Comparação de compósitos obtidos via RTM de resina epóxi e fibra de carbono com e sem descontinuidade nos tecidos

Technology is growing interest in the use of composites, due to the requirement of lighter materials and more resistant, factors essential to meet the project specifications and reduce the operational cost. In the production of high performance structural composites, considering the aerospace criteria, the domestic industry has shown interest in the process of resin transfer molding (RTM) for reproducibility and low cost. This process is suitable for producing components of polymeric composites with relatively simple geometries, consistent thicknesses, high quality finish with no size limitations. The objective of this work was machined carbon steel to make a matched-die tooling for RTM and produce two composite plates of epoxy resin and carbon fiber fabric with and without induced discontinuities, which were compared towards their impregnation with ultrasound, their properties via tensile tests and thermal analysis. In ultrasonic inspection, it was found good impregnation of the preform of both composites. In the thermal analysis it was possible to check the degradation temperature of the composites, the glass transition temperature and it was found that the composites showed no effective cure cycles, but presented good performance in the tensile test when compared with aluminum alloy 7050 T7451 . The results showed that the injection strategy was appropriate since the laminate exhibited a good quality for the proposed application

Síntese e caracterização dielétrica de filmes finos de Bi3NbO7 obtidos pelo método dos precursores poliméricos

Bi3NbO7 thin films were prepared by the polymeric precursor method. The precursor solutions were prepared with excess of bismuth ranging from 0% to 10% and the pH was controlled to be maintained between 8 and 9. This control was done by adding to the solution niobium and ethylene glycol. The final solution was clear and free of precipitation. After obtaining the precursor solution, has begun the process of characterization of powders with thermogravimetry (TG), differential thermal analysis and X-ray analysis (XRD). The films were obtained by the polymeric precursors, the method is advantageous because it is simple, and low cost involves steps and controlled stoichiometry. The films were annealed and characterized by XRD and SEM and also characterized according to their dialectics properties. We observed that the best results were obtained when the film is thermally at 800 ° C for two hours and 860 ° C for two hour. Under these conditions we obtain Bi3NbO7 thin films with good homogeneity, uniform distribution of the grains, but with the formation of secondary phase, which does not occur in treatments with lower temperature. The dielectric characterization showed that the produced film showed good characteristics with high dielectric constant and low loss

Síntese por reação em estado sólido de pós cerâmicos multifuncionais à base de CaCu3Ti4O12 modificados com estrôncio

The study of ceramic materials is constantly evolving, especially in research related to advanced ceramics. Once these have many applications, this paper relates to synthesis by solid state reaction of calcium copper titanate (CCTO) ceramic material means doping with strontium. The powders were characterized using thermal analysis techniques such as TG (thermogravimetry), DTA (differencial thermal analysis), dilatometry, X-ray diffraction (XRD) and scanning electron microscopy (SEM). The compositions have submitted weight loss at around 6% with respect to carbonates used, and was attributed a temperature of 950° C to perform the calcination according to thermogravimetric analysis. After the process of calcination and milling, the particles presented approximately spherical shapes and high percentages of substitution Ca2+ with Sr2+ was evident by the presence of necks between to particles due to the milling calcination. Analyses with Energy Dispersive Spectroscopy (EDS) showed stoichiometries in different samples very similar to the theoretical stoichiometry

Influência do condicionamento ambiental sobre as propriedades viscoelásticas de compósitos aramida/epóxi

The increasing application of structural composites in the aerospace industry is mainly due to its low specific weight coupled with its excellent mechanical properties when in service. As a result of climatic variations that pass the aircraft is of paramount importance to study the influence of weathering on this type of material when subjected to such changes. The purpose of this work is to evaluate the mechanical behavior of specimens of kevlar fiber /epoxy matrix composites, by dynamic mechanical thermal analysis (DMA) and interlaminar shear strength tests (ILSS), after passing through three environmental conditioning: saline fog, hygrothermal and ultraviolet radiation. From the results, we concluded that the laminate was molded supplied homogeneously, not presenting problems such as porosity, delaminations or cracks inside. After a period of 625 hours of exposure to hygrothermal conditioning, we observed a 1,2% maximum of absorption of moisture. Samples subjected to the conditioning by UV irradiation (600 hours) and salt spray showed a reduction of about 24,30% and 32,30%, respectively, on the shear strength (ILSS). In DMA analysis is not observed significant changes on the glass transition temperature. However, when considering the storage modulus of the samples conditioned by UV radiation (1200 hours), salt spray and hygrothermal conditioning there is an increase of 5,34% , 7,19% and 5,57% respectively

Síntese e caracterização estrutural de pigmentos cerâmicos a base de cromita por método químico

