Phase relations in the system BiO1.5–SrO–CuO at 1123 K

Phase relations in the system Bi-Sr-Cu-O at 1123 K have been investigated using optical microscopy, electron-probe microanalysis (EPMA) and powder X-ray diffraction (XRD) of equilibrated samples. Differential thermal analysis (DTA) was used to confirm liquid formation for compositions rich in BiO1.5. Compositions along the three pseudo-binary sections and inside the pseudo-ternary triangle have been examined. The attainment of equilibrium was facilitated by the use of freshly prepared SrO as the starting material. The loss of Bi2O3 from the sample was minimized by double encapsulation. A complete phase diagram at 1123 K is presented. It differs significantly from versions of the phase diagram published recently.

Potentiometric determination of activities in the two-phase fields of the system Na2O---(α)Al2O3

Three compounds have been found to be stable in the pseudobinary system Na2O---(α)Al2O3 between 825 and 1400 K; two nonstoichiometric phases, β-alumina and β″-alumina, and NaAlO2. The homogeneity of β-alumina ranges from 9.5 to 11 mol% Na2O, while that of β″-alumina from 13.3 to 15.9 mol% Na2O at 1173 K. The activity of Na2O in the two-phase fields has been determined by a solid-state potentiometric technique. Since both β- and β″-alumina are fast sodium ion conductors, biphasic solid electrolyte tubes were used in these electrochemical measurements. The open circuit emf of the following cells were measured from 790 to 980 K: [GRAPHICS] The partial molar Gibbs' energy of Na2O relative to gamma-Na2O in the two-phase regions can be represented as: DELTA-GBAR(Na2O)(alpha- + beta-alumina) = -270,900 + 24.03 T, DELTA-GBAR(Na2O)(beta- + beta"-alumina) = -232,700 + 56.19 T, and DELTA-GBAR(Na2O)(beta"-alumina + NaAlO2) = -13,100 - 4.51 T J mol-1. Similar galvanic cells using a Au-Na alloy and a mixture of Co + CoAl(2+2x)O4+3x + (alpha)Al2O3 as electrodes were used at 1400 K. Thermodynamic data obtained in these studies are used to evaluate phase relations and partial pressure of sodium in the Na2O-(alpha) Al2O3 system as a function of oxygen partial pressure, composition and temperature.

Nucleotide sequence of the 3terminal region of belladonna mottle virus (renamed Physalis mottle virus) RNA and analysis of the evolutionary relationships among tymoviral coat proteins

The 3' terminal 1255 nt sequence of Physalis mottle virus (PhMV) genomic RNA has been determined from a set of overlapping cDNA clones. The open reading frame (ORF) at the 3' terminus corresponds to the amino acid sequence of the coat protein (CP) determined earlier except for the absence of the dipeptide, Lys-Leu, at position 110-111. In addiition, the sequence upstream of the CP gene contains the message coding for 178 amino acid residues of the C-terminus of the putative replicase protein (RP). The sequence downstream of the CP gene contains an untranslated region whose terminal 80 nucleotides can be folded into a characteristic tRNA-like structure. A phylogenetic tree constructed after aligning separately the sequence of the CP, the replicase protein (RP) and the tRNA-like structure determined in this study with the corresponding sequences of other tymoviruses shows that PhMV wrongly named belladonna mottle virus [BDMV(I)] is a separate tymovirus and not another strain of BDMV(E) as originally envisaged. The phylogenetic tree in all the three cases is identical showing that any subset of genomic sequence of sufficient length can be used for establishing evolutionary relationships among tymoviruses.

Reduction In Metal-Mold Reactivity In Titanium Castings Through The Use Of Sodium Aluminate As Binder In Zircon Sand Molds

The present work is aimed at evaluating an alternative moulding system, namely, sodium aluminate bonded zircon sand mould and assess its suitability in relation to the much studied sodium silicate bonded zircon sand moulding system. It is described in the study presented here that with regard to metal - mould reaction, sodium aluminate bonded zircon sand mould system is a superior viable system as compared to sodium silicate bonded zircon moulding system at mould firing temperatures of 873 - 1473 K.

