Effect of disinfectants on the hardness and roughness of reline acrylic resins

Purpose: Potential effects on hardness and roughness of a necessary and effective disinfecting regimen (1% sodium hypocholorite and 4% chlorhexidine) were investigated for two hard chairside reline resins versus a heat-polymerizing denture base acrylic resin. Materials and Methods: Two standard hard chairside reliners (Kooliner and Duraliner II), one heat-treated chairside reliner (Duraliner II +10 minutes in water at 55°C), and one standard denture base material (Lucitone 550) were exposed to two disinfecting solutions (1% sodium hypochlorite; 4% chlorhexidine gluconate), and tested for two surface properties [Vickers hardness number (VHN, kg/mm2); Roughness (Ra, μm)] for different times and conditions (1 hour after production, after 48 hours at 37 ± 2°C in water, after two disinfection cycles, after 7 days in disinfection solutions, after 7 days in water only). For each experimental condition, eight specimens were made from each material. Data were analyzed by analysis of variance followed by Tukey's test, and Student's t-test (p= 0.05). Results: For Kooliner (from 6.2 ± 0.3 to 6.5 ± 0.5 VHN) and Lucitone 550 (from 16.5 ± 0.4 to 18.4 ± 1.7 VHN), no significant changes in hardness were observed either after the disinfection or after 7 days of immersion, regardless of the disinfectant solution used. For Duraliner II (from 4.0 ± 0.1 to 4.2 ± 0.1 VHN), with and without heat treatment, a small but significant increase in hardness was observed for the specimens immersed in the disinfectant solutions for 7 days (from 4.3 ± 0.2 to 4.8 ± 0.5 VHN). All materials showed no significant change in roughness (Kooliner: from 0.13 ± 0.05 to 0.48 ± 0.24 μm; Duraliner II, with and without heat treatment: from 0.15 ± 0.04 to 0.29 ± 0.07 μm; Lucitone 550: from 0.44 ± 0.19 to 0.49 ± 0.15 μm) after disinfection and after storage in water for 7 days. Conclusions: The disinfectant solutions, 1% sodium hypochlorite and 4% chlorhexidine gluconate, caused no apparent damage on hardness and roughness of the materials evaluated. Copyright © 2006 by The American College of Prosthodontists.

Effects of Plasma Immersion Ion Implantation (PIII) of nitrogen on hardness, composition and corrosion resistance of Ti-6Al-4V alloy

Ti-6Al-4V samples have been treated by PHI processing at different temperatures (400-800°C), treatment time (30-150 min) and plasma potential (100 and 420 V). Hardness measurements results showed an enhancement of the hardness for all implanted samples. XRD results detected the Ti 2N phase and the best corrosion resistance was found for the samples processed at higher temperature and lower PIII time.

Effect of 10% carbamide peroxide dental bleaching on microhardness of filled and unfilled sealant materials

Purpose: The purpose of this study was to quantitatively evaluate the effect of 10% carbamide peroxide on the microhardness of pit and fissure sealant materials. Methods: Fluroshield, Vitroseal Alfa, and one unfilled (Clinpro) sealants were placed in Teflon matrices (4 mm in diameter by 2 mm in height) and polymerized for 40 seconds. A total of 20 specimens were prepared for each material, in which half were assigned as the control group (stored in artificial saliva and no bleaching treatment). For the remaining half, Clarigel Gold bleaching agent (10% carbamide peroxide) was placed over the specimen surface for 4 hours/day during 4 weeks. When specimens were not under bleaching treatment, they were kept in artificial saliva. Afterwards, specimens were subjected to Knoop microhardness testing using a 25-g load for 5 seconds. Five measurements were made on the sealants' surfaces and then calculated in Knoop hardness values. The data were statistically analyzed by two-way analysis of variance and Tukey's tests with a 5% confidence level. Results: The results of this in vitro study showed that the application of a carbamide peroxide-based bleaching material significantly affected the microhardness values of filled sealant materials. The bleaching agent did not affect the microhardness of the unfilled sealant. CLINICAL SIGNIFICANCE: The results of this in vitro study suggest that the bleaching agents altered the surface hardness of filled sealant restorative materials. This could possibly lead to increased wear and surface roughness. © 2006, Copyright the authors.

