Densification and coarsening of SnO2-based materials containing manganese oxide

The present work presents results on natural sintering of tin dioxide ceramics, prepared by a chemical route or by conventional mixing and containing manganese (X-Mn = Mn/(Mn + Sn)(atomic) with 0 less than or equal to X(Mn)less than or equal to 0.15). This cation, which is practically insoluble in SnO2 network, stays at the grain surface. During thermal treatment (500 degrees C less than or equal to T-s less than or equal to 1400 degrees C), as long as the manganese surface concentration is lower than a critical value, equal to 5.10(-6) mol m(-2), no densification takes place. As soon as this value is reached, densification and grain growth occur simultaneously. The shrinkage kinetics is fast and high rho/rho(t) values can be obtained (for example. rho/rho(t)=0.95 for T-s=1300 degrees C and X-Mn=0.004). The dependence between manganese content, manganese distribution, grain size and sintering behaviour is also discussed. (C) 1998 Published by Elsevier B.V. Limited.

Evaluation of shear bond strength at the interface of two porcelains and pure titanium injected into the casting mold at three different temperatures

Statement of problem. Titanium has physical and mechanical properties, which have led to its increased use in dental prostheses despite casting difficulties due to high melting point and formation of oxide layers which affect the metal-ceramic bond strength.Purpose. This in vitro study evaluated the shear bond strength of the interface of 2 dental porcelains and pure titanium injected into a mold at 3 different temperatures.Material and methods. Using commercially pure (cp) titanium bars (Titanium, Grade I) melted at 1668degreesC and cast at mold temperatures of 430degreesC, 700degreesC or 900degreesC, 60 specimens were machined to 4 x 4 mm, with a base of 5 x 1 mm. The 4-mm surfaces were airborne-particle abraded with 100 mum aluminum oxide before applying and firing the bonding agent and evaluating the 2 porcelains (Triceram/Triline ti and Vita Titankeramik). Ten specimens were prepared for each temperature and porcelain combination Shear bond testing was performed in a universal testing machine, with a 500-kg load cell and crosshead speed of 0.5 mm/min. The specimens were loaded until failure. The interfaces of representative fractured specimens of each temperature were examined with a scanning electron microscope (SEM) and energy dispersive spectrometer (EDS). Data for shear bond strength (MPa) were statistically analyzed by 2-way ANOVA and the Tukey test (alpha = .05).Results. The results showed significant differences for the metal/porcelain interaction effect (P = .0464). There were no significant differences for the 2 porcelains (P = .4250). The Tukey test showed a significant difference between the pair cp Ti 430degreesC Triceram and cp Ti 900degreesC Triceram, with respective mean values and SDs of 59.74 +/- 11.62 and 34.03 +/- 10.35 MPa.Conclusion. Triceram porcelain showed a bond strength decrease with an increase in the mold temperature for casting titanium. The highest bond strength for Vita porcelain and the best metal-ceramic interface observed with the SEM were found with the mold temperature of 700degreesC.

Systematic consideration of petiole anatomy of species of Echinodorus Richard (Alismataceae) from north-eastern Brazil

Petiole anatomy of the north-eastern Brazilian species Echinodorus glandulosus, E. palaefolius, E. pubescens, E subalatus, E lanceolatus and E paniculatus were examined. All species had petioles with an epidermis composed of tabular cells with thin walls. The chlorenchyma just below the epidermis alternates with collateral vascular bundles. The interior of the petiole is filled by aerenchyma with ample open spaces or lacunas. The lacunas are bridged at intervals by plates, or by diaphragm-like linkages. There are lactiferous ducts and groups of fibres throughout the entire length of the petiole, but more frequently in the chlorenchyma. Important taxonomic characteristics for the genus Echinodorus include the shape and outline of the petiole in transversal section, the presence of winged extensions, and the number of vascular bundle arcs. Exceptions occur in E. lanceolatus and E. paniculatus, whose petioles have similar anatomic patterns. A comparative chart of the petiole anatomic characteristics analyzed is presented. (c) 2007 Elsevier GmbH. All rights reserved.

