Effect of Surface Treatments on the Bond Strength between Composite Resin and Acrylic Resin Denture Teeth

Purpose: This investigation studied the effects of 3 surface treatments on the shear bond strength of a light-activated composite resin bonded to acrylic resin denture teeth. Materials and Methods: The occlusal surfaces of 30 acrylic resin denture teeth were ground flat with up to 400-grit silicon carbide paper. Three different surface treatments were evaluated: (1) the flat ground surfaces were primed with methyl methacrylate (MMA) monomer for 180 seconds; (2) light-cured adhesive resin was applied and light polymerized according to the manufacturer's instructions; and (3) treatment 1 followed by treatment 2. The composite resin was packed on the prepared surfaces using a split mold. The interface between tooth and composite was loaded at a cross-head speed of 0.5 mm/min until failure. Results: Analysis of variance indicated significant differences between the surface treatments. Results of mean comparisons using Tukey's test showed that significantly higher shear bond strengths were developed by bonding composite resin to the surfaces that were previously treated with MMA and then with the bonding agent when compared to the other treatments. Conclusion: Combined surface treatment of MMA monomer followed by application of light-cured adhesive resin provided the highest shear bond strength between composite resin and acrylic resin denture teeth.

Kinesiographic study of complete denture movement related to mucosa displacement in edentulous patients.

The mucosa that covers the residual ridges of edentulous patients may present some distortion or displacement when occlusal loading is applied in complete dentures. This distortion and movement of the denture can result in acceleration of residual ridge resorption and loss of retention and stability. The aim of this study was to analyze the pattern of upper complete denture movement related to underlying mucosa displacement. A sample of 10 complete denture wearers was randomly selected, which had acceptable upper and lower dentures and normal volume and resilience of residual ridges. The kinesiographic instrument K6-I Diagnostic System was used to measure denture movements, according to the method proposed by Maeda et al.7, 1984. Denture movements were measured under the following experimental conditions: (A) 3 maximum voluntary clenching cycles and (B) unilateral chewing for 20 seconds. The results showed that under physiological load, oral mucosa distortion has two distinct phases: a fast initial displacement as load is applied and a slower and incomplete recovery when load is removed. Intermittent loading such as chewing progressively reduces the magnitude of the denture displacement and the recovery of the mucosa is gradually more incomplete.

Zygomatic bone: Anatomic bases for osseointegrated implant anchorage

Purpose: The aim of the present study was to evaluate zygomatic bone thickness considering a possible relationship between this parameter and cephalic index (Cl) for better use of Cl in the implant placement technique. Materials and Methods: Cl was calculated for 60 dry Brazilian skulls. The zygo matic bones of the skulls were divided into 13 standardized sections for measurement. Bilateral measurements of zygomatic bone thickness were made on dry skulls. Results: Sections 5, 6, 8, and 9 were appropriate for implant anchorage in terms of location. The mean thicknesses of these sections were 6.05 mm for section 5, 3.15 mm for section 6, 6.13 mm for section 8, and 4.75 mm for section 9. In only 1 section, section 8, did mean thickness on 1 side of of the skull differ significantly from mean thickness on the other side (P <.001). Discussion: For the relationship between quadrant thick ness and Cl, sections 6 and 8 varied independently of Cl. Section 5 associated with brachycephaly, and section 9 associated with subbrachycephaly, presented variations in the corresponding thickness. Conclusion: Based on the results, implants should be placed in sections 5 and 8, since they presented the greatest thickness, except in brachycephalic subjects, where thickness was greatest in section 5, and in subbrachycephalic subjects, where thickness was greatest in section 9. Cl did not prove to be an appropriate parameter for evaluating zygomatic bone thickness for this sampling.

