Growth and annealing properties of Mg0.4Al2.4O4 crystal

Mg0.4Al2.4O4 single crystals with good optical quality were successfully grown by the Czochralski method. The transmission spectrum indicated that the absorption edge of the crystal was at 220nm, while no apparent absorption peaks were found. The X-ray diffraction and DSC curve analysis showed that Mg0.4Al2.4O4 crystal was stable at room temperature. While after annealing in the air and hydrogen atmosphere at about 1200 degrees C,Mg0.4Al2.4O4 decomposed into Al2O3 and (MgO)(0.4)(Al2O3)(x) (0.4 < x < 1.2). The reaction mainly occurred on the crystal surface, barely inside. (C) 2008 Elsevier B.V. All rights reserved.

Thickness dependence of structure and optical properties of silver films deposited by magnetron sputtering

A series of silver films with different thickness were prepared under identical conditions by direct current magnetron sputtering. The optical properties of the silver films were measured using spectrophotometric techniques and the optical constants were calculated from reflection and transmission measurements made at near normal incidence. The results show that the optical properties and constants are affected by films' thickness. Below the critical thickness of 17 nm at which Ag film forms a continuous film, the optical properties and constants vary significantly as the thickness of films increases and then tends to a stable value which is reached at 41 nm. X-ray diffraction measurements were carried out to examine the structure and stress evolution of the Ag films as a function of films' thickness. It was found that the interplanar distance of (111) orientation decreases when the film thickness increases and tends to be close to that of bulk material. The compressive strains also decrease with increasing thickness. (C) 2007 Published by Elsevier B.V.

Optical and electrical properties of TiOx thin films deposited by electron beam evaporation

The TiOx thin films were prepared by electron beam evaporation using TiO as the starting material. The effect of the annealing temperature on the optical and electrical properties was investigated. The spectra of X-ray photoelectron spectroscopy reveal that Ti in the films mainly exist in the forms of Ti2+ and Ti3+ below 400 degrees C 24h annealing. The charge transfer between different titanium ion contribute greatly to the color, absorption, and electrical resistance of the films. (c) 2006 Elsevier Ltd. All rights reserved.

Hole-Phonon Relaxation and Photocatalytic Properties of Titanium Dioxide and Zinc Oxide: First-Principles Approach

First-principles calculations for the temporal characteristics of hole-phonon relaxation in the valence band of titanium dioxide and zinc oxide have been performed. A first-principles method for the calculations of the quasistationary distribution function of holes has been developed. The results show that the quasistationary distribution of the holes in TiO2 extends to an energy level approximately 1eV below the top of the valence band. This conclusion in turn helps to elucidate the origin of the spectral dependence of the photocatalytic activity of TiO2. Analysis of the analogous data for ZnO shows that in this material spectral dependence of photocatalytic activity in the oxidative reactions is unlikely.

Luminescence and Magnetic Properties of Two Three -Dimensional Terbium and Dysprosium MOFs Based on Azobenzene-4,4 '-Dicarboxylic Linker

We report the in situ formation of two novel metal-organic frameworks based on terbium and dysprosium ions using azobenzene-4,4-dicarboxylic acid (H(2)abd) as ligand, synthesized by soft hydrothermal routes. Both materials show isostructural three-dimensional networks with channels along a axis and display intense photoluminescence properties in the solid state at room temperature. Textural properties of the metal-organic frameworks (MOFs) have been fully characterized although no appreciable porosity was obtained. Magnetic properties of these materials were studied, highlighting the dysprosium material displays slightly frequency-dependent out of phase signals when measured under zero external field and under an applied field of 1000 Oe.

Sensitivity of wear rates in the micro-scale abrasion test to test conditions and material hardness

Micro-scale abrasion (ball cratering) tests were performed with different combinations of ball and bulk specimen materials, under different test conditions, such as load and abrasive slurry concentration. Wear modes were classified into two types: with rolling particle motion and with grooving particle motion. Wear rates observed with rolling particle motion were relatively insensitive to test conditions, whereas with grooving motion they varied much more. It is suggested that rolling abrasion is therefore a more appropriate mode if reproducible test results are desired. The motion of the abrasive particles can be reliably predicted from the knowledge of hardnesses and elastic properties of the ball and the specimen, and from the normal load and the abrasive slurry concentration. General trends in wear resistance measured in the micro-scale abrasion test with rolling particle motion are similar to those reported in tests with fixed abrasives with sliding particle motion, although the variation in wear resistance with hardness is significantly smaller. © 2004 Published by Elsevier B.V.

Desenvolvimento e implementação de algoritmo para análise de dutos fabricados ou reparados com material compósito carregados com pressão interna utilizando o método dos elementos finitos.

