Anodic oxidation of formaldehyde on Pt-modified SnO2 thin film electrodes prepared by a sol-gel method

Pt-modified SnO2 electrodes were prepared onto titanium substrates in the form of thin films of similar to2 mum at different temperatures in the range from 200 to 400degreesC. Surface morphology was examined by scanning electron microscopy (SEM). It was found that Pt-SnO2 sol-gel layers are significantly rough and have a low porosity. X-ray diffraction (XRD) studies showed that the films consist of Pt nanoparticles with average size varying from about 5 to 10 nm, depending on the preparation temperature, and amorphous tin oxide. X-ray photoelectron spectroscopy (XPS) was employed to determine the superficial composition of the electrodes and demonstrated the presence of Sn4+ in all the samples. XPS spectra of the Pt 4f electrons showed the presence of Pt in the zero-valence state as well as in ionic forms. The general electrochemical behavior was characterized by cyclic voltammetry in 1 mol l(-1) HClO4 and the electrocatalytic activity towards the oxidation of formaldehyde was investigated by potential sweeps and chronoamperometry. The results obtained show that the Pt-SnO2/Ti system exhibits a significant catalytic activity for the oxidation of formaldehyde, with an onset potential below 0.1 V. (C) 2004 Elsevier Ltd. All rights reserved.

Characterization of an all sol-gel electrochromic device WO3/Ormolyte/CeO2-TiO2

Electrochemical lithium intercalation in thin films of CeO2-TiO2 and WO3, prepared by the sol-gel technique was investigated with cyclic voltammetry and spectroelectrochemical techniques in propylene carbonate solutions. A solid state system having the configuration WO3/Ormolyte/CeO2-TiO2 has been assembled. The solid electrolyte, an organically modified electrolyte (ormolyte), was prepared with different [O]/[Li] ratios. The transmittance variation of this system during a potentiostatic step from -0.7 V to 0.8 V was about 35% at 550 nm.

Structural properties of silica gels prepared from oxalic-acid-catalyzed tetraethoxysilane sonohydrolysis

About similar to 2.1 x 10(-3) Mol SiO2 cm(-3) and similar to 88%-volume liquid-phase silica wet gels were prepared from oxalic-acid-catalyzed tetraethoxysilane (TEOS) sonohydrolysis. Aerogels were obtained by supercritical CO2 extraction. The samples were analyzed by thermogravimetry, small-angle X-ray scattering and nitrogen adsorption. Wet gels can be described as mass fractal structures with fractal dimension D similar to 1.94 and structural characteristic length zeta changing between similar to 3.3 to similar to 3.0 nm in the studied range of the catalyst concentration. A fraction of the porosity is apparently eliminated in the supercritical process. The values of the BET specific surface S-BET, the total pore volume V-p and the mean pore size l(p) of the aerogels were found to change almost randomly around the mean values S-BET = 874 m(2) g(-1), V-p = 0.961 cm(3) g(-1) and l(p) = 4.4 nm with catalyst concentration variation. These values were not substantially different from those from an equivalent HCl-catalyzed aerogel. (c) 2007 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Preparation and characterization of erbium and ytterbium co-doped sol-gel SiO2 : HfO2 films for planar waveguides

This work reports on the preparation of erbium and ytterbium co-doped SiO2:HfO2 single mode planar waveguides using the sol-gel method. Silica nanoparticles were prepared from tetraethylorthosilicate in basic media and the films were characterized by transmission electron microscopy, scanning electron microscopy, mechanical profilometry, M-lines spectroscopy based on prism coupling technique, X-ray diffractometry, infrared spectroscopy and photoluminescence spectroscopy. The film thicknesses and the refractive indexes were adjusted in order to satisfy a future efficient coupling to single mode optical fiber. Films suitable for both weak and strong light confinement were prepared varying hafnia concentration into the silica matrix. The lifetime values of erbium I-4(13/2) state were measured in order to investigate the influence of clustering and hydroxyl groups on the fluorescence quantum efficiency of the I-4(13/2) level, responsible for the emission at 1.55 mu m attributed to the I-4(13/2) -> I-4(15/2) transition. The high lifetime values suggest the absence of erbium clusters and the elimination of hydroxyl groups by rapid thermal process. (c) 2007 Elsevier B.V. All rights reserved.