Adsorption of silanes bearing nitrogenated Lewis bases on SiO 2/Si (100) model surfaces

The present paper describes the one-pot procedure for the formation of self-assembled thin films of two silanes on the model oxidized silicon wafer, SiO2/Si. SiO2/Si is a model system for other surfaces, such as glass, quartz, aerosol, and silica gel. MALDI-TOF MS with and without a matrix, XPS, and AFM have confirmed the formation of self-assembled thin films of both 3-imidazolylpropyltrimethoxysilane (3-IPTS) and 4-(N- propyltriethoxysilane-imino)pyridine (4-PTSIP) on the SiO2/Si surface after 30 min. Longer adsorption times lead to the deposition of nonreacted 3-IPTS precursors and the formation of agglomerates on the 3-IPTS monolayer. The formation of 4-PTSIP self-assembled layers on SiO2/Si is also demonstrated. The present results for the flat SiO2/Si surface can lead to a better understanding of the formation of a stationary phase for affinity chromatography as well as transition-metal-supported catalysts on silica and their relationship with surface roughness and ordering. The 3-IPTS and 4-PTSIP modified SiO2/Si wafers can also be envisaged as possible built-on-silicon thin-layer chromatography (TLC) extraction devices for metal determination or N-heterocycle analytes, such as histidine and histamine, with on-spot MALDI-TOF MS detection. © 2005 Elsevier Inc. All rights reserved.

Effect of post-polymerization heat treatments on the cytotoxicity of two denture base acrylic resins

Introduction: Most denture base acrylic resins have polymethylmethacrylate in their composition. Several authors have discussed the polymerization process involved in converting monomer into polymer because adequate polymerization is a crucial factor in optimizing the physical properties and biocompatibility of denture base acrylic resins. To ensure the safety of these materials, in vitro cytotoxicity assays have been developed as preliminary screening tests to evaluate material biocompatibility. 3H-thymidine incorporation test, which measures the number of cells synthesizing DNA, is one of the biological assays suggested for cytotoxicity testing. Aim: The purpose of this study was to investigate, using 3H-thymidine incorporation test, the effect of microwave and water-bath post-polymerization heat treatments on the cytotoxicity of two denture base acrylic resins. Materials and Methods: Nine disc-shaped specimens (10 x 1 mm) of each denture base resin (Lucitone 550 and QC 20) were prepared according to the manufacturers' recommendations and stored in distilled water at 37°C for 48 h. The specimens were assigned to 3 groups: 1) post-polymerization in a microwave oven for 3 min at 500 W; 2) post-polymerization in water-bath at 55°C for 60 min; and 3) without post-polymerization. For preparation of eluates, 3 discs were placed into a sterile glass vial with 9 mL of Eagle's medium and incubated at 37°C for 24 h. The cytotoxic effect of the eluates was evaluated by 3H-thymidine incorporation. Results: The results showed that the components leached from the resins were cytotoxic to L929 cells, except for the specimens heat treated in water bath (p<0.05). Compared to the group with no heat treatment, water-bath decreased the cytotoxicity of the denture base acrylic resins. Conclusion: The in vitro cytotoxicity of the tested denture base materials was not influenced by microwave post-polymerization heat treatment.

Prosthetic rehabilitation of a bone defect with a teeth-implant supported, removable partial denture

The use of teeth-implant, mucosa-supported removable dentures for rehabilitation of partially edentulous patients involves highly complex biomechanical aspects. This type of prosthesis associates 3 kinds of support that react differently to the functional and parafunctional forces developed in the oral cavity. Although the construction of removable partial dentures may seem paradoxical when osseointegrated implants are placed, in some cases, this option is an excellent alternative to solve difficulties related to the anatomic, biologic, psychomotor, and financial conditions of the patient. This article reports on a case in which a teeth-implant, mucosa-supported removable partial denture was the option of choice for a patient with financial and anatomic limitations, having a large structural loss of the residual alveolar ridge caused by trauma by a gunshot injury at the mandible. The 5-year follow-up did not reveal any type of biomechanical or functional problem. Copyright © 2006 by Lippincott Williams and Wilkins.

Nasal width as a guide for the selection of maxillary complete denture anterior teeth in four racial groups

