Push-out Bond Strength of Fiber Posts Luted with Unfilled Resin Cement

Purpose: The study evaluates the behavior of different adhesive systems and resin cements in fiber post placement, with the intent to clarify the possible role of unfilled resin as a luting material for fiber posts. Materials and Methods: Two luting agents (Dual-Link and Unfilled Resin) for cementing fiber posts into root canals were applied either with All-Bond 2 or One-Step Plus, or without an adhesive system, and challenged with the push-out test. Slices of roots restored with posts were loaded until post segment extrusion in the apical-coronal direction. Failure modes were analyzed under SEM. Results: Push-out strength was significantly influenced by the luting agent (p < 0.05), but not by the bonding strategy (p > 0.05). The best results were obtained in combination with Unfilled Resin with One-Step Plus. Dual-Link groups failed mainly cohesively within the cement, while Unfilled Resin demonstrated more adhesive fracture at the post interface. Conclusion: The results of this study support the hypothesis that adhesive unfilled resin application is essential for achieving high bond strength to radicular dentin.

The efficacy of a highly concentrated fluoride dentifrice on bovine enamel subjected to erosion and abrasion

Background. Researchers have proposed the use of fluoride for the prevention of enamel wear; however, only limited information is available about the impact of fluoridated dentifrices. Because tooth wear is a well-recognized dental problem, the authors conducted an in situ, ex vivo study to assess the efficacy of a highly concentrated fluoride dentifrice on bovine enamel subjected to erosion and abrasion. Methods. The authors conducted a double-blind, crossover in situ study consisting of three phases (seven days each). In each phase, the authors tested one of the dentifrices (5,000 parts per million fluoride [F]; 1,100 ppm F; no F). They performed erosive challenges with the use of cola drink (60 seconds, four times per day) and abrasive challenges via toothbrushing (30 seconds, four times per day). The authors determined the enamel loss via profilometry. Results. The authors tested the data by using two-way analysis of variance (P <.05). For the erosion-plus-abrasion condition, the study results showed that enamel wear was significantly higher than that with erosion alone. The findings showed no significant differences between the dentifrices regarding enamel wear. Conclusions. Within the in situ, ex vivo conditions of this study, the authors concluded that the highly concentrated fluoride dentifrice did not have a protective effect on enamel against erosion and erosion plus toothbrushing abrasion. Clinical Implications. Patients at risk of developing enamel erosion should benefit from preventive measures other than fluoride dentifrice, because even a highly concentrated fluoride dentifrice does not appear to prevent enamel erosion.

Cytotoxic effects and pulpal response caused by a mineral trioxide aggregate formulation and calcium hydroxide

Purpose: To evaluate: the in vivo pulpal response after pulpotomy with different capping agents. In addition, the in vitro cytotoxic effects of both materials were assessed by applying them on culture of pulp cells. Methods: For the in vivo test, the coronal pulp of 28 teeth of dogs was mechanically removed and the root pulps were capped with the following dental materials: Group 1: Pro-Root NITA (PRMTA); and Group 2 (control): calcium hydroxide saline paste (CH). After 60 days, the animals were sacrificed and the teeth processed for histological analysis. In the in vitro test, experimental extracts obtained from both capping agents were applied on the cultured MDPC-23 odontoblast-like cells. Results: In the root pulps capped with PRMTA or CH, coagulation necrosis partially replaced by dystrophic calcification as well as tubular dentin matrix laid down by elongated pulp cells was observed. None or mild inflammatory response occurred beneath the capped pulpal wound. Regarding the pulpal response, PRMTA and CH presented no statistical difference. However, the teeth capped CH presented greater healthy pulp loss which resulted in convex shape of the hard barrier than PRMTA. When applied on the cultured cells, it was demonstrated that PRMTA and CH solutions decreased the cell metabolic activity by 9.9% and 29.4%, respectively. CH caused higher cytotoxic effects to the MDPC-23 cells as well as deeper healthy pulp tissue loss than PRMTA. However, similar sequence of healing occurred after pulpotomy with both dental materials.