Eu3+ doped polyphosphate-aminosilane organic-inorganic hybrids

The preparation and characterization of new Eu3+ doped polyphosphate-aminosilane hybrids xerogels is reported. Eu3+ D-5(0) emission quantum efficiency ranges from 0.41 to 0.54 depending on the SUP ratio. These rather high values are due to the substitution of phosphate and amino groups for water in the Eu3+ coordination shell. Raman and Si-29 and C-13 CP-MAS NMR results suggest that no strong interaction exists between the polyphosphate and the siloxane parts. Not fully condensed siloxane colloidal domains seem to be homogeneously distributed in the polyphosphate network. Good optical quality and favorable Eu3+ spectroscopic characteristics suggest these new hybrids as good hosts for lanthanide ions in optical devices. (C) 2003 Published by Elsevier B.V.

Sol-gel Eu3+/Tm3+ doped transparent glass-ceramic waveguides

Eu3+ and Tm3+ doped lanthanum fluoride and lanthanum oxyfluoride are obtained from Eu3+, Tm3+ containing lanthanum fluoracetate solutions. The nature of the crystal phase obtained could be controlled by the temperature of heat treatment. Spectral characteristics of Eu3+ doped crystal phases were sufficiently different to allow utilization of Eu3+ as structural probes. Tm3+ emission at the technologically important spectral region of 1450nm could be observed for the fluoride and oxyfluoride crystal phases. The large bandwidth obtained (around 120nm) suggests potential applications in optical amplification. SiO2-LaF3-LaOF composite materials were also prepared. It is observed that for heat treatments above 800degreesC, fluorine loss, probably in the form of SiF4 hinder the observation of Tm3+ emission. Eu3+ spectroscopic characteristics clearly show the evolution of a fluoride like environment to an amorphous oxide one as the temperature of heat treatment increased. Thin films obtained by dip-coating on V-SiO2 substrates and treated at 300degreesC, 500degreesC and 800degreesC display guided modes in the visible and infrared regions. Optical characteristics (refractive index and films thickness) were obtained at 543.5, 632.8 and 1550nm. Attenuation as low as 1.8dB/cm was measured at 632.8nm. (C) 2004 Published by Elsevier B.V.

Effect of presence of an acid catalyst on structure and properties of iron-doped siloxane-polyoxyethylene nanocomposites prepared by sol-gel

In this work we investigate the effect of hydrochloric acid (HC) addition on the structure and thermal and magnetic properties of iron-doped siloxane-polyoxyethylene (POE) hybrids prepared by the sol-gel route. X-ray powder diffraction (XRD) and X-ray absorption near edge structure (XANES) results reveal the dominance of ferrihydrite nanoparticles and a mixture of this phase with FeCl4- species in the hybrid prepared without and with HCl, respectively. Thermal analysis reveals the existence of two crystalline polymeric phases in the hybrid prepared with HCl whereas hybrids prepared without HCl are amorphous. The 105 and 60 Angstrom sized ferrihydrite nanoparticles were detected by SAXS analysis of the composite prepared without and with HCl, respectively. The magnetic results suggest that in both samples antiferromagnetic nanoparticles coexist with small clusters/isolated ions. In the sample without HCl addition, larger particles dominate the magnetic behavior, while the opposite occurs for the sample prepared using HCl catalyst. (C) 2004 Elsevier B.V. All rights reserved.

Characterization of tin oxide based sol-gel coatings on borosilicate glasses by X-ray reflectivity

The X-ray reflectivity technique was applied in the study of tin oxide films deposited by sol-gel dip-coating on borosilicate glasses. The influence of the withdrawal speed and temperature of thermal treatment on the film structure was analyzed. We have compared the thermal evolution of the density and the shrinkage of the films with these properties measured for the monolithic xerogel by helium picnometry and thermomechanical analysis. In agreement with the Landau-Levich model, the layer thickness increases by increasing the withdrawal speed. Nevertheless, it decreases with the increase of the thermal treatment temperature, due to the densification process. The values of apparent density are smaller than the skeletal density, which shows that the films are porous. The comparison between the film and the monolith indicates that shrinkage during firing is anisotropic, occurring essentially perpendicular to the coating surface.

