Here, we report the crystallographic study of a lectin from Canavalia maritima seeds (ConM) and its relaxant activity on vascular smooth muscle, to provide new insights into the understanding of structure/function relationships of this class of proteins. ConM was crystallized and its structure determined by standard molecular replacement techniques. The amino acid residues, previously suggested incorrectly by manual sequencing, have now been determined as I17, I53, S129, S134, G144, S164, P165, S187, V190, S169, T196, and S202. Analysis of the structure indicated a dimer in the asymmetric unit, two metal binding sites per monomer, and loops involved in the molecular oligomerization. These confer 98% similarity between ConM and other previously described lectins, derived from Canavalia ensiformis and Canavalia brasiliensis. Our functional data indicate that ConM exerts a concentration-dependent relaxant action on isolated aortic rings that probably occurs via an interaction with a specific lectin-binding site on the endothelium, resulting in a release of nitric oxide. (C) 2005 Elsevier B.V. All rights reserved.

Low-temperature, self-nucleated growth of indium-tin oxide nanostructures by pulsed laser deposition on amorphous substrates

Indium-tin oxide nanostructures were deposited by excimer laser ablation in a nitrogen atmosphere using catalyst-free oxidized silicon substrates at 500 degrees C. Up to 1 mbar, nanowires grew by the vapor-liquid-solid (VLS) mechanism, with the amount of liquid material decreasing as the deposition pressure increased. The nanowires present the single-crystalline cubic bixbyite structure, oriented < 100 >. For the highest pressure used, pyramids were formed and no sign of liquid material could be observed, indicating that these structures grew by a vapor-solid mechanism. (c) 2006 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Dye-sensitized solar cell architecture based on indium-tin oxide nanowires coated with titanium dioxide

A new architecture for dye-sensitized solar cells is employed, based on a nanostructured transparent conducting oxide protruding from the substrate, covered with a separate active oxide layer. The objective is to decrease electron-hole recombination. The concept was tested by growing branched indium-tin oxide nanowires on glass using pulsed laser deposition followed by deposition of a sputtered titanium dioxide layer covering the wires. The separation of charge generation and charge transport functions opens many possibilities for dye-sensitized solar cell optimization. (c) 2007 Acta Materialia. Inc. Published by Elsevier Ltd. All rights reserved.

Structure characterization of molecular complexes for non-linear optical materials. II. 1 : 1 complexes of 4-methyl-morpholine-N-oxide (1) and 3-picoline-N-oxide (2) with 2,4,6-trinitrophenol, studied by X-ray, AM1 and DFT calculations

(1) C6H2N3O7- center dot C5H12NO2+, Mr = 346.26, P2(1)/c, a = 7.2356(6), b = 10.5765(9), c = 19.593(2) angstrom, 3 beta=95.101(6)degrees, V = 1493.5(2) angstrom(3), Z = 4, R-1 = 0.0414; (2) C6H2N3O7- center dot C6H8NO+, Mr = 38.24, P2(1)/n, a = 7.8713(5), b = 6.1979(7), c = 28.697(3) angstrom, beta = 90.028(7)degrees, V = 1400.0(2) angstrom(3), Z = 4, R-1 = 0.0416. The packing units in both compounds consist of hydrogen bonded cation-anion pairs. The (hyper)polarizabilities have been calculated for the crystallographic and optimized molecules, by AM1 and at the DFT/B3LYP(6-31G**) level.

PREPARATION AND CHARACTERIZATION OF TI(IV) OXIDE GRAFTED ONTO SILICA ON A SILICA-GEL SURFACE

Silica gel with a surface area of 500 m2g-1 and an average pore diameter of 60 angstrom was chemically modified with Ti(IV) oxide using the grafting method. The amount of metal oxide attached to the surface was 1.8.10(-3) mol g-1. The X-ray photoelectron spectra showed that the metal ion species on the surface are Ti(IV) in TiO2 and MTiO3 (M = Ca2+, Sr2+, Ba2+ and Pb2+), i.e. they have the binding energy of Ti2p3/2 = 458.7 eV. The dehydration of the solid at higher temperature increased the O(II)/Ti (O(II) = oxygen bound to titanium atom) ratio, presumably due to a reticulation of the hydrous Ti(IV) oxide on the silica surface at higher temperatures. Migration of Ti(IV) into the silica gel matrix was observed but the specific surface area was not significantly changed.