Post space debridement in oval-shaped canals: The use of a new ultrasonic tip with oval section

This study evaluates the effect on post space debridement in oval-shaped canals of an experimental ultrasonic tip with oval section (Satelec) compared with a circular ultrasonic tip (KaVo). Thirty teeth with an oval-shaped canal were endodontically treated and obturated and then randomly divided into 3 groups (n = 10) according to the procedure used for post space debridement: Satelec tip, Largo #2 drill + KaVo file, and Largo #2 drill + water. Debris and dentin tubules were evaluated by assigning scores to scanning electron microscope post spaces images; lower scores corresponded to fewer debris and higher number of open tubules. The Satelec group showed significantly lower debris and open tubules scores than KaVo group (p < .05) and control group (p < .05), which differed significantly between each other (p < .05). Also the debris and open tubules scores in different post space regions differed significantly among the experimental groups (p < .001). The oval ultrasonic tip resulted in a better post space debridement than a circular ultrasonic tip in oval-shaped canals.

Coupling of composite resin cements to quartz fiber posts: A comparison of industrial and ""chairside"" treatments of the post surface

Purpose: To evaluate the influence of surface treatments on microtensile bond strength of luting resin cements to fiber posts. Materials and Methods: Forty-two quartz fiber posts (Light Post, RTD) were divided into 7 groups (n = 6) according to the surface treatment. I and 11: experimental patented industrial treatment consisting of zirconium oxide coating and silanization (RTD); III: industrial treatment followed by adhesive application (XPBond, Dentsply Caulk); IV: adhesive (XPBond); V: adhesive (Prime&Bond NT, Dentsply Caulk); VI: silane (Calibra Silane, Dentsply Caulk); VII: no treatment. Adhesives were used in the self-curing mode. Two cements (Sealbond, RTD - group 1, and Calibra, Dentsply Caulk - groups 11 to VII) were applied on the posts to produce cylindrical specimens. Post/cement interfaces were evaluated under SEM. The surface of the industrially coated posts was examined using energy dispersive analysis by x-ray. Cylinders were cut to obtain microtensile sticks that were loaded in tension at a crosshead speed of 0.5 mm/min until failure. Statistical analysis was performed using Kruskal-Wallis analysis of variance followed by Dunn`s multiple range test for post-hoc comparisons (p < 0.05). Weibull analysis was also performed. Results: The post/cement bond strength was significantly higher on fiber posts treated industrially (I: 23.14 +/- 8.05 MPa; II: 21.56 +/- 7.07 MPa; III: 22.37 +/- 7.00 MPa) or treated with XPBond adhesive (IV: 21.03 +/- 5.34 MPa) when compared to Prime&Bond NT application (V: 14.05 +/- 5.06 MPa), silanization (VI: 6.31 +/- 4.60 MPa) or no treatment (VII: 4.62 +/- 4.31) of conventional fiber posts (p < 0.001). Conclusion: The experimental industrial surface treatment and the adhesive application enhanced fiber post to resin cement interfacial strength. Industrial pretreatment may simplify the clinical luting procedure.

Post space cleaning using a new nickel titanium endodontic drill combined with different cleaning regimens

This study compared the effect of two drills and five cleaning regimens on post space debridement. One hundred extracted premolars were instrumented and obturated with warm vertical compaction of gutta percha. The teeth were divided into two groups according to the drill used to remove gutta percha/sealer and for post space preparation: a Largo drill (Largo; Dentsply, St Quentin en Yvelines, France) or a MTwo-PF drill (Sweden&Martina, Due Carrare, Padova, Italy). The following cleaning regimens were used: EDTA, ultrasonics, ultrasonics + EDTA, phosphoric acid, and distilled water. Scanning electron microscopic images of the post spaces were taken, and the presence of debris and of open dentin tubules were evaluated. The ultrasonics + EDTA, phosphoric acid, and EDTA groups were comparable in open tubules scores for both drills and in debris scores after the use of MTwo-PF (p > 0.05). The ultrasonics and control groups performed significantly worse (p < 0.05). The MTwo-PF drill resulted as effective as the Largo drill in obtaining a good post space cleaning, especially when followed by ultrasonics + EDTA irrigant regimen.

