Influência do condicionamento ambiental sobre as propriedades viscoelásticas de compósitos aramida/epóxi

The increasing application of structural composites in the aerospace industry is mainly due to its low specific weight coupled with its excellent mechanical properties when in service. As a result of climatic variations that pass the aircraft is of paramount importance to study the influence of weathering on this type of material when subjected to such changes. The purpose of this work is to evaluate the mechanical behavior of specimens of kevlar fiber /epoxy matrix composites, by dynamic mechanical thermal analysis (DMA) and interlaminar shear strength tests (ILSS), after passing through three environmental conditioning: saline fog, hygrothermal and ultraviolet radiation. From the results, we concluded that the laminate was molded supplied homogeneously, not presenting problems such as porosity, delaminations or cracks inside. After a period of 625 hours of exposure to hygrothermal conditioning, we observed a 1,2% maximum of absorption of moisture. Samples subjected to the conditioning by UV irradiation (600 hours) and salt spray showed a reduction of about 24,30% and 32,30%, respectively, on the shear strength (ILSS). In DMA analysis is not observed significant changes on the glass transition temperature. However, when considering the storage modulus of the samples conditioned by UV radiation (1200 hours), salt spray and hygrothermal conditioning there is an increase of 5,34% , 7,19% and 5,57% respectively

Preparação e caracterização da casca de banana prata particulada para aplicação com reforço em compósito de matriz de PEAD

The waste, exaggerated and incorrect disposal of biomass are common practices in modern times where everything is disposable. However the growing concern with the nature and the environment compel man to give nobler destinations for these products through sustainability and recycling of waste. Banana peel is a residual biomass, which is not consumed. It generates tons of waste per week in São Paulo city. This trash is disposed in dumps and landfills, which could be reduced by using it as reinforcement in natural composites. The high density polyethylene (HDPE) is a polymer derived from the ethylene polymerization and is easily recycled. Which makes it a sustainable material. In the present work characteristics of the natural composite composed with banana peel and high-density polyethylene were studied. It was noted that removing the lignin present in the banana peel, the fiber introduces a significant improvement in thermal resistance. The preparation of composite was made with a ratio of 5% and 10% of reinforcement in comparison with polymeric matrix mass. Composites were thermally, mechanically and microscopically characterized. The addition of fiber in the polymer increased the mechanical strength of the composite. The fiber surface treatment with distilled water removed the amorphous material present in the fibers, improving significantly thermal stability and increasing crystallinity of the celullose. The addition of 5% fiber in mass to the polymer increased significantly the tensile strength and elasticity modulus for the composite. With 10% of fiber addiction there were also an improvement when compared with pure HDPE, but when compared with 5% composite the mechanical properties are slightly lower. This may be due to the fiber particle size, which are small and eventually become a hub of tension ... (Complete abstract click electronic access below)

Flexão e análise dinâmico-mecânica de compósitos 5HS e NCF com resina epóxi monocomponente produzidos por RTM

In order to study resin distribution and homogeneity of composite laminates manufactured by RTM, it was used CYCOM 890 monolithic toughened epoxy as a matrix with two different configurations of intermediated modulus (IM) carbon fibers: Satin Weave (5HS) and non crimp fabric (NCF). The injection parameters were defined based on Thermo Gravimetric Analysis (TG), Differential Scanning Calorimetry (DSC) and rheological analysis. After processing the material, the resin/fiber impregnation was studied using ultrasonic test, Thermo Gravimetric Analysis, Differential Scanning Calorimetry, Dynamic Mechanical Analysis (DMA) and flexural tests. Therefore, it was able to observe an internal residual stress during the cooling process in both laminates, higher in the composite using NCF fabric due to the lack of symmetry, although a good proportion of fiber/matrix has been verified by the lower values of flexural modulus deviation. The DMA enabled the visualization of glass transition and its association with the inter and intra molecular interaction and movement, in which the NCF composite presented better permeability due to the lowest temperature of glass transition, when compared to the Satin Weave composite

Confecção e avaliação de chapas de madeira aglomerada com aproveitamento de resíduos de marcenaria industrial

Pós-graduação em Engenharia Civil - FEIS

Estudo da influência da adição de resíduos de óleo em concretos para aplicação em pavimentos

Pós-graduação em Engenharia Civil - FEIS