Oxidative destruction of chlorobenzene and o-dichlorobenzene on a highly active catalyst: MnOx/TiO2-Al2O3

A highly active catalyst, MnOx/TiO2-Al2O3, was prepared by impregnating MnOx species on TiO2-modified Al2O3. The TiO2 species in TiO2-Al2O3 support is in a monolayer dispersion, and the MnOx species is again highly dispersed on TiO2-Al2O3 Support. The total oxidation of chlorobenzene and o-dichlorobenzene on MnOx/TiO2-Al2O3 catalyst can be achieved at 300 degreesC and 250 degreesC respectively, at the space velocity of 8000 h(-1). The activity of MnOx/TiO2-Al2O3 catalyst (Mn loading 11.2 wt%) is gradually increased in the first 10-20 h and then keeps stable at least for the measured 52 h at 16,000 h(-1). Furthermore, no chlorinated organic byproducts are detected in the effluent during the oxidative destruction of chlorobenzene and o-dichlorobenzene. It is proposed that the partially chlorinated and highly dispersed manganese oxide on a monolayer TiO2-modified Al2O3 is responsible for the high and stable activity for the total oxidation of chlorinated aromatics. (C) 2001 Academic Press.

Catalytic oxidation of chlorobenzene on supported manganese oxide catalysts

Total oxidation of chlorinated aromatics on supported manganese oxide catalysts was investigated. The catalysts have been prepared by wet impregnation method and characterized by XRD and TPR. Among the catalysts with the supports of TiO(2), Al(2)O(3) and SiO(2), titania supported catalyst (MnO(x)/TiO(2)) gives the highest catalytic activity. MnO(x)/TiO(2) (Mn loading, 1.9 wt.%) shows the total oxidation of chlorobenzene at about 400 degreesC. The activity can be stable for over 82 h except for the first few hours. At lower Mn loadings for MnO(x)/TiO(2), only one reduction peak appears at about 400 degreesC due to the highly dispersed manganese oxide. With the increase of Mn loading, another reduction peak emerges at about 500 degreesC, which is close to the reduction peak of bulk Mn(2)O(3) at 520 degreesC. TPR of the used catalyst is totally different from that of the fresh one indicating that the chemical state of the active species is changed during the chlorobenzene oxidation. The characterization studies of MnO(x)/TiO(2) showed that the highly dispersed MnO(x) is the precursor of the active phase, which can be converted into the active phase, mainly oxychlorinated manganese (MnO(y)Cl(z)), under working conditions of chlorobenzene oxidation. (C) 2001 Elsevier Science B.V. All rights reserved.