Influence of prior 810-nm-diode intracanal laser irradiation on hydrophilic resin-based sealer obturation

Dentin wall structural changes caused by 810-nm-diode laser irradiation can influence the sealing ability of endodontic sealers. The objective of this study was to evaluate the apical leakage of AH Plus and RealSeal resin-based sealers with and without prior diode laser irradiation. Fifty-two single-rooted mandibular premolars were prepared and divided into 4 groups, according to the endodontic sealer used and the use or non-use of laser irradiation. The protocol for laser irradiation was 2.5W, continuous wave in scanning mode, with 4 exposures per tooth. After sample preparation, apical leakage of 50% ammoniacal silver nitrate impregnation was analyzed. When the teeth were not exposed to irradiation, the Real Seal sealer achieved the highest scores, showing the least leakage, with significant differences at the 5% level (Kruskal-Wallis test, p = 0.0004), compared with AH Plus. When the teeth were exposed to the 810-nm-diode laser irradiation, the sealing ability of AH Plus sealer was improved (p = 0282). In the Real Seal groups, the intracanal laser irradiation did not interfere with the leakage index, showing similar results in the GRS and GRSd groups (p = 0.1009).

Effect of the addition of silanated silica on the mechanical properties of microwave heat-cured acrylic resin

Effect of the addition of silanated silica on the mechanical properties of microwave heat-cured acrylic resinObjectives: The purpose of this study was to evaluate the flexural strength and Vickers hardness of a microwave energy heat-cured acrylic resin by adding different concentrations of silane surface-treated nanoparticle silica.Methods: Acrylic resin specimens with dimensions of 65 x 10 x 2.5 mm were formed and divided into five experimental groups (n = 10) according to the silica concentration added to the acrylic resin mass (weight %) prior to polymerisation : G1, without silica; G2, 0.1% silica; G3, 0.5% silica; G4, 1.0% silica; and G5, 5.0% silica. The specimens were submitted to a three-point flexural strength test and to the Vickers hardness test (HVN). The data obtained were statistically analysed by ANOVA and the Tukey test (alpha = 0.05).Results: Regarding flexural strength, G5 differed from the other experimental groups (G1, G2, G3 and G4) presenting the lowest mean, while G4 presented a significantly higher mean, with the exception of group G3. Regarding Vickers hardness, a decrease in values was observed, in which G1 presented the highest hardness compared with the other experimental groups.Conclusion: Incorporating surface-treated silica resulted in direct benefits in the flexural strength of the acrylic resin activated by microwave energy; however, similar results were not achieved for hardness.

Flexural Strength of Four Adhesive Fixed Dental Prostheses of Composite Resin Reinforced with Glass Fiber

Purpose: To evaluate the flexural strength of two fixed dental prosthesis (FDP) designs simulating frameworks of adhesive fixed partial prostheses, reinforced or not by glass fiber.Materials and Methods: Forty specimens, made with composite resin, were divided into 4 groups according to the framework design and the presence of fiber reinforcement: A1 - occlusal support; A2: occlusal support + glass fiber; B1: occlusal and proximal supports; B2: occlusal and proximal supports + glass fiber. The specimens were subjected to the three-point bending test, and the data were submitted to two-way ANOVA and Tukey's test (5%).Results: Group A2 (97.9 +/- 38 N) was statistically significantly different from all other experimental groups, presenting a significantly lower mean flexural strength.Conclusion: The use of glass fibers did not improve the flexural strength of composite resin, and designs with occlusal and proximal supports presented better results than designs simulating only occlusal support.