A integridade de dutos ganha importância à medida em que o desenvolvimento da indústria expande a malha para transportar líquidos e gases num contexto de aumento das exigências ambientais. Um importante aliado para manutenção da integridade de dutos são reparos de materiais compósitos. Estes materiais apresentam baixa densidade, capacidade de direcionar resistência de acordo com as direções das solicitações, execução de reparo a frio sem necessidade de interromper produção ou grande maquinário. Este trabalho tem como objetivo desenvolver e implementar um algoritmo de elementos finitos que permita avaliar os esforços e a resistência das paredes de um tubos fabricados ou reparados com laminados de material compósito carregados com pressão interna. Entre as vantagens de desenvolver um programa tem-se: agilidade de avaliação, menor custo com licença, menores exigências computacionais, possibilidade de desenvolver o programa e o melhor entendimento da modelagem dos fenômenos. Utiliza-se como entrada do programa o diâmetro do duto, pressão interna e parâmetros do laminado. A modelagem em elementos finitos é realizada a partir da teoria clássica de laminados. Aplicando o carregamento resultante da pressão interna, determina-se os deslocamentos e são calculadas as tensões e aplicado o critério de falha de Tsai-Hill em cada camada. Estudos experimentais e numéricos encontrados na literatura foram simulados com o programa gerado e os resultados para propriedades do laminado, tensões nos dutos e pressão de ruptura apresentam concordância com os resultados da literatura.O programa ainda tem sua estrutura modificada para encontrar a pressão de falha a partir dos dados do laminado. O programa implementado permite uma avaliação rápida de resistência do reparo e possibilita avaliar rapidamente a resposta a mudanças nos parâmetros de projeto do laminado.

Flexoelectro-optic properties of chiral nematic liquid crystals in the uniform standing helix configuration.

The flexoelectro-optic effect describes the rotation of the optic axis of a short-pitch chiral nematic liquid crystal under the application of an electric field. We investigate the effect in the uniform standing helix, or "Grandjean" configuration. An in-plane electric field is applied. The director profile is determined numerically using a static one-dimensional continuum model with strong surface anchoring. The Berreman method is used to solve for plane-wave solutions to Maxwell's equations, and predict the optical properties of the resulting structure in general cases. By using a chiral nematic with short pitch between crossed polarizers an optical switch may be generated. With no applied field the configuration is nontransmissive at normal incidence, but becomes transmissive with an applied field. For this case, numerical results using the Berreman method are supplemented with an analytic theory and found to be in good agreement. The transmitted intensity as a function of tilt, the contrast ratio, and the tilt required for full intensity modulation are presented. The angular dependence of the transmission is calculated and the isocontrast curves are plotted. For typical material and cell parameters a switching speed of 0.017 ms and contrast ratio of 1500:1 at normal incidence are predicted, at a switch-on tilt of 41.5 degrees. Experimental verification of the analytic and numerical models is provided.

Studies on technological problems associated with the processing of cooked frozen prawns. Pt. 1. Preprocess storage conditions of raw material in relation to quality

The chemical and organoleptic properties of prawn held in ice for different days prior to cooking and the changes after freezing and subsequent storage were studied with three different species of prawn viz. Metapenaeus monoceros, Metapenaeus dobsoni and Parapeneopsis stylifera. The optimum period for which the prawn can be kept under ideal conditions of icing prior to cooking has been worked out.

Comparative studies on the canning properties of pomfrets and hilsa

Fresh silver pomfret, black pomfret and hilsa were canned at absolutely fresh and iced conditions and the qualities of the final products were studied comparatively in relation to the initial quality of the raw materials. Under identical conditions a maximum quantity of cook-drip and nitrogen contents were found to be lost in black pomfret and minimum in hilsa. Silver pomfret and black pomfret iced for 3 days gave fairly good products on canning while hilsa came out only as a satisfactory product on canning after the same ice storage period of the raw material.

Influence of particle properties on the erosive wear of sintered boron carbide

Sintered boron carbide is very hard, and can be an attractive material for wear-resistant components in critical applications. Previous studies of the erosion of less hard ceramics have shown that their wear resistance depends on the nature of the abrasive particles. Erosion tests were performed on a sintered boron carbide ceramic with silica, alumina and silicon carbide erodents. The different erodents caused different mechanisms of erosion, either by lateral cracking or small-scale chipping; the relative values of the hardness of the erodent and the target governed the operative mechanism. The small-scale chipping mechanism led to erosion rates typically an order of magnitude lower than the lateral fracture mechanism. The velocity exponents for erosion in the systems tested were similar to those seen in other work, except that measured with the 125 to 150 μm silica erodent. With this erodent the exponent was initially high, then decreased sharply with increasing velocity and became negative. It was proposed that this was due to deformation and fragmentation of the erodent particles. In the erosion testing of ceramics, the operative erosion mechanism is important. Care must be taken to ensure that the same mechanism is observed in laboratory testing as that which would be seen under service conditions, where the most common erodent is silica.

