A Mechanistic Model for the Water-Gas Shift Reaction over Noble Metal Substituted Ceria

The water-gas shift (WGS) reaction was carried out in the presence of Pd and Pt substituted nanocrystalline ceria catalysts synthesized by solution combustion technique. The catalysts were characterized by powder XRD and XPS. The noble metals were found to be present in ionic form substituted for the cerium atoms. The catalysts showed highactivity for the WGS reaction with high conversions below 250 degrees C. The products of reaction were only carbon dioxide and hydrogen, and no hydrocarbons were observed even in trace quantities. The reactions were carried out with different amounts of noble metal ion substitution and 2% Pt substituted ceria was found to be the best catalyst. The various possible mechanisms for the reaction were proposed and tested for their consistency with experimental data. The dual site mechanism best described the kinetics of the reaction and the corresponding rate parameters were obtained.

Raman and infra-red spectra of crystalline ammonium sulphamate

Raman spectrum of a single crystal of ammonium sulphamate has been recorded for the two different orientations using λ 2537 resonance radiation of the mercury as the exciter. Thirty-four Raman lines have been observed of which eight belong to the lattice oscillations. Weak hydrogen bonding of NH2 group in the crystal was predicted. The infra-red absorption spectrum of the substance was taken in the powder form in potassium bromide disc, using Carl Zeiss UR10 IR spectrometer. Thirty-five absorption maxima could be identified.

Raman and infra-red spectra of crystalline potassium sulphamate

Raman spectrum of a single crystal of potassium sulphamate has been recorded for the first time using λ 2536 radiation of mercury as the exciter. Thirty-three Raman lines have been observed of which nine belong to the lattice oscillations. The infra-red absorption spectrum of the substance was taken in the powder form in potassium bromide disc using Carl Zeiss UR 10 IR spectrometer. Thirty-six absorption maxima could be identified of which twenty-five have been recorded for the first time. The analysis clearly shows that the N-H bond in the crystalline potassium sulphamate is not hydrogen-bonded to any appreciable extent.

Effect of fuel on the formation structure, transport and magnetic properties of LaMnO3+nanopowders

Single-step low-temperature solution combustion (LCS) synthesis was adopted for the preparation of LaMnO3+ (LM) nanopowders. The powders were well characterized by powder X-ray diffraction (PXRD), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS),surface area and Fourier transform infrared spectroscopy (FTIR). The PXRD of as-formed LM showed a cubic phase but, upon calcination (900degrees C, 6 h), it transformed into a rhombohedral phase. The effect of fuel on the formation of LM was examined, and its structure and magnetoresistance properties were investigated. Magnetoresistance (MR) measurements on LM were carried out at 0, 1, 4 and 7 T between 300 and 10 K. LM (fuel-to-oxidizer ratio; = 1) showed an MR of 17% at 1 T, whereas, for 4 and 7 T, it exhibited an MR of 45 and 55%, respectively, near the TM-I. Metallic resistivity data below TM-I showed that the double exchange interaction played a major role in this compound. It was interesting to observe that the sample calcined at 1200 degrees C for 3 h exhibited insulator behavior.

Dielectric properties of (100-x)Li2B4O7-x(Ba5Li2Ti2Nb8O30) glasses and glass nanocrystal composites

Transparent glasses of various compositions in the system (100 -x)(Li2B4O7)-x(Ba5Li2Ti2Nb8O30) (5 <= x <= 20, in molar ratio) were fabricated by splat quenching technique. The glassy nature of the as-quenched samples was established by differential thermal analyses (DTA). X-ray powder diffraction studies confirmed the as-quenched glasses to be amorphous and the heat-treated to be nanocrystalline. Controlled heat-treatment of the as-quenched glasses at 500 degrees C for 8 h yielded nanocrystallites embedded in the glass matrix. High Resolution Transmission Electron Microscopy (HRTEM) of these samples established the size of the crystallites to be in the nano-range and confirmed the phase to be that of Ba5Li2Ti2Nb8O30 (BLTN) which was, initially, identified by X-ray powder diffraction. The frequency, temperature and compositional dependence of the dielectric constant and the electrical conductivity of the glasses and glass nanocrystal composites were investigated in the 100 Hz to 10 MHz frequency range. Electrical relaxations were analyzed using the electric modulus formalisms. The imaginary part of electric modulus spectra was modeled using an approximate solution of Kohlrausch-Williams-Watts relation. The frequency dependent electrical conductivity was rationalized using Jonscher's power law. The activation energy associated with the dc conductivity was ascribed to the motion of Li+ ions in the glass matrix. The activation energy associated with dielectric relaxation was almost equal to that of the dc conductivity, indicating that the same species took part in both the processes. (C) 2010 Elsevier B.V. All rights reserved.

Raman spectrum of C-deuteratedγ-glycine (NH 3+ CD2COO−)

The Raman spectrum of C-deuterated γ-glycine (NH3+CD2COO-) in the crystal powder form was taken using λ 2536·5 excitation. 26 Raman lines were recorded. Of these, eight lines are attributed to the external oscillations and eighteen Raman lines to the internal oscillations. Proper assignments are given to the observed frequencies.