Vickers hardness of cast commercially pure titanium and Ti-6Al-4V alloy submitted to heat treatments

The purpose of this study was to evaluate the effect of heat treatments on the Vickers hardness of commercially pure titanium and Ti-6Al-4V cast alloys. Six-millimeter-diameter cylindrical specimens were cast in a Rematitan System. Commercially pure titanium and Ti-6Al-4V alloy specimens were randomly assigned to 3 groups (n=10) that received the following heat treatments: control (no heat treatment); treatment 1 (T1): heating at 750°C for 2 h; and treatment 2 (T2): annealing at 955°C for 1 h and aging at 620°C for 2 h. After heat treatments, the specimens were embedded in acrylic resin and their surface was ground and polished and hardness was measured. Vickers hardness means (VHN) and standard deviations were analyzed statistically by Kruskal-Wallis test at 5% significance level. For commercially pure titanium, Vickers hardness means of group T2 (259.90 VHN) was significantly higher than those of the other groups (control - 200.26 VHN and T1 - 202.23 VHN), which presented similar hardness means to each other (p>0.05). For Ti-6Al-4V alloy, statistically significant differences were observed among the three groups: T2 (369.08 VHN), T1 (351.94 VHN) and control (340.51 VHN) (p<0.05). The results demonstrated different hardness of CP Ti and Ti-6Al-4V when different heat treatments were used. For CP Ti, VHN means of T2 group was remarkably higher than those of control and T1 group, which showed similar VHN means to each other. For Ti-6Al-4V alloy, however, VHN means recorded for each group may be presented as follows: T2>T1>control.

Cross-hole and seismic CPT tests in a tropical soil site

A large portion of Brazil is covered with tropical soils but literature about dynamic parameters of these soils is very limited. SCPT and cross-hole tests were carried out at an experimental research site inland in the state of São Paulo, Brazil. Shear wave velocities (VS) determined based on both tests are presented and compared. A good agreement was observed between both test results and the differences can be associated with soil variability, which was very sensitive to CPT tests. It was also observed that Go/q c ratio determined based on SCPT appears to be an interesting technique to help identify tropical soils. Copyright ASCE 2006.

Effect of disinfection treatments on the hardness of soft denture liner materials

Purpose: To evaluate the effects of disinfection treatments with chemical solutions (2% glutaraldehyde, 5% sodium hypochlorite, and 5% chlorhexidine) and microwave energy on the hardness of four long-term soft denture liners. Materials and Methods: Forty rectangular specimens of four soft lining materials (Molloplast-B, Ufi Gel P, Eversoft, and Mucopren soft) were made for each material. Ten samples of each material were immersed in different disinfectant solutions for 10 minutes or placed in a microwave oven for 3 minutes at 500 W. The hardness values were obtained with a Shore A durometer, before the first disinfection cycle (control), and also after two cycles of disinfection. Data were submitted to analysis of variance and Tukey's test (p < 0.01). Results: The highest value of hardness was obtained for Molloplast-B, independent of the disinfection technique. Mucopren soft demonstrated intermediate values and Ufi Gel P and Eversoft the lowest values of Shore A hardness. For Molloplast-B, the disinfection using glutaraldehyde demonstrated the highest value of hardness. The number of disinfections had no effect on the hardness values for all the materials studied and disinfection techniques. Conclusions: The application of two disinfection cycles did not change the Shore A hardness values for all the materials. The glutaraldehyde solution demonstrated the highest values of Shore A hardness for the Molloplast-B, Mucopren soft, and Ufi Gel P materials, while Eversoft did not present any differences in hardness when submitted to different disinfection treatments. Copyright © 2007 by The American College of Prosthodontists.

Planning accelerated life tests under Exponentiated-Weibull-Arrhenius model

Purpose - The purpose of this paper is to present designs for an accelerated life test (ALT). Design/methodology/approach - Bayesian methods and simulation Monte Carlo Markov Chain (MCMC) methods were used. Findings - In the paper a Bayesian method based on MCMC for ALT under EW distribution (for life time) and Arrhenius models (relating the stress variable and parameters) was proposed. The paper can conclude that it is a reasonable alternative to the classical statistical methods since the implementation of the proposed method is simple, not requiring advanced computational understanding and inferences on the parameters can be made easily. By the predictive density of a future observation, a procedure was developed to plan ALT and also to verify if the conformance fraction of the manufactured process reaches some desired level of quality. This procedure is useful for statistical process control in many industrial applications. Research limitations/implications - The results may be applied in a semiconductor manufacturer. Originality/value - The Exponentiated-Weibull-Arrhenius model has never before been used to plan an ALT. © Emerald Group Publishing Limited.

