Effect of air-particle abrasion protocols on the biaxial flexural strength, surface characteristics and phase transformation of zirconia after cyclic loading

This study evaluated the effect of air-particle abrasion protocols on the biaxial flexural strength, surface characteristics and phase transformation of zirconia after cyclic loading. Disc-shaped zirconia specimens (Ø: 15mm, thickness: 1.2mm) (N=32) were submitted to one of the air-particle abrasion protocols (n=8 per group): (a) 50μm Al2O3 particles, (b) 110μm Al2O3 particles coated with silica (Rocatec Plus), (c) 30μm Al2O3 particles coated with silica (CoJet Sand) for 20s at 2.8bar pressure. Control group received no air-abrasion. All specimens were initially cyclic loaded (×20,000, 50N, 1Hz) in water at 37°C and then subjected to biaxial flexural strength testing where the conditioned surface was under tension. Zirconia surfaces were characterized and roughness was measured with 3D surface profilometer. Phase transformation from tetragonal to monoclinic was determined by Raman spectroscopy. The relative amount of transformed monoclinic zirconia (FM) and transformed zone depth (TZD) were measured using XRD. The data (MPa) were analyzed using ANOVA, Tukey's tests and Weibull modulus (m) were calculated for each group (95% CI). The biaxial flexural strength (MPa) of CoJet treated group (1266.3±158A) was not significantly different than that of Rocatec Plus group (1179±216.4A,B) but was significantly higher than the other groups (Control: 942.3±74.6C; 50μm Al2O3: 915.2±185.7B,C). Weibull modulus was higher for control (m=13.79) than those of other groups (m=4.95, m=5.64, m=9.13 for group a, b and c, respectively). Surface roughness (Ra) was the highest with 50μm Al2O3 (0.261μm) than those of other groups (0.15-0.195μm). After all air-abrasion protocols, FM increased (15.02%-19.25%) compared to control group (11.12%). TZD also showed increase after air-abrasion protocols (0.83-1.07μm) compared to control group (0.59μm). Air-abrasion protocols increased the roughness and monoclinic phase but in turn abrasion with 30μm Al2O3 particles coated with silica has increased the biaxial flexural strength of the tested zirconia. © 2013 Elsevier Ltd.

Effect of the root canal final rinse protocols on the debris and smear layer removal and on the push-out strength of an epoxy-based sealer

The aim of the present study was to evaluate the efficacy of QMiX, SmearClear, and 17% EDTA for the debris and smear layer removal from the root canal and its effects on the push-out bond strength of an epoxy-based sealer by scanning electron microscopy (SEM). Forty extracted human canines (n=10) were assigned to the following final rinse protocols: G1-distilled water (control), G2-17% EDTA, G3-SmearClear, and G4-QMiX. The specimens were submitted to a SEM analysis to evaluate the presence of debris and smear layer, respectively, in the apical or cervical segments. In sequence, forty extracted human maxillary canines with the root canals instrumented were divided into four groups (n=10) similar to the SEM analysis study. After the filling with AH Plus, the roots were transversally sectioned to obtain dentinal slices. The specimens were submitted to a push-out bond strength test using an electromechanical testing machine. The statistical analysis for the SEM and push-out bond strength studies were performed using the Kruskal-Wallis and Dunn tests (α=5%). There was no difference among the G2, G3, and G4 efficacy in removing the debris and smear layer (P>0.05). The efficacy of these groups was superior to the control group. The push-out bond strength values of G2, G3, and G4 were superior to the control group. The ability to remove the debris and smear layer by SmearClear and QMiX was as effective as the 17% EDTA. The final rinse with these solutions promoted similar push-out bond strength values. © 2013 Wiley Periodicals, Inc.

