Preparation and optical properties of Ag/PPy composite colloids

Ag/PPy (polypyrrole) composite colloids were prepared through the reaction of silver nitrate with pyrrole solution in DNIF either in the dark, or under the irradiation of femtosecond laser (fs) pulse or UV lamp. The UV-vis spectra of the nanocomposite colloid display an intense absorption band around 620 nm, accompanied by a weak one around 470 nm. The colors and optical absorption spectra of as-synthesized colloids can be reversibly tuned between blue and red, corresponding to absorption band of 620 urn and 526 urn, within few seconds by adding base and acid solutions or gases in turn into the composite colloid suspension. In addition, excess of H+ solution enhanced the absorption band around 470 nm and, at the same time, depressed that around 620 nm. The possible mechanism for the formation and optical absorption properties of the Ag/PPy composite colloid was proposed. (C) 2006 Elsevier B.V. All rights reserved.

Bi2O3-B2O3-TiO2系统玻璃的形成能力研究

采用传统的玻璃熔融方法，研究了Bi2O3-B2O3-TiO2-RmOn四元系统的玻璃形成区（RmOn分别为La2O3、Sb2O3、ZrO2、SiO2和Nb2O5氧化物），给出了上述四元系统的玻璃形成范围。研究发现：Bi2O3-B2O3-TiO2-La2O3系统的玻璃形成范围最大，当TiO2的摩尔含量超过25％时，上述五个系统均不能形成玻璃。分剐熔制了摩尔分数55Bi2O3-35B2O3—5TiO2—5RmOn的玻璃（RmOn分别为La2O3、Sb2O3、ZrO2、SiO2和Nb2O5），测定了其红外吸收光

Effect of processing parameters on the optical properties of TiO2/ormosil planar waveguide

Hybrid TiO2/ormosil waveguiding films have been prepared by the sol-gel method at low thermal treatment temperature of 150° C. The influence of processing parameters including the molar ratios of titanium butoxide (Ti(OBu)(4))/3-glycidoxypropyltrimethoxysilane (GLYMO) and H2O/Ti(OBu)(4) (expressed as R), especially aging of sot on the optical properties was investigated. The optical properties of films were measured with scanning electron microscope (SEM), UV/VIS/NIR spectrophotometer (UV-Vis), m-line and the scattering-detection method. The results indicate that the film thickness increases with the increase of sol aging time, but the variation of refractive index as a function of sot aging time depends on the relative ratios of GLYMO to Ti(OBu)(4). Higher transmittance and lower attenuation of the planar waveguide can be obtained in the sol with lower Ti(OBu)(4) contents and shorter aging time.

Optical and surface properties of hybrid TiO2/ormosil planar waveguide prepared by the sol-gel process

Two kinds of silanes, 3-glycidoxypropyltrimethoxysilane (GLYMO) and 3-trimethoxysililpropylmethacrylate (TMSPM), were used to prepare ormosil waveguide films by the sol-gel method. Thirty percent Ti(OBu)(4) and 70% silane were contained in the precursor sets. The properties of films were measured by scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), UV/VIS/NIR spectrophotometer (UV-vis), atomic force microscopy (AFM), m-line and scattering-detection method. The films from GLYMO and TMSPM precursors exhibit similar thickness (2.58 mu m for GLYMO, 2.51 mu m for TMSPM) and refractive index (1.5438 for GLYMO, 1.5392 for TMSPM, lambda=632.8 nm), but the film from TMSPM precursor has higher propagation loss (1.024 dB/cm, lambda=632.8 nm) than the film prepared from GLYMO (0.569 dB/cm, lambda=632.8 nm). Furthermore, the film prepared from TMSPM is easy to be opaque and cracks during coating whereas the same phenomenon was not found for the film prepared with GLYMO. It is confirmed that GLYMO is a better precursor than TMSPM for waveguide film preparation. (C) 2005 Elsevier Ltd and Techna Group S.r.l. All rights reserved.