Purpose: Selecting artificial teeth for edentulous patients is difficult when pre-extraction records are not available. Various guidelines have been suggested for determining the width of the maxillary anterior denture teeth. This study was undertaken to evaluate the use of the nasal width as a guide for the selection of proper width maxillary anterior denture teeth in four racial groups of the Brazilian population. Materials and Methods: One hundred and sixty subjects (40 Whites, 40 Mulattos, 40 Blacks, and 40 Asians) were selected. Using a sliding caliper, the nasal width and the intercanine distance were measured. The Pearson product-moment correlation coefficient was used to determine the relationship between the above measurements. A prediction was made of the percentage of subjects of the White, Mulatto, Black, and Asian populations in which the selection error due to the clinical application of the method of the nasal width would be within 0 to 2 mm, within 2 to 4 mm, and greater than 4 mm. Results: The four racial groups showed a weak correlation between the intercanine distance and the nasal width. In 39.7% of the White, 55.7% of the Mulatto, 81.9% of the Black, and 48.2% of the Asian populations, errors greater than 4 mm would be present with the use of the nasal width. Conclusions: The correlation found between the intercanine distance and the nasal width was not high enough to be used as a predictive factor. The relationship between natural tooth width and artificial tooth width as predicted by the nasal width showed that the nasal width method is not accurate for all the studied groups. Copyright © 2006 by The American College of Prosthodontists.

Bond strength of hard chairside reline resins to a rapid polymerizing denture base resin before and after thermal cycling

Purpose: This study assessed the shear bond strength of 4 hard chairside reline resins (Kooliner, Tokuso Rebase Fast, Duraliner II, Ufi Gel Hard) to a rapid polymerizing denture base resin (QC-20) processed using 2 polymerization cycles (A or B), before and after thermal cycling. Materials and Methods: Cylinders (3.5 mm x 5.0 mm) of the reline resins were bonded to cylinders of QC-20 polymerized using cycle A (boiling water-20 minutes) or B (boiling water; remove heat-20 minutes; boiling water-20 minutes). For each reline resin/polymerization cycle combination, 10 specimens (groups CAt e CBt) were thermally cycled (5 and 55°C; dwell time 30 seconds; 2,000 cycles); the other 10 were tested without thermal cycling (groups CAwt ad CBwt). Shear bond tests (0.5 mm/min) were performed on the specimens and the failure mode was assessed. Data were analyzed by 3-way ANOVA and Newman-Keuls post-hoc test (α=.05). Results: QC-20 resin demonstrated the lowest bond strengths among the reline materials (P<.05) and mainly failed cohesively. Overall, the bond strength of the hard chairside reline resins were similar (10.09±1.40 to 15.17±1.73 MPa) and most of the failures were adhesive/cohesive (mixed mode). However, Ufi Gel Hard bonded to QC-20 polymerized using cycle A and not thermally cycled showed the highest bond strength (P<.001). When Tokuso Rebase Fast and Duraliner II were bonded to QC-20 resin polymerized using cycle A, the bond strength was increased (P=.043) after thermal cycling. Conclusions: QC-20 displayed the lowest bond strength values in all groups. In general, the bond strengths of the hard chairside reline resins were comparable and not affected by polymerization cycle of QC-20 resin and thermal cycling.

Effect of disinfection treatments on the hardness of soft denture liner materials

Purpose: To evaluate the effects of disinfection treatments with chemical solutions (2% glutaraldehyde, 5% sodium hypochlorite, and 5% chlorhexidine) and microwave energy on the hardness of four long-term soft denture liners. Materials and Methods: Forty rectangular specimens of four soft lining materials (Molloplast-B, Ufi Gel P, Eversoft, and Mucopren soft) were made for each material. Ten samples of each material were immersed in different disinfectant solutions for 10 minutes or placed in a microwave oven for 3 minutes at 500 W. The hardness values were obtained with a Shore A durometer, before the first disinfection cycle (control), and also after two cycles of disinfection. Data were submitted to analysis of variance and Tukey's test (p < 0.01). Results: The highest value of hardness was obtained for Molloplast-B, independent of the disinfection technique. Mucopren soft demonstrated intermediate values and Ufi Gel P and Eversoft the lowest values of Shore A hardness. For Molloplast-B, the disinfection using glutaraldehyde demonstrated the highest value of hardness. The number of disinfections had no effect on the hardness values for all the materials studied and disinfection techniques. Conclusions: The application of two disinfection cycles did not change the Shore A hardness values for all the materials. The glutaraldehyde solution demonstrated the highest values of Shore A hardness for the Molloplast-B, Mucopren soft, and Ufi Gel P materials, while Eversoft did not present any differences in hardness when submitted to different disinfection treatments. Copyright © 2007 by The American College of Prosthodontists.