Tribological properties of mems materials measured on a small-scale device

Micro-electro-mechanical systems, MEMS, is a rapidly growing interdisciplinary technology within the general field of Micro-Systems Technology which deals with the design and manufacture of miniaturised machines with major dimensions at the scale of tens, to perhaps hundreds, of microns. Because they depend on the cube of a representative dimension, component masses and inertias rapidly become small as size decreases whereas surface and tribological effects, which often depend on area, become increasingly important. Although MEMS components and their areas of contact are small, tribological conditions, measured by contact pressures or acceptable wear rates, are demanding and technical and commercial success will require careful measurement and precise control of surface topography and properties. Fabrication of small numbers of MEMS devices designed to test potential material combinations can be prohibitively expensive and thus there is a need for small scale test facilities which mimic the contact conditions within a micro-machine without themselves requiring processing within a full semiconductor foundry. The talk will illustrate some initial experimental results from a small-scale experimental device which meets these requirements, examining in particular the performance of Diamond-Like-Carbon coatings on a silicon substrate. Copyright © 2005 by ASME.

Viscoelastic properties of bone as a function of hydration state determined by nanoindentation

Spherical indentation creep testing was used to examine the effect of hydration state on bone mechanical properties. Analysis of creep data was based on the elastic-viscoelastic correspondence principle and utilized a direct solution for the finite loading-rate experimental conditions. The zero-time shear modulus was computed from the creep compliance function and compared to the indentation modulus obtained via conventional indentation analysis, based on an elastic unloading response. The method was validated using a well-known polymer material under three different loading conditions. The method was applied to bone samples prepared with different water content by partial exchange with ethanol, where 70% ethanol was considered as the baseline condition. A hydration increase was associated with a 43% decrease in stiffness, while a hydration decrease resulted in a 20% increase in bone tissue stiffness.

Evaluation of quality of shark livers using bio-chemical properties and organoleptic score sheet

Shark livers are considered as an important raw material providing a quality fish oil. It has been reported to aid white — blood-cell production and act as an active ingredient in hemorrhoid treatments. It is also reported that liver oil as a good supplement of vitamin A and poly-unsaturated fatty acids which are important to the development of brain cells in human. Freshness of livers is very important to extract better quality oil. In Sri Lanka, the annual shark production amounts to 8000t, however the quality of livers collected from landing sites has not being measured yet. Present study was conducted to evaluate the quality of silky (Charcarninus fakiformis) shark livers available in Negombo and Beruwala landing sites in the West Coast of Sri Lanka and also to study the relationship between organoleptic and bio-chemical correlation on freshness of shark livers. Liver samples which were collected from landing sites in the West coast of Sri Lanka, were evaluated for external and internal colour, texture and odour. Total volatile nitrogen (TVN), pH value, free fatty acid (FFA%) and peroxide (PV) values of livers were also determined to assess quality. According to the organoleptic scoring system 4.3% of liver samples were categorized as best in quality while 30.4%, 56.5% and 8.7% rated as good, medium and poor in quality respectively at the Negombo and Beruwala landing sites. Bio-chemical analysis showed that the better quality livers had the highest score for sensory evaluation and low values for TVN, FFA and peroxide value while low quality livers gave low score for sensory evaluation and high TVN, FFA, peroxide values. Correlation coefficient of organoleptic scores against total volatile nitrogen value, pH value, free fatty acid % and peroxide value of shark livers were determined by statistical analysis. Organoleptic score of shark livers was found to be highly.

Microstructure and superconducting properties of single grains of Y-Ba-Cu-O containing Y-2411(M) and Y2O3

Y-Ba-Cu-O (YBCO) single grains have the potential to generate large trapped magnetic fields for engineering applications, and research on the processing and properties of this material has attracted interest world-wide over the past 20 years. In particular, the introduction of flux pinning centers to the large grain microstructure to improve its current density Jc, and hence trapped field, has been investigated extensively. Y2Ba 4CuMO2 [Y-2411(M)], where M = Nb, Ta, Mo, W, Ru, Zr, Bi and Ag, has been discovered recently to form very effective flux pinning centers due primarily to its ability to form nano-size inclusions in the superconducting phase matrix. However, the addition of the Y-2411(M) phase to the precursor composition complicates the melt-processing of single grains. The addition of Y2O3 to the precursor composition, however, broadens the growth window of single YBCO grains containing Y-2411 (M). We report an investigation of the microstructures and superconducting properties of single grains of this composition grown by top seeded melt growth (TSMG). © 2010 IEEE.