A HIGH-RESOLUTION SOLID-STATE NMR AND DSC STUDY OF MISCIBILITY AND CRYSTALLIZATION BEHAVIOR OF POLY(VINYL ALCOHOL)/POLY(N-VINYL-2-PYRROLIDONE) BLENDS

Blends of crystallizable poly(vinyl alcohol) (PVA) with poly(N-vinyl-2-pyrrolidone) (PVPy) were studied by C-13 cross-polarization/magic angle spinning (CP/MAS) n.m.r. and d.s.c. The C-13 CP/MAS spectra show that the blends were miscible on a molecular level over the whole composition range studied, and that the intramolecular hydrogen bonds of PVA were broken and intermolecular hydrogen bonds between PVA and PVPy formed when the two polymers were mixed. The results of a spin-lattice relaxation study indicate that blending of the two polymers reduced the average intermolecular distance and molecular motion of each component, even in the miscible amorphous phase, and that addition of PVPy into PVA has a definite effect on the crystallinity of PVA in the blends over the whole composition range, yet there is still detectable crystallinity even when the PVPy content is as high as 80 wt%. These results are consistent with those obtained from d.s.c. studies.

IONIC-CONDUCTIVITY AND DYNAMIC MECHANICAL RELAXATION OF A 2-COMPONENT EPOXY NETWORK-LICLO4 ELECTROLYTE SYSTEM

The correlation between mechanical relaxation and ionic conductivity was investigated in a two-component epoxy network-LiClO4 electrolyte system. The network was composed of diglycidyl ether of polyethylene glycol (DGEPEG) and triglycidyl ether of glycerol (TGEG). The effects of salt concentration, molecular weight of PEG in DGEPEG and the proportion of DGEPEG (1000) in DGEPEG/TGEG ratio on the ionic conductivity and the mechanical relaxation of the system were studied. It was found that, among the three influential factors, the former reinforces the network chains, reduces the free volume fraction and thus increases the relaxation time of the segmental motion, which in turn lowers the ionic conductivity of the specimen. Conversely, the latter two increase the free volume and thus the chain flexibility, showing an opposite effect. From the iso-free-volume plot of the shift factor log at and reduced ionic conductivity, it is noted that the plot can be used to examine the temperature dependence of segmental mobility and seems to be useful to judge whether the incorporated salt has been dissociated completely. Besides, the ionic conductivity and relaxation time at constant reference temperature are linearly correlated with each other in all the three cases. This result gives an additional experimental confirmation of the coordinated motion model of the ionic hopping with the moving polymer chain segment, which is generally used to explain the ionic conduction in non-glassy amorphous polymer electrolytes.

STATISTICAL THERMODYNAMICS OF POLYDISPERSE POLYMERS

A statistical thermodynamics theory of polydisperse polymers based on a lattice model of fluids is formulated. Pure polydisperse polymer can be completely characterized by three scale factors and the molecular weight distribution of the system. The equation of state does not satisfy a simple corresponding-states principle, except for a polymer fluid of sufficiently high molecular weight. The relationships between thermal expansion coefficient alpha and isothermal compressibility beta with reduced variables are also predicted.

RADIATION-INDUCED CRYSTAL DEFECTS IN PTFE

Changes induced in the crystal structure of PTFE by irradiation at different temperatures have been investigated. In the dose and temperature range examined, the density of PTFE was observed to increase continuously with increasing dose due to the radiation-induced increase in crystallinity, while after post-irradiation annealing at 380-degrees-C, the density was observed to increase for samples irradiated at 20-degrees-C, and to begin to decrease after a certain dose for samples irradiated at 150 and 200-degrees-C. On the basis of the observation of radiation-induced separation of the melting peak of PTFE and its stability relative to the change in the rate of heating, the observed decrease in density was explained as being due to the radiation-induced crosslinking and/or branching inhibiting the process of crystallization and existing in the crystalline region as defects.

STRUCTURE OF MESOMORPHIC FORM OF ISOTACTIC POLYPROPYLENE

The structure of quenched isotactic polypropylene (iPP) films, including samples etched with fuming nitric acid (FNA), has been studied by infrared (IR) spectra, wide-angle x-ray diffraction (WAXD), small-angle x-ray scattering (SAXS), and differential scanning calorimetry (DSC) measurements. The changes of IR, SAXS, DSC, and WAXD results induced by annealing for etched samples have been compared with those for unetched ones. The IR absorbance spectrum of the quenched iPP etched by FNA did not change. In addition, the SAXS intensity did not increase when these samples were annealed, indicating that the total (IR) crystallinity (i.e., the content of chain segments in the helical conformations) of the etched samples does not increase. However, WAXD patterns of the samples changed in a manner similar to those of the unetched one, from the original two blurred diffraction peaks to the sharp crystal patterns of alpha-form iPP, suggesting that the mesomorphic (or liquid crystal-like) phase has reorganized to alpha-form crystals. It is concluded that the change of WAXD of quenched iPP films during annealing results mainly from transformation of order in the mesomorphic phase, rather than only from an increase of crystal size. In other words, mesomorphic-form iPP is not constituted by any known crystals (such as alpha or beta crystals) in small sizes; its WAXD pattern reflects truly the degree of order in the mesomorphic phase.