Effect of microwave disinfection on physical and mechanical properties of acrylic resins

This study evaluated the effect of microwave energy on the hardness, impact strength and flexural strength of the Clássico, Onda-Cryl and QC-20 acrylic resins. Aluminum die were embedded in metallic or plastic flasks with type III dental stone, in accordance with the traditional packing technique. A mixing powder/liquid ratio was used according to the manufacturer's instructions. After polymerization in water batch at 74°C for 9 h, boiling water for 20 min or microwave energy at 900 W for 10 min, the specimens were deflasked after flask cooling at room temperature, and submitted to finishing. Specimens non-disinfected and disinfected by microwave irradiation were submitted to hardness, impact and flexural strength tests. Each specimen was immersed in distilled water and disinfected in a microwave oven calibrated to 650 W for 3 min. Knoop hardness test was performed with 25 g load for 10 s, impact test was carried out using the Charpy system with 40 kpcm, and 3-point bending test with a crosshead speed of 0.5 mm/min until fracture. Data were submitted to statistical analysis by ANOVA and Tukey's test (α=0.05). Disinfection by microwave energy decreased the hardness of Clássico and Onda-Cryl acrylic resins, but no effect was observed on the impact and flexural strength of all tested resins.

α-SiAION: Development and machining test on gray cast iron

The α-SiAlON ceramic cutting tool insert is developed. Silicon nitride and additives powders are pressed and sintered in the form of cutting tool inserts at temperature of 1900 °C. The physics and mechanical properties of the inserts like green density, weight loss, relative density, hardness and fracture toughness are evaluated. Machining studies are conducted on grey cast iron workpiece to evaluate the performance of α-SiAlON ceramic cutting tool. In the paper the cutting tool used in higher speed showed an improvement in the tribological interaction between the cutting tools and the grey cast iron workpiece resulted in a significant reduction of flank wear and roughness, because of better accommodation and the presence of the graphite in gray cast iron. The above results are discussed in terms of their affect at machining parameters on gray cast iron.

Properties advanced of the silicon nitride based ceramics and recent performance on automotive parts manufacture by machining process: Advanced Ceramics, demand Forecast

Automotive parts manufacture by machining process using silicon nitride-based ceramic tool development in Brazil already is a reality. Si 3N4-based ceramic cutting tools offer a high productivity due to their excellent hot hardness, which allows high cutting speeds. Under such conditions the cutting tool must be resistant to a combination of mechanical, thermal and chemical attacks. Silicon nitride based ceramic materials constitute a mature technology with a very broad base of current and potential applications. The best opportunities for Si3N 4-based ceramics include ballistic armor, composite automotive brakes, diesel particulate filters, joint replacement products and others. The goal of this work was to show latter advance in silicon nitride manufacture and its recent evolution on machining process of gray cast iron, compacted graphite iron and Ti-6Al-4V. Materials characterization and machining tests were analyzed by X-Ray Diffraction, Scanning Electron Microscopy, Vickers hardness and toughness fracture and technical norm. In recent works the authors has been proved to advance in microstructural, mechanical and physic properties control. These facts prove that silicon nitride-based ceramic has enough resistance to withstand the impacts inherent to the machining of gray cast iron (CI), compacted graphite iron (CGI) and Ti-6Al-4V (6-4). Copyright © 2008 SAE International.

Classification of lumber of Eucalyptus using non-destructive tests

Classification and standardization of the sawn wood is a usual activity, developed by countries that come as great consumers of this material. Brazil does not practice the classification of sawn wood. This work had the main objective of evaluating the sensibility of most common non-destructive tests in the classification of dimension lumber from fast grown Eucalyptus plantation. Wood was obtained from genetic material cultivated at Minas Gerais State, Brazil. 296 beams of structural dimensions (6 cm × 12 cm × 280 cm) from 10 different clones of Eucalyptus were sampled. Beams were non-destructively (stress wave, ultrasound and transverse vibration) and destructively (static bending and compression parallel to grain) tested. Non-destructive results showed sensibility in the classification of structural dimension lumber, being possible to establish wave velocity intervals that attend to the main strength classes reported by Wooden Structures Brazilian Code.

Influence of pre-heat treatment and different light-curing units on Vickers hardness of a microhybrid composite resin

The aim of this study was to evaluate the hardness of a dental composite resin submitted to temperature changes before photo-activation with two light-curing unite (LCUs). Five samples (4 mm in diameter and 2 mm in thickness) for each group were made with pre-cure temperatures of 37, 54, and 60°C. The samples were photo-activated with a conventional quartz-tungsten-halogen (QTH) and blue LED LCUs during 40 s. The hardness Vickers test (VHN) was performed on the top and bottom surfaces of the samples. According to the interaction between light-curing unit and different pre-heating temperatures of composite resin, only the light-curing unit provided influences on the mean values of initial Vickers hardness. The light-curing unit based on blue LED showed hardness mean values more homogeneous between the top and bottom surfaces. The hardness mean values were not statistically significant difference for the pre-cure temperature used. According to these results, the pre-heating of the composite resin provide no influence on Vickers hardness mean values, however the blue LED showed a cure more homogeneous than QTH LCU. © 2009 Pleiades Publishing, Ltd.

