AM(1-x)Al(x)O(3-x) (A=Na or K; M=Nb or Ta): New anion-deficient Perovskite oxides exhibiting oxide ion conduction

Anion-deficient perovskite oxides of the formula AM(1-x)Al(x)O(3-x) (A = Na or K; M = Nb or Ta) have been prepared for 0 < x less than or equal to 0.5. Diffraction experiments reveal that while the potassium compounds adopt orthorhombic/cubic perovskite structures similar to the parent KNbO3/KTaO3, the sodium compound, NaNb0.5Al0.5O2.5, possesses a brownmillerite/LaSr-CuAlO5-like superstructure. Al-27 NMR spectra show an exclusive tetrahedral oxygen coordination for AI(III) in Na-Nb0.5Al0.5O2.5 (I) and both tetrahedral and octahedral coordination for Al(III) in KNb0.5Al0.5O2.5 (II). The results suggest a long-range and short-range ordering of oxide ion vacancies in I and II respectively. Electrical conductivity measurements show a significant oxide ion conduction for KNb1-xAlxO3-x, with the conductivity increasing with x up to x = 0.5. The differences in the Arrhenius plots of the ionic conductivity of I and II have been rationalized in terms of the long-range and short-range ordering of oxide ion vacancies in the anion-deficient perovskite oxides.

Concentration-dependent NMR and conductivity studies of (PEG)(x)NH4ClO4

Films of (PEG)(x)NH4ClO4 (x = 5 to 1000) were prepared and characterized. The physical properties are observed to be a sensitive function of concentration. Hygroscopicity increases as salt content increases. Conductivity peaks (sigma = 2.7 x 10(-6) S/cm) at x = 46. The H-1 NMR line width has a minimum at x = 46, while that of Cl-35 monotonically increases with salt concentration, indicating that the complex is essentially a protonic conductor.

Evidence for correlation effects in Sr2RuO4 from resonant and x-ray photoemission spectroscopy

We study the electronic structure of Sr2RuO4, a noncuprate layered superconductor (T-c=0.93 K), using electron spectroscopy. X-ray photoemission spectroscopy shows that the single particle occupied density of states (DOS) is in fair agreement with the calculated DOS. However, resonant photoemission spectroscopy across the Ru 4p-4d threshold establishes the existence of a correlation satellite to the Ru 4d band. The results indicate substantial charge-transfer character at the Fermi level, with on-site correlations U-dd comparable in magnitude to the Ru-O hopping integral, like the cuprates.

Exceptionally long crystal formation from 4-(3-bromopropyloxy)salicylaldehyde. X-ray crystallographic investigation

Unusually long (>14 cm) crystalline needles grow from 4-(3-bromopropyloxy)salicylaldehyde 1 presumably as a consequence of Br ... Br interactions; the powdered form of 1 shows one order of magnitude greater SHG activity realtive to urea.

Low temperature synthesis and hcaracterization of Ag2S1-x Tez(O

A low-temperature route for the synthesis of Ag2S,Ag2Te and their solid solutions Ag2S1-xTex(0 less-than-or-equal-to x less-than-or-equal-to 1) is reported. Ag2S is prepared by the direct addition of silver nitrate solution to thiourea, while Ag2Te is prepared by reacting silver nitrate solution with tellurium in nitric acid and subsequently reducing it with hydrazine hydrate. The solid solutions of Ag2S and Ag2Te are obtained by the addition of nitrate solutions of silver and tellurium to thiourea followed by its reduction with hydrazine hydrate. The method enables the synthesis of low-temperature crystalline phase of Ag2S1-xTex solid solutions. The powder X-ray diffraction studies suggest that the solid solutions of compositions x < 0.3 have a phase akin to alpha-Ag2S and those with compositions x > 0.6 are similar to alpha-Ag2Te. In the intermediate range of compositions (x = 0.4 and 0.5), the solid solutions are found to be mixtures of alpha-Ag2S and alpha-Ag2Te phases which transform totally to alpha-Ag2S phase on prolonged annealing at about 473 K.