Insulin Suppresses Atrophy- and Autophagy-related Genes in Heart Tissue and Cardiomyocytes Through AKT/FOXO Signaling

Insulin is an important regulator of the ubiquitin-proteasome system (UPS) and of lysosomal proteolysis in cardiac muscle. However, the role of insulin in the regulation of the muscle atrophy-related Ub-ligases atrogin-1 and MuRF1 as well as in autophagy, a major adaptive response to nutritional stress, in the heart has not been characterized. We report here that acute insulin deficiency in the cardiac muscle of rats induced by streptozotocin increased the expression of atrogin-1 and MuRF1 as well as LC3 and Gabarapl1, 2 autophagy-related genes. These effects were associated with decreased phosphorylation levels of Akt and its downstream target Foxo3a; this phenomenon is a well-known effect that permits the maintenance of Foxo in the nucleus to activate protein degradation by proteasomal and autophagic processes. The administration of insulin increased Akt and Foxo3a phosphorylation and suppressed the diabetes-induced expression of Ub-ligases and autophagy-related genes. In cultured neonatal rat cardiomyocytes, nutritional stress induced by serum/glucose deprivation strongly increased the expression of Ub-ligases and autophagy-related genes; this effect was inhibited by insulin. Furthermore, the addition of insulin in vitro prevented the decrease in Akt/Foxo signaling induced by nutritional stress. These findings demonstrate that insulin suppresses atrophy- and autophagy-related genes in heart tissue and cardiomyocytes, most likely through the phosphorylation of Akt and the inactivation of Foxo3a. © Georg Thieme Verlag KG.

Cysteine proteinase inhibitors regulate human and mouse osteoclastogenesis by interfering with RANK signaling

The cysteine proteinase inhibitor cystatin C inhibited RANKL-stimulated osteoclast formation in mouse bone marrow macrophage cultures, an effect associated with decreased mRNA expression of Acp5, Calcr, Ctsk, Mmp9, Itgb3, and Atp6i, without effect on proliferation or apoptosis. The effects were concentration dependent with half-maximal inhibition at 0.3 μM. Cystatin C also inhibited osteoclast formation when RANKL-stimulated osteoclasts were cultured on bone, leading to decreased formation of resorption pits. RANKL-stimulated cells retained characteristics of phagocytotic macrophages when cotreated with cystatin C. Three other cysteine proteinase inhibitors, cystatin D, Z-RLVG-CHN2 (IC50 0.1 μM), and E-64 (IC 50 3 μM), also inhibited osteoclast formation in RANKL-stimulated macrophages. In addition, cystatin C, Z-RLVG-CHN2, and E-64 inhibited osteoclastic differentiation of RANKL-stimulated CD14+ human monocytes. The effect by cystatin C on differentiation of bone marrow macrophages was exerted at an early stage after RANKL stimulation and was associated with early (4 h) inhibition of c-Fos expression and decreased protein and nuclear translocation of c-Fos. Subsequently, p52, p65, IκBα, and Nfatc1 mRNA were decreased. Cystatin C was internalized in osteoclast progenitors, a process requiring RANKL stimulation. These data show that cystatin C inhibits osteoclast differentiation and formation by interfering intracellularly with signaling pathways downstream RANK. © FASEB.

Effect of final irrigation protocols on microhardness and erosion of root canal dentin

The aim of this study was to evaluate the effect of final irrigation protocols (17% EDTA, BioPure MTAD, SmearClear, and QMiX) on microhardness and erosion of root canal dentin. Fifty roots were sectioned transversely at the cement-enamel junction and each root was sectioned horizontally into 4-mm-thick slices. The samples were divided into five groups (n=10) according to the final irrigation protocol: G1: distilled water (control group); G2: 17% EDTA; G3: BioPure MTAD; G4: SmearClear; and G5: QMiX. The dentin microhardness was then measured with a load of 25 g for 10 s. Initially, the reference microhardness values were obtained for the samples without any etching. The same samples were then submitted to the final irrigation protocols. A new measure was realized and the difference between before and after the procedures was the dentin microhardness reduction. In sequence, the specimens were submitted to SEM analysis to verify the dentinal erosion. The Kruskal Wallis and Dunn tests (α=5%) were used to compare the results. The dentin microhardness decreased for all final irrigation protocols. There was no significant difference between groups 2, 3, 4, and 5 (P>0.05), but this groups presented significant dentin microhardness reduction than G1 (P<0.05). In G2, occurred the highest incidence of dentinal erosion (P<0.05). 17% EDTA, BioPure MTAD, SmearClear, and QMiX promoted significant dentin microhardness reduction. © 2013 Wiley Periodicals, Inc.

