Investigation of Mn-Implanted n-Si by Low-Energy Ion Beam Deposition

Mn ions were implanted to n-type Si(0 0 1) single crystal by low-energy ion beam deposition technique with an energy of 1000 eV and a dose of 7.5 x 10^{17} cm^{-2}. The samples were held at room temperature and at 300degreesC during implantation. Auger electron spectroscopy depth profiles of samples indicate that the Mn ions reach deeper in the sample implanted at 300degreesC than in the sample implanted at room temperature. X-ray diffraction measurements show that the structure of the sample implanted at room temperature is amorphous while that of the sample implanted at 300degreesC is crystallized. There are no new phases found except silicon both in the two samples. Atomic force microscopy images of samples indicate that the sample implanted at 300degreesC has island-like humps that cover the sample surface while there is no such kind of characteristic in the sample implanted at room temperature. The magnetic properties of samples were investigated by alternating gradient magnetometer (AGM). The sample implanted at 300degreesC shows ferromagnetic behavior at room temperature.

Explosive consolidation of amorphous cobalt-based alloys

This paper addresses the explosive consolidation of amorphous cobalt-based alloys. Using the experimental setup introduced in the present paper, specimens with high compact density, excellent magnetic properties and great wearability have been made. In comparison with permalloy and ferrite, the present specimens exhibit superior magnetic properties. Therefore, the compact is deemed as being a promising material for magnetic recording heads.

Deformation Behavior Of Fe-Based Bulk Metallic Glass During Nanoindentation

Fe-based bulk metallic glasses (BMGs) normally exhibit super high strength but significant brittleness at ambient temperature. Therefore, it is difficult to investigate the plastic deformation behavior and mechanism in these alloys through conventional tensile and compressive tests due to lack of distinct macroscopic plastic strain. In this work, the deformation behavior of Fe52Cr15Mo9Er3C15B6 BMG was investigated through instrumented nanoindentation and uniaxial compressive tests. The results show that serrated flow, the typical plastic deformation feature of BMGs, could not be found in as-cast and partially crystallized samples during nanoindentation. In addition, the deformation behavior and mechanical properties of the alloy are insensitive to the applied loading rate. The mechanism for the appearance of the peculiar deformation behavior in the Fe-based BMG is discussed in terms of the temporal and spatial characteristics of shear banding during nanoindentation.

Effect of Fe content on the thermal stability and dynamic mechanical behavior of NdAlNiCu bulk metallic glasses

The dependence of microstructure and thermal stability on Fe content of bulk Nd60Al10Ni10Cu20-xFex (0 less than or equal to x less than or equal to 20) metallic glasses is investigated by means of differential scanning calorimetry (DSC), X-ray diffraction (XRD) and high-resolution transmission electron micrograph (HRTEM). All samples exhibit typical amorphous feature under the detect limit of XRD, however, HRTEM results show that the microstructure of Nd60Al10Ni10Cu20-xFex alloys changes from a homogeneous amorphous phase to a composite structure consisting of clusters dispersed in amorphous matrix by increasing Fe content. Dynamic mechanical properties of these alloys with controllable microstructure are studied, expressed via storage modulus, the loss modulus and the mechanical damping. The results reveal that the storage modulus of the alloy without Fe added shows a distinct decrease due to the main a relaxation. This decrease weakens and begins at a higher temperature with increasing Fe content. The mechanism of the effect of Fe addition on the microstructure and thermal stability in this system is discussed in terms of thermodynamics viewpoints. (C) 2004 Elsevier B.V. All rights reserved.

Microstructural evolution and formation of nanocrystalline intermetallic compound during surface mechanical attrition treatment of cobalt