Evaluation of hardness and colour change of soft liners after accelerated ageing.

INTRODUCTION: Soft liners have been developed to offer comfort to denture wearers. However, this comfort is compromised when there is a change in the properties of the material, causing colour change, solubility, absorption and hardening. These characteristics can compromise the longevity of soft liners. AIM: The aim of this in vitro study was to investigate the effect of ageing on both the hardness and colour change of two soft liners following accelerated ageing. METHODS: Two denture liners, one resin based (Trusoft, Bosworth, Illinois, USA) and one silicone based (Ufi Gel P, Voco GMBH, Cuxhaven, Germany), were tested in this study for both hardness (using the Shore A scale) and colour change (using the CIE L*a*b* colour scale), initially and after 1008 hours (6 weeks) of accelerated ageing. Statistical analysis was performed using the unpaired t-test with the Welch correction. RESULTS: These indicated that both materials increased in hardness and underwent colour change after accelerated ageing. The initial hardness of Trusoft was far lower than that of Ufi Gel P (18.2 Shore A units vs 34.8 Shore A units). However, for Trusoft the changes for both hardness (from 18.2 to 52.1 Shore A units) and colour change (16.85 on the CIE L*a*b* colour scale) were greater than those for Ufi Gel P, for which hardness changed from 34.8 to 36.5 Shore A units and the colour change was 5.19 on the CIE L*a*b* colour scale. CONCLUSIONS: Ufi Gel P underwent less hardness and colour change after accelerated ageing than Trusoft. On the other hand, the use of Trusoft may be preferable in cases where initial softness is a major consideration, such as when relining an immediate denture after implant surgery.

The use of slot filter in piezocone tests for site characterization of tropical soils

The use of piezocone tests with a slot filter filled with automotive grease for site characterization of tropical soils is assessed. Laboratory tests using the slot filter filled with automotive grease as well as the conventional porous piezo-element saturated with glycerin were carried out to evaluate the pore pressure (u 2) transducer response. CPTu tests using piezo-elements saturated with glycerin and the slot filter filled with grease were pushed side by side in different research sites in Brazil. Estimates of mechanical and hydraulic soil parameters were made based on pore pressure dissipation curves from using both techniques. Laboratory test results indicate that the pore pressure response using the slot filter with grease was delayed when compared to the piezo-element saturated with glycerin, since grease has a higher viscosity. For tropical soils, the records of u2 in piezocone tests using slot filter with grease presented larger peaks than with porous element saturated with glycerin. Records of u2 using the slot filter above the groundwater table suggest the increase of the degree of saturation in unsaturated zone, where porous filter can be desaturated by suction. The slot filter can be used to help the interpretation of the soil profile with deep groundwater level as well as to help detecting its position for some studied soils. The results shown high repeatability for all study sites. This technique is much easier to handle, especially for tropical soils, where the groundwater table is usually deep and pre-drilling is expensive and time consuming. © 2009 IOS Press.

Evaluation of hardness and surface roughness of two maxillofacial silicones following disinfection

The purpose of this study was to evaluate the Shore A hardness and surface roughness of two silicones for maxillofacial prosthetic treatment, under the influence of chemical disinfection and storage. Twenty-eight specimens were obtained, half of which were made of Silastic MDX 4-4210 silicone and, the other half were made of Silastic 732 RTV silicone. The specimens were divided into four groups: Silastic 732 RTV and MDX 4-4210 with disinfection 3 times a week with Efferdent tablets and the same materials without disinfection. The hardness of the materials was analyzed with a Shore A Durometer. The surface roughness was established by a digital portable roughness tester, initially and 2 months after the confection of the specimens. A variance test was applied (2-way ANOVA), followed by Tukey test (the level of significance was set at 1%). The storage time factor statistically influenced (p < 0.01) the materials' properties of hardness and roughness. MDX 4-4210 (28.59 Shore A, 0.789 Ra) presented higher values than Silastic 732 RTV (18.08 Shore A, 0.656 Ra) for both properties. Regarding the disinfection period, there was no significant difference in any of the materials tested. © 2009 Sociedade Brasileira de Pesquisa Odontológica.