Density improvement of the sol-gel dip-coated SnO2 films by chemical surface modification

We compare the effect of organic (Tiron (R)) and inorganic (Mn(11)) additives on the low temperature (< 600 degrees C) densification of the sol-gel dip-coated SnO2 films. The structural and compositional properties of the samples were investigated by X-ray reflectometry (XRR), X-ray absorption spectroscopy (XAS) and X-ray photoelectron spectroscopy (XPS). The results suggest that the replacement of hydroxyl groups at the particle surface by Tiron (R) reduces the level of agglomeration of the sol, increasing the particles packing and the apparent density of the coatings. Undoped and Mn-doped films drawn from a Tiron (R) containing suspension show after firing at 500 degrees C a porosity reduction of 12 and 8.6%, respectively. The porosity decrease is less pronounced (4.3%) for the film without additives. Both XAS and XPS data show the presence of trivalent manganese. The formation of a non-homogeneous solid solution characterised by the presence of Mn(111) replacing tin atom near to the crystallite surface was evidenced by XAS. Additionally, XPS results reveal the presence of metallic Sn at the surface of films containing Tirono. (c) 2005 Elsevier Ltd. All rights reserved.

Effect of reaction time on the particle size of ZnO and ZnO : Ce obtained by a sol-gel method

In this work particles of ZnO of size range 33-56 Angstrom were prepared by a sol-gel method. The effect of reaction time on the particle size of ZnO or ZnO:Ce was investigated by transmission electron microscopy measurements, UV-vis absorption and luminescence spectroscopy. A linear increase of the mean particle size is observed as a function of reaction time. The cerium-doped particles are bigger than the pure ZnO ones obtained at the same reaction time. A shift to lower energy at the maximum of the bands is observed in all absorption, emission and excitation spectra as a function of particle growth. From the absorption spectra the optical energy gap values (Eg) for these particles were determined. In the quantum size regime, Eg was found to decrease with particle growth.

Study of the selectivity of SnO2 supported membranes prepared by a sol-gel route

In this work the sol-gel process was used to prepare SnO2 supported membranes with an average pore size of 2.5 nm. The effects of salt concentration (NaCl or CaCl2) and of the pH of the aqueous solutions used on the flux and selectivity through the SnO2 membrane were analyzed by permeation experiments and the results interpreted taking account of the zeta potential values determined from the electrophoretic mobility of the SnO2 powder aqueous dispersion. The results show that the ion flux (Na+, Ca2+ and Cl-) throughout the membrane is determined by the electrostatic repulsion among these species and the surface charge at the tin oxide-solution interface.

Nanostructure and luminescent properties of sol-gel derived europium-doped amine functionalised hybrids

The effect of doping by europium triflate on the nanoscopic structure of organic-inorganic hybrid formed by a siliceous network containing pendant amine-terminated propyl chains, called aminosils, was investigated by Small-Angle X-ray Scattering (SAXS). It appears that the composites exhibit a two-level structure. The first level consists of well-condensed cubic-like siloxane octamers, with a radius of gyration around 2 angstrom. The second level is formed by the aggregation of these siloxane nanodomains to form larger structures, in which the nanodomains are spatially correlated and separated by the organic pendant chains. Europium doping inhibits the aggregation between siloxane octamers, leading to a less compact second-level structure. This can be explained by the Eu3+ stop coordination close to the external surface of the siloxane nanodomains, as detected by luminescence spectroscopy.

Wettability and photodegradation activity of sol-gel dip-coated zinc oxide films

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Rheological Characterization of Hydrophylic Gels

Rheological characteristics of gels were studied, with the focus on their use as a cosmetic base. Some ideal characteristics can be predicted by the rheological characterization, such as the performance, with easy application and without dripping or forming lumps and bubbles. Moreover, it is possible to detect signs of physical instability. The gels were prepared with sodium carboxymethyl cellulose 3% and 5%, with Carbopol 940 (INCI: Carbomer) and with Carbopol Ultrez (INCI: Acrylates/C10-30 alkyl acrylate crosspolymer). The tests performed were yield stress, stress sweep and creep and recovery. The gel with 3% of sodium carboxymethyl cellulose presented the most appropriated behavior and can be indicated as the most suitable cosmetic base.