993 resultados para concrete buildings
Resumo:
A voluminous literature exists on the analysis of water-soluble ions extracted from gypsum crusts and patinas formed on building surfaces. However, less data is available on the intermediate dust layer and the important role its complex matrix and constituents play in crust/patina formation. To address this issue, surface dust samples were collected from two buildings in the city of Budapest. Substrate properties, different pollution levels and environmental variations were considered by collecting samples from a city centre granite building exposed to intense traffic conditions and from an oolitic limestone church situated in a pedestrian area outside and high above the main pollution zone. Selective extraction examines both water-soluble ions (Ca2+, Mg2+, Na+, K+, Cl-, NO3- SO42-) and selected elements (Fe, Mn, Zn, Cu, Cr, Pb, Ni) from the water-soluble, exchangeable/carbonate, amorphous Mn, amorphous Fe/Mn, crystalline Fe/Mn, organic and residual phases, their mobility and potential to catalyse heterogeneous surface reactions. Salt weathering processes are highlighted by high concentrations of water-soluble Ca2+, Na+, Cl- and SO42-- at both sites. Manganese, Zn and Cu and to a lesser extent Pb and Ni, are very mobile in the city centre dust, where 30%, 54%, 38%, 11% and 11% of their totals are bound by the water-soluble phase, respectively. Church dust shows a sharp contrast for Mn, Zn, Cu and Pb with only 3%, 1%, 12% and 3% of their totals being bound by the water-soluble phase respectively. This may be due to (a) different environmental conditions at the church e.g. lower humidity (b) continuous replenishment of salts under intensive city centre traffic conditions (c) enrichment in oxidisable organic carbon by a factor of 4.5 and a tenfold increase in acidity in the city centre dust.
Strength and drying shrinkage properties of concrete containing furnace bottom ash as fine aggregate
Resumo:
This paper reviews statistical models obtained from a composite factorial design study, which was carried out to determine the influence of three key parameters of mixture composition on filling ability and passing ability of self-consolidating concrete (SCC). This study was a part of the European project “Testing SCC”- GRD2-2000-30024. The parameters considered in this study were the dosages of water and high-range water-reducing admixture (HRWRA), and the volume of coarse aggregates. The responses of the derived statistical models were slump flow, T50 , T60, V-funnel flow time, Orimet flow time, and blocking ratio (L-box). The retention of these tests was also measured at 30 and 60 minutes after adding the first water. The models are valid for mixtures made with 188 to 208 L/m3 (317 to 350 lb/yd3) of water, 3.8 to 5.8 kg/m3 (570 to 970 mL/100 kg of binder) of HRWRA, and 220 to 360 L/m3 (5.97 to 9.76 ft3/yd3) of coarse aggregates. The utility of such models to optimize concrete mixtures and to achieve a good balance between filling ability and passing ability is discussed. Examples highlighting the usefulness of the models are presented using isoresponse surfaces to demonstrate single and coupled effects of mixture parameters on slump flow, T50 , T60 , V-funnel flow time, Orimet flow time, and blocking ratio. The paper also illustrates the various trade-offs between the mixture parameters on the derived responses that affected the filling and the passing ability.
Resumo:
Slurries with high penetrability for production of Self-consolidating Slurry Infiltrated Fiber Concrete (SIFCON) were investigated in this study. Factorial experimental design was adopted in this investigation to assess the combined effects of five independent variables on mini-slump test, plate cohesion meter, induced bleeding test, J-fiber penetration test and compressive strength at 7 and 28 days. The independent variables investigated were the proportions of limestone powder (LSP) and sand, the dosages of superplasticiser (SP) and viscosity agent (VA), and water-to-binder ratio (w/b). A two-level fractional factorial statistical method was used to model the influence of key parameters on properties affecting the behaviour of fresh cement slurry and compressive strength. The models are valid for mixes with 10 to 50% LSP as replacement of cement, 0.02 to 0.06% VA by mass of cement, 0.6 to 1.2% SP and 50 to 150% sand (% mass of binder) and 0.42 to 0.48 w/b. The influences of LSP, SP, VA, sand and W/B were characterised and analysed using polynomial regression which identifies the primary factors and their interactions on the measured properties. Mathematical polynomials were developed for mini-slump, plate cohesion meter, J-fiber penetration test, induced bleeding and compressive strength as functions of LSP, SP, VA, sand and w/b. The estimated results of mini-slump, induced bleeding test and compressive strength from the derived models are compared with results obtained from previously proposed models that were developed for cement paste. The proposed response models of the self-consolidating SIFCON offer useful information regarding the mix optimization to secure a highly penetration of slurry with low compressive strength