FIBER TYPES DISTRIBUTION IN THE DIGASTRIC MUSCLE OF TUFTED CAPUCHIN MONKEY (CEBUS-APELLA)

Fiber types distribution in the diagastric muscle of tufted capuchin monkey was studied by means of NADH-TR, myosin-ATPase, after alkaline and acid preincubations and SDH histochemical reactions. Three different types of fibers were found presenting an equal distribution. The percentage and types of fibers were as follow: 18.2 % SO (Slow Oxydative), 38.4 % FOG (Fast Oxydative Glycolytic) and 43.4 % FG (Fast Glycolytic). FG fibers revealed the largest area. The relatively high concentration of fast twitch (81.2 %) seems to indicate this muscle is involved with the acceleration and fast speed of jaw movements. Aerobic metabolism represented by SO + FOG fibers (56.6 %) suggests that this muscle possesses an additional role than that related to the lowering of the jaw.

Fracture strength of bovine incisors after intra-radicular treatment with MTA in an experimental immature tooth model

Aim To evaluate, using an experimental immature tooth model, the fracture resistance of bovine incisors submitted to different reinforcement treatments with mineral trioxide aggregate (MTA).Methodology An immature tooth model was created by sectioning the coronal and apical portions of 40 bovine incisors 8 mm above and 12 mm below the cementoenamel junction. The root canals were irrigated with 1.0% sodium hypochlorite. They were enlarged both coronally and apically using number 703 carbide burs (ISO: 500-104-168-007-021) and their internal diameter was standardized to 2.1 mm. The specimens were assigned to four groups (n = 10): GI-control (without filling); GII-apical MTA plug + filling with gutta-percha and endodontic sealer; GIII-filling with MTA; GIV-apical MTA plug + filling with MTA + metallic post (Reforpost I). A polyether impression material was used to simulate the periodontal ligament. The specimens were submitted to a compressive load at a crosshead speed of 0.5 mm min(-1) in a servo-hydraulic universal testing machine (MTS 810) applied at 45 degrees to the long axis of the tooth until failure. Data were submitted to statistical analysis by the Kruskal-Wallis test at 5% significance level.Results GIV presented the highest fracture resistance (32.7N) and differed significantly from the other groups (P < 0.05). No statistically difference was found between GII (16.6N) and GIII (23.4N) (P > 0.05). GIII had a significantly higher fracture resistance than GI (P < 0.05).Conclusions the use of MTA + metallic post as an intra-radicular reinforcement treatment increased the resistance to fracture of weakened bovine teeth in an experimental immature tooth model.

Hardness and compressive strength of indirect composite resins: effects of immersion in distilled water

The aim of this study was to evaluate the effect of ageing in distilled water on the hardness and compressive strength of a direct composite resin Z100, a feldspatic porcelain (Noritake) and three indirect composites (Artglass, Solidex and Targis). For the Vickers hardness tests, five disk-shaped specimens (2 x 4 mm) of each material were prepared according to the manufacturers' instructions. The hardness tests were conducted using a Vickers diamond indentor. Compressive strength measurements were recorded on cylindrical specimens with a diameter of 6 mm and a length of 12 mm. The compression tests were carried out with a constant cross-head speed of 0.5 mm min(-1) on a mechanical test machine. For each material, 10 specimens were tested after 7 days of dry storage at 37 +/- 1 degreesC and 10 specimens were tested after water storage at 37 +/- 1 degreesC for 180 days. Noritake porcelain specimens showed higher hardness values than the composites. Among the composite materials, Z100 promoted the highest VHN values, regardless of the ageing periods. The results showed that Solidex and Z100 had the highest compressive strength values. Ageing in water reduced the hardness for all composites, but had no long-term effect on the compressive strength.

Determination of pore size distribution in soybean seed coats by mercury porosimetry

In this work we applied mercury porosimetry for the investigation of soybean seed coats. By using this method it was possible to determine the pore size distribution and also the pore size dispersion that is present in seed coats. The results showed that for the studied soybean genotype the seed coats had a characteristic pore diameter, but deviation of this size was not negligible. Finally, the results were confirmed by electron microscopy.

