Orientation of Syndiotactic Polystyrene Crystallized in Cylindrical Nanopores

Syndiotactic polystyrene (sPS) nanorods with different diameters have been prepared by using anodic aluminum oxide templates, and the orientation of the sPS crystals in the nanorods has been investigated by FT-IR spectroscopy. It is found that the c axis of the beta' crystals preferentially oriented perpendicular to the axis of the nanorod, and the degree of orientation is lower as the diameter of the nanorod decreases. This unexpected result is attributed to nuclei formed at the surface of the nanopores and their subsequent growth, in addition to the preferential growth compatible with the pore direction by the nuclei formed in the bulk film and in the nanorods.

Crystallization behavior of poly(epsilon-caprolactone) in poly(epsilon-caprolactone) and poly(vinyl methyl ether) mixtures

The morphological development and crystallization behavior of poly(epsilon-caprolactone) (PCL) in miscible mixtures of PCL and poly(vinyl methyl ether) (PVME) were investigated by optical microscopy as a function of the mixture composition and crystallization temperature. The results indicated that the degree of crystallinity of PCL was independent of the mixture composition upon melt crystallization because the glass-transition temperatures of the mixtures were much lower than the crystallization temperature of PCL. The radii of the PCL spherulites increased linearly with time at crystallization temperatures ranging from 42 to 49 degrees C. The isothermal growth rates of PCL spherulites decreased with the amount of the amorphous PVME components in the mixtures. Accounting for the miscibility of PCL/PVME mixtures, the radial growth rates of PCL spherulites were well described by a kinetic equation involving the Flory-Huggins interaction parameter and the free energy for the nuclei formation in such a way that the theoretical calculations were in good agreement with the experimental data. From the analysis of the equilibrium melting point depression, the interaction energy density of the PVME/PCL system was calculated to be -3.95 J/cm(3).

Time-dependent DNA condensation induced by amyloid beta-peptide

The major protein component of the amyloid deposition in Alzheimer's disease is a 39-43 residue peptide, amyloid beta (A beta). A beta is toxic to neurons, although the mechanism of neurodegeneration is uncertain. Evidence exists for non-B DNA conformation in the hippocampus of Alzheimer's disease brains, and A beta was reportedly able to transform DNA conformation in vitro. In this study, we found that DNA conformation was altered in the presence of A beta, and A beta induced DNA condensation in a time-dependent manner. Furthermore, A beta sheets, serving as condensation nuclei, were crucial for DNA condensation, and Cu2+ and Zn2+ ions inhibited A beta sheet-induced DNA condensation. Our results suggest DNA condensation as a mechanism of A beta toxicity.

Relating the molecular structure and crystallization behavior of polypropylene

The crystallization behavior of two polypropylene (PP) resins as used for biaxially oriented polypropylene (BOPP) and general injection mold applications, respectively, has been intensively investigated and compared by means of polarized light optical micrography (POM), differential scanning calorimetry (DSC), conventional transmission electron microscopy (TEM), and high resolution transmission electron microscopy (HRTEM). It is found that both molecular weight distribution and isotacticity of polypropylene strongly affect its crystallization characteristics, e.g., the number of crystal nuclei at the initial stage, crystallization dynamics, the morphology, size and perfection of crystals in the final product, and so on. The results indicate an appropriate molecular structure is vital in producing high-quality BOPP film.

Fractionated crystallization of dispersed PA6 phase of PP/PP-g-MAH/PA6 blends

Fractionated crystallization behavior of dispersed PA6 phase in PP/PA6 blends compatibilized with PP-g-MAH was investigated by scanning electron microscopy (SEM), differential scanning calorimeter (DSC), polarized light microscopy (PLM), and wide-angle X-ray diffraction (WAXD) in this work. The lack of usual active heterogeneities in the dispersed droplet was the key factor for the fractionated crystallization of PA6. The crystals formed with less efficient nuclei might contain more defects in the crystal structures than those crystallized with the usual active nuclei. The lower the crystallization temperature, the lesser the perfection of the crystals and the lower crystallinity would be. The fractionated crystallization of PP droplets encapsulated by PA6 domains was also observed. The effect of existing PP-g-MAH-g-PA6 copolymer located at the interface on the fractionated crystallization could not be detected in this work.

Miscibility and crystallization behavior of PBT/epoxy blends

The miscibility and the isothermal crystallization kinetics for PBT/Epoxy blends have been studied by using differential scanning calorimetry, and several kinetic analyses have been used to describe the crystallization process. The Avrami exponents n were obtained for PBT/Epoxy blends. An addition of small amount of epoxy resin (3%) leads to an increase in the number of effective nuclei, thus resulting in an increase in crystallization rate and a stronger trend of instantaneous three-dimensional growth. For isothermal crystallization, crystallization parameter analysis showed that epoxy particles could act as effective nucleating agents, accelerating the crystallization of PBT component in the PBT/Epoxy blends. The Lauritzen-Hoffman equation for DSC isothermal crystallization data revealed that PBT/Epoxy 97/3 had lower nucleation constant K, than 100/0, 93/7, and 90/10 PBT/Epoxy blends. Analysis of the crystallization data of PBT/Epoxy blends showed that crystallization occurs in regime II. The fold surface free energy, sigma(e) = 101.7-58.0 x 10(-3) J/m(2), and work of chain folding, q = 5.79-3.30 kcal/mol, were determined. The equilibrium melting point depressions of PBT/Epoxy blends were observed and the Flory-Huggins interaction parameters were obtained.