Disinfection protocols to prevent cross-contamination between dental offices and prosthetic laboratories

Control of cross-contamination between dental offices and prosthetic laboratories is of utmost importance to maintain the health of patients and dental office staff. The purpose of this study was to evaluate disinfection protocols, considering antimicrobial effectiveness and damage to the structures of prostheses. Solutions of 1% sodium hypochlorite, 2% chlorhexidine digluconate, 50% vinegar and sodium perborate were evaluated. Specimens were contaminated in vitro with standardized suspensions of Candida albicans, Streptococcus mutans, Escherichia coli, Staphylococcus aureus and Bacillus subtilis spores. Disinfection by immersion for 10. min was performed. Final counts of microorganisms were obtained using the plating method. Results were statistically compared by Kruskal-Wallis ANOVA and Dunn's test. The surface roughness of 40 specimens was analyzed before and after 10 disinfection cycles, and results were compared statistically using Student's t test. The solution of 50% vinegar was as effective as 1% sodium hypochlorite and 2% chlorhexidine against C. albicans, E. coli and S. mutans. The sodium perborate solution showed the lowest antimicrobial effectiveness. Superficial roughness increased after cycles in 1% sodium hypochlorite (p=0.02). Solutions of 1% sodium hypochlorite, 2% chlorhexidine and 50% vinegar were effective for the disinfection of heat-polymerized acrylic specimens. Sodium hypochlorite increased the superficial roughness. © 2013 King Saud Bin Abdulaziz University for Health Sciences.

Air-particle abrasion on zirconia ceramic using different protocols: Effects on biaxial flexural strength after cyclic loading, phase transformation and surface topography

This study evaluated the effect of different air-particle abrasion protocols on the biaxial flexural strength and structural stability of zirconia ceramics. Zirconia ceramic specimens (ISO 6872) (Lava, 3M ESPE) were obtained (N=336). The specimens (N=118, n=20 per group) were randomly assigned to one of the air-abrasion protocols: Gr1: Control (as-sintered); Gr2: 50 μm Al2O3 (2.5 bar); Gr3: 50 μm Al2O3 (3.5 bar); Gr4: 110 μm Al2O3(2.5 bar); Gr5: 110 μm Al2O3 (3.5 bar); Gr6: 30 μm SiO2 (2.5 bar) (CoJet); Gr7: 30 μm SiO2(3.5 bar); Gr8: 110 μm SiO2 (2.5 bar) (Rocatec Plus); and Gr9: 110 μm SiO2 (3.5 bar) (duration: 20 s, distance: 10 mm). While half of the specimens were tested immediately, the other half was subjected to cyclic loading in water (100,000 cycles; 50 N, 4 Hz, 37 °°C) prior to biaxial flexural strength test (ISO 6872). Phase transformation (t→m), relative amount of transformed monoclinic zirconia (FM), transformed zone depth (TZD) and surface roughness were measured. Particle type (p=0.2746), pressure (p=0.5084) and cyclic loading (p=0.1610) did not influence the flexural strength. Except for the air-abraded group with 110 μm Al2O3 at 3.5 bar, all air-abrasion protocols increased the biaxial flexural strength (MPa) (Controlnon-aged: 1030±153, Controlaged: 1138±138; Experimentalnon-aged: 1307±184-1554±124; Experimentalaged: 1308±118-1451±135) in both non-aged and aged conditions, respectively. Surface roughness (Ra) was the highest with 110 μm Al2O3(0.84 μm. FM values ranged from 0% to 27.21%, higher value for the Rocatec Plus (110 μm SiO2) and 110 μm Al2O3 groups at 3.5 bar pressure. TZD ranged between 0 and 1.43 μm, with the highest values for Rocatec Plus and 110 μm Al2O3 groups at 3.5 bar pressure. © 2013 Elsevier Ltd.