Nanocrystalline intermetallic Co3Fe7 was produced on the surface of cobalt via surface mechanical attrition (SMA). Deformationinduced diffusion entailed the formation of a series of solid solutions. Phase transitions occurred depending on the atomic fraction of Fe in the surface solid solutions: from hexagonal close-packed (<4% Fe) to face-centered cubic (fcc) (4-11% Fe), and from fcc to body-centered cubic (>11% Fe). Nanoscale compositional probing suggested significantly higher Fe contents at grain boundaries and triple junctions than grain interiors. Short-circuit diffusion along grain boundaries and triple junctions dominate in the nanocrystalline intermetallic compound. Stacking faults contribute significantly to diffusion. Diffusion enhancement due to high-rate deformation in SMA was analyzed by regarding dislocations as solute-pumping channels, and the creation of excess vacancies. Non-equilibrium, atomic level alloying can then be ascribed to deformation-induced intermixing of constituent species. The formation mechanism of nanocrystalline intermetallic grains on the SMA surface can be thought of as a consequence of numerous nucleation events and limited growth. (C) 2007 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

La estructura y propiedades magnéticos de las nanopartículas de Fe50Ni50 obtenidas mediante el método de explosión eléctrica de hilo

[Es]Actualmente ninguna área científica es ajena a la revolución de la nanociencia; las nanopartículas atraen el interés de muchos investigadores desde el punto de vista de la ciencia fundamental y para sus aplicaciones tecnológicas. Las nanopartículas ofrecen la posibilidad de fabricar sensores que sean capaces de detectar desde un virus hasta concentraciones de substancias patógenas que no pueden ser detectadas por los métodos convencionales. Hoy en día existes 82 tratamientos contra el cáncer basadas en la utilización de nanopartículas y los materiales composite con nanopartículas se utilizan como medio de protección frente la radiación del rango de microondas. En la rama de ciencias ambientales, las nanopartículas metálicas sirven como materiales anticontaminantes. En este trabajo se ha estudiado la estructura y las propiedades magnéticas de las nanopartículas de FeNi preparadas mediante el método de explosión eléctrica de hilo. Con la técnica de Rayos–X(DRX) se ha determinado que las nanopartículas se cristalizan en un sistema cúbico FCC con un parámetro de celda de 3.596 Å, también, se ha obtenido el tamaño de dominio coherente que es de 35 nm. La muestra se ha sometido a un programa de temperatura controlada para seguir la evolución de la estructura cristalina y del tamaño del cristal, tanto en atmósfera oxidante como en vacío. Para el aprendizaje de los microscopios utilizados en este trabajo, se ha asistido al curso “Fundamentos de microscopia electrónica de barrido y microanálisis” impartido por SGIker de la UPV/EHU. Se han empleado los microscopios electrónicos SEM y TEM para obtener imágenes de gran resolución de la muestra y analizar su contenido elemental. Partiendo de las imágenes sacadas por el SEM se ha calculado el valor medio del tamaño de las partículas de la muestra, 58 nm. Mediante el Mastersizer 2000 se ha medido el tamaño de las partículas y/o agregados por método de difracción láser, disgregando la muestra todo lo posible hasta conseguir el tamaño medio que se aproxime al de una sola partícula, 100nm. Por último, para la caracterización magnética se ha servido del VSM que mide el momento magnético de una muestra cuando ésta vibra en presencia de un campo magnético estático, consiguiendo una imanación de saturación de 125 emu/g. Hemos fabricado y caracterizado las nanopartículas magnéticas de hierro-níquel y los resultados obtenidos han sido enviados a un congreso especializado de ciencia de materiales (ISMANAM - 2013, Italia).

Exchange biased FeNi/FeMn bilayers with coercivity and switching field enhanced by FeMn surface oxidation

FeNi/FeMn bilayers were grown in a magnetic field and subjected to heat treatments at temperatures of 50 to 350 degrees C in vacuum or in a gas mixture containing oxygen. In the as-deposited state, the hysteresis loop of 30 nm FeNi layer was shifted. Low temperature annealing leads to a decrease of the exchange bias field. Heat treatments at higher temperatures in gas mixture result in partial oxidation of 20 nm thick FeMn layer leading to a nonlinear dependence of coercivity and a switching field of FeNi layer on annealing temperature. The maximum of coercivity and switching field were observed after annealing at 300 degrees C.

