退火对电子束热蒸发193nm Al2O3/MgF2反射膜性能的影响

设计并镀制了193nm Al2O3/MgF2反射膜,对它们在空气中分别进行了250-400℃的高温退火,测量了样品的透射率光谱曲线和绝对反射率光谱曲线.发现样品在高反射区的总的光学损耗随退火温度的升高而下降,而后趋于饱和.采用总积分散射的方法对样品在不同退火温度下的散射损耗进行了分析,发现随着退火温度的升高散射损耗有所增加.因此,总的光学损耗的下降是由于吸收损耗而不是散射损耗起主导作用.对Al2O3材料的单层膜进行了同等条件的退火处理,由它们光学性能的变化推导出它们的折射率和消光系数的变化,从而解释了相应

Influence of different post-treatments on the structure and optical properties of zinc oxide thin films

Zinc oxide (ZnO) films with c-oriented were grown on fused quartz glass substrates at room temperature using dc reactive magnetron sputtering. The as-grown films were annealed at 700 degrees C in air and bombarded by ion beam, respectively. The effects of post-treatments on the structural and optical properties of the ZnO films were investigated by X-ray diffraction (XRD), photoluminescence (PL), optical transmittance and absorption measurements. The XRD spectra indicate that the crystal quality of ZnO films has been improved by both the post-treatments. Compared with the as-grown sample, both annealed and bombarded samples exhibited blueshift in the UV emission peaks, and a strong green emission was found in the annealed ZnO film. In both optical transmittance and absorption spectra, a blueshift of the band-gap edge was observed in the bombarded film, while a redshift was observed in the annealed film. (c) 2004 Elsevier B.V. All rights reserved.

反射式相位延迟器的性能研究

多层介质反射镜在非正入射的时候，两个不同的偏振态之间会产生不同的相移。通过优化设计，入射角为45°，在1285～1345nm之间p，s波获得了270°±0．15°的相移和99．5％以上的反射率。对使用的膜系进行了每层光学厚度的误差分析。用离子柬溅射技术制备相位延迟膜，在大气中对样品进行不同温度的退火，用分光光度计测试了光谱特性和用椭偏仪测试了相位特性。结果表明，未退火的样品在相应波段获得了267．5°±0．5°的相移和99．6％以上的反射率；根据拟合分析，最外层的误差和折射率与设计值的偏差是发生相移偏小的

1064nm倍频波长分离膜的制备与性能研究

通过对主膜系添加匹配层并借助计算机对膜系进行优化，设计出结构规整、性能优良的1064ilm倍频波长分离膜。用电子束蒸发及光电极值监控技术在K9玻璃基底上沉积薄膜，将样品置于空气中在260℃温度下进行3h热退火处理。然后用Lambda 900分光光度计测量了样品的光谱性能；用表面热透镜(STL)技术测量了样品的弱吸收值；用调Q脉冲激光装置测试了样品的抗激光损伤阈值(LIDT)。实验结果发现，样品的实验光谱性能与理论光谱性能有很好的一致性。退火前后其光谱性能几乎没有发生温漂，说明薄膜的温度稳定性好；同时退火使

退火对ZrO2薄膜微结构及激光损伤阈值的影响

利用电子束蒸发方法在Yb:YAG晶体和熔融石英衬底上沉积单层ZrO2薄膜,分别在673 K和1 073 K的温度下经过12 h退火以后,通过X射线衍射(XRD)分析了薄膜晶相,计算了薄膜的晶粒尺寸;利用表面热透镜技术获得了薄膜的吸收;测量了退火后薄膜的激光损伤阈值.实验结果表明:两种衬底上的薄膜结构受到退火温度和衬底表面结构的影响,高温退火有利于单斜相的形成,含单斜相的ZrO2薄膜具有较高的激光损伤阈值,而由于衬底的吸收,Yb:YAG晶体上薄膜的损伤阈值远小于石英衬底上薄膜的损伤阈值.

退火对电子束热蒸发Al2O3薄膜性能影响的实验研究

用电子束热蒸发方法镀制了Al2O3材料的单层膜，对它们在空气中进行了250～400℃的高温退火。对样品的透射率光谱曲线进行了测量，计算了样品的消光系数、折射率和截止波长。通过X射线衍射仪(XRD)测量分析了薄膜的微观结构，采用表面轮廓仪测量了样品的表面均方根粗糙度。结果发现随着退火温度的提高光学损耗下降，薄膜结构在退火温度为400℃时仍然为无定形态，样品的表面粗糙度随退火温度的升高而增加。引起光学损耗下降起主导作用的是吸收而不是散射，吸收损耗的下降主要是由于退火使材料吸收空气中的氧而进一步氧化，从而使薄膜

Ta2O5膜在532, 800 和 1064 nm波长的n-on-1体系下的激光损伤阈值研究

Ta2O5膜采用传统的电子束蒸发方法制备，并在氧气中673 K的条件下进行了退火12 h处理。首先在1-on-1体系下对Ta2O5膜进行了532和1064 nm波长下的激光损伤阈值（LIDT） 研究，然后在n-on-1体系下分别对532，800和1064 nm三种波长下的激光损伤阈值进行了研究。结果表明在n-on-1体系下Ta2O5膜在532和1064 nm波长下的阈值均高于1-on-1体系下的阈值。此外，在n-on-1体系下，薄膜的阈值随波长增加而增大。同时发现，在氧气中进行退火对Ta2O5膜的光学性能

Effect of process parameters on laser damage threshold of TiO2 coatings

We investigate the laser damage behaviour of an electron-beam-deposited TiO2 monolayer at different process parameters. The optical properties, chemical composition, surface defects, absorption and laser-induced damage threshold (LIDT) of Elms are measured. It is found that TiO2 Elms with the minimum absorption and the highest LIDT can be fabricated using a TiO2 starting material after annealing. LIDT is mainly related to absorption and is influenced by the non-stoichiometric defects for TiO2 films. Surface defects show no evident effects on LIDT in this experiment.

