Preparation of refractory calcium aluminate cement using the sonochemical process

Calcium aluminate cements (CAC) were prepared using the sonochemical process, followed by heat treatment. A study was made of the action of ultrasonic waves and the influence of thermal treatment conditions on two initial molar compositions of 1:1 and 1:2 of calcia:alumina. The aqueous suspension containing the raw materials (A-50 alumina and CaO) was subjected to an ultrasonic bath, followed by drying and burning at 1000, 1200 and 1300 ºC. These cements were characterized by SEM, XRD and the mechanical strength was evaluated by splitting tensile tests, using commercial cement as a reference. Furthermore, the phases were semi-quantified using the Rietveld method. The results show that hydration and sonochemical action increased the reactivity of the raw materials during firing and that phase formation is dependent on the thermal treatment conditions. The CAC cements were obtained at temperatures at least 200 ºC lower than those used in conventional methods, indicating the potential of this route of synthesis.

Rotary peeling yield of Schizolobium amazonicum (Leguminosae - Caesalpinioideae)

The tropical tree Schizolobium amazonicum is native from the Amazonian forest, naturally occurring in Brazil, Peru and Colombia. This work aimed to study the veneer yield made from this species. For this purpose, 50 logs from S. amazonicum were rotary peeled in a plywood industry installed in Brazilian Amazon region. The results indicated that S. amazonicum had a peeling yield similar or even higher than those usually obtained for species traditionally used for this purpose in Brazil, like those of Pinus and Eucalyptus. It was also observed that the dendrometric parameters of the log can be used to estimate the peeling yield in this species.

Activity of some isoenzymatic systems in stored coffee grains

Considering the worldwide consumption of coffee, it is natural that throughout the history many people have dedicated the research to markers that contribute somehow on gauging its quality. This research aimed to evaluate the biochemical performance of arabica coffee during storage. Coffee in beans (natural) and in parchment (pulped) dried in concrete terrace and in dryer with heated air were packed in jute bags and stored in not controlled environmental conditions. Enzymatic activities of superoxide dismutase, catalase, peroxidase, polyphenoloxidase, esterase and lipoxygenase in coffee grains were evaluated at zero, three, six, nine and twelve months by means of electrophoresis. Independently of the drying method, the activity of isoenzymatic complexes highlighted deteriorative processes in stored grains of coffee. The treatments 60/40º C and 60º C used to reduce the water content imposed a greater stress condition, accelerated metabolism of natural coffee in the storage with decreased activity of defense mechanisms due to latent damage in these grains. Natural coffees are more sensible to high drying temperatures and its quality reduces faster than pulped coffee in the storage.

Effect of thermal modification on the physical properties of juvenile and mature woods of Eucalyptus grandis

This study aimed to evaluate the effect of thermal treatment on the physical properties of juvenile and mature woods of Eucalyptus grandis. Boards were taken from 30-year-old E. grandis trees. The boards were thermally modified at 180 °C in the Laboratory of Wood Drying and Preservation at UNESP, Botucatu, Sao Paulo state, Brazil. The results showed that thermal modification caused: (1) decrease of 6.8% in the density at 0% equilibrium moisture content of mature wood; (2) significant decreases of 14.7% and 35.6% in the maximum volumetric swellings of juvenile and mature woods, respectively; (3) significant decreases of 13.7% and 21.3% in the equilibrium moisture content of juvenile and mature woods, respectively. The influence of thermal modification in juvenile wood was lower than in mature wood and caused greater uniformity in the physical variations between these types of wood in E. grandis.

Behavior of the brown-rot fungus Gloeophyllum trabeum on thermally-modified Eucalyptus grandis wood

In this study, we aimed evaluate the behavior of the brown-rot fungus Gloeophylum trabeum and white-rot fungus Pycnoporus sanguineus on thermally-modified Eucalyptus grandis wood. To this end, boards from five-year-eleven-month-old E. grandis trees, taken from the Duratex-SA company stock, were thermally-modified between 180 ºC and 220 ºC in the Laboratory of Wood Drying and Preservation at Universidade Estadual Paulista - UNESP, Botucatu, Sao Paulo state Brazil. Samples of each treatment were tested according to the ASTM D-2017 (2008) technical norm. The accelerated decay caused by the brown-rot fungus G. trabeum was compared with the decay caused by the white-rot fungus P. sanguineus, studied by Calonego et al. (2010). The results showed that (1) brown-rot fungus caused greater decay than white-rot fungus; and (2) the increase in temperature from 180 to 220 ºC caused reductions between 28.2% and 70.0% in the weight loss of E. grandis samples incubated with G. trabeum.

