Studies of the germination response of seeds subjected to artificial stresses are provided tools for better understanding of the survivability and adaptation of these species in natural stress conditions such as drought or saline soils, common in agricultural and forest regions, contributing significantly to the development of management strategies. Thus, the purpose of this study was to evaluate the possible effects of water and salt stress on germination of Urochloa decumbens and Urochloa ruziziensis. The test was conducted at the Faculty of Technology of São Paulo, campus of Capon Bonito. The seeds were sown with four replicates of 50 seeds in paper soaked in solutions with the potentials of 0.0, -0.2, -0.4 and -0.8 MPa, induced with polyethylene glycol (PEG 6000) and NaCl. The germination test was conducted at 25 degrees C in the presence of light, evaluating the first test score at seven days after sowing, and weekly germination (normal seedlings) until 35 days. We calculated the index of germination rate. The results allowed the conclusion that water stress causes a greater reduction in force, speed of germination and cumulative germination of seeds of U. decumbens and U. ruziziensis than salt stress. The species U. decumbens showed higher tolerance to water and salt stresses.

Fresamento com ar quente: uma proposta para minimizar a formação de trincas térmicas em ferramentas de metal duro

This work presents the results, analyses and conclusions about a study carried out with objective of minimizing the thermal cracks formation on cemented carbide inserts during face milling. The main focus of investigation was based on the observation that milling process is an interrupted machining process, which imposes cyclic thermal loads to the cutting tool, causing frequent stresses changes in its superficial and sub-superficial layers. These characteristics cause the formation of perpendicular cracks from cutting edge which aid the cutting tool wear, reducing its life. Several works on this subject emphasizing the thermal cyclic behavior imposed by the milling process as the main responsible for thermal cracks formation have been published. In these cases, the phenomenon appears as a consequence of the difference in temperature experienced by the cutting tool with each rotation of the cutter, usually defined as the difference between the temperatures in the cutting tool wedge at the end of the cutting and idle periods (T factor). Thus, a technique to minimize this cyclic behavior with objective of transforming the milling in an almost-continuous process in terms of temperature was proposed. In this case, a hot air stream was applied into the idle period, during the machining process. This procedure aimed to minimize the T factor. This technique was applied using three values of temperature from the hot air stream (100, 350 e 580 oC) with no cutting fluid (dry condition) and with cutting fluid mist (wet condition) using the hot air stream at 580oC. Besides, trials at room temperature were carried out. Afterwards the inserts were analyzed using a scanning electron microscope, where the quantity of thermal cracks generated in each condition, the wear and others damages was analyzed. In a general way, it was found that the heating of the idle period was positive for reducing the number of thermal cracks during face milling with cemented carbide inserts. Further, the cutting fluid mist application was effective in reducing the wear of the cutting tools.

Clássicos versus Keynes: a abordagem formal de David Champernowne

Este texto tem por objetivo ressaltar um aspecto que não tem sido tratado com a devida profundidade na literatura que estuda a formalização da Teoria Geral do Emprego, dos Juros e da Moeda de John Maynard Keynes (1936). Mais precisamente, o texto destaca a estratégia de formalização adotada por David G. Champernowne em seu artigo intitulado Unemployment, Basic and Monetary: the classical analysis and the keynesian, publicado em 1935-36 na Review of Economic Studies. Chamamos a atenção para o fato dele distinguir a teoria clássica da teoria de Keynes não apenas pelos pressupostos adotados por cada teoria, mas principalmente pela construção de subsistemas a partir de um sistema geral, com características recursivas (relações de causalidade) distintas. As explicações em prosa, a descrição algébrica das funções comportamentais e condições de equilíbrio e a ilustração por meio de diagramas, além da escolha de conjuntos específicos de variáveis para representar cada uma das teorias e suas diferentes versões são aspectos deste artigo de Champernowne que merecem uma análise mais minuciosa.

Métodos e estratégias em proteômica e suas aplicações na área vegetal

A implementação da espectrometria de massa (MS) para as análises de peptídeos (MS) e de aminoácidos (MS em tandem ou MS/MS) tornou possível a identificação de centenas de proteínas em experimentos únicos. Uma grande variedade de estratégias está disponível atualmente para o fracionamento e a purificação de amostras, a identificação de proteínas, a quantificação, a análise de modificações pós-traducionais (MPT's) e os estudos de interação. Dessa forma, a proteômica abre novas perspectivas na biologia de plantas com ênfase nos estudos de variabilidade genética, estresses fisiológicos e desenvolvimento de plantas.