Monte Carlo simulation of low temperature phase diagrams of YBa2Cu3O6+x

We report the results of Monte Carlo simulation of oxygen ordering in the oxygen deficient portion (x<0.5) of YBa2Cu3O6+x at low temperatures. We find qualitative agreement among cluster - variation, Monte Carlo and transfer matrix methods. However, low temperature and ground state simulations clearly indicate the presence of a tetragonal phase. There is also evidence for two second order phase transition lines separating the tetragonal and the �double cell� ortho II phase. The effect of decreasing the inter-chain repulsion on oxygen ordering has also been investigated.

Monte Carlo study of the phase boundary of YBa2Cu3O6 +x

A model hamiltonian previously introduced to study the oxygen ordering is considered. The phase boundary is isolated by studying the relaxation behaviour of the order parameters. Our results are consistent with the published Monte Carlo results except at low temperatures.

Giant magnetoresistance in lanthanum strontium yttrium manganese oxides (La(1-x)Sr(x-z)YuMnO(3))

Electron transport and magnetic properties of several compositions of the La1-xSx-zYzMnO3 system have been investigated in order to explore the effect of yttrium substitution on the magnetoresistance and related properties of these manganates. Yttrium substitution lowers the T-c and the insulator-metal transition temperature, while increasing the peak resistivity. A comparison of the properties of La1-xSrx-zYzMnO3 with the corresponding La1-xCax-zYzMnO3 compositions shows that the observed properties can be related to the average size of the A-site cations.

H-1 MAS NMR study of protonic conduction in layered HNbWO6 center dot xH(2)O (x=1.5, 0.5)

H-1 Magic Angle Spinning (MAS) NMR of layered HNbWO6 . xH(2)O (x = 1.5, 0.5) is carried out at room temperature and at various spinning speeds (1-12 kHz). Results on the fully hydrated sample (x = 1.5) are consistent with the model of diffusion of H3O+ ions within the layers. In the partially dehydrated sample (x = 0.5) an exchange between the distinctly present cage protons and H3O+ protons leads to protonic conduction.

Microstructure control and wear of Al2O3-SiC-(Al,Si) composites made by melt oxidation

Ceramic matrix composites of Al2O3-SiC-(Al,Si) have been fabricated by directed melt oxidation of aluminum alloys into SiC particulate preforms. The proportions of Al2O3, alloy, and porosity in the composite can be controlled by proper selection of SLC particle size and the processing temperature. The wear resistance of composites was evaluated in pin-on-disk experiments against a hard steel substrate. Minimum wear rate comparable to conventional ceramics such as ZTA is recorded for the composition containing the highest fraction of alloy, owing to the development of a thin and adherent tribofilm with a low coefficient of friction.

Structural, optical and EPR studies on ZnO:Cu nanopowders prepared via low temperature solution combustion synthesis

Cu (0.1 mol%) doped ZnO nanopowders have been successfully synthesized by a wet chemical method at a relatively low temperature (300 degrees C). Powder X-ray diffraction (PXRD) analysis, scanning electron microscopy (SEM), Transmission electron microscopy (TEM), Fourier transformed infrared (FTIR) spectroscopy, UV-Visible spectroscopy, Photoluminescence (PL) and Electron Paramagnetic Resonance (EPR) measurements were used for characterization. PXRD results confirm that the nanopowders exhibit hexagonal wurtzite structure of ZnO without any secondary phase. The particle size of as-formed product has been calculated by Williamson-Hall (W-H) plots and Scherrer's formula is found to be in the range of similar to 40 nm. TEM image confirms the nano size crystalline nature of Cu doped ZnO. SEM micrographs of undoped and Cu doped ZnO show highly porous with large voids. UV-Vis spectrum showed a red shift in the absorption edge in Cu doped ZnO. PL spectra show prominent peaks corresponding to near band edge UV emission and defect related green emission in the visible region at room temperature and their possible mechanisms have been discussed. The EPR spectrum exhibits a broad resonance signal at g similar to 2.049, and two narrow resonances one at g similar to 1.990 and other at g similar to 1.950. The broad resonance signal at g similar to 2.049 is a characteristic of Cu2+ ion whereas the signal at g similar to 1.990 and g similar to 1.950 can be attributed to ionized oxygen vacancies and shallow donors respectively. The spin concentration (N) and paramagnetic susceptibility (X) have been evaluated and discussed. (C) 2011 Elsevier B. V. All rights reserved.