INFLUENCE of DIFFERENT SURFACE CONDITIONING PROTOCOLS on MICROTENSILE BOND STRENGTH of SELF-ADHESIVE RESIN CEMENTS TO DENTIN

Statement of problem. According to manufacturers, bonding with self-adhesive resin cements can be achieved without any pretreatment steps such as etching, priming, or bonding. However, the benefit of saving time with these simplified luting systems may be realized at the expense of compromising the bonding capacity.Purpose. The purpose of this study was to assess whether different dentin conditioning protocols influence the bond performance of self-adhesive resin cements to dentin.Material and methods. Flat dentin surfaces from 48 human molars were divided into 4 groups (n=12): 1) control, no conditioning; 2) H(3)PO(4), etching with 37% H(3)PO(4) for 15 seconds; 3) SEBond, bonding with self-etching primer adhesive (Clearfil SE Bond); and 4) EDTA, etching with 0.1M EDTA for 60 seconds. The specimens from each dentin pre-treatment were bonded using the self-adhesive cements RelyX Unicem, Maxcem or Multilink Sprint (n=4). The resin-cement-dentin specimens were stored in water at 37 degrees C for 7 days, and serially sectioned to produce beam specimens of 1.0 mm(2) cross-sectional area. Microtensile bond strength (mu TBS) testing was performed at 1.0 mm/min. Data (MPa) were analyzed by 2-way ANOVA and Tukey multiple comparisons test (alpha=.05). Fractured specimens were examined with a stereomicroscope (x40) and classified as adhesive, mixed, or cohesive. Additional bonded interfaces were evaluated under a scanning electron microscope (SEM).Results. Cement-dentin mu TBS was affected by the dentin conditioning approach (P <.001). RelyX Unicem attained statistically similar bond strengths to all pre-treated dentin surfaces. H(3)PO(4)-etching prior to the application of Maxcem resulted in bond strength values that were significantly higher than the other groups. The lowest mu TBS were attained when luting Multilink Sprint per manufacturers' recommendations, while H(3)PO(4)-etching produced the highest values followed by Clearfil SE bonding and EDTA. SEM observations disclosed an enhanced potential of the self-adhesive cements to form a hybrid layer when applied following manufacturer's instructions.Conclusions. When evaluated self-adhesive resin cements are used, selectively etching dentin with H(3)PO(4) prior to luting results in the most effective bonding. (J Prosthet Dent 2011;105:227-235)

Does Adhesive Resin Application Contribute to Resin Bond Durability on Etched and Silanized Feldspathic Ceramic?

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

A Strain Gauge Analysis of Microstrain Induced by Various Splinting Methods and Acrylic Resin Types for Implant Impressions

Purpose: The aim of this study was to investigate the level of microstrain that is exerted during polymerization of acrylic resins used for splinting during implant impressions. Material and Methods: Two acrylic resins (GC Pattern Resin, Duralay II) and square transfer coping splinting methods were evaluated by means of strain gauge analysis. Two implants were embedded in a polyurethane block, and the abutments were positioned. Sixty specimens were prepared using two square transfer Copings that were rigidly connected to each other using the acrylic resins. The specimens were randomly divided into three groups of 20 each for the splinting methods: Method 1 was a one-piece method; in method 2, the splint was separated and reconnected after 17 minutes; and in method 3, the splint was separated and reconnected after 24 hours. In each group, half the specimens were splinted with GC Pattern Resin and the other half were splinted with Duralay II. Three microstrain measurements were performed by four strain gauges placed on the upper surface of the polyurethane blocks at 5 hours after resin polymerization for all groups. The data were analyzed statistically. Results: Both resin type and splinting method significantly affected microstrain. interaction terms were also significant. Method 1 in combination with Duralay II produced significantly higher microstrain (1,962.1 mu epsilon) than the other methods with this material (method 2: 241.1 mu epsilon; method 3: 181.5 mu epsilon). No significant difference was found between splinting methods in combination with GC Pattern Resin (method 1: 173.8 mu epsilon; method 2: 112.6 mu epsilon; method 3: 105.4 mu epsilon). Conclusions: Because of the high microstrain generated, Duralay II should not be used for one-piece acrylic resin splinting, and separation and reconnection are suggested. For GC Pattern Resin, variations in splinting methods did not significantly affect the microstrain created. Int J Oral Maxillofac Implants 2012;27:341-345