Flexural strength of autopolymerizing denture reline resins with microwave postpolymerization treatment

Statement of problem. Microwave postpolymerization has been Suggested as a method to improve the mechanical strength of repaired denture base materials. However, the effect of microwave heating oil the flexural strength of the autopolymerizing denture reline resins has not been investigated.Purpose. This study analyzed the effect of microwave postpolymerization on the flexural strength of 4 autopolymerizing reline resins (Duraliner II, Kooliner, Ufi Gel Hard, and Tokuso Rebase Fast) and 1 heat-polymerized resin (Lucitone 550).Material and methods. For each material, 80 specimens (64 X 10 X 3.3 mm) were polymerized according to the manufacturer's instructions and divided into 10 groups (n = 8). Control group specimens remained as processed. Before testing, the specimens were Subjected to postpolymerization in a microwave oven using different power (500, 5,50, or 650 W) and time (3, 4, or 5 Minutes) settings. Load measurements (newtons) were made at a crosshead speed of 5 mm/min using a 3-point bending device with a span of 50 mill. The flexural strength values were calculated in MPa. Data analyses included 3-way and 2-way analysis of variance and the Tukey Honestly Significant Difference test (alpha=.05).Results. The flexural strengths of resins Duraliner 11 and Kooliner were significantly increased (P=.0015 and P=.0046, respectively) with the application of microwave irradiation using different time/power combinations. The materials Lucitone 550, Tokuso Rebase Fast, and Ufi Gel Hard demonstrated no significant strength improvement compared to the corresponding control. Only after microwave postpolymerization irradiation for 3 minutes at 550 W did Lucitione 550 show significantly higher flexural strength than Tokuso Rebase Fast and Ufi Gel Hard relining resins.Conclusion. Microwave postpolymerization irradiation can be an effective method for increasing the flexural strength of Duraliner II (at 650 W) and Kooliner (at 550 W and 650 W for 5 minutes).

Densification and electrical conductivity of fast fired manganese-doped ceria ceramics

Reactive pure and manganese-doped (5% and 10 at.%) ceria nanosized powders were prepared by the polymeric precursor technique. Physical properties of powder materials were studied by X-ray diffraction, nitrogen adsorption, and diffuse reflectance infrared Fourier transform spectroscopy. Characterization of powder compacts after fast firing at 1200 degrees C for 5 min was carried out by scanning electron microscopy and impedance spectroscopy measurements. The bulk apparent density of sintered pellets was determined for pellets of different compositions sintered at 1200 degrees C. A gradual decrease of the particle size occurs with increasing doping content. Relatively high values of apparent density were obtained after fast firing doped specimens at 1200 degrees C. DRIFT spectra evidence that a fraction of Mn ions was segregated onto particles surface. The electrical resistivity of sintered pellets reveals different mechanisms of conduction depending on the Mn content. (C) 2005 Elsevier B.V All rights reserved.

EFFECT OF TREATMENT WITH GROWTH-REGULATORS AND SCARIFICATION ON THE TOLERANCE TO WATER-STRESS IN SEEDS OF ORYZA-SATIVA LCVIAC-165

The effect of treatment of seeds of Oryza sativa L. cv. IAC 165 with gibberellic acid, 6-benzyladenine and ethrel on the tolerance to the water stress were analysed. Gibberellic acid had no effect and 6-benzyladenine and ethrel promoted slight increase in the tolerance to water stress, specially in darkness. After scarification, those growth regulator presented no effect. Our results suggest that 6-benzyladenine and ethrel promoted water stress tolerance due to the decrease in the resistance of the seed coat to embryo expansion.

Determination of the maximum force due to skull impact in fights between sheep of the Ovis aries species

The present article presents a means of determining the maximum impact force between two bodies from the determination of the involved impulse in the impact and the sound emitted by the shock of the bodies during this impact.It also presents a case study applied to the shock between the skulls of male sheep of the Ovis aries species. These animals do not possess horns and dispute the territorial leadership by fighting, during which the skull is used as a weapon of attack, similar to a battering ram.Initially, a revision of basic physics approaching the theory of impulse is made, which shows that the average force during an impact can be obtained by the quantity of movement of the bodies. In its turn, the quantity of movement is obtained through the average speed of approach and the mass of the bodies. The maximum force is obtained from the average force, using the approach of the Force X Time curve with the Sonorous Intensity X Time Curve.In order to study the case of a shock between two sheep, the mass of the bodies was obtained through direct weighing and the average speed of approach obtained indirectly through filming, thus making possible the calculation of the average force. The Sonorous Intensity X Time Curve was obtained through the recording of the sound of the impact during a filmed fight, with later manipulation through computer programs. With this data the maximum force exercised between the skull of the sheep during the impact was obtained, which will be used in later studies.