A Study on iron-based amorphous alloys : alloy development, thermodynamics and soft magnetism

Metallic glass has since its debut been of great research interest due to its profound scientific significance. Magnetic metallic glasses are of special interest because of their promising technological applications. In this thesis, we introduced a novel series of Fe-based alloys and offer a holistic review of the physics and properties of these alloys. A systematic alloy development and optimization method was introduced, with experimental implementation on transition metal based alloying system. A deep understanding on the influencing factors of glass forming ability was brought up and discussed, based on classical nucleation theory. Experimental data of the new Fe-based amorphous alloys were interpreted to further analyze those influencing factors, including reduced glass transition temperature, fragility, and liquid-crystal interface free energy. Various treatments (fluxing, overheating, etc.) were discussed for their impacts on the alloying systems' thermodynamics and glass forming ability. Multiple experimental characterization methods were discussed to measure the alloys' soft magnetic properties. In addition to theoretical and experimental investigation, we also gave a detailed numerical analysis on the rapid-discharge-heating-and-forming platform. It is a novel experimental system which offers extremely fast heating rate for calorimetric characterization and alloy deformation.

Crystal Coulomb energies: I. Organic donor-acceptor complexes--a review. II. Classical Ewald calculations of the Coulomb binding energy of four donor-acceptor crystals and Wurster's blue perchlorate. III. A rapid-convergence quantum-mechanical formalism for crystal electronic energies

Chapter I

Theories for organic donor-acceptor (DA) complexes in solution and in the solid state are reviewed, and compared with the available experimental data. As shown by McConnell et al. (Proc. Natl. Acad. Sci. U.S., 53, 46-50 (1965)), the DA crystals fall into two classes, the holoionic class with a fully or almost fully ionic ground state, and the nonionic class with little or no ionic character. If the total lattice binding energy 2ε₁ (per DA pair) gained in ionizing a DA lattice exceeds the cost 2ε_o of ionizing each DA pair, ε₁ + ε_o less than 0, then the lattice is holoionic. The charge-transfer (CT) band in crystals and in solution can be explained, following Mulliken, by a second-order mixing of states, or by any theory that makes the CT transition strongly allowed, and yet due to a small change in the ground state of the non-interacting components D and A (or D⁺ and A^-). The magnetic properties of the DA crystals are discussed.

Chapter II

A computer program, EWALD, was written to calculate by the Ewald fast-convergence method the crystal Coulomb binding energy E_C due to classical monopole-monopole interactions for crystals of any symmetry. The precision of E_C values obtained is high: the uncertainties, estimated by the effect on E_C of changing the Ewald convergence parameter η, ranged from ± 0.00002 eV to ± 0.01 eV in the worst case. The charge distribution for organic ions was idealized as fractional point charges localized at the crystallographic atomic positions: these charges were chosen from available theoretical and experimental estimates. The uncertainty in E_C due to different charge distribution models is typically ± 0.1 eV (± 3%): thus, even the simple Hückel model can give decent results.

E_C for Wurster's Blue Perchl orate is -4.1 eV/molecule: the crystal is stable under the binding provided by direct Coulomb interactions. E_C for N-Methylphenazinium Tetracyanoquino- dimethanide is 0.1 eV: exchange Coulomb interactions, which cannot be estimated classically, must provide the necessary binding.

EWALD was also used to test the McConnell classification of DA crystals. For the holoionic (1:1)-(N,N,N',N'-Tetramethyl-para- phenylenediamine: 7,7,8,8-Tetracyanoquinodimethan) E_C = -4.0 eV while 2ε_o = 4.6₅ eV: clearly, exchange forces must provide the balance. For the holoionic (1:1)-(N,N,N',N'-Tetramethyl-para- phenylenediamine:para-Chloranil) E_C = -4.4 eV, while 2ε_o = 5.0 eV: again EC falls short of 2ε₁. As a Gedankenexperiment, two nonionic crystals were assumed to be ionized: for (1:1)-(Hexamethyl- benzene:para-Chloranil) E_C = -4.5 eV, 2ε_o = 6.6 eV; for (1:1)- (Napthalene:Tetracyanoethylene) E_C = -4.3 eV, 2ε_o = 6.5 eV. Thus, exchange energies in these nonionic crystals must not exceed 1 eV.

