In Vitro Study of Fracture Load and Fracture Pattern of Ceramic Crowns: A Finite Element and Fractography Analysis

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Effect of Resin Cement System and Root Region on the Push-out Bond Strength of a Translucent Fiber Post

Objectives: This study evaluated the bond strength of luting systems for bonding glass fiber posts to root canal dentin. The hypothesis tested was that there are no differences in bond strength of glass fiber posts luted with different cement systems.Methods: Forty bovine incisors were randomly assigned to five different resin cement groups (n=8). After endodontic treatment and crown removal, translucent glass fiber posts were bonded into the root canal using five different luting protocols (self-cured cement and etch-and-rinse adhesive system; dual-cured cement and etch-and-rinse adhesive system; self-cured cement and self-etch adhesive system; dual-cured cement and self-etch adhesive system; and dual-cured self-adhesive cement). Push-out bond strength was evaluated at three different radicular levels: cervical, middle, and apical. The interface between resinous cement and the post was observed using a stereoscopic microscope.Results: Analysis of variance showed a statistically significant difference among the cements (p<0.05) and the root canal thirds (p<0.05). The self-adhesive resinous cement had lower values of retention.Conclusions: The resin cements used with etch-and-rinse and self-etch adhesive systems seem to be adequate for glass fiber post cementation.

Ovary peltate trichomes of Zeyheria montana (Bignoniaceae): Developmental ultrastructure and secretion in relation to function

center dot Background and Aims Nectar production in the Bignoniaceae species lacking a nectariferous functional disc is ascribed to trichomatic glands around the ovary base and/or on the inner corolla wall. Nevertheless, knowledge about the secretion and function of these glands is very incomplete. The purpose of this paper is to study, from a developmental viewpoint, the ultrastructure, histochemistry and secretory process of the peltate trichomes on the ovary of Zeyheria montana, a species in the Bignoniaceae which has a rudimentary disc.center dot Methods Samples of the gynoecium at various developmental stages were fixed and processed for light and electron microscopy. Histochemistry and cytochemistry tests were performed to examine the chemical composition of exudates. Thin layer chromatography was used to determine the presence of alkaloids and terpenes in gynoecium and fruit extracts, and in fresh nectar stored in the nectar chamber.center dot Key Results Peltate trichomes at different developmental stages appear side by side from floral budding up to pre-dispersal fruit. Large plastids with an extensive internal membrane system consisting of tubules filled with lipophilic material, abundant smooth endoplasmic reticulum, few Golgi bodies, lipophilic deposits in the smooth endoplasmic reticulum and mitochondria, and scattered cytoplasmic oil droplets are the main characteristics of mature head cells. The secretion which accumulates in the subcuticular space stains positively for hydrophilic and lipophilic substances, with lipids prevailing for fully peltate trichomes. Histochemistry and thin layer chromatography detected terpenes and alkaloids. Fehling's test to detect of sugars in the secretion was negative.center dot Conclusions the continuous presence and activity of peltate trichomes on the ovary of Z. montana from early budding through to flowering and fruiting set, and its main chemical components, alkaloids and terpenes, suggest that they serve a protective function and are not related to the floral nectar source or to improving nectar quality.

Growth and reproductive dynamics of the South American red shrimp, Pleoticus muelleri (Crustacea: Solenoceridae), from the southeastern coast of Brazil

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Repeated unrewarded scent exposure influences the food choice of stingless bee foragers, Melipona scutellaris

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Frugivory on Margaritaria nobilis L.f. (Euphorbiaceae): poor investment and mimetism.

