Microwave preparation and sintering of industrially important perovskite oxides: LaMO3 (M = Cr, Co, Ni)

Perovskite oxides LaMO3 (M = Cr, Co, Ni), have been successfully prepared using microwaves of 2.45 GHz. Microwave preparation is rapid, clean and energy efficient. Preparation of LaCrO3, LaCoO3 and LaNiO3 has been achieved in 3 min, 5 min and 10 min respectively. Direct reaction between component oxides is used for the preparation of LaCrO3 and LaCoO3, whereas nitrates are used as starting materials for LaNiO3 preparation. Products have been characterized using XRD, IR spectroscopy and SEM. Their dc electrical conductivity has also been studied and their fracture behaviour has been examined. All three microwave prepared oxide powders are of submicron size. These perovskite oxides have been sintered to very high densities using microwaves. Possible mechanisms of the microwave-material interaction both during preparation and during sintering have been discussed.

Temperature effect on hydrocarbon-enhanced nitric oxide conversion using a dielectric barrier discharge reactor

Experimental investigations into the effect of temperature on conversion of NO in the presence of hydrocarbons (ethylene, acetylene and n-hexane) are presented. An AC energized dielectric barrier discharge reactor was used as the plasma reactor. The experiments were carried out at different temperatures up to 200 degreesC. The discharge powers were measured at all the temperatures. The discharge power was found to increase with temperature. NO conversion in the presence of ethylene and n-hexane was better than that of acetylene at all temperatures. The addition of acetylene at room temperature showed no better conversion of NO compared to no additive case. While at higher temperatures, it could enhance the conversion of NO. A slight enhancement in NO and NOx removal was observed in the presence of water vapor. (C) 2003 Elsevier Science B.V. All rights reserved.

Geotechnical Characterization of Some Indian Bentonites for their Use as Buffer Material in Geological Repository

The present study examines the geotechnical properties of Indian bentonite clays for their suitability as buffer material in deep geological repository for high-level nuclear wastes. The bentonite samples are characterized for index properties, compaction, hydraulic conductivity and swelling characteristics. Evaluation of geotechnical properties of the compacted bentonite-sand admixtures, from parts of NW India reveals swelling potentials and hydraulic conductivities in the range of 55 % - 108 % and 1.2 X 10 –10 cm/s to 5.42x 10 –11 cm/s respectively. Strong correlation was observed between ESP (exchangeable sodium percentage) and liquid limit/swell potential of tested specimens. Relatively less well-defined trends emerged between ESP and swell pressure/hydraulic conductivity. The Barmer-1 bentonite despite possessing relatively lower montmorillonite content of 68 %, developed higher Atterberg limit and swell potential, and exhibited comparable swelling pressure and hydraulic conductivity as other bentonites with higher montmorillonite contents (82 to 86 %). The desirable geotechnical properties of Barmer clay as a buffer material is attributed to its large ESP (63 %) and, EMDD (1.17 Mg/m3) attained at the experimental compactive stress(5 MPa).

Studies on the deposition and characterization of silicon oxide films for optical coating applications

Silicon oxide films were deposited by reactive evaporation of SiO. Parameters such as oxygen partial pressure and substrate temperature were varied to get variable and graded index films. Films with a refractive index in the range 1.718 to 1.465 at 550 nm have been successfully deposited. Films deposited using ionized oxygen has the refractive index 1.465 at 550 nm and good UV transmittance like bulk fused quartz. Preparation of graded index films was also investigated by changing the oxygen partial pressure during deposition. A two layer antireflection coating at 1064nm has been designed using both homogeneous and inhomogeneous films and studied their characteristics.