Secagem de celulases de origem fúngica por spray-drying

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Micropartículas lipídicas sólidas obtidas por spray drying para liberação intraocular de ibuprofeno

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Textured macro- and mesoporous alumina samples designed in the presence of different surfactant types

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Effect of Indomethacin on Surface Treatment and Intracanal Dressing of Replanted Teeth in Dogs

Purpose: This study evaluated the healing process of teeth replanted after root treatment and intracanal dressing with indomethacin alone or indomethacin with calcium hydroxide (Ca[OH](2)).Materials and Methods: Through a case-control study, 24 teeth of 6 adult dogs were extracted, dried, and divided into 4 groups according to the root surface treatment protocols performed before replantation and the intracanal medication used after replantation. In group 1 (negative control), root surfaces were treated by immersion in a 0.9% saline solution and then replanted. In the other groups, the roots were immersed for 10 minutes in Ca(OH)(2) (group 2), indomethacin (group 3), or a solution of indomethacin and Ca(OH)(2) (group 4). After 2 weeks, group 1 teeth were subjected to single-visit root canal treatment and obturation with gutta-percha and sealer consisting of zinc oxide and eugenol. The teeth in the other groups were subjected to intracanal dressing with the same material used for immersion. After an additional period of 28 weeks, the animals were euthanized and the jaws containing the replanted teeth were processed for histologic analysis. Histometric values were statistically analyzed, with significance set at a P value less than or equal to .05.Results: Group 1 exhibited significantly more normal periodontium than group 4 (P = .02). Total resorption was greater in group 4 than in group 1 (P = .02). No statistically significant difference in the percentage of surface resorption or in total inactive resorption was observed between the groups.Conclusions: The findings of this study suggest that intracanal dressing and topical root treatment with Ca(OH)(2) with or without indomethacin is not recommended for teeth dried for 50 minutes, but the use of indomethacin alone as root surface treatment for delayed tooth replantation deserves further study using longer drying periods. In addition, the present results suggest that a single-visit root canal, performed up to 2 weeks after replantation, might be indicated for teeth dried for up to 50 minutes. (C) 2014 American Association of Oral and Maxillofacial Surgeons

Structural and thermal properties of spray-dried methotrexate-loaded biodegradable microparticles

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Influence of abutment-to-fixture design on reliability and failure mode of all-ceramic crown systems

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Wettability of chlorhexidine treated non-carious and caries-affected dentine

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

HYGROSCOPIC PROPERTIES OF ORANGE PULP AND PEEL

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of Post-silanization Heat Treatments of Silanized Feldspathic Ceramic on Adhesion to Resin Cement

