高硅氧发光玻璃的制备及其荧光性能

abstract {Silica glass is an attractive host matrix for the emission ions of rare earth and transition metal ions because it has small thermal expansion coefficient, strong thermal resistance, large fracture strength and good chemical durability and so on. However, a major obstacle to using it as the host matrix is a phenomenon of concentration quenching. In this paper, we introduces a novel method to restrain the concentration quenching by using a porous glass with SiO₂ content > 95% (in mass) and prepare intense fluorescence high-SiO₂ glasses and high-SiO₂ laser glass. The porous glass with high-SiO₂ content was impregnated with rare-earth and transition metal ions, and consequently sintered into a compact non-porous glass in reduction or oxidization atmospheres. Various intense fluorescence glasses with high emission yields, a vacuum ultraviolet-excited intensely luminescent glass, high silica glass containing high concentration of Er³⁺ ion, ultrabroad infrared luminescent Bi-doped high silica glass and Nd³⁺-doped silica microchip laser glass were obtained by this method. The porous glass is also favorable for co-impregnating multi-active-ions. It can bring effective energy transferring between various active ions in the glass and increases luminescent intensity and extend range of excitation spectrum. The luminescent active ions-doped high-SiO₂ glasses are potential host materials for high power solid-state lasers and new transparent fluorescence materials.}

钕离子掺杂和钕铝共掺高硅氧玻璃的光谱性质研究

Nd-doped and Nd-Al-codoped high silica glasses were obtained by sintering porous glass impregnated with Nd3+ and Al3+ ions. The absorption, fluorescence spectra and fluorescence lifetime of Nd-doped and Nd-Al-codoped high silica glasses were measured. The intensity parameters Omega(1), ( t = 2, 4, 6), fluorescence lifetime, radiative quantum efficiency and stimulated emission cross section were calculated by Judd-Ofelt theory. The effect of aluminum codoping on the fluorescence and structural properties of Nd-doped silica glass has been discussed. By comparing the spectroscopic properties with other Nd-doped oxide glasses and commercial silicate glasses, this Nd-doped high silica glass is likely to be a promising laser material for use in high power and high repetition rate lasers.

热处理对共沉淀法制备YAG纳米粉体性能的影响

以Al（NO3）3和Y（NO3）3为原料，采用共沉淀法制备出粒度大小为60-100nm，颗粒呈球形的纯相YAG纳米粉。研究了前驱物在不同条件下热处理对YAG纳米粉体性能的影响，并对前驱物在焙烧过程中的物相变化进行了观察。发现延长前驱物在低温下的干燥时间会导致晶粒尺寸增大，而采用在晶化温度前后分别进行保温的方法可在较低的温度获得纯相的YAG粉体。对比了焙烧温度和保温时间对产物粒度的影响，结果表明：在保证粉体晶化完全的前提下，升高焙烧温度比延长保温时间对晶粒尺寸有更显著的影响。

Characterization of Er3+-doped Na2O-WO3-TeO2 glass for ion-exchanged waveguide amplifiers and lasers

Er^(3+)-doped Na2O-WO3-TeO2 glass consistent with standard ion-exchange technology has been fabricated and characterized. The measured absorption and emission spectra of the glass were analyzed by the Judd-Ofelt and McCumber theories. The intensity parameters are Ω2 = 7.01

Property studies of optical waveguide formed by 6.0 MeV carbon ion implantation into Nd : silicate glass

Nd:silicate glass was implanted at room temperature by 6.0 MeV C3+ ions with a dose of 2.0 x 10(15) ions cm(-2). A waveguide with thickness of about 6.3 mu m was formed. The prism-coupling method was used to observe the dark modes of the waveguide at 633 nm and 1539 nm, respectively. There are three dark modes at 633 nm, of which one is the enhanced-index mode. The propagation loss of the enhanced-index mode in the waveguide measured at 633 nm is 0.42 dB cm(-1) after annealing at 217 degrees C for 35 min. The reflectivity calculation method was applied to simulate the refractive index profiles in the waveguide. The mode optical near-field output at 633 nm was presented.

Efficient laser oscillation of Yb : Y3Al5O12 single crystal grown by temperature gradient technique

Low-threshold and highly efficient continuous-wave laser performance of Yb:Y3Al5O12 (Yb:YAG) single crystal grown by a temperature gradient technique (TGT) was achieved at room temperature. The laser can be operated at 1030 and 1049 nm by varying the transmission of the output coupler. Slope efficiencies of 57% and 68% at 1049 and 1030 nm, respectively, were achieved for 10 at. % Yb:YAG sample in continuous-wave laser-diode pumping. The effect of pump power on the laser emission spectrum of both wavelengths is addressed. The near-diffraction-limited beam quality for different laser cavities was achieved. The excellent laser performance indicates that TGT-grown Yb:YAG crystals have very good optical quality and can be potentially used in high-power solid-state lasers.

Infrared (1.2-1.6 mu m) luminescence in Yb, Cr : YAG with 940 nm diode pumping

Infrared (1.2-1.6 mum) luminescence in a yttrium aluminium garnet (YAG) crystal, co-doped with Yb (10 at.%) and Cr (0.05 at.%) ions, was investigated under CW laser diode pumping (lambda = 940 nm). The Cr4+ emission band was observed with its peak at 1.35 mum and measured to be about 6% with respect to Yb3+ IR luminescence (lambda = 1.03 mum). Analysis of the crystal absorption and luminescence spectra allows one to conclude that Yb3+-Cr4+ energy transfer is a mechanism responsible for the B-3(2)(T-3(2))-B-3(1)((3)A(2)) emission of Cr4+ ions. This crystal is promising as an efficient source of the near infrared emission. (C) 2004 Elsevier B.V. All rights reserved.

Yb：YAG晶体的红外闪烁特性

用脉冲电子束激发测量了不同Yb^3+掺杂浓度的Yb：YAG晶体的红外(IR)闪烁发光性能。Yb：YAG晶体的IR闪烁发光具有高的光产额和长的衰减时间，但存在浓度猝灭效应和温度依赖关系。Yb：YAG晶体的IR闪烁性能还与晶体品质有关，相同掺杂浓度的Yb：YAG晶体，品质优异的会获得更高的光产额。这一初步的研究成果表明，部分掺Yb^3+晶体有可能用于医学成像装置。