Bcl-X-L translocation in renal tubular epithelial cells in vitro protects distal cells from oxidative stress

Background. The molecular pathogenesis of different sensitivities of the renal proximal and distal tubular cell populations to ischemic injury, including ischemia-reperfusion (IR)-induced oxidative stress, is not well-defined. An in vitro model of oxidative stress was used to compare the survival of distal [Madin-Darby canine kidney (MDCK)] and proximal [human kidney-2 (HK-2)] renal tubular epithelial cells, and to analyze for links between induced cell death and expression and localization of selected members of the Bcl-2 gene family (anti-apoptotic Bcl-2 and Bcl-X-L, pro-apoptotic Bax and Bad), Methods. Cells were treated with 1 mmol/L hydrogen peroxide (H2O2) Or were grown in control medium for 24 hours. Cell death (apoptosis) was quantitated using defined morphological criteria. DNA gel electrophoresis was used for biochemical identification. Protein expression levels and cellular localization of the selected Bcl-2 family proteins were analyzed (West ern immunoblots, densitometry, immunoelectron microscopy). Results. Apoptosis was minimal in control cultures and was greatest in treated proximal cell cultures (16.93 +/- 4.18% apoptosis) compared with treated distal cell cultures (2.28 +/- 0.85% apoptosis, P < 0.001). Endogenous expression of Bcl-X-L and Bax, but not Bcl-2 or Bad, was identified in control distal cells, Bcl-X-L and Bax had nonsignificant increases (P > 0.05) in these cells. Bcl-2, Bax, and Bcl-X-L, but not Bad, were endogenously expressed in control proximal cells. Bcl-X-L was significantly decreased in treated proximal cultures (P < 0.05), with Bas and Bcl-2 having nonsignificant increases (P > 0.05). Immunoelectron microscopy localization indicated that control and treated hut surviving proximal cells had similar cytosolic and membrane localization of the Bcl-2 proteins. In comparison, surviving cells in the treated distal cultures showed translocation of Bcl-X-L from cytosol to the mitochondria after treatment with H2O2, a result that was confirmed using cell fractionation and analysis of Bcl-XL expression levels of the membrane and cytosol proteins. Bax remained distributed evenly throughout the surviving distal cells, without particular attachment to any cellular organelle. Conclusion. The results indicate that in this in vitro model, the increased survival of distal compared with proximal tubular cells after oxidative stress is best explained by the decreased expression of anti-apoptotic Bcl-X-L in proximal cells, as well as translocation of Bcl-X-L protein to mitochondria within the surviving distal cells.

X-ray fluorescence with synchrotron radiation to elemental analysis of lead and calcium content of primary teeth

Primary teeth were analyzed by micro-SRXRF. The aim of this study was to determine the elemental distribution of lead and calcium in different regions of primary incisor of children living in a notoriously contaminated area (Santo Amaro da Purificacao, Bahia State, Brazil). The measurements were performed in standard geometry of 45 incidence, exciting with a white beam and using a conventional system collimation (orthogonal slits) in the XRF beamline at the Synchrotron Light National Laboratory (Campinas, Brazil). (C) 2009 Elsevier Ltd. All rights reserved.

Flat-Oval Root Canal Preparation with Self-Adjusting File Instrument: A Micro-Computed Tomography Study

Introduction: The aim of this study was to evaluate the root canal preparation in flat-oval canals treated with either rotary or self-adjusting file (SAF) by using micro-tomography analysis. Methods: Forty mandibular incisors were scanned before and after root canal instrumentation with rotary instruments (n = 20) or SAF (n = 20). Changes in canal volume, surface area, and cross-sectional geometry were compared with preoperative values. Data were compared by independent sample t test and chi(2) test between groups and paired sample t test within the group (alpha = 0.05). Results: Overall, area, perimeter, roundness, and major and minor diameters revealed no statistical difference between groups (P > .05). In the coronal third, percentage of prepared root canal walls and mean increases of volume and area were significantly higher with SAF (92.0%, 1.44 +/- 0.49 mm(3), 0.40 +/- 0.14 mm(2), respectively) than rotary instrumentation (62.0%, 0.81 +/- 0.45 mm(3), 0.23 +/- 0.15 mm2, respectively) (P < .05). SAF removed dentin layer from all around the canal, whereas rotary instrumentation showed substantial untouched areas. Conclusions: In the coronal third, mean increases of area and volume of the canal as well as the percentage of prepared walls were significantly higher with SAF than with rotary instrumentation. By using SAF instruments, flat-oval canals were homogenously and circumferentially prepared. The size of the SAF preparation in the apical third of the canal was equivalent to those prepared with #40 rotary file with a 0.02 taper. (J Endod 2011;37:1002-1007)