Degree of conversion and molecular weight of one denture base and three reline resins submitted post-polymerization treatments

The effect of post-polymerization treatments (MW-microwave irradiatron and WB-water-bath) on the degree of conversion (DC) of three reline resins (Ufi Gel hard-U, Kooliner-K, and Tokuso Rebase Fast-T) and one denture base resin (Lucitone 550-L), submitted to two polymerization cycles (LS-short and LL-long), was evaluated by using FT-Raman spectroscopy (n = 5). The molecular weight (Mw) of the powder of all materials and of K polymerized specimens (control; MW; and WB; n = 3) was analyzed using GPC. DC data were analyzed using Kruskal-Wallis test (α = .05). For control specimens, there were no significant differences between U (68%) and LL (77%) and among LL, K (81%), and T (84%). LS (92%) had the highest DC (P<0.05). Only material K exhibited an increased DC after WB (P<0.05). All powders had Mw from 4.0 × 105 to 6.5 × 105 and narrow Mw distributions (2.1 to 3.6). Polymerization and post-polymerization produced K specimens with Mw similar to that of K powder.

Factors affecting the strength of denture repairs: Topics of interest

Fracture of dentures is a common clinical finding in daily prosthodontic practice, resulting in great inconvenience to both patient and dentist. A satisfactory repair should be cost-effective, simple to perform, and quick; it should also match the original color and not cause distortion to the existing denture. Different repair materials, surface designs, and mechanical and chemical surface treatments have been recommended in order to obtain stronger repairs. This article reviews some of the available literature with regard to the most important factors that may influence the strength of denture repairs. © 2007 by The American College of Prosthodontists.

Effect of a post-polymerization treatments on the flexural strength and vickers hardness of reline and acrylic denture base resins

This study evaluated the effect of water-bath and microwave post-polymerization treatments on the flexural strength and Vickers hardness of four autopolymerizing reline resins (Duraliner II-D, Kooliner-K, Tokuso Rebase Fast-TR and Ufi Gel Hard C-UGH) and one heat-polymerized acrylic resin (Lucitone 550-L), processed using two polymerization cycles (short cycle - 90 minutes at 73°C and 100°C for 30 minutes; and long cycle - 9 hours at 71°C). For each material, thirty specimens (64 x 10 x 3.3 mm) were made and divided into 3 groups (n=10). Specimens were tested after: processing (control group); water-bath at 55°C for 10 minutes (reline materials) or 60 minutes (L); and microwave irradiation. Flexural strength tests were performed at a crosshead speed of 5 mm/min using a three-point bending device with a span of 50 mm. The flexural strengths values were calculated in MPa. One fragment of each specimen was submitted to Vickers hardness test. Data were analyzed by 2-way ANOVA followed by Tukey's HSD test (α=0.05). L microwaved specimens (short cycle) exhibited significantly higher flexural strength means than its respective control group (p<0.05). Water-bath promoted a significant increase (p<0.05) in flexural strength of K and L (long cycle). The hardness of the tested materials was not influenced by the post-polymerization treatments. Post-polymerization treatments could be used to improve the flexural strength of some materials tested.

Complete denture masticatory efficiency: a literature review

The restoration of masticatory function and esthetics is an important aim in dentistry mainly when patients present with extensive tooth loss. The aim of mastication is to reduce food size to produce a homogeneous bolus appropriate to be swallowed. For edentulous patients, chewing efficiency is reduced because dental arches are replaced by artificial teeth. The aim of this study is to present factors related to chewing efficiency for the edentulous patient.

Dual path: A concept to improve the esthetic replacement of missing anterior teeth with a removable partial denture

The dual path of insertion concept for removable partial denture (RPD) design may be used in esthetically demanding situations. When compared to conventional RPDs, the main advantage of this design is the minimal use of clasps. This clinical report describes the treatment of a patient with an anterior maxillary edentulous area using a dual path RPD. The diagnostic cast was surveyed to ensure the adequacy of the undercuts on the mesial surfaces of the anterior abutments, where rigid minor connectors were placed. Inverted V-shaped canine cingulum rest seats were prepared to provide resistance to tooth movement during function. The dual path RPD concept allows excellent esthetic results, minimizes tooth preparation, and reduces the tendency toward plaque accumulation in a Kennedy class IV partially edentulous arch. © 2008 by The American College of Prosthodontists.