(Por) entre pedra e tela: a construção de uma memória republicana (Natal - 1906-1919)

This work, from a perspective that thinks the space as a historical category, and especially as a relationship which stresses the role of objects, proposes an analysis of the construction of a Republican memory in the city of Natal in the early twentieth century. This research will focus mainly on two objects: the obelisk opened in 1917, and the Andre de Albuquerque Square on the occasion of the celebration of Frei Miguelinho´s death centenary and the paint Julgamento de Frei Miguelinho ordered by the State Government to the painter Antonio Parreiras, picture that was in the Salão Nobre do Palácio do Poder Executivo of that time. In a geral way this work intend to analyse the construction of this memory as well as the role of these objects in this process. To achieve that, we propose to trace ways and networks to follow the possible associations(between people, events, images, discourses, objects, institutios etc.) in the constitution of mutual belongings. Thus, our procedure was to follow these objects through the pathways in which they became possible, so that in the end we could defend the idea that they are active participants of the process that establish them.

Modeling of interfaces in two-dimensional problems using solid finite elements with high aspect ratio

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

2D evaluation of crack openings using smeared and embedded crack models

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influência da velocidade de avanço do rebolo nos danos de aços endurecidos retificados

A tendência mundial é o aumento da produtividade e da produção de peças cada vez mais sofisticadas, com elevado grau de tolerância geométrica, dimensional, com bom acabamento superficial, com baixo custo. A retificação é responsável pelo acabamento final no processo de usinagem de um material. No entanto, danos gerados nesta fase de produção comprometem todos os recursos utilizados nas fases anteriores. Grande parte dos problemas ocorridos na retificação deve-se à enorme temperatura gerada pelo processo devido às condições de usinagem. Atribui-se à velocidade de avanço, que está diretamente relacionada com a produtividade, os danos ocorridos na retificação, ficando esta variável limitada até valores que não proporcione danos. Neste trabalho, através da variação da velocidade de avanço no processo de retificação cilíndrica externa do aço ABNT D6, racionalizando a aplicação de dois fluidos de corte e usando um rebolo superabrasivo de CBN (nitreto de boro cúbico) com ligante vitrificado, avaliou-se a influência da velocidade de avanço nos danos superficiais de aços endurecidos. Os resultados permitiram concluir que a velocidade de avanço associada a uma eficiente refrigeração e lubrificação, não provocou danos térmicos (queima, trincas, tensões de tração) ao material. Tensões residuais e a rugosidade do material retificado apresentaram uma correlação com as condições de usinagem. O trabalho concluiu ser capaz um aumento dos índices de produtividade sem provocar danos nos componentes retificados.

Evaluation of the thermal damages in inlet engine valves varying the grinding wheels and the cutting fluids

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Finite-Element Analysis of Stress on Dental Implant Prosthesis

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influence of the grinding wheel's dive speed on the damage of rectified hardened steels

The world tendency is the increase of the productivity and the production of pieces more and more sophisticated, with high degree of geometric and dimensional tolerances, with good surface finish and low cost. Rectification is responsible for the final finish in the machining process of a material. However, damages generated in this production phase affect all the resources used in the previous processes. Great part of the problems happennig in the rectification process is due to the enormous temperature generated in this activity because of the machining conditions. The dive speed, which is directly related to the productivity, is considered responsible for the damages that occur during rectification, limiting its values to those that do not cause such damages. In this work, through the variation of the dive speed in the process of cylindrical grinding of type ABNT D6 steel, rationalizing the application of two cutting fluids and using a CBN (cubic boron nitrate) abrasive wheel with vitrified blond, the influence of the dive speed on the surface damages of hardened steels was evaluated. The results allowed to say that the dive speed, associated to an efficient cooling and lubrication, didn't provoke thermal damages (including heated zones, cracks and tension stresses) to the material. Residual stresses and the roughness of rectified materials presented a correlation with the machining conditions. The work concluded that it is possible to increase the productivity without provoking damages in the rectified components.

Influence of shot peening and hard chromium electroplating on the fatigue strength of 7050-T7451 aluminum alloy

Chromium electrodeposition is a technique for the production of functional coatings on engineering components. These coatings are extensively micro-cracked and present high level of hardness, resistance to corrosion and wear and low coefficient of friction. In this paper the shot peening influence on the fatigue strength of aluminum 7050-T7451 alloy chromium electroplated, was investigated.The shot peening process was carried out to create residual stresses using ceramic and glass shots. A hard chromium electroplated coating of 100 mu m thickness was performed on the base material and the shot peened base material surfaces. S-N curves were obtained in axial and bending fatigue tests and compared with the 7050-T7451 aluminum alloy. In order to study the influence of residual stresses on fatigue life, the behavior of compressive residual stress field was measured by an X-ray tensometry.An increase in the axial fatigue strength of 25% and 50% of ceramic and glass shots, respectively, was observed. The lower performance in fatigue life for ceramic-shot peening may be attributed to higher surface damage, as a consequence of the overpeening intensity performed. However, in bending fatigue the behavior was practically equivalent for both processes. Fracture surface analysis by scanning electron microscopy was used to observe crack origin sites from shot peened and chromium electroplated samples. (C) 2006 Elsevier Ltd. All rights reserved.