Alteration in cellular viability, pro-inflammatory cytokines and nitric oxide production in nephrotoxicity generation by Amphotericin B: Involvement of PKA pathway signaling

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Effects of different intensities of physical exercise on insulin sensitivity and protein kinase B/Akt activity in skeletal muscle of obese mice

Objetivo: Investigar os efeitos do exercício físico agudo com diferentes intensidades sobre a sensibilidade à insulina e a atividade da proteína quinase B/Akt no músculo esquelético de camundongos obesos. Método: Foram utilizados camundongos Swiss, divididos aleatoriamente em quatro grupos, que receberam dieta padrão (grupo controle) ou dieta hiperlipídica (grupos obeso sedentário e grupos obesos exercitados 1 e 2), por período de 12 semanas. Dois diferentes protocolos de exercício foram utilizados: natação durante 1 hora com ou sem sobrecarga de 5% da massa corporal. O teste de tolerância à insulina foi realizado para estimar a sensibilidade à insulina. E os níveis protéicos da proteína quinase B/Akt e de sua fosforilação foram determinados no músculo esquelético dos camundongos, através da técnica de Western blot. Resultado: Uma sessão de exercício físico foi capaz de inibir a resistência à insulina em decorrência de uma dieta hiperlipídica. Foi possível demonstrar um aumento na fosforilação da proteína quinase B/Akt, melhora da sinalização da insulina e redução da glicemia de jejum nos camundongos que realizaram 1 hora de natação sem sobrecarga adicional e nos camundongos que realizaram 1 hora de natação com sobrecarga adicional de 5% de sua massa corporal. Entretanto, não houve diferença significativa entre os grupos que realizaram o exercício em diferentes intensidades. Conclusão: Independente da intensidade, o exercício físico aeróbio conseguiu aumentar a sensibilidade à insulina e a fosforilação da proteína quinase B/Akt, revelando ser uma boa forma de tratamento e prevenção do diabetes tipo 2.

Nanometer Scale Titanium Surface Texturing Are Detected by Signaling Pathways Involving Transient FAK and Src Activations

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Application of two segmentation protocols during the processing of virtual images in rapid prototyping: ex vivo study with human dry mandibles

The aim of this study was to evaluate the accuracy of virtual three-dimensional (3D) reconstructions of human dry mandibles, produced from two segmentation protocols (outline only and all-boundary lines).Twenty virtual three-dimensional (3D) images were built from computed tomography exam (CT) of 10 dry mandibles, in which linear measurements between anatomical landmarks were obtained and compared to an error probability of 5 %.The results showed no statistically significant difference among the dry mandibles and the virtual 3D reconstructions produced from segmentation protocols tested (p = 0,24).During the designing of a virtual 3D reconstruction, both outline only and all-boundary lines segmentation protocols can be used.Virtual processing of CT images is the most complex stage during the manufacture of the biomodel. Establishing a better protocol during this phase allows the construction of a biomodel with characteristics that are closer to the original anatomical structures. This is essential to ensure a correct preoperative planning and a suitable treatment.

Reliability of peak running speeds obtained from different incremental treadmill protocols

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Modulation of cell proliferation, survival and gene expression by RAGE and TLR signaling in cells of the innate and adaptive immune response: role of p38 MAPK and NF-KB

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Concentrations of and application protocols for hydrogen peroxide bleaching gels: Effects on pulp cell viability and whitening efficacy

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)