Standard Gibbs' energies of formation of BaCuO2, Y2Cu2O5 and Y2BaCuO5

The Gibbs' energies of formation of BaCuO2, Y2Cu2O5 and Y2BaCuO5 from component oxides have been measured using solid state galvanic cells incorporating CaF2 as the solid electrolyte under pure oxygen at a pressure of 1.01 x 10(5) Pa Because the superconducting compound YBa2Cu3O7-delta coexists with any two of the phases CuO, BaCuO2 and Y2BaCuO5, the data on BaCuO2 and Y2BaCuO5 obtained in this study provide the basis for the evaluation of the Gibbs' energy of formation of the 1-2-3 compound at high temperatures.

Thermodynamics Of Aluminum Strontium Alloys

The activity of strontium in liquid Al-Sr alloys (X(Sr) less-than-or-equal-to 0.17) at 1323 K has been determined using the Knudsen effusion-mass loss technique. At higher concentrations (X(Sr) greater-than-or-equal-to 0.28), the activity of strontium has been determined by the pseudoisopiestic technique. Activity of aluminium has been derived by Gibbs-Duhem integration. The concentration - concentration structure factor of Bhatia and Thornton at zero wave vector has been computed from the thermodynamic data. The behaviour of the mean square thermal fluctuation in composition and the thermodynamic mixing functions suggest association tendencies in the liquid state. The associated solution model with Al2Sr as the predominant complex can account for the properties of the liquid alloy. Thermodynamic data for the intermetallic compunds in the Al-Sr system have been derived using the phase diagram and the Gibbs' energy and enthalpy of mixing of liquid alloys. The data indicate the need for redetermination of the phase diagram near the strontium-rich corner.

Vapor-Pressure Of Calcium Corresponding To The Reduction Of Calcia By Aluminum

The equilibrium pressure of calcium corresponding to the reduction reaction 6CaO (s) + 2Al (l) half-arrow-right-over-half-arrow-left 3CaO.Al2O3 (s) + 3Ca (g) has been measured by Knudsen effusion - mass loss analysis in the temperature range 1190 - 1500 K. The measured vapour pressure can be expressed as a function of temperature by the relation: log p(Ca) (Pa) = -10,670/T + 9.267 The calcium generated is partially absorbed by aluminium to form an alloy. The equilibrium composition of the alloy at 1373 K was found to be 22 mol% Ca - 78 mol% Al. The measured vapour pressure is in good agreement with that computed from thermodynamic data.

Thermodynamic Properties of Niobium Oxides

Thermodynamic properties of three oxides of niobium have been measured using solid state electrochemical cells incorporating yttria-doped thoria (YDT) as the electrolyte in the temperature range T = (1000 to 1300) K. The standard Gibbs energies of formation of NbO, NbO2, and NbO2.422 from the elements can be expressed as: Delta(f)G(NbO)(o) +/- 547/J . mol(-1) = -414 986 + 86.861(T/K) Delta(f)G(NbO2)(o) +/- 548/J . mol(-1) = -779 864 + 164.438(T/K) Delta(f)G(NbO2.422)(o) +/- 775/J . mol(-1) = -911 045 + 197.932(T/K) The results are discussed in comparison with thermodynamic data reported in the literature. The new results refine data for NbO and NbO2 presented in standard data compilations. There are no data in thermodynamic compilations for NbO2.422 (Nb12O29). In the absence of the heat capacity and enthalpy of formation measurements, only the Gibbs energy of formation of NbO2.422 can be assessed. The free energy of formation of stoichiometric Nb2O5 is evaluated on the basis of measurements on NbO2.422 and information available in the literature on phase boundary compositions and isothermal variation of nonstoichiometric parameter with oxygen potential for Nb2O5-x. The results suggest a minor revision of data for Nb2O5. A minimum in the Gibbs energy of mixing for the system Nb-O occurs in the nonstoichiometric domain of Nb2O5-x with x = 0.036.