Europium(III)-containing zinc oxide from Pechini method

ZnO:Eu3+ (0.1 and 3 at%) with average particle size of 500 nm were prepared by the Pechini method. Photoluminescence spectroscopy evidences that there is no energy transfer between ZnO and Eu3+ ion. The emission spectrum at 77 K shows that Eu3+ ions occupy at least three different sites in ZnO:Eu 3 at% sample. The experimental intensity parameter Omega(2) indicates that Eu3+ ions in the sample doped with 3 at% occupy sites where 4-configurational levels can better mix with opposite-parity states than those in the sample doped with 0.1 at%. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Polyol-mediated synthesis of ultrafine tin oxide nanoparticles for reversible Li-ion storage

A simple, cheap and versatile, polyol-mediated fabrication method has been extended to the synthesis of tin oxide nanoparticles on a large scale. Ultrafine SnO2 nanoparticles with crystallite sizes of less than 5 nm were realized by refluxing SnCl2 . 2H(2)O in ethylene glycol at 195 degrees C for 4 h under vigorous stirring in air. The as-prepared SnO2 nanoparticles exhibited enhanced Li-ion storage capability and cyclability, demonstrating a specific capacity of 400 mAh g(-1) beyond 100 cycles. (c) 2006 Elsevier B.V. All rights reserved.

Characterization of tin oxide based sol-gel coatings on borosilicate glasses by X-ray reflectivity

The X-ray reflectivity technique was applied in the study of tin oxide films deposited by sol-gel dip-coating on borosilicate glasses. The influence of the withdrawal speed and temperature of thermal treatment on the film structure was analyzed. We have compared the thermal evolution of the density and the shrinkage of the films with these properties measured for the monolithic xerogel by helium picnometry and thermomechanical analysis. In agreement with the Landau-Levich model, the layer thickness increases by increasing the withdrawal speed. Nevertheless, it decreases with the increase of the thermal treatment temperature, due to the densification process. The values of apparent density are smaller than the skeletal density, which shows that the films are porous. The comparison between the film and the monolith indicates that shrinkage during firing is anisotropic, occurring essentially perpendicular to the coating surface.

Antimony oxide based glasses

Glass formation has been investigated in binary systems based on antimony oxide as the main glass former: (100-x)Sb2O3-xWO3, (5 < x < 65), (100 - x)Sb2O3-xSbPO(4), (5 < x < 80) and (100 - x)Sb2O3-x[Sb(PO3)(3)](n), (10 < x < 40). Ternary systems derived from the Sb2O3-WO3 binary glass have also been studied: Sb2O3-WO3-BaF2 Sb2O3-WO3-NaF and Sb2O3-WO3-[Sb(PO3)(3)](n). Glass transition temperature ranges from 280 degreesC to 380 degreesC. It increases as the concentration in tungsten oxide or antimony phosphate increases. Refractive index is larger than 2. Tungsten-containing glasses are yellow in transmission and turn green at the largest WO3 content. Optical transmission and temperatures of glass transition, T-g, onset of the crystallization. T-x, and maximum of crystallization, T-p, have been measured using differential scanning calorimetry (DSC). These glasses have potential photonic applications. (C) 2001 Elsevier B.V. B.V. All rights reserved.

Tin-doped indium oxide nanobelts grown by carbothermal reduction method

This communication discusses the formation of doped nanobelts produced by a simple route. Tin-doped indium oxide (ITO) nanobelts were obtained by a carbothermal reduction method. The nanostructures were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy-dispersive X-ray spectroscopy (EDX) and wavelength-dispersive X-ray spectroscopy (WDX). The results show that the nanobelts have a cubic structure, are single crystalline and doped with tin and grow in the [400] direction.