Chapter III

A rapid-convergence quantum-mechanical formalism is derived to calculate the electronic energy of an arbitrary molecular (or molecular-ion) crystal: this provides estimates of crystal binding energies which include the exchange Coulomb inter- actions. Previously obtained LCAO-MO wavefunctions for the isolated molecule(s) ("unit cell spin-orbitals") provide the starting-point. Bloch's theorem is used to construct "crystal spin-orbitals". Overlap between the unit cell orbitals localized in different unit cells is neglected, or is eliminated by Löwdin orthogonalization. Then simple formulas for the total kinetic energy Q^(XT)_λ, nuclear attraction [λ/λ]^XT, direct Coulomb [λλ/λ'λ']^XT and exchange Coulomb [λλ'/λ'λ]^XT integrals are obtained, and direct-space brute-force expansions in atomic wavefunctions are given. Fourier series are obtained for [λ/λ]^XT, [λλ/λ'λ']^XT, and [λλ/λ'λ]^XT with the help of the convolution theorem; the Fourier coefficients require the evaluation of Silverstone's two-center Fourier transform integrals. If the short-range interactions are calculated by brute-force integrations in direct space, and the long-range effects are summed in Fourier space, then rapid convergence is possible for [λ/λ]^XT, [λλ/λ'λ']^XT and [λλ'/λ'λ]^XT. This is achieved, as in the Ewald method, by modifying each atomic wavefunction by a "Gaussian convergence acceleration factor", and evaluating separately in direct and in Fourier space appropriate portions of [λ/λ]^XT, etc., where some of the portions contain the Gaussian factor.

Conduction-electron localized-moment interaction in palladium-silicon base amorphous alloys containing transition metals

The electrical and magnetic properties of amorphous alloys obtained by rapid quenching from the liquid state have been studied. The composition of these alloys corresponds to the general formula M_xPd_80-xSi₂₀, in which M stands for a metal of the first transition series between chromium and nickel and x is its atomic concentration. The concentration ranges within which an amorphous structure could be obtained were: from 0 to 7 for Cr, Mn and Fe, from 0 to 11 for Co and from 0 to 15 for Ni. A well-defined minimum in the resistivity vs temperature curve was observed for all alloys except those containing nickel. The alloys for which a resistivity minimum was observed had a negative magnetoresistivity approximately proportional to the square of the magnetization and their susceptibility obeyed the Curie-Weiss law in a wide temperature range. For concentrated Fe and Co alloys the resistivity minimum was found to coexist with ferromagnetism. These observations lead to the conclusion that the present results are due to a s-d exchange interaction. The unusually high resistivity minimum temperature observed in the Cr alloys is interpreted as a result of a high Kondo temperature and a large s-d exchange integral. A low Fermi energy of the amorphous alloys (3.5 eV) is also responsible for the anomalies due to the s-d exchange interaction.

Ferromagnetic Resonance Force Microscopy

A new approach to magnetic resonance was introduced in 1992 based upon detection of spin-induced forces by J. Sidles [1]. This technique, now called magnetic resonance force microscopy (MRFM), was first demonstrated that same year via electron paramagnetic resonance (EPR) by D. Rugar et al. [2]. This new method combines principles of magnetic resonance with those of scanned probe technology to detect spin resonance through mechanical, rather than inductive, means. In this thesis the development and use of ferromagnetic resonance force microscopy (FMRFM) is described. This variant of MRFM, which allows investigation of ferromagnetic samples, was first demonstrated in 1996 by Z. Zhang et al. [3]. FMRFM enables characterization of (a) the dynamic magnetic properties of microscale magnetic devices, and (b) the spatial dependence of ferromagnetic resonance within a sample. Both are impossible with conventional ferromagnetic resonance techniques.

Ferromagnetically coupled systems, however, pose unique challenges for force detection. In this thesis the attainable spatial resolution - and the underlying physical mechanisms that determine it - are established. We analyze the dependence of the magnetostatic modes upon sample dimensions using a series of microscale yttrium iron garnet (YIG) samples. Mapping of mode amplitudes within these sample is attained with an unprecedented spatial resolution of 15μm. The modes, never before analyzed on this scale, fit simple models developed in this thesis for samples of micron dimensions. The application of stronger gradient fields induces localized perturbation of the ferromagnetic resonance modes. The first demonstrations of this effect are presented in this study, and a simple theoretical model is developed to explain our observations. The results indicate that the characteristics of the locally-detected ferromagnetic modes are still largely determined by the external fields and dimensions of the entire sample, rather than by the localized interaction volume (i.e., the locale most strongly affected by the local gradient field). Establishing this is a crucial first step toward understanding FMRFM in the high gradient field limit where the dispersion relations become locally determined. In this high gradient field regime, FMRFM imaging becomes analogous with that of EPR MRFM.

