Influence of membrane-solution interface on the selectivity of SnO2 ultrafiltration membranes

SnO2 supported membranes, presenting 3.0 nm average pore size, have been produced by sol casting on alumina tubular substrate using aqueous colloidal suspensions prepared by sol-gel route. The selectivity and flux throughout SnO2 membrane were analyzed by permeation experiments, using a laboratory tangential filtration pilot equipped with a monotubular membrane. To evaluate the effect of the surface charge at the membrane-solution interface, aqueous salt solutions (NaCl, Na2SO4, CaCl, and CaSO4) of different ionic strength have been filtered and the results correlated with the values of zeta potential measured at several pH. The results show that the retention coefficient is dependent on the electrolyte present in aqueous solution decreasing as: (dication, monoanion) > (monocation, monoanion) approximate to (monocation, dianion) > (dication, dianion). The surface charge and the cation adsorption capacity play a determinant role in these selectivity sequences. (C) 2001 Elsevier B.V. B.V. All rights reserved.

Spatial distribution of solutes and water in sucrose solution dehydrated apples

Half-fresh apples were immersed in sucrose solution (50% w/w, 27 degrees C) during different times of exposition (2, 4, and 8 h). Then each fruit was sliced from the transversal exposed surface. Density, water, and sugar content were determined for each slice. A mathematical model was fitted to experimental data of water and sucrose content considering the global flux and the tissue shrinkage. By numerical analysis, the binary effective diffusion coefficients as a function of concentration were calculated, using material coordinates and integrating simultaneously two differential equations (for water and sucrose). The coefficients obtained are one or even two orders of magnitude lower than the ones for pure solutions and present an unusual concentration dependence. This comparison shows the influence of the tissue resistance to the diffusion.

Synthesis, ferroelectric and optical properties of (Pb,Ca)TiO3 thin films by soft solution processing

Calcium modified lead titanate sol was synthesized using a soft solution processing, the so-called polymeric precursor method. In soft chemistry method, soluble precursors such as lead acetate trihydrate, calcium carbonate and titanium isopropoxide, as starting materials, were mixed in aqueous solution. Pb0.7Ca0.3TiO3 thin films were deposited on platinum-coated silicon and quartz substrates by means of the spinning technique. The surface morphology and crystal structure, dielectric and optical properties of the thin films were investigated. The electrical measurements were conducted on metal-ferroelectric-metal (MFM) capacitors. The typical measured small signal dielectric constant and dissipation factor at a frequency of 100 kHz were 299 and 0.065, respectively, for a thin film with 230 nm thickness annealed at 600degreesC for 2 h. The remanent polarization (2P(r)) and coercive field (E-c) were 32 muC/cm(2) and 100 kV/cm, respectively. Transmission spectra were recorded and from them, refractive index, extinction coefficient, and band gap energy were calculated. Thin films exhibited good optical transmissivity, and had optical direct transitions. The present study confirms the validity of the DiDomenico model for the interband transition, with a single electronic oscillator at 6.858 eV. The optical dispersion behavior of PCT thin film was found to fit well the Sellmeir dispersion equation. The band gap energy of the thin film, annealed at 600degreesC, was 3.56 eV. The results confirmed that soft solution processing provides an inexpensive and environmentally friendly route for the preparation of PCT thin films.