Thermodynamic properties of strontium titanates Sr2TiO4, Sr3Ti2O7, Sr4Ti3O10, and SrTiO3

The chemical potentials of SrO in two-phase fields (TiO2 + SrTiO3) (SrTiO3 + Sr4Ti3O10) (Sr4Ti3O10 + Sr3Ti2O7) and (Sr3Ti2O7 + Sr2TiO4) of the pseudo-binary system (SrO + TiO2) have been measured in the temperature range (900 to 1250) K relative to pure SrO as the reference state using solid-state galvanic cells incorporating single crystal SrF2 as the electrolyte The cells were operated under pure oxygen at ambient pressure The standard Gibbs free energies of formation of strontium titanates SrTiO3 Sr4Ti3O10 Sr3Ti2O7 and Sr2TiO4 from their component binary oxides were derived from the reversible electromotive force (EMF) of the cells For the formation of the four compounds from their component oxides TiO2 with rutile structure and SrO the standard Gibbs free energy changes are given by Delta G((ox))(SrTiO3) +/- 89/(J mol(-1)) = -121878 + 3 881(T/K) Delta G((ox))(Sr4Ti3O10) +/- 284/(J mol(-1)) = -409197 + 14 749(T/K) Delta G((ox))(Sr3Ti2O7) +/- 190/(J mol(-1)) = -285827 + 10 022(T/K) Delta G((ox))(Sr2TiO4) +/- 110/(J mol(-1))= -159385 + 3 770(T/K) The reference state for solid TiO2 is the rutile form The results of this study are in good agreement with Gibbs free energy of formation data reported in the literature for SrTiO3 but differ significantly with data for Sr4Ti3O10 For Si3Ti2O7 and Si2TiO4 experimental measurements are not available in the literature for direct comparison with the results obtained in this study (C) 2010 Elsevier Ltd All rights reserved

Thermal expansion of doped lanthanum gallates

Thermal expansion of several compositions of Sr and Mg-doped LaGaO3 including an A-site deficient composition (La0.9Sr0.1)(0.98)(Ga0.8Mg0.2)O-2.821 were measured in the temperature range from 298 to 1273 K. The effect of doping on thermal expansion was studied by varying the composition at one site of the perovskite structure (either A or B), while keeping the composition at the other site invariant. Thermal expansion varied nonlinearly with temperature and exhibited an inflexion between 550 and 620 K, probably related to the change in crystal structure from orthorhombic to rhombohedral. The dependence of average thermal expansion coefficient (alpha (av)) on the dopant concentration on either A or B site of the perovskite structure was found to be linear, when the composition at the other site was kept constant. Mg doping on the B-site had a greater effect on the average thermal expansion coefficient than Sr doping on the A-site. Cation deficiency at the A-site decreases thermal expansion when compositions at both sites are held constant.

Phase relationships in the system Ni-W-O and thermodynamic properties of NiWO,

The phase diagram of the Ni-W-O system at 1200 K was established by metallographic and X-ray identification of the phases present after equilibration at controlled oxygen potentials. The oxygen partial pressures over the samples were fixed by metered streams of CO+CO2 gas mixtures. There was only one ternary oxide, nickel tungstate (NiWO4), in the Ni-W-O system at a total pressure of 1 atm, and this compound decomposed to a mixture of Ni+WO2.72 on lowering the oxygen potential. The Gibbs' free energy of formation of NiWO4 was determined from the measurement of the e.m.f. of the solid oxide galvanic cell, Pt, Ni+NiWO4+WO2.72/CaO-ZrO2/Ni+NiO, Pt and thermodynamic properties of tungsten and nickel oxides available in the literature. For the reaction, NiO(s)+WO3(s)rarrNiWO4(s) DeltaG°=–10500–0.708 T (±250) cal mol–1.