FMRFM has also been employed to characterize magnetic multilayers, similar to those utilized in giant magnetoresistance (GMR) devices, on a lateral scale 40 x 40μm. This is orders of magnitude smaller than possible via conventional methods. Anisotropy energies, thickness, and interface qualities of individual layers have been resolved.

This initial work clearly demonstrates the immense and unique potential that FMRFM offers for characterizing advanced magnetic nanostructures and magnetic devices.

Preparação e caracterização de microesferas poliméricas à base de metacrilato de glicidila e divinilbenzeno com propriedades magnéticas

Nesta Dissertação, foram sintetizadas microesferas poliméricas com propriedades magnéticas à base de metacrilato de glicidila e divinilbenzeno pela técnica de polimerização em suspensão. O material utilizado para conferir as propriedades magnéticas ao copolímero foi magnetita sintetizada no laboratório. Foram estudados os efeitos da modificação da magnetita com ácido oleico, da velocidade de agitação, do teor de agente reticulante, do teor de material magnético adicionado e do teor de agente de suspensão sobre as características das partículas poliméricas obtidas. As microesferas foram caracterizadas quanto ao seu aspecto morfológico, à estabilidade térmica, à incorporação de material magnético e quanto às suas propriedades magnéticas. A quantidade de partículas de ferro incorporadas foi afetada pela velocidade de agitação durante a síntese, pelo teor de material magnético adicionado, pela fase de dispersão do material magnético e pelo teor de monômeros no copolímero. A estabilidade térmica dos copolímeros foi afetada, principalmente, pelo teor de material magnético incorporado e pelo teor de monômeros, levando em consideração resinas com a mesma quantidade de material magnético adicionado. A magnetização de saturação para as microesferas foi afetada pelo teor de material magnético incorporado. A modificação da superfície da magnetita com ácido oleico foi considerada importante para a incorporação do material magnético na matriz do copolímero.Partículas poliméricas magnéticas com comportamento superparamagnéticos foram obtidas com morfologia esférica e magnetização de saturação de 7,11 (emu/g), utilizando razão molar de monômeros de 50/50 %, 1 % de PVA, 20 % de magnetita modificada com ácido oleico adicionada à fase orgânica e velocidade de agitação mecânica de 500 rpm

Preparação de microesferas poliméricas à base de estireno, acetato de vinila e divinilbenzeno com propriedades magnéticas

Microesferas poliméricas magnéticas à base de estireno (STY), divinilbenzeno (DVB), acetato de vinila (VAc) e ferro foram preparadas via polimerização em suspensão e semissuspensão. Foram estudadas as influências da concentração de VAc adicionado na polimerização e a presença de ferro sobre as características das partículas poliméricas obtidas. Estas partículas foram caracterizadas por espectrometria de absorção na região do infravermelho (FT-IR), análise térmica (TGA/DTA), microscopia óptica (MO), microscopia eletrônica de varredura (SEM) e magnetometria de amostra vibrante (VSM). Foram obtidas com sucesso microesferas poliméricas com propriedades magnéticas à base de estireno, divinilbenzeno e acetato de vinila. Estes materiais apresentaram bom controle morfológico, com maior rendimento na faixa de 120 a 75 m. Apresentaram também boas propriedades magnéticas (22,62 a 73,75 emu/g) com comportamento próximo de materiais superparamagnéticos e boa estabilidade térmica (444 C)

Síntese e caracterização de copolímeros à base de poli(metacrilato de metila) e divinilbenzeno com propriedades magnéticas