Physicochemical Properties of Methacrylate Resin-based Root Canal Sealers

Introduction: This study assessed in vitro the physicochemical properties of 2 methacrylate resin-based sealers (Epiphany SE and Hybrid Root SEAL), comparing the results with a well-established epoxy resin-based sealer (AH Plus). Methods: Five samples of each material were used for each test (setting time, flow, radiopacity, dimensional change after setting, and solubility) according to American National Standards Institute/American Dental Association (ANSI/ADA) Specification 57. The samples were assigned to 3 groups: I, AH Plus; II, Epiphany SE; and III, Hybrid Root SEAL. The distilled and deionized water used at the solubility test was submitted to atomic absorption spectrometry to observe the presence of Ca2+, K+, Ni2+, and Zn2+ ions. In addition, the surface morphology of the specimens was analyzed by means of scanning electron microscopy (SEM). Statistical analysis was performed by using one-way analysis of variance and Tukey-Kramer test (P < .05). Results: Flow, radiopacity, and solubility of all sealers were in accordance with ANSI/ADA. The setting time of Hybrid Root SEAL did not agree with ANSUADA requirements. The dimensional change of all sealers was greater than the values considered acceptable by ANSI/ADA. The spectrometry analysis showed significant Ca2+ ions release for AH Plus. In SEM analysis, Hybrid Root SEAL presented spherical monomers with inferior size than AH Plus and Epiphany SE. Conclusions: It might be concluded that physicochemical properties of the tested sealers conformed to ANSI/ADA (2000) standardization, except for the setting time of Hybrid Root SEAL and the dimensional change of all sealers, which did not fulfill the ANSI/ADA requirements. (J Endod 2010;36:1531-1536)

Ultrastructural Analysis of Radicular Dentine Surface Submitted to CO(2) Laser at Different Parameters

Background: There are no reported studies comparing different parameter settings of the CO(2) laser and irradiation direction considering their effect on the morphology of radicular dentine surface. Purpose: To evaluate the alterations of radicular dentine (cervical, middle, and apical thirds) irradiated with CO(2) laser at different potencies and irradiation directions. Study Design: Roots of 35 canines were prepared and randomly distributed according to the laser potency: GI: no laser treatment (control) (n = 5); GII, 2 W (n = 10); GIII: 4 W (n = 10); GIV: 6 W (n = 10). Each group (excepting GI) was divided in two subgroups according to the irradiation distance (n = 5): (A) parallel and (B) perpendicular to the root canal walls. The roots were splited longitudinally and analyzed by scanning electron microscopy in a qualiquatitative way. The scores were submitted to Kruskal-Wallis and Dunn`s tests. Results: No significant statistical differences were observed among root canal thirds (P > 0.05). The specimens irradiated with 2 W were statistically different (P < 0.05) from those irradiated with 4 and 6 W, which were statistically similar between themselves (P > 0.05). With 2, 4, and 6 W at in parallel irradiation and 2 W in perpendicular direction, the surface showed a fissured aspect. With 4 W in perpendicular direction and 6 W in parallel and perpendicular direction, surface was modified by laser action and exhibited fused areas. Conclusions: The intensity of the effects is dependent on the laser-irradiation dosimetries. Alterations were more intense when higher parameters were used. Microsc. Res. Tech. 72:737-743, 2009. (C) 2009 Wiley-Liss, Inc.

Bond strength of Epiphany (TM) Sealer combined with different adhesive systems photo-activated with LED and QTH

The Epiphany (TM) Sealer is a new dual-curing resin-based sealer and has been introduced as an alternative to gutta-percha and traditional root canal sealers. The canal filling is claimed to create a seal with the dentinal tubules within the root canal system producing a `monoblock` effect between the sealer and dentinal tubules. Therefore, considering the possibility to incorporate the others adhesive systems, it is important to study the bond strength of the resulting cement. Forty-eight root mandibular canines were sectioned 8-mm below CEJ. The dentine discs were prepared using a tapered diamond bur and irrigated with 1% NaOCl and 17% EDTA. Previous the application Epiphany (TM) Sealer, the Epiphany (TM) Primer, AdheSE, and One Up Bond F were applied to the root canal walls. The LED and QTH (Quartz Tungsten Halogen) were used to photo-activation during 45 s with power density of 400 and 720 mW/cm(2), respectively. The specimens were performed on a universal testing machine at a cross-head speed of 1 mm/min until bond failure occurred. The force was recorded and the debonding values were used to calculate Push-out bond strength. The analysis of variance (ANOVA) and Tukey`s post-hoc tests showed significant statistical differences (P < 0.05) to Epiphany (TM) Sealer/Epiphany (TM) Primer/QTH and EpiphanyTM Sealer/AdheSE/QTH, which had the highest mean values of bond strength. The efficiency of resin-based filling materials are dependent the type of light curing unit used including the power density, the polymerization characteristics of these resin-based filling materials, depending on the primer/adhesive used.