Dehiscent fruits of Euphorbiaceae usually have two stages of seed dispersal, autochory followed by myrmecochory. Two stages of Margaritaria nobilis seed dispersal were described, the first stage autochoric followed by ornithocoric. Their dehiscent fruits are green and after they detached from the tree crown and fall on the ground, they open and expose blue metallic cocas. We studied the seed dispersal system of Margaritaria nobilis in a semi-deciduous forest in Brazil. In 80 h of focal observations, we recorded only 12 visits of frugivores, however the thrush Turdus leucomelas was the only frugivore that swallowed the fruits on the tree crown. Pitylus fuliginosus (Fringilidae) and Pionus maximiliani (Psittacidae) were mainly pulp eaters, dropping the seeds below the tree. on the forest floor, after fruits dehiscence, jays (Cyanocorax chrysops), guans (Penelope superciliaris), doves (Geotrygon montana) and collared-peccaries (Pecari tajacu) were observed eating the blue diaspores of M. nobilis. Experiments in captivity showed that scaly-headed parrots (Pionus maximiliani), toco toucans (Ramphastos toco), jays (Cyanochorax chrysops), and guans (Penelope superciliaris) consumed the fruits and did not prey on the seeds before consumption. The seeds collected from the feces did not germinate in spite of the high viability. The two stages of seed dispersal in M. nobilis resembles the dispersal strategies of some mimetic species. However M. nobilis seeds are associated with an endocarp, it showed low investment in nutrients, and consistent with this hypothesis, M. nobilis shared important characteristics with mimetic fruits, such as bright color display, long seed dormancy and protection by secondary compounds.

Morphology, development and homologies of the perianth and floral nectaries in Croton and Astraea (Euphorbiaceae-Malpighiales)

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Visceral pigmentation in four Dendropsophus species (Anura: Hylidae): Occurrence and comparison

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Microhabitat use by Peucetia flava (Oxyopidae) on the glandular plant Rhyncanthera dichotoma (Melastomataceae)

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Structural resistance in immature teeth using root reinforcements in vitro

The purpose of this study was to evaluate in vitro the efficacy of root reinforcements by light-cured composite resin or zirconium fiber post in simulated immature non-vital teeth. Fifty-six bovine incisors teeth were used for this study. The crown of each tooth was removed in the medium third to obtain a standard length of 30 mm. The specimens were divided into four groups (n = 14): G1) the root canals were instrumented and enlarged to simulate immature non-vital teeth and were reinforced with a light-cured composite resin using a translucent curing post (Luminex system); (G2) the specimens were instrumented, enlarged and they received root reinforcement with zirconium fiber post; G3 (positive control): they received similar treatment to the G1 and G2 groups, but did not receive root reinforcement; G4 (negative control): the roots were not weakened and did not receive reinforcement. Every tooth was submitted to compressive force using an Instron testing machine with an angle of 45&DEG; at a speed of 1 mm min(-1) until the fracture. The results showed a markedly increased resistance to fracture in the G1 and G2 (122.38 and 122.08 kgf, respectively). Among the results of G1 and G2 there was not any significant difference (P > 0.05) but they were significantly different from the control groups (P < 0.05). The conclusion is that the use of root reinforcements with zirconiun fiber post or composite resin can increase significantly the structural resistance of the weakened teeth, decreasing the risk of the fracture.

Dentine microhardness after different methods for detection and removal of carious dentine tissue