Nesta dissertação, foram sintetizados copolímeros à base de poli(metacrilato de metila) (PMMA), divinilbenzeno (DVB) com propriedades magnéticas pela técnica de polimerização em suspensão. O material utilizado para conferir propriedade magnética foi o ferro. Foi estudada a influência das variáveis reacionais para a formação de microesferas (ordem de adição das fases orgânica e aquosa e a dispersão do ferro antes e após a pré-polimerização), o efeito da concentração de ferro adicionado na polimerização, a influência da razão molar MMA/DVB na formação do copolímero, o efeito do tipo de agente de suspensão e a velocidade de agitação para a síntese dos copolímeros. Os copolímeros foram caracterizados quanto à morfologia, estabilidade térmica, teor de ferro incorporado, distribuição de tamanho de partículas, propriedades magnéticas, área superficial, volume e tamanho de poros. As análises de propriedades magnéticas mostraram que os materiais obtidos não apresentaram ciclos de histerese, estando assim próximos de um material com propriedades superparamagnéticas, com magnetização de saturação entre 8,0 e 13,0 emu/g. Os copolímeros sintetizados com velocidade de agitação 500 RPM, temperaturade 90 C, tempo de polimerização de 24h, monômeros MMA/DVB 50/50 (% molar); razão volumétrica fase orgânica/fase aquosa 1/3, diluente heptano, grau de diluição 100% apresentaram melhor controle morfológico, melhor magnetização de saturação, tamanho de partículas menores e maior tamanho de poros

Effects of magnetostriction and superlattice formation in ferromagnetic thin films

The contribution to the magnetic uniaxial perpendicular anisotropy which arises from substrate constraint through magnetostrictive effects has been measured in Ni-Fe and Ni-Co thin films evaporated on substrates at room temperature. This was accomplished by measuring the perpendicular anisotropy before and after removal of the film from the substrate. Data are given for the fcc crystal structure regions of both alloy systems, but data for Ni-Co include compositions with less than 60% Ni which have a small percentage of the hcp phase mixed with the fcc phase. The constraint contribution to the perpendicular anisotropy correlates well with the value of the bulk magnetostriction constant using the equation ∆K_˔=3/2λ_sσ. Measured values of isotropic stress for films thicker than 600 Å were 1.6 x 10¹⁰ dyn/cm². In films less than 600 Å thick the isotropic stress decreased with decreasing thickness. After removal of the films from the substrates, the measured perpendicular anisotropy deviated from the expected geometrical shape anisotropy near pure Ni in both alloys. This indicates that additional significant sources of anisotropy exist at these compositions.

The effect of substrate constraint on the crystalline anisotropy K₁ of Ni-Fe epitaxial films has been studied by use of a film removal technique, which involves the evaporation of an epitaxial layer of LiF on MgO, the epitaxial growth of the metallic film on the LiF, and the stripping of the film with water soluble tape. Films ranging in composition from 50% to 100% Ni have been studied. For compositions below 90% Ni the experimental values agree reasonably well with the first order theoretical prediction, ∆K₁=[-9/4(C₁₁-C₁₂)λ² 100+9/2C₄₄λ²111].

In order to compare the magnetic properties of epitaxial thin films more completely with the properties of bulk single crystals, Ni-Fe films ranging in composition from 60% to 90% Ni, which were evaporated epitaxially on (100) MgO substrates, have been subsequently annealed at 400°C in a vacuum of less than 10^-7 Torr to form the ordered Ni₃Fe structure near the 75% composition. This ordered structure has been confirmed by electron diffraction.

The saturation magnetization at Ni₃Fe increased about 6% with ordering which is in good agreement with previous bulk data. Measurements of the magnetocrystalline anisotropy energy K₁ for the epitaxial films show the same large changes with ordering as observed in bulk single crystal samples. In the (001) plane the magnetostriction constants ^λ100, ^λ111 are directly related to the induced anisotropy due to a uniform uniaxial strain in the [100] and [110] directions respectively. Assuming that the elastic constants of a film are the same as in bulk material and are unchanged by ordering, the changes in strain sensitivity with ordering for the epitaxial films are found to be in good agreement with values predicted from bulk data. The exchange constant A as measured by ferromagnetic resonance has been measured at the Ni₃Fe composition and found to increase 25% with ordering. This seems to indicate a significant increase in the Curie temperature which has only been inferred indirectly for bulk material.