Influence of glycosidic linkage on the nature of carbohydrate binding in beta-prism I fold lectins: An X-ray and molecular dynamics investigation on banana lectin-carbohydrate complexes

The three crystal structures reported here provide details of the interactions of mannose and the mannosyl-alpha-1,3-mannose component of a pentamannose with banana lectin and evidence for the binding of glucosyl-alpha-1,2-glucose to the lectin. The known structures involving the lectin include a complex with glucosyl-beta-1,3-glucose. Modeling studies on the three disaccharide complexes with the reducing end and the nonreducing end at the primary binding site are also provided here. The results of the Xray and modeling studies show that the disaccharides with an alpha-1,3 linkage prefer to have the nonreducing end at the primary binding site, whereas the reducing end is preferred at the site when the linkage is beta-1,3 in mannose/glucose-specific beta-prism I fold lectins. In the corresponding galactose-specific lectins, however, alpha-1,3-linked disaccharides cannot bind the lectin with the nonreducing end at the primary binding site on account of steric clashes with an aromatic residue that occurs only when the lectin is galactose-specific. Molecular dynamics simulations based on the known structures involving banana lectin enrich the information on lectin-carbohydrate interactions obtained from crystal structures. They demonstrate that conformational selection as well as induced fit operate when carbohydrates bind to banana lectin.

Quasicrystals, crystals and multiple twins in rapidly solidified Al-Cr-Si, Al-Mn-Si and Al-Mn-Cr-Si alloys

The coexistence of quasicrystals and rational approximant structures (RAS) has been observed in melt-spun Al80Cr14Si6, Al80Mn14Si6 and Al75Mn10Cr5Si10 alloys. The presence of a b.c.c. alpha-AlMnSi phase in Al-Mn-Si and alpha-AlMnSi(Cr) phase in Al-Mn-Cr-Si has been seen. A multiple twinning around an irrational axis of the RAS has been reported in an aggregate of fine size cubic crystallites in all three alloys. Selected area diffraction patterns show that the crystalline aggregate symmetry is linked to the icosahedral point group symmetry (m35). Various ways of expressing the twin relationship in the cubic crystalline aggregates have been discussed. The thermal stability of the icosahedral phase at high temperatures reveals that the icosahedral phase in Al-Mn-Si and Al-Mn-Cr-Si alloys transforms to alpha-AlMnSi at temperatures of 690 and 670 K, respectively. In Al-Cr-Si alloy, heating to a high temperature (615 K) leads to the transformation of the icosahedral phase into a new metastable phase having an ordered cubic structure equivalent to alpha-AlMnSi. The occurrence of multiple twinning leading to icosahedral symmetry in the as-spun Al-Cr-Si alloy is presumably due to this metastable phase. Copyright (C) 1996 Acta Metallurgica Inc.

Quantum corrections to the conductivity in a perovskite oxide: A low-temperature study of LaNi1-xCoxO3 (0?x?0.75)

In this paper we propose to study the evolution of the quantum corrections to the conductivity in an oxide system as we approach the metal-insulator (M-I) transition from the metallic side. We report here the measurement of the low-temperature (0.1 K0.65), m takes on large values and ?(0)=0. We explain the temperature dependence of ?(T), for T<2 K, on the metallic side (x?0.4), as arising predominantly from electron-electron interactions, taking into account the diffusion-channel contribution (which gives m=0.5) as well as the Cooper-channel contribution. In this regime, the correction to conductivity, ??(T), is a small fraction of ?(T). However, as the M-I transition is approached (x?xc), ??(T) starts to dominate ?(T) and the above theories fail to explain the observed ?(T).

Dielectric function and optical conductivity of TiOx (0.8

Reflection electron energy-loss spectra are reported for the family of compounds TiOx over the entire homogeneity range (0.8 < a: < 1.3). The spectra exhibit a plasmon feature on the low-energy side, while several interband transitions are prominent at higher energies. The real and imaginary parts of dielectric functions and optical conductivity for these compounds are determined using the Kramers-Kronig analysis. The results exhibit systematic behavior with varying oxygen stoichiometry.