Investigation on isothermal and non-isothermal crystallization kinetics of poly (epsilon-caprolactone)

The crystallization kinetics and the development of lamellar structure during the isothermal crystallization of poly (epsilon-caprolactone) (PCL) were investigated by means of differential scanning calorimetry (DSC) and real-time synchrotron small angle X-ray scattering (SR-SAXS) techniques, respectively. The Avrami analysis was performed to obtain the kinetics parameters. The value of Avrami index, n, is about 3, demonstrating a three-dimensional spherulitic growth on heterogeneous nuclei in the process of isothermal crystallization. The activation energy and the surface free energy of chain folding for isothermal crystallization were determined according to the Arrhenius equation and Hoffman-Lauritzen theory, respectively. In the process of nonisothermal crystallization of PCL, the value of Avrami index, n, is about 4, which demonstrates a three-dimensional spherulitic growth on homogeneous nuclei. In addition, lamellar parameters were obtained from the analysis of SR-SAXS data.

Oriented crystallization process of polypropylene fractions

Melting recrystallization processes of melt-sheared films of polypropylene (S28C) fractions have been investigated in situ by polarized optical microscope equipped with CCD camera and hot-stage. Actually, the morphological developments in the melting recrystallization are partially reappearance of oriented crystallization processes during melt-shearing the fractions, which is due to a memory effect of oriented structure of polymer. For low molecular weight fraction, only incomplete spherulites with some orientation along shear direction are observed in the melting recrystallization processes of the sheared films. For middle molecular weight fractions, extended chain fiber crystals(or bands) are formed first at higher temperatures, and the bands can act as self-nuclei (i. e., row nuclei), resulting in epitaxial growth of chain-folded lamellae(or fibril), i. e., the formation of cylindrites, with further decrease of the crystallization temperature. For high molecular weight fraction, however, it is not possible to shear the melt film because of its high melt viscosity. When the low molecular weight fraction in which no fiber crystals or cylindrites are observed, are mixed with small amount(about 1%-2%) of the high molecular weight fraction, quite large number of cylindrites are formed during the melting recrystallization process of its sheared film, which implies that the component of high molecular weight plays an important role in the formation of cylindrites during the shear process of polypropylene.

分级聚丙烯的取向结晶过程

聚丙烯熔体在剪切或应变应力作用下 ,分子链发生取向形成伸直链纤维晶 ,这些先取向形成的纤维晶成为其后结晶的晶核 .这种线形排列的特殊自晶核被称作排核 ( Row nuclei) [1] .排核诱导的结晶温度高于异相核和均相核 .折叠链片晶在排核上附生生长 ,形成具有柱状对称性的超分子结构 ,称为柱状晶 ( Cylindrite) [2 ,3] .聚合物的分子量 ,剪切温度和剪切速度等因素对柱状晶的生成有很大影响 [4 ,5] .本文选用不同级分的聚丙烯样品 ,利用高分子 (特别是取向结晶 )的记忆效应 [6,7] ,研究了剪切后薄膜试样在熔融重结晶过程中柱状晶的形成和发展过程 ,讨论了分子量及其分布 ,特别是高分子量组分对聚丙烯取向结晶过程的影响 ,探索链结构与凝聚态结构间的相互关系 .1　实验部分1 .1　原料　聚丙烯分级样品由中国石油化工集团公司北京化工研究院提供 ,采用升温淋洗分级方法对聚丙烯 S2 8C( Montell,含质量分数为 0 .32 %的共聚乙烯 ,熔融指数 2 .1 )进行分级 .本文选用了1 1 0 ,1 1 8,1 2 5和 1 40℃ 4个级分 ,分别称作 S2 8C1 1 0 ...

Effect of end substitution on optical properties and molecular orientation of distyrylbenzene derivatives in thin film

Three distyrylbenzene (DSB) derivatives were vacuum-evaporated on a (001) surface of KBr. DSB derivative molecules formed nuclei by interaction between the electron donative methoxyl group and Br- ion of the substrate crystal and oriented their longitudinal axis obliquely to the substrate surface. The peak shift between the emission peaks of solution and film decreased depending on the number of substituent. This phenomenon was originated to reduction of molecular interaction between neighboring molecules by steric hindrance of end substituents. (C) 2000 Elsevier Science S.A. All rights reserved.

