Tissue response to an epoxy resin-based root canal sealer

The objective of the present study was to evaluate two different types of root canal sealers: AH Plus (an epoxy resin-based sealer) and Fill Canal (a zinc oxide-eugenol based sealer). A total of 34 root canals with vital pulp from dogs' premolars were used. After instrumentation, the root canals were filled with gutta-percha and AH Plus or gutta-percha and Fill Canal sealers using a classical technique of lateral condensation. After histological processing, the sections were stained with hematoxylineosin or Mallory's trichrome stain. Inflammatory cells or areas of necrosis were not associated with AH Plus. Hard tissue formation apically to the material was observed in 14 specimens. The Fill Canal sealer presented an inflammatory response of moderate intensity in the periapical region, mainly adjacent to the material.

Reactionary dentinogenesis after applying restorative materials and bioactive dentin matrix molecules as liners in deep cavities prepared in nonhuman primate teeth

Objective: the aim of this in vivo study was to evaluate the response of the pulp-dentin complex following application of resin-modified glass-ionomer cement, calcium hydroxide hard-setting cement and EDTA-soluble preparation of dentine matrix proteins (ESDP) in deep cavities prepared in non-human primate teeth. Methods: Eighteen deep Class V buccal cavities were prepared in premolars of four capuccin monkeys. In Groups 1 and 2, the cavity floor was lined with ESDP or a resin-modified glass-ionomer cement (Vitrebond - 3M ESPE), respectively. In Group 3 (control), the cavity was lined with a hard setting calcium hydroxide cement (Dycal - Dentsply). The cavities were subsequently filled with amalgam. After 6 months, the animals were sacrificed and the teeth were prepared for microscopic assessment. Six-micron thick serial sections were stained with H/E, Masson's trichrome and Brown & Brenn techniques. Results: No inflammatory pulpal response was observed for all experimental and control Groups. However, the amount of reactionary dentin deposition differed between groups in the rank order ESDP (Group 1) > calcium hydroxide (Group 3) > resin-modified glass-ionomer (Group 2). These differences were statistically significant. Conclusions: All materials were biocompatible when applied in deep cavities. ESDP stimulated higher deposition of reactionary dentin matrix than Vitrebond and Dycal.

Pulpal temperature increases with Er : YAG laser and high-speed handpieces

Statement of problem. During tooth preparation, both high-speed handpieces and lasers generate heat, which, if not controlled, can cause pulpal necrosis.Purpose. The aim of this study was to compare temperature increases produced by a high-speed dental handpiece with those produced by a relatively new instrument, the Er:YAG (erbium: yttrium-aluminum-garnet) laser.Material and methods. Thirty bovine mandibular incisors were reduced to an enamel/dentin thickness of 2.5 mm. Class V preparations were completed to a depth of 2.0 mm, measured with a caliper or by a mark oil the burs. A thermocouple was placed inside the pulp chamber to determine temperature increases (degreesC). Analysis was performed on the following groups (n = 10): Group 1, high-speed handpiece without water cooling, Group 11, high-speed handpiece with water cooling (30 mL/min), and Group III, the noncontact Er:YAG laser (2.94 mum at 350 mJ/10 Hz) with water cooling (4.5 mL/min). The temperature increases were recorded by a computer linked to the thermocouples. The data were analyzed using the Kruskal-Wallis test. The Dunn multiple comparison test was used as post hoc test (alpha = .05).Results. The average temperature rises were: 11.64degreesC (+/-4.35) for Group 1, 0.96degreesC (+/-0.71) for Group 11, and 2.69degreesC (+/-1.12) for Group III. There were no statistical differences between Groups 11 and III, both 11 and III differed from Group I significantly (P = .000 and P = .002, respectively).Conclusion. The preparations made with the high-speed and the laser instrument generated similar heat increases under water cooling. Water cooling was essential to avoid destructive temperature increases when using both the high-speed handpiece and laser.

Sealing evaluation of the cervical base in intracoronal bleaching

Discoloration of non-vital teeth is an esthetic deficiency frequently requiring bleaching treatment. The purpose of this study was to evaluate in vitro the cervical base efficacy in order to prevent or to minimize the leakage along the root canal filling and into the dentinal tubules. Thirty-eight extracted single-root human teeth were used, which were biomechanically prepared, filled, and divided into three experimental groups: G1, a cervical base was applied (3 mm of thickness) below the cemento-enamel junction, with resin-modified glass-ionomer cement (Vitremer); G2, the base was done with glass-ionomer cement (Vidrion R); and G3 (Control), did not receive any material as base. A mixture of sodium perborate and hydrogen peroxide 30% was placed inside the pulp chamber for 3 days, and the access opening was sealed with Cimpat. This procedure was repeated thrice. Soon after this, a paste of calcium hydroxide was inserted into the pulp chamber for 14 days. All teeth were covered with two layers of sticky wax, except the access opening, and immersed in blue India Ink for 5 days. The results did not show statistically significant differences between the three groups concerning the leakage inside the dentinal tubules. Regarding the apical direction, a statistical difference (ANOVA P < 0.05) was observed among the experimental group G1 and control group G3. No statistically significant difference was observed between G2 and G3 groups. Therefore, the placement of a cervical base before internal bleaching procedures is still recommended.