The Influence of Cutting Speed and Cutting Initiation Location in Specimen Preparation for the Microtensile Bond Strength Test

Purpose: This study evaluated the effect of cutting initiation location and cutting speed on the bond strength between resin cement and feldspathic ceramic.Materials and Methods: Thirty-six blocks (6.4 x 6.4 x 4.8 mm) of ceramic (Vita VM7) were produced. The ceramic surfaces were etched with 10% hydrofluoric acid gel for 60 s and then silanized. Each ceramic block was placed in a silicon mold with the treated surface exposed. A resin cement (Variolink II) was injected into the mold over the treated surface and polymerized. The resin cement-ceramic blocks were divided into two groups according to experimental conditions: a) cutting initiation location - resin cement, ceramic and interface; and b) cutting speed - 10,000, 15,000, and 20,000 rpm. The blocks were sectioned to achieve non-trimmed bar specimens. The microtensile test was performed in a universal testing machine (1 mm/min). The failure modes were examined using an optical light microscope and SEM. Bond strength results were analyzed using one-way ANOVA and Tukey's test (alpha = 0.05).Results: Significant influences of cutting speed and initiation location on bond strength (p < 0.05) were observed. The highest mean was achieved for specimens cut at 15,000 rpm at the interface (15.12 +/- 5.36 MPa). The lowest means were obtained for specimens cut at the highest cutting speed in resin cement (8.50 +/- 3.27 MPa), and cut at the lowest cutting speed in ceramic (8.60 +/- 2.65MPa). All groups showed mainly mixed failure (75% to 100%).Conclusion: The cutting speed and initiation location are important factors that should be considered during specimen preparation for microtensile bond strength testing, as both may influence the bond strength results.

Evaluation of interface characterization and adhesion of glass ceramics to commercially pure titanium and gold alloy after thermal- and mechanical-loading

Objectives. This study evaluated the effect of thermal- and mechanical-cycling on the shear bond strength of three low-fusing glassy matrix dental ceramics to commercial pure titanium (cpTi) when compared to conventional feldspathic ceramic fused to gold alloy.Methods. Metallic frameworks (diameter: 5 min, thickness: 4 mm) (N = 96, n = 12 per group) were cast in cpTi and gold alloy, airborne particle abraded with 150 mu m aluminum oxide. Low-fusing glassy matrix ceramics and a conventional feldspathic ceramic were fired onto the alloys (thickness: 4mm). Four experimental groups were formed; Gr1 (control group): Vita Omega 900-Au-Pd alloy; Gr2: Ticeram-cpTi; Gr3: Super Porcelain Ti-22-cpTi and G4: Vita Titankeramik-cpTi. While half of the specimens from each ceramic-metal combination were randomly tested without aging (water storage at 37 C for 24h only), the other half were first thermocycled (6000 cycles, between 5 and 55 C, dwell time: 13 s) and then mechanically loaded (20,000 cycles under SON load, immersion in distilled water at 37 C). The ceramic-alloy interfaces were loaded under shear in a universal test machine (cross-head speed: 0.5 mm/min) until failure occur-red. Failure types were noted and the interfaces of the representative fractured specimens from each group were examined with stereo microscope and scanning electron microscope (SEM). in an additional study (N = 16, n = 2 per group), energy dispersive X-ray spectroscopy (EDS) analysis was performed from ceramic-alloy interfaces. Data were analyzed using ANOVA and Tukey's test.Results. Both ceramic-metal combinations (p < 0.001) and aging conditions (p < 0,001) significantly affected the mean bond strength values. Thermal- and mechanical-cycling decreased the bond strength (MPa) results significantly for Gr3 (33.4 +/- 4.2) and Gr4 (32.1 +/- 4.8) when compared to the non-aged groups (42.9 +/- 8.9, 42.4 +/- 5.2, respectively). Gr1 was not affected significantly from aging conditions (61.3 +/- 8.4 for control, 60.7 +/- 13.7 after aging) (p > 0.05). Stereomicroscope images showed exclusively adhesive failure types at the opaque ceramic-cpTi interfacial zone with no presence of ceramic on the substrate surface but with a visible dark titanium oxide layer in Groups 2-4 except Gr1 where remnants of bonder ceramic was visible. EDS analysis from the interfacial zone for cpTi-ceramic groups showed predominantly 34.5-85.1% O(2) followed by 1.1-36.7% Aland 0-36.3% Si except for Super Porcelain Ti-22 where a small quantity of Ba (1.4-8.3%), S (0.7%) and Sn (35.3%) was found. In the Au-Pd alloy-ceramic interface, 56.4-69.9% O(2) followed by 15.6-26.2% Si, 3.9-10.9% K, 2.8-6% Na, 4.4-9.6% Al and 0-0.04% Mg was observed.Significance. After thermal-cycling for 6000 times and mechanical-cycling for 20,000 times, Triceram-cpTi combination presented the least decrease among other ceramic-alloy combinations when compared to the mean bond strength results with Au-Pd alloy-Vita Omega 900 combination. (c) 2008 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Does the Ultrasonic Cleaning Medium Affect the Adhesion of Resin Cement to Feldspathic Ceramic?