The ceramic pigments are colored inorganic substances that during the process of dispersion in the ceramic glazes and subsequent calcination, are stable against physical and chemical attack. Therefore, they are crystalline compounds applied in the ceramic industry for coloring vitreous base. In this study, the Pechini method was used for obtaining the pigment CuCr2O4 with heat treatment at the temperatures of 800, 900 and 1000 ° C. The powder pigments were characterized on their structural, morphological and colorimetric aspects. The thermal analysis conducted on an amorphous precursor in a TG / DTA indicates the weight loss in the entire temperature range investigated, with characteristic exothermic peak of the elimination of the organic composition of the precursor around 300°C. The development of the crystalline phases were investigated by XRD, using a diffractometer with Cu Ka radiation and graphite monochromator, where it was observed the presence of crystalline phases corresponding to Cr2O3 and CuCr2O4.The measurements of the specific surface area of the powders pigments were carried out in an equipment Micromeritcs, model ASAP 2000, using N2 as gas of adsorption/desorption. The colorimetric measurements of the pigments were made in a colorimeter Gretac Macbeth Color-eye spectrophotometer 2180 / 2180UV in CIELAB standards. Based on the obtained results, it can be verified the thermal stability of the powder pigments of green coloration, which enables it as an alternative to the materials currently used in the manufacture of ceramic tiles.

Laser irradiation and thermal treatment inducing selective crystallization in Sb2O3-Sb2S3 glassy films

The influence of both thermal treatment and laser irradiation on the structural and optical properties of films in the Sb 2 O 3 –Sb 2 S 3 system was investigated. The films were prepared by RF-sputtering using glass compositions as raw materials. Irreversible photodarkening effect was observed after exposure the films to a 458nm solid state laser. It is shown, for the first time, the use of holographic technique to measure “in situ”, simultaneously and independently, the phase and amplitude modulations in glassy films. The films were also photo-crystallized and analysed “in situ” using a laser coupled to a micro-Raman equipment. Results showed that Sb 2 S 3 crystalline phase was obtained after irradiation. The effect of thermal annealing on the structure of the films was carried out. Different from the result obtained by irradiation, thermal annealing induces the crystallization of the Sb 2 O 3 phase. Photo and thermal induced effects on films were studied using UV–Vis and Raman spectroscopy, atomic force microscopy (AFM), thermal analysis (DSC), X-ray diffraction, scanning electron microscopy (MEV) and energy-dispersive X-ray spectroscopy (EDX).

EStudo fundamental da interação de nanopartículas metálicas com íons terras raras em vidros e vitrocerâmicas para aplicações na região do infravermelho

Pós-graduação em Química - IQ

Liberação controlada de nutrientes e novos sistemas para avaliação de espécies químicas empregadas na fertilização

Pós-graduação em Química - IQ

Adsorção-fotodegradação do herbicida paraquate em água pela argila Na-Bentonita e por novos materiais TiO2-Bentonita, TiO2/ZnOBentonita, Al/Fe-Bentonita e Al/Fe.Cu-Bentonita

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

The effects of heat-moisture treatment on avocado starch granules: thermoanalytical and structural analysis

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Effect of cryoprotectants on the reconstitution of silica nanoparticles produced by sol-gel technology

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Thermal stability and thermal decomposition of the antihypertensive drug amlodipine besylate

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Preparation and thermal decomposition of solid state cobalt, nickel, copper and zinc chelates of ethylenediaminetetraacetic acid

Solid state chelates of general formula H-2[M(EDTA)] . nH2O, where M is Co, Ni, Cu or Zn, and EDTA is ethylenediaminetetraacetate, were prepared. Thermogravimetry-derivative thermogravimetry (TG-DTG), differential thermal analysis (DTA) and complexometry were used to characterize and to study the thermal stability and thermal decomposition of these compounds.

Mechanochemical synthesis of CaTiO3 from CaCO3 - TiO2 mixture

The synthesis of calcium titanate, CaTiO3, was performed by mechanical activation and thermal treatment. Milling for up to 360 minutes in a planetary ball mill mechanically activated an equimolar mixture of CaCO 3 and TiO2 powders. A small amount of mechanically activated mixtures was pressed into briquettes and calcined at 850°C for two hours. The effect of mechanical activation on the solid-state reaction was studied using X-ray powder diffraction and differential thermal analysis. The change of morphology and size of powder particles due to milling, were determined by SEM, while BET analysis was used to determine the specific surface area of the powder. The sintering process was followed by a dilatometer during thermal treatment up to 1300°C. The main conclusion of the analysis of conducted investigations is that CaTiO3 ceramics can be obtained from an activated mixture at a much lower temperature than reported in the literature owing to acceleration of the chemical reaction and sintering.

Thermal behaviour of the basic carbonates of lanthanum-europium

The basic carbonates of lanthanum with 10%, 20%, 50% and 80% of europium were prepared by precipitation from homogeneous solutions via the hydrolysis of urea, without the addition of an auxiliary anion, at two different temperatures. Elemental analysis, complexometric methods, X-ray diffraction patterns, solid state IR absorption, thermogravimetry/derivative thermogravimetry (TG/DTG) and differential thermal analysis (DTA) were used to characterise the compounds and study their thermal behaviour.