Pvridoxine deficiency causes physiologically significant decrease in brain serotonin (5-HT) due to decreased decarboxylation of 5- hvdroxvtrvptophan (5-HTP). We have examined the effect of pyridoxine deficiency on indoleamine metabolism in the pineal gland, a tissue with high indoleamine turnover. Adult male Sprague-Dawley rats were fed either a pyridoxine-supplemented or pyridoxinedeficient diet for 8 weeks. Pyridoxine deficiency did not alter the pattern of circadian rhythm of pineal 5-HT. 5-hvdroxvindoleacetic acid (5-HIAA), V-acetvlserotonin (NAS). and melatonin. However the levels of these compounds were significantly lower in the pineal glands of pyridoxine-deficient animals. Pineal 5-HTP levels were consistently higher in the pyridoxine-deficient animals and a conspicuous increase was noticed at 22.00 h. Increase in pineal NAS and melatonin levels caused by isoproterenol (5 mg kg at 17.00 h) were significantly lower (P < 0.05) in the pyridoxine-deficient animals. Treatment of pyridoxine-deficient rats with pvridoxine restored the levels of pineal 5-HT, 5-HIAA. NAS. and melatonin to values seen in pyridoxine-supplemented control animals. These results suggest that 5-HT availability could be an important factor in the regulation of the synthesis of pineal NAS and melatonin.

A Novel Accelerator Combination for the Low Temperature Curing of Silica-Filled NBR Compounds

Zinc salts of ethyl, isopropyl, and butyl xanthates were prepared in the laboratory. The effect of these xanthates in combination with zinc diethyldithiocarbamate (ZDC) on the vulcanization of silica-filled NBR compounds has been studied at different temperatures. The cure times of these compounds were compared with that of NBR compounds containing tetramethylthiuram disulphide/dibenzthiazyl disulphide. The rubber compounds with the xanthates and ZDC were cured at various temperatures from 60 to 150°C. The sheets were molded and properties such as tensile strength, tear strength, crosslink density, elongation at break, compression set, abrasion resistance, flex resistance, heat buildup, etc. were evaluated. The properties showed that zinc salt of xanthate/ZDC combination has a positive synergistic effect on the cure rate and mechanical properties of NBR compounds.

Synergism of Xanthate/Dithiocarbamate Accelerator in Carbon Black Filled NR Compounds

Zinc salts of ethyl, isopropyl and butyl xanthates were prepared in the laboratory. The effect of these xanthates with zinc diethyldithiocarbamate (ZDC) on the vulcanization of HAF filled NR compound has been studied at different temperatures. The rubber compounds with the three xanthate accelerators and ZDC were cured at various temperatures from 60°C to 150°C. The sheets were moulded and properties such as tensile strength , tear strength , cross-link density, elongation -at-break, compression set, heat build up, abrasion resistance, flex resistance , etc. were evaluated . The properties showed that zinc xanthate/ZDC accelerator combination has a positive synergistic effect on the mechanical properties of NR compounds. The curing of HAF filled NR compound containing zinc xanthate /ZDC is slightly slower than the curing of the corresponding gum compounds . It is observed that, by gradually increasing the amount of the accelerator, the cure time of black filled NR compound can be made equal to that of the gum compou

Use of Amine Terminated Liquid Natural Rubber as a Plasticiser in Filled NR andNBR Compounds

Amine Terminated Liquid Natural Rubber (ATNR) was used as a plasticiser in filled NR and NBR compounds replacing oil/DOP. The scorch time and cure time were found to be lowered when ATNR was used as the plasticiser. ATNR was found to improve the mechanical properties like tensile strength, tear strength and modulus of the vulcanizates . The ageing resistance of the vulcanizates containing ATNR was superior compared to the vulcanizates containing oil/DOP.