Purpose: To evaluate the effect of post-silanization heat treatment of a silane agent and rinsing with hot water of silanized CAD/CAM feldspathic ceramic surfaces on the microtensile bond strength between resin cement and the ceramic, before and after mechanical cycling.Materials and Methods: Blocks measuring 10 x 5.7 x 3.25 mm(3) were produced from feldspathic ceramic cubes (VITA Mark II, VITA Zanhfabrik). Each ceramic block was duplicated in composite resin using a template made of polyvinylsiloxane impression material. Afterwards, ceramic and corresponding resin composite blocks were ultrasonically cleaned and randomly divided according to the 5 strategies used for conditioning the ceramic surface (n = 10): GHF: etching with hydrofluoric acid 10% + rinsing with water at room temperature + silanization at 20 degrees C; G20: silanization; G77: silanization + oven drying at 77 degrees C; G20r: silanization + hot water rinsing; G77r: silanization + oven drying at 77 C + hot water rinsing. The resin and ceramic blocks were cemented using a dual-curing resin cement. Every group was divided in two subgroups: aging condition (mechanical cycling, designated as a) or non-aging (designated as n). All the bonded assemblies were sectioned into microsticks for microtensile bond strength (mu TBS) testing. The failure mode of the tested specimens was assessed and mu TBS data were statistically analyzed in two ways: first 2-way ANOVA (GHF, G20 and G77 in non-aging/aging conditions) and 3-way ANOVA (temperature x rinsing x aging factors, excluding GHF), followed by Tukey's test (p = 0.05).Results: The 2-way ANOVA revealed that the mu TBS was significantly affected by the surface treatment (p < 0.001) but not by aging (p = 0.68), and Tukey's test showed that G77-n/G77-a (18.0 MPa) > GHF-n/GHF-a (12.2 MPa) > G20-n/G20-a (9.1 MPa). The 3-way ANOVA revealed that the mu TBS was significantly affected by the heat treatment and rinsing factors (p < 0.001), but not affected by aging (p = 0.36). The rinsing procedure decreased, while oven drying increased the bond strengths. Group G77, in both non-aging and aging conditions (18.6-17.4 MPa), had the highest bond values. Failure modes were mainly mixed for all groups.Conclusion: Oven drying at 77 degrees C improved the bond strength between the resin cement and feldspathic ceramic, but hot water rinsing reduced the bond strength and should not be recommended.

Effect of Surface Conditioning Modalities on the Repair Bond Strength of Resin Composite to the Zirconia Core / Veneering Ceramic Complex

Purpose: This study evaluated the effect of different surface conditioning protocols on the repair strength of resin composite to the zirconia core / veneering ceramic complex, simulating the clinical chipping phenomenon.Materials and Methods: Forty disk-shaped zirconia core (Lava Zirconia, 3M ESPE) (diameter: 3 mm) specimens were veneered circumferentially with a feldspathic veneering ceramic (VM7, Vita Zahnfabrik) (thickness: 2 mm) using a split metal mold. They were then embedded in autopolymerizing acrylic with the bonding surfaces exposed. Specimens were randomly assigned to one of the following surface conditioning protocols (n = 10 per group): group 1, veneer: 4% hydrofluoric acid (HF) (Porcelain Etch) + core: aluminum trioxide (50-mu m Al2O3) + core + veneer: silane (ESPE-Sil); group 2: core: Al2O3 (50 mu m) + veneer: HF + core + veneer: silane; group 3: veneer: HF + core: 30 mu m aluminum trioxide particles coated with silica (30 mu m SiO2) + core + veneer: silane; group 4: core: 30 mu m SiO2 + veneer: HF + core + veneer: silane. Core and veneer ceramic were conditioned individually but no attempt was made to avoid cross contamination of conditioning, simulating the clinical intraoral repair situation. Adhesive resin (VisioBond) was applied to both the core and the veneer ceramic, and resin composite (Quadrant Posterior) was bonded onto both substrates using polyethylene molds and photopolymerized. After thermocycling (6000 cycles, 5 degrees C-55 degrees C), the specimens were subjected to shear bond testing using a universal testing machine (1 mm/min). Failure modes were identified using an optical microscope, and scanning electron microscope images were obtained. Bond strength data (MPa) were analyzed statistically using the non-parametric Kruskal-Wallis test followed by the Wilcoxon rank-sum test and the Bonferroni Holm correction (alpha = 0.05).Results: Group 3 demonstrated significantly higher values (MPa) (8.6 +/- 2.7) than those of the other groups (3.2 +/- 3.1, 3.2 +/- 3, and 3.1 +/- 3.5 for groups 1, 2, and 4, respectively) (p < 0.001). All groups showed exclusively adhesive failure between the repair resin and the core zirconia. The incidence of cohesive failure in the ceramic was highest in group 3 (8 out of 10) compared to the other groups (0/10, 2/10, and 2/10, in groups 1, 2, and 4, respectively). SEM images showed that air abrasion on the zirconia core only also impinged on the veneering ceramic where the etching pattern was affected.Conclusion: Etching the veneer ceramic with HF gel and silica coating of the zirconia core followed by silanization of both substrates could be advised for the repair of the zirconia core / veneering ceramic complex.