Bond Strength of Fiber Posts to Weakened Roots After Resin Restoration With Different Light-Curing Times

Introduction: This study evaluated the bond strength of translucent fiber posts to experimentally weakened radicular dentin restored with composite resin and polymerized with different light-exposure time. Methods: Roots of 60 maxillary incisors were used. Twenty-four hours after obturation, the filling materials of root canals were removed to a depth of 12 mm, and 4 groups were randomly formed. In 3 groups, root dentin was flared to produce a space between fiber post and canal walls. In the control group, the roots were not experimentally weakened. The flared roots were bulk restored with composite resin, which was light-activated through the translucent post for 40, 80, or 120 seconds. Posts were cemented, and after 24 hours, all roots were sectioned transversely in the coronal, middle, and apical regions, producing 1-mm-thick slices. Push-out test was performed, and failure modes were observed. Results The quantitative analysis showed significant statistical difference only among groups (P <.001). Comparing the weakened/restored groups, composite light-exposure time did not influence the results. Overall, adhesive failures occurred more frequently than other types of failures. Cohesive failures occurred only in the weakened/restored roots. Conclusions Intracanal root restoration with composite resin and translucent fiber posts provided similar or higher bond strength to dentin than the control group, regardless of the light-exposure time used for polymerization. (J Endod 2009;35:1034-1039)

Atomic Absorption Spectrometry and Scanning Electron Microscopy Evaluation of Concentration of Calcium Ions and Smear Layer Removal With Root Canal Chelators

Aim. The aim of this study was to evaluate the concentration of calcium ions and smear layer removal by using root canal chelators according to flame atomic absorption spectrophotometry and scanning electron microscopy. Forty-two human maxillary central incisors were irrigated with 15% ethylenediaminetetraacetic acid (EDTA), 10% citric acid, 10% sodium citrate, apple vinegar, 5% acetic acid, 5% malic acid, and sodium hypochlorite. The concentration of calcium ions was measured by using flame atomic absorption spectrometry, and smear layer removal was determined by scanning electron microscopy. Mean +/- standard deviation, one-way analysis of variance, Tukey-Kramer, Kruskal-Wallis, Dunn, and kappa tests were used for statistical analysis. The use of 15% EDTA resulted in the greatest concentration of calcium ions followed by 10% citric acid; 15% EDTA and 10% citric acid were the most efficient solutions for removal of smear layer. (J Endod 2009;35:727-730)

Bond Strength of Epiphany Sealer Prepared with Resinous Solvent

This study evaluated in vitro the bond strength of Epiphany sealer prepared with resinous solvent of Epiphany system (Thinning resin) by using a push-out test. Forty maxillary canines were sectioned transversally below the cementoenamel junction to provide 4-mm-thick dentin disks that were centered in aluminum rings and embedded in acrylic resin. Root canals were prepared with tapered diamond bur. Intraradicular dentin was treated with 1% NaOCl for 30 minutes, 17% ethylenediaminetetraacetic acid for 5 minutes, and flushed with distilled water for 1 minute. The specimens were randomly distributed into 4 groups (n = 10) according to the filling material: GI, Epiphany without photoactivation; GII, Epiphany prepared with solvent without photoactivation; Gill, Epiphany followed by photoactivation; and GIV, Epiphany prepared with solvent followed by photoactivation. After the setting time, the specimens were submitted to the push-out test. The highest mean value (14.91 +/- 2.82 MPa) was obtained with Epiphany prepared with solvent followed by photoactivation (GIV), which was statistically different (P < .01) from the other groups. Groups I (8.15 +/- 2.47 MPa), II (9.46 +/- 2.38 MPa), and III (9.80 +/- 2.51 MPa) had inferior bond strength values and were statistically similar among themselves (P > .01). The resinous solvent of Epiphany system increased the bond strength of Epiphany sealer to dentin walls when followed by photoactivation. (J Endod 2009;35: 251-255)