Influence of anodization on the fatigue strength of 7050-T7451 aluminium alloy

In recent years, with higher demand for improved quality and corrosion resistance, recovered substrates have been extensively used. Consequently residual stresses originated from these coatings reduce the fatigue strength of a component. Due to this negative influence occasioned by corrosion resistance protective coatings, an effective process like shot peening must be considered to improve the fatigue strength. The shot peening treatment pushes the crack sources beneath the surface in most of medium and high cycle cases due to the compressive residual stress field (CRSF) induced. The aim of this study was to evaluate the influence on the fatigue life of anodic films grown on 7050-T7451 aluminium alloy by sulphuric acid anodizing, chromic acid anodizing and hard anodizing. The influence on the rotating and reverse bending fatigue strength of anodic films grown on the aluminium alloy is to degrade the stress life fatigue performance of the base material.A consistent gain in fatigue life in relation to the base material was obtained through the shot peening process in coated specimens, associated to a residual stress field compressive near the surface, useful to avoid fatigue crack nucleation and delay or even stop crack propagation.

Effect of electroless nickel interlayer on the fatigue strength of chromium electroplated AISI 4340 steel

Deposition of wear-resistant hard chromium plating leads to a decrease in the fatigue strength of the base material. Despite the effective protection against wear and corrosion, fatigue life and environmental requirements result in pressure to identify alternatives or to improve conventional chromium electroplating mechanical characteristics. An interesting, environmentally safer and cleaner alternative for the replacement of hard chronic plating is tungsten carbide thermal spray coating, applied by high velocity oxyfuel (HVOF) process.To improve the fatigue strength of aeronautical steel chromium electroplated, shot peening is a successfully used method. Multiple lacer systems of coatings are considered to have larger resistance to crack propagation in comparison with simple layer.The aim of this study was to analyze the effect of nickel underplate on the fatigue strength of hard chromium plated AISI 4340 steel in two mechanical conditions: HRc 39 and HRc 52.Rotating bending fatigue tests results indicate that the clectroless nickel plating underlayer is responsible for the increase in fatigue strength of AISI 4340 steel chromium electroplated. This behavior may be attributed to the largest toughness/ductility and compressive residual stresses which, probably, arrested or delayed the inicrocrack propagation from the hard chromium external layer. The compressive residual stress field (CRSF) induced by the electroplating process was determined by X-ray diffraction method. The evolution of fatigue strength compressive residual stress field CRSF and crack sources are discussed and analyzed by SEM. (c) 2006 Elsevier Ltd. All rights reserved.

Effects of surface treatments on the fatigue strength of AISI 4340 aeronautical steel

Internal residual stresses significantly influence the fatigue strength of coated materials. It is well known that chromium plating is the most used electrodeposited coating for important industrial applications. However, pressure to identify alternatives or to improve the chromium electroplating process have increased in recent years, related to the reduction in fatigue strength of the base material and to environmental requirements. The high efficiency and fluoride free hard chromium electroplating there called accelerated) is an improvement to the conventional process. One environmentally safer and cleaner alternative to hard chromium plating is tungsten carbide thermal spray coating applied by the High Velocity Oxy-Fuel (HVOF) process. To increase the fatigue strength of chromium plated materials, coating thickness and microcracks density are important parameters to be controlled. Techniques as compressive residual stresses induced by shot peening and multilayers, are also used. The aim of this study was to analyse the effects on AISI 4340 steel, in the rotating bending fatigue behaviour, of the: tungsten carbide thermal spray coating applied by HP/HVOF process; chemical nickel underplate, and shot peening process applied before coating deposition, in comparison to hard chromium electroplatings. Rotating bending fatigue test results indicate better performance for the conventional hard chromium plating in relation to the accelerated hard chromium electroplating. Tungsten carbide thermal spray coating and accelerated hard chromium plate over nickel resulted in higher fatigue strength when compared to samples conventional or accelerated hard chromium plated. Shot peening showed to be an excellent alternative to increase fatigue strength of AISI 4340 steel hard chromium electroplated. (C) 2001 Elsevier B.V. Ltd. All rights reserved.