Influence of heat treatment on spectroscopic properties of Er3+ in multicomponent ZrF4-ZnF2-AlF3-YF3-MF2 (M = Ca, Sr, Ba) based glass

Er3+ doped multicomponent fluoride based glass was prepared. These precursor fluoride glass samples were then heated using different schedules. Crystalline phase particles were successfully precipitated in the multicomponent fluoride glass samples after heat treatment. The influence of heat treatment on the spectroscopic properties of Er3+ in multicomponent fluoride based glass samples were discussed. Small changes of the Judd-Ofelt parameters Omega(i) (i = 2,4,6) were found in multicomponent fluoride glass samples before and after heat treatment compared to oxyfluoride telluride glass. Preparation conditions used to produce transparent multicomponent fluoride glass ceramics doped with rare-earth ions are discussed. (c) 2007 Elsevier B.V. All rights reserved.

Influence of B2O3 to the inhomogeneous broadening and spectroscopic properties of Er3+/Yb3+ codoped fluorophosphate glasses

In a three-components fluorophosphate glass system, the introduction of H3BO3 brings some valuable influence to the spectroscopic and thermal properties of the glasses. With H3BO3 increases from 2 to 20mol%, ohm(6), S-ed4113/2, FWHM, T-g and fluorescence lifetime change from 3.21 x 10(-20) cm(2), 1.77 x 10(-20) cm(2), 45 nm, 480 degrees C and 8.8 ms to 4.66 x 10(-20) cm(2), 2.11 x 10(-20) cm(2), 50 nm, 541 degrees C and 7.4 ms, respectively. sigma(abs), sigma(emi), FWHM x tau(f) x sigma(emi) has a maximum when H-3 BO3 is 11 mol%. T-g and T-x-T-g increases with H3BO3 introduction. Results showed that in fluorophosphate glasses, proper amount of B2O3 can be used as a modifier to suppress upconversion and improve spectroscopic properties, broadband property and crystallization stability of the glasses while keeps the fluorescence lifetime relatively high. (c) 2005 Elsevier B.V. All rights reserved.

The influence of OH groups on laser performance in phosphate glasses

Because of the influence of OH groups in phosphate glasses on the radiation of rare-earth ions, the laser performance is degraded. The laser efficiency and the small signal gain experiment of several phosphate glass samples have been done, the concentration of OH groups in glasses was calculated from the measured absorption coefficient at 3.47 μm. It is shown that the concentration of OH groups in phosphate glasses can seriously influence the laser output characteristics, and the OH groups have worse influence on the laser amplifier than laser oscillator.

Influence of TeO2, PbF2, ZnF2 on the spectroscopic and lasing properties of Yb3+ doped fluorophosphate glass

The influence of TeO2 on the crystallization stability, thermal stability, spectroscopic and lasing properties of Yb3+ doped fluorophosphate (FP) glass was studied. It is shown that 2 mol% TeO2 is the optimum doping amount which results in better spectroscopic and lasing properties as well as improve the crystallization and thermal stabilities of the glass. In order to enhance the physical and optical properties further, the effect of PbF2 and ZnF2 to the TeO2 contained FP glasses is also investigated, which shows that PbF2 has advantages in improving the crystallization properties while ZnF2 is preferable in enhancing spectroscopic and lasing properties. Results indicate that the co-existence of TeO2, PbF2 or ZnF2 is an effective way to enhance the spectroscopic, lasing and physical properties of Yb3+ doped FP glasses. (c) 2004 Published by Elsevier B.V.

Influence of phosphate precursors on the structures of sodium aluminophosphate sols, gels and glasses

Transparent and homogeneous aluminophosphate gels and glasses have been widely synthesized through an aqueous sol-gel route, extending significantly the glass-forming range compared to that accessible via the melt-cooling route. Different phosphorus precursors, sodium polyphosphate (NaPO3) and orthophosphate species (NaH2PO4 and/or H3PO4) were compared with regard to the macroscopic properties and the microscopic structure of the resultant gels and glasses as characterized by extensive high-resolution liquid- and solid-state NMR. Sodium polyphosphate solution results in a substantially wider composition range of homogenous gel formation than orthophosphate solutions, and the two routes produce significant structural differences in the sol and xerogel states. Nevertheless, the structures of the glasses obtained upon gel annealing above 400 degrees C are independent of the P-precursors used. (c) 2007 Elsevier B.V. All rights reserved.

Influence of vapor transport equilibration on the crystal quality and thermal-expansion coefficients of gamma-LiAlO2

gamma-LiAlO2 (LAO) single crystal has been grown by the Czochralski method. However, its quality was deteriorated due to lithium volatilization during the crystal growth. The full width at half maximum value drops from 116.9 to 44.2 arc sec after the LAO slice was treated by vapor transport equilibration at 1000, 1100, and 1200 degrees C/48 h in sequence. The treated slice shows higher optical transmission than the as-grown one in the measured wavelength range of 190-1900 nm, meanwhile, its absorption edge exhibits a blueshift. According to Raman spectra, the treated slice has homogeneous quality at different depths from surface to 0.01 mm. The expansion coefficient of the treated slice for a axis drops from 17.2398x10(-6)/degrees C to 16.5240x10(-6)/degrees C, and that for c axis drops from 10.7664x10(-6)/degrees C to 10.0786x10(-6)/degrees C.