doped SnO2 thin films present high electrical conductivity, even in the presence of high porosity, supporting the hypothesis that nanostructured material must possess strong electrical conductivity. This work involves important aspects that can be applied to the development of high performance transparent conducting thin film. (C) 2003 Elsevier B.V. All rights reserved.

Electrical characterization of lanthanum-modified bismuth titanate thin films obtained by the polymeric precursor method

Lanthanum-modified bismuth titanate, Bi4-xLaxTi3O12 (BLT), thin films with a La concentration ranging from 0 to 0.75 were grown on Pt/Ti/SiO2/Si substrates using a polymeric precursor solution and spin-coating method. The scanning electron microscopy shows a change of morphology with increasing the lanthanum concentration. The BLT films show well-saturated polarization-electric field curves whit remnant polarizations of 14.7, 20.5, 21.5, and 20.4 muC/cm(2) for x = 0, 0.25, 0.50 and 0.75, respectively. The dielectric constant of BLT (x = 0.75 mol% La) is equal to 158 while dielectric loss remain low (tandelta = 0.0018).

Drude's model calculation rule on electrical transport in Sb-doped SnO2 thin films, deposited via sol-gel

The evaluation of free carrier concentration based on Drude's theory can be performed by the use of optical transmittance in the range 800-2000 nm (near infrared) for Sb-doped SnO2 thin films. In this article, we estimate the free carrier concentration for these films, which are deposited via sol-gel dip-coating. At approximately 900 mn, there is a separation among transmittance curves of doped and undoped samples. The plasma resonance phenomena approach leads to free carrier concentration of about 5 x 1020 cm(-3). The increase in the Sb concentration increases the film conductivity; however, the magnitude of measured resistivity is still very high. The only way to combine such a high free carrier concentration with a rather low conductivity is to have a very low mobility. It becomes possible when the crystallite dimensions are taken into account. We obtain grains with 5 nm of average size by estimating the grain size from X-ray diffraction data, and by using line broadening in the diffraction pattern. The low conductivity is due to very intense scattering at the grain boundary, which is created by the presence of a large amount of nanoscopic crystallites. Such a result is in accordance with X-ray photoemission spectroscopy data that pointed to Sb incorporation proportional to the free electron concentration, evaluated according to Drude's model. (c) 2006 Elsevier Ltd. All rights reserved.

The effect of microwave annealing on the electrical characteristics of lanthanum doped bismuth titanate films obtained by the polymeric precursor method

Lanthanum doped bismuth titanate thin films (Bi3.25La0.75Ti3O12-BLT) were produced by the polymeric precursor method and crystallized in a domestic microwave oven and in conventional furnace. Using platinum coated silicon substrates configuration, ferroelectric properties of the films were determined with remanent polarization P-r and a coercive field E-c of 3.9 mu C/cm(2) and 70 kV/cm for the film annealed in the microwave oven and 20 mu C/cm(2) and 52 kV/cm for the film annealed in conventional furnace, respectively. The films annealed in conventional furnace exhibited excellent retention-free characteristics at low infant periods indicating that BLT thin films can be a promise material for use in nonvolatile memories. on the other hand, the pinning of domains wall causes a strong decay at low infant periods for the films annealed in the microwave furnace which makes undesireable the application for future FeRAMS memories. (c) 2005 Elsevier B.V. All rights reserved.

Influence of Ta2O5 on the electrical properties of ZnO- and CoO-doped SnO2 varistors

SnO2-based varistors doped with 0.5% cobalt, 0.5% zinc and various tantalum amounts were prepared by the solid-state route. Experimental evidence shows that small quantities of Ta2O5 improve the nonlinear properties of the samples significantly. It was found that samples doped with 0.05 mol% Ta2O5 exhibit the highest density (98.5%), the lowest electric breakdown field (E-b = 1050 V/cm) and the highest coefficient of nonlinearity (alpha = 11.5). The effect of Ta2O5 dopant could be explained by the substitution of Ta5+ by Sn4+. (C) 2004 Elsevier Ltd and Techna S.r.l. All rights reserved.