FACTORS AFFECTING THE ROLE OF SIO2 IN MGCL2-SUPPORTED ZIEGLER-NATTA COPOLYMERIZATION CATALYSTS

This paper describes the roles of silica (SiO2), the butoxy ligand (-OBu) and ethyl benzoate (EB) on ethylene/1-butene copolymerization with MgCl2/SiO2-supported titanium catalysts. The distribution of SiO2 and of the elements Mg and Ti was observed by means of an energy-dispersed X-ray microanalyzer on a scanning electron microscope (SEM). An inversed Si/Mg ratio results, at invariant Ti/Mg ratio and -OBu content, in higher catalyst efficiency and higher comonomer incorporation, with a correspondingly decreased crystallinity of the copolymers. Thus, the inert carrier SiO2 favors copolymerizability, as seen from the values of the reactivity ratios. The copolymer compositional distribution is also affected by the SiO2 content, as seen from the DSC curves of the copolymers. As to the copolymer morphology, addition of SiO2 makes the copolymer particles larger and more uniform.

THE EFFECT OF RADIATION-INDUCED CROSS-LINKING ON THE RELAXATION OF TAUT TIE MOLECULES DURING ANNEALING OF DRAWN LDPE

Shrinkage, retractive stress, and infrared dichroism of the drawn low-density polyethylene (LDPE) as-drawn and irradiated by Co-60-ray have been measured under different annealing conditions. The shrinkage and the disorientation of the irradiated sample was undergone more rapidly than that of unirradiated one as the temperature was continuously increased, surpassing a certain value, and a higher degree of shrinkage and disorientation was achieved finally for the irradiated sample when the samples were annealed with free ends. For the samples heated isothermally with fixed ends, the retractive stress went through a maximum and then attenuated to a limited value, and the degree of such a stress attenuation for the unirradiated sample was much more than that for the irradiated sample. These results show that the taut tie molecules (TTMs) in drawn PE can relax by the pulling of chain segments out of crystal blocks that they anchored in at elevated temperatures higher than the a transition and also by the displacing of microfibrils if the samples were annealed with free ends. The cross-links produced by irradiation prohibit the former process. It was further observed that the dependence of the average extinction coefficient of the band at 2016 cm-1 on that of the band at 1894 cm-1 is related to irradiation and annealing conditions, which has also been explained by the relaxation of TTMs and the function of irradiation-induced cross-linking on the relaxation.

SEQUENCE STRUCTURE OF ETHYLENE-VINYL SUBSTITUTED COPOLYMER WITH C-13 NMR .4.

The substituent chemical shift (SCS) has been applied to the assignment of the C-13 NMR spectrum of chlorinated polyethylene (CPE). CPE of different chlorine contents has been employed and their sequence structure discussed. The results show that characteristic of CPE with medium chlorine content is the dichloroethane structure in molecular chain. SCS parameters have been obtained from the C-13 NMR spectra. It was found that the effects of chlorine content and temperature on SCS are negligible, but the substituent parameter S1 reduced by 0.39 ppm when C2Cl4 was added to solvent ODCB.

A HIGH-RESOLUTION SOLID-STATE NMR-STUDY OF THE MISCIBILITY, MORPHOLOGY, AND TOUGHENING MECHANISM OF POLYSTYRENE WITH POLY(2,6-DIMETHYL-1,4-PHENYLENE OXIDE) BLENDS

An extended Goldman-Shen pulse sequence was used to observe indirectly the proton spin diffusion in the blends of polystyrene (PS) with poly(2,6-dimethyl-1,4-phenylene oxides) (PPO). The results indicate that the average distance between PS and PPO is less than 5 angstrom in the intimately mixed phase, but there are heterogeneous domains on a 100-angstrom scale. The data of spin relaxation of carbons, T1(C), for homopolymers and their blends suggest that there is a strong pi-pi electron conjugation interaction between the aromatic rings of PS and those of PPO, while the aromatic rings of PPO drive the aromatic rings of PS to move cooperatively. It is the cooperative motion that markedly improves the impact strength of PS.

AN ALL-SOLID-STATE LITHIUM POLYANILINE RECHARGEABLE CELL

The performance of an all-solid-state cell having a lithium negative electrode, a modified polyethylene oxide (PEO)-epoxy resin (ER) electrolyte, and a polyaniline (PAn) positive electrode has been studied using cyclic voltammetry, charge/discharge cycling, and polarization curves at various temperatures. The redox reaction of the PAn electrode at the PAn/modifed PEO-ER interface exhibits good reversibility. At 50-80-degrees-C, the Li/PEO-ER-LiClO4/PAn cell shows more than 40 charge/discharge cycles, 90% charge/discharge efficiency, and 54 W h kg-1 discharge energy density (on PAn weight basis) at 50-mu-A between 2 and 4 V. The polarization performance of the battery improves steadily with increase in temperature.