Studies on phosphorus oxychloride and aluminium chloride complex

1. Anhydrous aluminium chloride reacts with phosphorus oxychloride to give a complex with a composition AlCl3.2 POCl3 which can be prepared in the form of a free flowing powder. 2. The phosphorus oxychloride-aluminium chloride complex in nitrobenzene dissociates into AlCl3.POCl3 and POCl3 as indicated by the cryoscopic measurements. 3. The solution of the complex in nitrobenzene has a higher specific conductivity than the corresponding electrical conductivities of individual components. Similar higher electrical conductance is observed when the two components are mixed in nitrobenzene in different proportions. 4.When a solution of anhydrous aluminium chloride in nitrobenzene is titrated conductometrically against a solution of phosphorus oxychloride in nitrobenzene, a limiting value in the conductivity is reached at point corresponding to the molecular composition, the components in the ratio of 1:2 AlCl3: POCl3 in solution. 5. The absorption maxima of the complex in nitrobenzene solution differ from the absorption maximum of the individual components.

A coaxial capacitive voltage divider for oscilloscopic recording of nanosecond high voltage pulses

A coaxial capacitance voltage divider with a ratio of 110 and a rise time much less than 2.5 ns was developed for use with a transmission line pulse generator capable of producing 100 kV rectangular pulses of 2 mu s duration. The low voltage arm of the divider is a 3 cm long tube of titania (TiO2) turned out from a cylindrical compact. The compact was made by first pressing titania powder using a suitable binder and then sintering at controlled temperatures. The tube was slipped over the terminating end of the pulse-forming cable to form the divider with the cable capacitance.

Enhanced Ion Anisotropy by Nonconventional Coordination Geometry: Single-Chain Magnet Behavior for a [{(FeL)-L-II}(2){Nb-IV(CN)(8)}] Helical Chain Compound Designed with Heptacoordinate Fe-II

Nonconventional heptacoordination in combination with efficient magnetic exchange coupling is shown to yield a 1-D heteronuclear {(FeNbIV)-Nb-II} compound with remarkable magnetic features when compared to other Fe(II)-based single chain magnets (SCM). Cyano-bridged heterometallic {3d-4d} and {3d-5d} chains are formed upon assembling Fe(II) bearing a pentadentate macrocycle as the blocking ligand with octacyano metallates, [M(CN)(8)](4-) (M = Nb-IV, Mo-IV, W-IV.) X-ray diffraction (single-crystal and powder) measurements reveal that the [{(H2O)Fe(L-1)}{M(CN)(8)}{Fe(L-1)}](infinity) architectures consist of isomorphous 1-D polymeric structures based on the alternation of {Fe(L-1)}(2+) and {M(CN)(8)}(4-) units (L-1 stands for the pentadentate macrocycle). Analysis of the magnetic susceptibility behavior revealed cyano-bridged {Fe-Nb} exchange interaction to be antiferromagnetic with J = -20 cm(-1) deduced from fitting an Ising model taking into account the noncollinear spin arrangement. For this ferrimagnetic chain a slow relaxation of its magnetization is observed at low temperature revealing a SCM behavior with Delta/k(B) = 74 K and tau(0) = 4.6 x 10(-11) s. The M versus H behavior exhibits a hysteresis loop with a coercive field of 4 kOe at 1 K and reveals at 380 mK magnetic avalanche processes, i.e., abrupt reversals in magnetization as H is varied. The origin of these characteristics is attributed to the combination of efficient {Fe-Nb} exchange interaction and significant anisotropy of the {Fe(L-1)) unit. High field EPR and magnetization experiments have revealed for the parent compound [Fe(L-1)(H2O)(2)]Cl-2 a negative zero field splitting parameter of D approximate to -17 cm(-1). The crystal structure, magnetic behavior, and Mossbauer data for [Fe(L-1)(H2O)(2)]Cl-2 are also reported.

Enhanced Ion Anisotropy by Nonconventional Coordination Geometry: Single-Chain Magnet Behavior for a [{(FeL)-L-II}(2){Nb-IV(CN)(8)}] Helical Chain Compound Designed with Heptacoordinate Fe-II

Nonconventional heptacoordination in combination with efficient magnetic exchange coupling is shown to yield a 1-D heteronuclear {(FeNbIV)-Nb-II} compound with remarkable magnetic features when compared to other Fe(II)-based single chain magnets (SCM). Cyano-bridged heterometallic {3d-4d} and {3d-5d} chains are formed upon assembling Fe(II) bearing a pentadentate macrocycle as the blocking ligand with octacyano metallates, [M(CN)(8)](4-) (M = Nb-IV, Mo-IV, W-IV.) X-ray diffraction (single-crystal and powder) measurements reveal that the [{(H2O)Fe(L-1)}{M(CN)(8)}{Fe(L-1)}](infinity) architectures consist of isomorphous 1-D polymeric structures based on the alternation of {Fe(L-1)}(2+) and {M(CN)(8)}(4-) units (L-1 stands for the pentadentate macrocycle). Analysis of the magnetic susceptibility behavior revealed cyano-bridged {Fe-Nb} exchange interaction to be antiferromagnetic with J = -20 cm(-1) deduced from fitting an Ising model taking into account the noncollinear spin arrangement. For this ferrimagnetic chain a slow relaxation of its magnetization is observed at low temperature revealing a SCM behavior with Delta/k(B) = 74 K and tau(0) = 4.6 x 10(-11) s. The M versus H behavior exhibits a hysteresis loop with a coercive field of 4 kOe at 1 K and reveals at 380 mK magnetic avalanche processes, i.e., abrupt reversals in magnetization as H is varied. The origin of these characteristics is attributed to the combination of efficient {Fe-Nb} exchange interaction and significant anisotropy of the {Fe(L-1)) unit. High field EPR and magnetization experiments have revealed for the parent compound [Fe(L-1)(H2O)(2)]Cl-2 a negative zero field splitting parameter of D approximate to -17 cm(-1). The crystal structure, magnetic behavior, and Mossbauer data for [Fe(L-1)(H2O)(2)]Cl-2 are also reported.