Purpose: To evaluate the effect of different cleaning media on the adhesion of resin cement to feldspathic ceramic after etching.Materials and Methods: The cementation surfaces of ceramic blocks (N = 20, n = 5 per group) were etched with 10% hydrofluoric acid (HF) gel for 20 s and rinsed for 60 s. They were then randomly assigned to 4 groups: G1: air-water spray+drying (control); G2: ultrasonic cleaning in distilled water for 4 min+drying; G3: ultrasonic cleaning in 99.5% acetone for 4 min+drying; G4: ultrasonic cleaning in 70% alcohol for 4 min+drying. The ceramic blocks were silanized and cemented (RelyX ARC) to the composite blocks. Subsequently, the microtensile bond strength test (mu TBS) was performed. In addition, EDS analysis was made to assess the elemental composition of the conditioned and cleaned ceramic surfaces.Results: A significantly higher mean mu TBS was obtained when specimens had been ultrasonically cleaned in distilled water (G2: 18.8 +/- 0.4 MPa) (p < 0.05) compared to other groups (G1: 16.6 +/- 0.5; G3: 16.1 +/- 0.9; G4: 15.8 +/- 1.4) (one-way ANOVA). EDS analysis indicated the presence of F- only in G1. Dissolved precipitates after HF etching were removed by ultrasonic cleaning.Conclusion: Cleaning the HF-etched ceramic surface ultrasonically in distilled water is recommended, instead of rinsing it with air-water spray only.

Fracture resistance of endodontically treated teeth with different heights of crown ferrule restored with prefabricated carbon fiber post and composite resin core by intermittent loading

This study evaluated the fracture resistance of endodontically treated teeth restored with prefabricated carbon fiber posts and varying quantities of coronal dentin. Sixty freshly extracted upper canines were randomly divided into groups of 10 teeth each. The specimens were exposed to 250,000 cycles in a controlled chewing simulator. All intact specimens were subjected to a static load (N) in a universal testing machine at 45 degrees to the long axis. Data were analyzed by 1-way analysis of variance and Tukey test (alpha = .05). Significant differences (P < .001) were found among the mean fracture forces of the test groups (positive control, 0 mm, 1 mm, 2 mm, 3 mm, and negative control groups: 1022.82 N, 1008.22 N, 1292.52 N, 1289.19 N, 1255.38 N, and 1582.11, respectively). These results suggested that the amount of coronal dentin did not significantly increase the fracture resistance of endodontically treated teeth restored with prefabricated carbon fiber post and composite resin core. (Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2008;106:e52-e57)