Studies on Conductive Silicone Rubber Compounds

ABSTRACT: The electrical conductivity of silicone rubber vulcanizates containing carbon blacks [e.g., acetylene black, lamp black, and ISAF (N-234) black] were investigated. The change in electrical conductivity with varying amounts of carbon blacks and the temperature dependence was measured. The mechanical properties like tensile strength, tear strength, elongation at break, hardness, etc., of the vulcanizates were determined. A comparative study of the electrical conductivity of the composites revealed that the electrical conductivity of the composites made with acetylene black was higher than that of the composites made of other blacks.

Studies on the Dipping Characteristics of RVNRL and NRLatex Compounds

ABSTRACT: The dipping characteristics of radiation-vulcanized natural rubber latex and natural rubber latex compounds were investigated with a lab-model semiautomatic dipping machine. The effect of the variation of the speed of immersion and withdrawal, dwell time, compound viscosity, and concentration of coagulant on the thickness of the latex deposit was investigated. The results of the study show that the deposit thickness depends on the withdrawal speed of the former, the concentration of the coagulant, dwell times, and the viscosity of the latex compounds

Rubber Seed Oil: A Multipurpose Additive in NR and SBR Compounds

ABSTRACT: Rubber seed oil was used as a multipurpose ingredient in natural rubber (NR) and styrene butadiene rubber (SBR) compounds. The study shows that the oil, when substituted for conventional plasticiser, imparts excellent mechanical properties to NR and SBR vulcanizates. Further, it also improves aging resistance, reduces cure time, increases abrasion resistance and flex resistance, and reduces blooming.

A Study on the Use of Castor Oil as Plasticizer in Natural Rubber Compounds

Mechanical properties and thermal degradation of natural rubber compounds containing castor oil were studied to evaluate its suitability as plasticizer. Naphthenic oil was used as a reference plasticizer. The cure time was marginally lower in the case of castor oil mixes, probably due to the presence offree fatty acids in it. The tear strength and modulus were better in the case of mixes containing castor oil, while most of the other mechanical properties were comparable to the mixes containing naphthenic oil. The heat build up and compression set were higher than that of the naphthenic oil mixes. Thermal studies showed an increase of 8 °C in the temperature of initiation of degradation and an increase of 6 °C in the temperature at which the peak rate of degradation occurred. The peak rate of degradation was comparable to that of the reference compound

A Study on the Use of Coconut Oil as Plasticiser in Natural Rubber Compounds

Mechanical properties and thermal degradation characteristics of natural rubber compounds captaining coconut oil were compared with that of a control compound containing naphthenic oil. Cure time was marginally lower in the case of coconut oil mixes, probably due to the presence of free fatty acids. Tensile strength , tear strength, resilience and abrasion resistance were better than the naphthenic oil-based compounds . Compression set and hardness were marginally inferior The coconut oil mixes had a crosslink density comparable to that of the reference compound. Thermal studies showed that the temperature of initiation of degradation was increased by 10°C and the temperature at which the peak rate of degradation occured was increased by 7°C. The peak rate of degradation was compa rable to the control compound.

Synthesis, characterization, and structure of a new cobalt(II) Schiff-base complex with quinoxaline- 2-carboxalidine-2-amino-5-methylphenol

The mononuclear cobalt(II) complex [CoL2] H2O (where HL is quinoxaline-2-carboxalidine- 2-amino-5-methylphenol) has been prepared and characterized by elemental analysis, conductivity measurement, IR, UV-Vis spectroscopy, TG-DTA, and X-ray structure determination. The crystallographic study shows that cobalt(II) is distorted octahedral with each tridentate NNO Schiff base in a cis arrangement. The crystal exhibits a 2-D polymeric structure parallel to [010] plane, formed by O-H...N and O-H... O intermolecular hydrogen bonds and pye stacking interactions, as a racemic mixture of optical enantiomers. The ligand is a Schiff base derived from quinoxaline-2-carboxaldehyde

(Z)-2-Amino-3-[(E )-benzylideneamino]but-2-enedinitrile

The asymmetric unit of the title compound, C11H8N4, contains two independent molecules. In the crystal structure, intermolecular N—H.....N hydrogen bonds link molecules into ribbons extended in the [100] direction