There are several methods for identifying carious dentinal tissue aiming to avoid removal of healthy dentinal tissue. Objectives: The purpose of this study was to test different methods for the detection of carious dentinal tissue regarding the amount of carious tissue removed and the remaining dentin microhardness after caries removal. Material and methods: The dentin surfaces of 20 bovine teeth were exposed and half of the surface was protected with nail polish. Cariogenic challenge was performed by immersion in a demineralizing solution for 14 days. After transverse cross-section of the crown, the specimens were divided into four groups (n=10), according to the method used to identify and remove the carious tissue: "Papacarie", Caries-detector dye, DIAGNOdent and Tactile method. After caries removal, the cross-sectional surface was included in acrylic resin and polished. In a microhardness tester, the removed dentin thickness and the Vickers microhardness of the following regions were evaluated: remaining dentin after caries removal and superficial and deep healthy dentin. Results: ANOVA and Tukey's test (alpha=0.05) were performed, except for DIAGNOdent, which did not detect the presence of caries. Results for removed dentin thickness were: "Papacarie" (424.7 +/- 105.0; a), Caries-detector dye (370.5 +/- 78.3; ab), Tactile method (322.8 +/- 51.5; bc). Results for the remaining dentin microhardness were: "Papacarie" (42.2 +/- 10.5; bc), Caries-detector dye (44.6 +/- 11.8; bc), Tactile method (24.3 +/- 9.0; d). Conclusions: DIAGNOdent did not detect the presence of carious tissue; Tactile method and "Papacarie" resulted in the least and the most dentinal thickness removal, respectively; Tactile method differed significantly from "Papacarie" and Caries-detector dye in terms of the remaining dentin microhardness, and Tactile method was the one which presented the lowest microhardness values.

Effects of cement thickness and bonding on the failure loads of CAD/CAM ceramic crowns: Multi-physics FEA modeling and monotonic testing

Objective. To determine the influence of cement thickness and ceramic/cement bonding on stresses and failure of CAD/CAM crowns, using both multi-physics finite element analysis and monotonic testing.Methods. Axially symmetric FEA models were created for stress analysis of a stylized monolithic crown having resin cement thicknesses from 50 to 500 mu m under occlusal loading. Ceramic-cement interface was modeled as bonded or not-bonded (cement-dentin as bonded). Cement polymerization shrinkage was simulated as a thermal contraction. Loads necessary to reach stresses for radial cracking from the intaglio surface were calculated by FEA. Experimentally, feldspathic CAD/CAM crowns based on the FEA model were machined having different occlusal cementation spaces, etched and cemented to dentin analogs. Non-bonding of etched ceramic was achieved using a thin layer of poly(dimethylsiloxane). Crowns were loaded to failure at 5 N/s, with radial cracks detected acoustically.Results. Failure loads depended on the bonding condition and the cement thickness for both FEA and physical testing. Average fracture loads for bonded crowns were: 673.5 N at 50 mu m cement and 300.6 N at 500 mu m. FEA stresses due to polymerization shrinkage increased with the cement thickness overwhelming the protective effect of bonding, as was also seen experimentally. At 50 mu m cement thickness, bonded crowns withstood at least twice the load before failure than non-bonded crowns.Significance. Occlusal "fit" can have structural implications for CAD/CAM crowns; pre-cementation spaces around 50-100 mu m being recommended from this study. Bonding benefits were lost at thickness approaching 450-500 mu m due to polymerization shrinkage stresses. (C) 2012 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Marginal and Internal Discrepancies Related to Margin Design of Ceramic Crowns Fabricated by a CAD/CAM System

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

The interaction between atoms of Au and Cu with clean Si(111) surface: A study combining synchrotron radiation grazing incidence X-ray fluorescence analysis and theoretical calculations

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Refractive index changes in photochromic SbPO4-WO3 glass by exposure to band-gap radiation

We report photoinduced photo-darkening in SbPO4-WO3 glass by exposure to 532 nm light with a power density of 143 mW/cm(2). The time of exposure was varied between 0 and 256 min following which visible photo-darkening, peaking at 850 nm was observed. Spectrophotometer measurement of absorption was performed for both treated and untreated regions of the sample. Time exposure to below band-gap light results in a single exponent Gaussian absorption function over an exceptionally wide range of wavelengths (500 nm-1600 nm), with a 1/e width of 647.5 nm. Kramers-Kronig transform of the change in the absorption indicates a negative local change in the refractive index. The dispersed refractive index change at 1550 nm, Delta n, is calculated to be similar to -5 x 10(-8). The peak absorption increases with time of exposure and the photo-darkening remains irreversible at room temperature. Crown Copyright (C) 2010 Published by Elsevier B.V. All rights reserved.