Phase identification in a series of liquid crystalline TPP polyethers and copolyethers having highly ordered mesophase structures. 6. Structure changes from smectic to columnar phases in a series of copolyethers containing odd and even numbers of methylene units in equal molar composition

A series of liquid crystalline copolyethers has been synthesized from 1-(4-hydroxy-4'-biphenyl)-2-(4-hydroxyphenyl)propane and different alpha,omega-dibromoalkanes [coTPP(n/m)]. In this report, coTPPs having n = 5, 7, 9, 11 and m = 12 are studied, which represent copolyethers having both varying odd number and a fixed even number of methylene units. The compositions were fixed at an equal molar ratio (50/50). These coTPPs(nlm) show multiple phase transitions during cooling and heating in differential scanning calorimetry experiments. The undercooling dependence of these transitions is found to be small, indicating that these transitions are close to equilibrium, Although the coTPPs possess a high-temperature nematic (N) phase, the periodicity order along the chain direction is increasingly disturbed when the length of the odd-numbered methylene units decreases from n 11 to 5. in the coTPPs(5/12, 7/12, and 9/12), wide-angle X-ray diffraction experiments at different temperatures show that, shortly after the N phase formation during cooling, the lateral molecular packing improves toward a hexagonal lattice, as evidenced by a gradual narrowing of the scattering halo. This process represents the possible existence of an exotic N phase, which serves as a precursor to the columnar (Phi(H)) phase. A further decrease in temperature leads to a (PH phase having a long-range ordered, two-dimensional hexagonal lattice. In coTPP(11/12), the phase structures are categorized as highly ordered and tilted, smectic and smectic crystal phases, similar to homoTPPs, such as the smectic F (S-F) and smectic crystal G (SCG) phases. An interesting observation is found for coTPP(9/12), wherein a structural change from the high-temperature Phi(H) phase to the low-temperature S-F phase occurs. It can be proven that, upon heating, the well-defined layer structure disappears and the lateral packing remains hexagonal. The overall structural differences in this series of coTPPs between those of the columnar and highly ordered smectic phases are related to the disorders introduced into the layer structure by the dissimilarity of the methylene unit lengths in the comonomers.

Thermal analysis of ethylene propylene copolymer-grafted-acrylic acid

The thermal properties of ethylene propylene copolymer-grafted-acrylic acid (EP-g-AA) were investigated by using differential scanning calorimetry (DSC). Compared with the ethylene propylene copolymer (EP), the peak values of the melting temperature (T-m) of the propylene sequences in the grafted EP changed a little, the crystallization temperature (T-c) increased about 8-12 degrees C, and the melting enthalpy (Delta H-m) increased about 4-6 J/g. The isothermal crystallization kinetics of grafted and ungrafted samples was carried out by DSC. Within the scope of the researched crystallization temperature, the Avrami exponent (n) of the ungrafted sample was 1.6-1.8, and that of grafted samples were all above 2, which indicated that the grafted monomer could become the crystal nuclei for the crystallization of propylene sequence. With increasing grafted monomer content, the crystallization rate of propylene sequence in grafted EP increased; it might be the result of rapid nucleation rate and crystal growth rate.

Crystallization kinetics in mixtures of poly(epsilon-caprolactone) and poly(styrene-co-acrylonitrile)

Isothermal crystallization kinetics in the miscible mixtures of poly(epsilon-caprolactone) (PCL) and poly(styrene-co-acrylonitrile) (SAN) have been investigated as a function of the composition and the crystallization temperature by optical microscopy. The radial growth rates of the spherulites have been described by a kinetic equation including the interaction parameter and the free energy for the formation of secondary crystal nuclei. Fold surface free energies decrease slightly with the increase of SAN content. The experimental findings show that the influence of the glass transition temperature of the mixture, which is related to the chain mobility, on the rate of crystallization predominates over the influence of the surface free energies. This indicates that the glass transition temperature of the mixture should be of more importance, so that the growth rates decrease when the content of the noncrystallizable component increases. In addition, the Flory-Huggins interaction parameter obtained by fitting the kinetic equation with experimental data is questionable.

Study on the interaction of rare earth with 3,5,3'-triiodothyronine

The stability constants for rare earth complexes with 3,5,3'-triiodothyronine were determined at 37 degrees C end an ionic strength of 0.15 mole/L NaCl. The lanthanide induced shifts were measured for H-1 nuclei of 3,5,3'-triiodothyronine. The coordination of rare earth with 3, 5, 3'-triiodothyronine was discussed.

Isothermal crystallization of PP-g-GMA copolymer

The overall isothermal crystallization kinetics for neat polypropylene and grafted polypropylene systems were investigated. The rate constants were corrected assuming the heterogeneous nucleation and three dimensional growth of polypropylene spherulites. A semiempirical equation for the radial growth rate of polypropylene spherulites was developed as a function of temperature, and was used to determine the number of effective nuclei of different temperatures. The number of nuclei in grafted samples was estimated to be 10(2)-10(3) times larger than that of neat polypropylene. (C) 1997 John Wiley & Sons, Inc.