The influence of thermal treatment on the preparation of PNM and PMN-PT thin films

Ferroelectric thin films belong to a class of materials with great technological importance in optic fibers, micro-electromechanical systems, and microprocessors and computers memories.The (1-x)PbMg1/3Nb2/3O3(x)PbTiO3 (PMN-PT) thin films, with x=0, 0.1, 0.35 and 0.5, were prepared by Pechini's process and deposited by spin-coating on Si(100), Pt/Ti/SiO2/Si(100) and quartz substrates. The goal of the present paper is to verify the thermal treatment influence on the perovskite phase formation, which is desirable for these applications. The phase formation was analyzed by X-ray diffraction. The film's surface was characterized by atomic force microscopy to analyze the roughness and the homogeneity. The results of this study indicate that the optimum conditions for obtaining the perovskite phase using a Pt/Ti/SiO2/Si(100) substrate, were drying each deposited layer at 140 degreesC (heating plate), and a final thermal treatment at 600 degreesC for 3 h in a closed system with a lead-rich atmosphere. (C) 2003 Elsevier B.V. All rights reserved.

Electrical properties of lanthanum doped Bi4Ti3O12 thin films annealed in different atmospheres

Pure-and lanthanun doped Bi4Ti3O12 thin films were deposited on Pt/Ti/SiO2/Si substrate using a polymeric precursor solution. Annealing in static air and oxygen atmosphere was performed at 700 degrees C for 2 h. The obtained films were characterized by X-ray diffraction and atomic force microscopy. The dielectric constant and dissipation factor were measured in the frequency region from 1 kHz to 1 MHz. Electrical characterization of the films pointed to ferroelectricity via hysteresis loop. Films annealed in static air possess a dielectric constant higher than films annealed in oxygen atmosphere due to differences in the grain size, crystallinity and structural defects. A regularly shaped hystereses loop is observed after annealing in static air. The obtained results suggest that the annealing in oxygen atmosphere can increase the trapped charge and the relaxation phenomenon. (c) 2006 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Combined experimental and theoretical investigations of the photoluminescent behavior of Ba(Ti,Zr)O-3 thin films

The correlation between experimental data and theoretical calculations have been investigated to explain the photoluminescence at room temperature of Ba(Ti0.75Zr0.25)O-3 (BTZ) thin films prepared by the polymeric precursor method. The degree of structural order-disorder was investigated by X-ray diffraction, Fourier transform infrared spectroscopy, ultraviolet-visible absorption spectroscopy and photoluminescence (PL) measurements. First-principles quantum mechanical calculations based on density functional theory (B3LYP level) were employed to study the electronic structure of ordered and deformed asymmetric models. The electronic properties are analyzed and the relevance of the present theoretical and experimental results on the PL behavior is discussed. The presence of localized electronic levels and a charge gradient in the band gap due to a break in symmetry, are responsible for the PL in disordered BTZ lattice. (c) 2007 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Influence of viscosity and ionic concentration on morphology of PLZT thin films

PLZT thin films were prepared by a dip-coating process using Pechini's method. The PLZT solution was obtained from the mixture of the cation solutions. The viscosity of the solution was adjusted in the range of 20-40 cP, while the ionic concentration was adjusted in the range of 0.1 and 0.2 M. PLZT solutions were deposited on Si (1 0 0) substrate with withdrawal speed at 5 mm/min. The coated substrates were thermally treated with heating rate of 1 degreesC/min up to 300 and 5 degreesC/ min up to 650 degreesC in order to obtain homogeneous and crack free films. The influence of viscosity and ionic concentration on crystallization and morphology of PLZT (9/65/35) thin film will be discussed. (C) 2001 Elsevier B.V. B.V. All rights reserved.

Influence of oxygen atmosphere on crystallization and properties of LiNbO3 thin films

Thin films of lithium niobate were deposited on the Pt/Ti/SiO2 (111) substrates by spin coating from the polymeric precursor method (Pechini process). Annealing in static air and oxygen atmosphere was performed at 500 degreesC for 3 h. The films obtained were characterized by X-ray diffraction, scanning electron microscopy and transmission electron microscopy. The dielectric constant and dissipation factor were measured in frequency region from 10 Hz to 10 MHz. Electrical characterization of the films pointed to ferroelectricity via hysteresis loop. The influence of oxygen atmosphere on crystallization, morphology and properties of LiNbO3 thin films is discussed. (C) 2003 Elsevier Ltd. All rights reserved.

Characterization of lanthanum-doped bismuth titanate thin films prepared by polymeric precursor method

Lanthanum-modified bismuth titanate, Bi4-xLaxTi3O12 (BLT), with x ranging from 0 to 0.75 was grown on Pt/Ti/SiO2/Si substrates using a polymeric precursor solution and spin-coating method. The dielectric constant of highly doped bismuth titanate was equal to 148 while dielectric losses remained low (tan delta = 0.0018), and the films showed well-saturated polarization-electric field curves (2P(r) = 40.6 muC/cm(2) and V-c = 0.99 V). The leakage current densities improve for the lanthanum-doped system. For five-layered BLT films with x = 0.75, a charge storage density of 35 fC/mum(2) and a thickness of 320 nm were found. (C) 2004 Elsevier B.V. All rights reserved.