Influence of deposition conditions on the microstructure of oxides thin films

Thin films of ZrO2, HfO2 and TiO2 were deposited on kinds of substrates by electron beam evaporation (EB), ion assisted deposition (IAD) and dual ion beam sputtering (DIBS). Then some of them were annealed at different temperatures. X-ray diffraction (XRD) was applied to determine the crystalline phase and the grain size of these films, and the results revealed that their microstructures strongly depended on the deposition conditions such as substrate, deposition temperature, deposition method and annealing temperature. Theory of crystal growth and migratory diffusion were applied to explain the difference of crystalline structures between these thin films deposited and treated under various conditions. (c) 2007 Elsevier B.V. All rights reserved.

Optical and electrical properties of TiOx thin films deposited by electron beam evaporation

The TiOx thin films were prepared by electron beam evaporation using TiO as the starting material. The effect of the annealing temperature on the optical and electrical properties was investigated. The spectra of X-ray photoelectron spectroscopy reveal that Ti in the films mainly exist in the forms of Ti2+ and Ti3+ below 400 degrees C 24h annealing. The charge transfer between different titanium ion contribute greatly to the color, absorption, and electrical resistance of the films. (c) 2006 Elsevier Ltd. All rights reserved.

两种后处理方法对HfO2薄膜性能的影响

利用电子束蒸发和光电极值监控技术制备了氧化铪薄膜，并分别用两种后处理方法（空气中退火和氧等离子体轰击）对样品进行了处理．然后，对样品的透过率、吸收和抗激光损伤阈值进行了测试分析．实验结果表明，两种后处理方法都能不同程度地降低了氧化铪薄膜的吸收损耗、提高了抗激光损伤阈值．实验结果还表明，氧等离子体轰击的后处理效果明显优于热退火，样品的吸收平均值在氧等离子体后处理前后分别为34．8ppm和9．0ppm，而基频（1 064nm）激光损伤阈值分别为10．0J／cm^2和21．4J／cm^2．

LBO晶体上1064，532nm倍频增透膜的镀制及性能分析

用电子束蒸发沉积方法在X切LBO（X-LBO）晶体上镀制了两种不同膜系结构的1064和532nm倍频增透膜，其中一种膜系结构为基底／ZrO2／Y2O3／A12O3／SiO2／空气，另一种为基底／0．5Al2O3／ZrO2／Y2O3／A12O3／SiO2／空气，两种膜系结构的主要差别在于有无氧化铝过渡层。测量了薄膜的反射率光谱曲线，发现两种增透膜在1064和532nm处的反射率均小于0．5％，实际镀制结果与理论设计曲线的差异主要是由材料折射率的变化引起的。且对样品在空气环境中进行了温度为473K的退火处理，

沉积速率对热舟蒸发LaF3薄膜性能的影响

用热舟蒸发方法在不同的沉积速率下制备了LaF3单层膜,并对部分单层膜进行了真空退火。分别采用X射线衍射(XRD),Lambda 900 光谱仪和355 nm Nd∶YAG脉冲激光测试了薄膜的晶体结构、透射光谱和激光损伤阈值(LIDT),并通过透射光谱计算得到样品的折射率和消光系数。实验结果表明,增大沉积速率有利于LaF3薄膜的结晶和择优生长,可以提高薄膜的致密性和折射率,但薄膜的抗激光损伤能力有所下降;沉积速率太大,又会恶化薄膜的结晶性能,同时薄膜中产生大量孔洞,薄膜的机械强度降低,导致薄膜的折射率减小和

退火对HfO2/SiO2多层膜残余应力的影响

用电子束蒸发方法在BK7基底上沉积了HfO2/SiO2多层膜。研究了200℃到400℃的退火对残余应力的影响。结果表明退火前的薄膜残余应力为压应力，在200℃退火后发展为张应力，然后张应力值随着退火温度的升高而增大。在400℃退火后，由于张应力太大，薄膜表面出现了裂纹。同时，随着退火温度的升高，晶粒尺寸长大，晶面间距降低。残余应力的变化与结构的演变相对应。

SiO2保护层和退火对Ta2O5薄膜激光损伤阈值影响的对比研究

Ta2O5薄膜采用传统的电子束蒸发方法沉积在BK7基底上。文中对SiO2保护层和退火对Ta2O5薄膜的激光损伤阈值的不同影响进行了研究。结果表明，SiO2保护层不会影响薄膜内的电场分布，薄膜微结构和微缺陷密度，但是会使薄膜的吸收稍微增大；而退火对降低薄膜的微缺陷密度和吸收较有效。SiO2保护层和退火都有利于提高Ta2O5薄膜的抗激光损伤能力，并且退火对提高阈值的影响更为明显。此外，采用SiO2保护层和退火结合的方法，获得了具有最大激光损伤阈值的薄膜。