Synthesis and Densification of Monolithic Zirconium Carbide by Reactive Hot Pressing

Synthesis and densification of monolithic zirconium carbide (ZrC) has been carried out by reactive hot pressing of zirconium (Zr) and graphite (C) powders in the molar ratios 1:1, 1.25:1, 1.5:1, and 2:1 at 40 MPa, 1200 degrees-1600 degrees C. Monolithic ZrC could be synthesized with a C/Zr ratio similar to 0.5-1.0 and the post heat-treated samples have the lattice parameter in the range 4.665 to 4.698 A. Densification improves with an increasing deviation from the stoichiometry. Fine-grained (similar to 1 mu m) and nearly fully dense material (99% RD) could be obtained at a temperature as low as 1200 degrees C with C/Zr similar to 0.67. Microstructural and XRD observations suggest that densification occurred at low temperatures with nonstoichiometric Zr-C powder mixtures.

Vapour phase synthesis of salol over solid acids via transesterification

The transesterification of methyl salicylate with phenol has been studied in vapour phase over solid acid catalysts such as ZrO2, MoO3 and SO42- or Mo(VI) ions modified zirconia. The catalytic materials were prepared and characterized for their total surface acidity, BET surface area and powder XRD patterns. The effect of mole-ratio of the reactants, catalyst bed temperature, catalyst weight, flow-rate of reactants, WHSV and time-on-stream on the conversion (%) of phenol and selectivity (%) of salol has been investigated. A good yield (up to 70%) of salol with 90% selectivity was observed when the reactions were carried out at a catalyst bed temperature of 200 degrees C and flow-rate of 10 mL/h in presence of Mo(VI)/ZrO2 as catalyst. The results have been interpreted based on the variation of acidic properties and powder XRD phases of zirconia on incorporation of SO42- or Mo(VI) ions. The effect of poisoning of acid sites of SO42- or Mo(VI) ions modified zirconia on total surface acidity, powder XRD phases and catalytic activity was also studied. Possible reaction mechanisms for the formation of salol and diphenyl ether over acid sites are proposed.

Consideration on thermal decomposition of calcium hydroxide pellets for energy storage

The reversible chemical reaction of Ca(OH)2/CaO appears to be attractive for storage of solar thermal energy, in view of the nonpolluting and nontoxic nature of the reactants. This paper presents some data on thermal decomposition of calcium hydroxide pellets along with its additives of aluminum, aluminum hydroxide, zinc, and copper. The addition of aluminum and zinc powder enhanced the rate of decomposition considerably at 450°C, but copper had no effect. Considerations on the effect of additives are also discussed in some detail, though their effects are not established with certainty. There is some evidence that heat transfer into the pellet, and the number of potential nucleation sites due to thermal stresses, influence the kinetics and mechanism of decomposition.

Thermal behaviours of sulphur-selenium mixtures

The thermal behaviours of sulphur, selenium and their mixtures have been studied over the range 40–450Dagger. It has been shown that the polymerization threshold temperature of sulphur,T Ø, decreases with increasing selenium content and follows the equilibrium copolymerization model proposed by Tobolsky and Owen. The formation of octa-atomic species Se8–xSx, where 8 >x > 4, takes place only after sulphur is in the liquid state. The rate of polymerization is enhanced by the addition of increasing amounts of selenium and this is reflected in the higher polymerization peak temperatures. The X-ray powder diffractograms show that all the sulphur-selenium melts belong to the same phase as that of SeS, though the constituent atoms are randomly distributed.

Photocatalytic Activity of Microwave Plasma-Synthesized TiO2 Nanopowder

Nanocrystalline TiO2 was synthesized using the microwave plasma technique and characterized using X-ray diffraction, transmission electron microscopy, scanning electron microscopy, laser particle size analyzer, UV-vis spectroscopy and BET surface area analyzer. The synthesized TiO2 powder crystallized in anatase phase and the crystallite sizes were in nanometers. The photocatalytic activity of the compound was determined and compared against the activity of the commercial Degussa P-25 TiO2 catalyst. The degradation rates of the dyes were found to be higher over the synthesized TiO2 as compared to that over commercial Degussa P-25 TiO2.