2-COMPONENT EPOXY NETWORK-LICLO4 POLYMER ELECTROLYTE

An epoxy network-LiClO4 electrolyte system was prepared from diglycidyl ether of polyethylene glycol and triglycidyl ether of glycerol, cured in the presence of LiClO4 only. Various techniques were used to characterize the chemical structure of the precursors and the correlation between the viscoelasticity and conductivity of the cured films was examined.

EPITAXIAL CRYSTALLIZATION OF HDPE ON IPP IN HDPE/IPP BLENDS

Unique crystalline morphologies of solution-cast films of HDPE/iPP blends were investigated by means of transmission electron microscopy (TEM), electron diffraction, metal shadowing and specimen-tilt techniques. The unique morphologies come from an epitaxial crystallization of HDPE on iPP. The contact planes of the two kinds of crystals are (100) of HDPE and (010) of iPP, while the intercrossing angle between their chain axes is about 50-degrees. The HDPE existed with different crystalline morphologies in the two kinds of crystalline regions of iPP spherulites, i.e. cross-hatched and single-crystal-type structures. Based on structural analysis, two models of epitaxial growth of HDPE on iPP are proposed.

THE IMPEDANCE STUDY OF MODIFIED PEO POLYMER ELECTROLYTE

The ultra-thin modified PEO (polyethylene oxide)-LiClO4 polymer electrolyte film (50-mu-m) was obtained by solution-casting technique. Impedance spectra were taken on the cells consisting of above PEO film electrolyte and ion-blocking or nonblocking electrodes. The ambient conductivity as high as 1.33 X 10(-4)S cm-1 could be achieved for PEO electrolyte modified by the crosslinking. It was shown that the resistance at the interface between solid polymer electrolyte and lithium electrode is growing with increasing the storage time. At high temperature, as 96-degrees-C, the ionic transport is clearly controlled by diffusion.

STRUCTURE AND PROPERTIES OF SEQUENTIALLY POLYMERIZED PROPYLENE-B-[ETHYLENE-CO-PROPYLENE]-B-PROPYLENE COPOLYMERS

The structure and properties of presumed block copolymers of polypropylene (PP) with ethylene-propylene random copolymers (EPR), i.e., PP-EPR and PP-EPR-PP, have been investigated by viscometry, transmission electron microscopy, dynamic mechanical analysis, differential scanning calorimetry, gel permeation chromatography, wide-angle x-ray diffraction, and other techniques testing various mechanical properties. PP-EPR and PP-EPR-PP were synthesized using delta-TiCl3-Et2AlCl as a catalyst system. The results indicate that the intrinsic viscosity of these polymers increases with each block-building step, whereas the intrinsic viscosity of those prepared by chain transfer reaction (strong chain-transfer reagent hydrogen was introduced between block-building steps during polymerization) hardly changes with the reaction time. Compared with PP / EPR blends, PP-EPR-PP block copolymers have lower PP and polyethylene crystallinity, and lower melting and crystallization temperatures of crystalline EPR. Two relaxation peaks of PP and EPR appear in the dynamic spectra of blends. They merge into a very broad relaxation peak with block sequence products of the same composition, indicating good compatibility between PP and EPR in the presence of block copolymers. Varying the PP and EPR content affects the crystallinity, density, and morphological structure of the products, which in turn affects the tensile strength and elongation at break. Because of their superior mechanical properties, sequential polymerization products containing PP-EPR and PP-EPR-PP block copolymers may have potential as compatibilizing agents for isotactic polypropylene and polyethylene blends or as potential heat-resistant thermoplastic elastomers.

CHARACTERIZATION OF GAMMA-IRRADIATED CRYSTALLINE POLYMER .3. THERMAL-BEHAVIOR OF GAMMA-IRRADIATED POLYAMIDE-1010

Thermal behaviour of gamma-irradiated plain PA1010 and PA1010 containing different amounts of difunctional cross-linking agent BMI was investigated. In DSC endo- and exotherm, it was found that during irradiation, the presence of BMI markedly changes the melting and crystallisation characteristics of PA1010. A supposition that the network of BMI-containing specimens is rather loose in structure was proposed to explain the discrepancy in thermal behaviour between these two kinds of specimens. The supposition was further ascertained by the less brittleness in mechanical property of specimens containing BMI. Besides, the complexity of the thermal behaviour of gamma-irradiated PA1010 was discussed and attributed mainly to the increase in sigma-e, the fold surface free energy of chain fold crystals.