Popcorn (Zea mays L. var. everta) yield and yield components as influenced by the timing of broadcast flaming

Farmers are interested in producing popcorn under organic production systems and propane flaming could be a significant component of an integrated weed management program. The objective of this study was to collect baseline information on popcorn tolerance to broadcast flaming as influenced by propane dose and crop growth stage at the time of flaming. Field experiments were conducted at the Haskell Agricultural Laboratory of the University of Nebraska, Concord, NE in 2008 and 2009 using five propane doses (0, 13, 24, 44 and 85 kg ha(-1)) applied at the 2-leaf, 5-leaf and 7-leaf growth stages. Propane was applied using a custom-built research flamer driven at a constant speed of 6.4 km h(-1). Crop response to propane dose was described by log-logistic models on the basis of visual estimates of crop injury, yield components (plants m(-2), ears plant(-1), kernels cob(-1) and 100-kernel weight) and grain yield. Popcorn response to flaming was influenced by the crop growth stage and propane dose. Based on various parameters evaluated, popcorn flamed at the 5-leaf showed the highest tolerance while the 2-leaf was the most susceptible stage. The maximum yield reductions were 45%, 9% and 16% for the 2-leaf, 5-leaf and 7-leaf stages, respectively. In addition, propane doses that resulted in a 5% yield loss were 23 kg ha(-1) for the 2-leaf and 7-leaf and 30 kg ha(-1) for the 5-leaf stage. Flaming has a potential to be used effectively in organic popcorn production if properly used. (C) 2010 Elsevier Ltd. All rights reserved.

Self-fertility and polyembryony in South American yellow trumpet trees (Handroanthus chrysotrichus and H. ochraceus, Bignoniaceae): a histological study of postpollination events

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Structural and spectroscopic study of oxyfluoride glasses and glass-ceramics using europium ion as a structural probe

Transparent oxyfluoride glasses and beta-PbF(2) nanocrystals containing glass-ceramics were prepared with varying Eu(3+) content (0.3, 0.4, 0.5 and 0.6%). The effect of Eu(3+) content on the preparation of glass-ceramics was investigated. From differential scanning calorimetry, the T(x)-T(g)(T(x)-temperature of the onset of crystallization; T(g)-glass transition temperature) parameter for glasses has shown slight variation, and an exothermic peak near T(g) called the ceramization temperature (T(c)) has been observed. Heat treatments were performed at this temperature to obtain transparent glass-ceramics containing beta-PbF(2) nanocrystals, identified by x-ray diffraction. Heat treatments for different periods of time were performed and were observed to be very important in the control of the crystal size and of the crystallization rate. Based upon the absorption spectra, the scattering level due to the presence of beta-PbF(2) nanocrystals in the glass-ceramics was observed to be similar to that for the mother glasses. Detailed analysis of emission spectra and decay time measurements led to the identification of Eu(3+) ions as the beta-PbF(2) crystalline phase. Excitation spectra at 70 K show the interaction of Eu(3+) ions with the fluorogermanate network.

Teste de envelhecimento acelerado em sementes de quiabo

The objective of this research was to study the accelerated aging test to evaluate the okra vigor seed. Were used four okra seed lots cv. "Santa Cruz". The initial seed lot quality was evaluate by the moisture content, germination, first germination count, speed of germination index and seedling emergence. The experiment was carried out in two phases: the first one the seeds were submitted to the accelerate aging with and without NaCl salt solution aging periods of 48, 72, 96 and 120 hours, at 41 and 45(0) C temperature. The second phase the best procedures as for as accelerated aging and temperatures were repeated. The period of 72h and 41 C with and without NaCl saturated solution was the most adequate for the lot classification in distint vigor levels.