Influência das espécies ativas na absorção de intersticiais durante a carbonitretação a plasma do TI

Physical-chemical properties of Ti are sensible to the presence of interstitial elements. In the case of thermochemical treatments plasma assisted, the influence of different active species is not still understood. In order to contribute for such knowledge, this work purposes a study of the role played by the active species atmosphere into the Ar N2 CH4 carbonitriding plasma. It was carried out a plasma diagnostic by OES (Optical Emission Spectroscopy) in the z Ar y N2 x CH4 plasma mixture, in which z, y and x indexes represent gas flow variable from 0 to 4 sccm (cm3/min). The diagnostic presents abrupt variations of emission intensities associated to the species in determined conditions. Therefore, they were selected in order to carry out the chemical treatment and then to investigate their influences. Commercial pure Ti disks were submitted to plasma carbonitriding process using pre-established conditions from the OES measurements while some parameters such as pressure and temperature were maintained constant. The concentration profiles of interstitial elements (C and N atoms) were determined by Resonant Nuclear Reaction Analysis (NRA) resulting in a depth profile plots. The reactions used were 15N(ρ,αγ)12C and 12C(α,α)12C. GIXRD (Grazing Incidence X-Ray Diffraction) analysis was used in order to identify the presence of phases on the surface. Micro-Raman spectroscopy was used in order to qualitatively study the carbon into the TiCxN1 structure. It has been verified which the density species effectively influences more the diffusion of particles into the Ti lattice and characteristics of the layer formed than the gas concentration. High intensity of N2 + (391,4 nm) and CH (387,1 nm) species promotes more diffusion of C and N. It was observed that Hα (656,3 nm) species acts like a catalyzer allowing a deeper diffusion of nitrogen and carbon into the titanium lattice.

Adição de nanopartículas de Ti em matriz de Fe através da deposição por magnetron sputtering

Microalloyed steels constitute a specific class of steel with low amount of carbon and microalloying elements such as Vanadium (V), Niobium (Nb) and Titanium (Ti). The development and application of microalloyed steels and steels in general are limited to the handling of powders with particles of submicron or nanometer dimensions. Therefore, this work presents an alternative in order to construction of microalloyed steels utilizing the deposition by magnetron sputtering technique as a microalloying element addiction in which Ti nanoparticles are dispersed in an iron matrix. The advantage of that technique in relation to the conventional metallurgical processes is the possibility of uniformly disperse the microalloying elements in the iron matrix. It was carried out deposition of Ti onto Fe powder in high CH4, H2, Ar plasma atmosphere, with two deposition times. After the deposition, the iron powder with nanoparticles of Ti dispersed distributed, were compacted and sintered at 1120 ° C in resistive furnace. Characterization techniques utilized in the samples of powder before and after deposition of Ti were Granulometry, Scanning Electron Microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX) and X-ray diffraction (DRX). In the case of sintered samples, it was carried out characterization by SEM and Vickers Microhardness assays. The results show which the deposition technique by magnetron sputtering is practicable in the dispersion of particles in iron matrix. The EDX microanalysis detected higher percentages of Ti when the deposition were carried out with the inert gas and when the deposition process was carried out with reactive gas. The presence of titanium in iron matrix was also evidenced by the results of X-ray diffraction peaks that showed shifts in the network matrix. Given these results it can be said that the technique of magnetron sputtering deposition is feasible in the dispersion of nanoparticles of iron matrix in Ti.

Sobrevivência e tamanho populacional do Tiê-preto Tachyphonus Rufus (aves: thraupidae) em fragmento de restinga no extremo Norte da Mata Atlântica

For a long time, we believed in the pattern that tropical and south hemisphere species have high survival. Nowadays results began to contradict this pattern, indicating the need for further studies. Despite the advanced state of the study of bird population parameters, little is known about their variation throughout the year and the factors affecting them. Reproduction, for example, is one factor that may alter adult survival rates, because during this process the breeding pair allocates resources to maintain itself to maintain offspring, making itself more susceptible to diseases and predation. The aim of this study was to estimate survival and population size of a Central and South America passerine, Tachyphonus rufus (Boddaert, 1783), testing hypotheses about the factors that define these parameters. We performed data collection between Nov/2010 and ago/2012 in 12 ha plot, in a fragment of Atlantic Forest in northeastern Brazil. We used capture-mark-recapture methods to generate estimates using Closed Design Robust model in the program MARK. We generated Multi-state models to test some assumptions inherent to Closed Robust Design. The influence of co-variables (time, rain and reproductive cycle) and the effect of transient individuals were measured. Capture, recapture and apparent survival parameters were defined by reproductive cycle, while temporary dispersal was influence by rain. The estimates showed a higher apparent survival during the non-breeding period (92% ± 1%) than during breeding (40% ± 9%), revealing a cost of reproduction and suggesting a trade-off between surviving and reproducing. The low annual survival observed (34%) did not corroborate the pattern of high rates expected for a tropical bird. The largest population size was estimated to be 56 individuals in Nov/11, explained by high recruitment of juveniles, while the lowest observed in May/12: 10 individuals, probably as a result of massive influx of competitor species. Results from this study add to the growing literature on life history of Neotropical species. We encourage studies like this especially in Brazil, where there are few information, and suggest that covariates related to habitat quality and environmental changes should be tested, so that we can generate increasingly reliable models

Genetic parameters and relationships of heifer pregnancy and age at first calving with weight gain, yearling and mature weight in Nelore cattle

The objectives of the current study were to investigate the additive genetic associations between heifer pregnancy at 16 months of age (HP16) and age at first calving (AFC) with weight gain from birth to weaning (WG), yearling weight (YW) and mature weight (MW), in order to verify the possibility of using the traits measured directly in females as selection criteria for the genetic improvement of sexual precocity in Nelore cattle. (Co)variance components were estimated by Bayesian inference using a linear animal model for AFC, WG, YW and MW and a nonlinear (threshold) animal model for HP16. The posterior means of direct heritability estimates were: 0.45 +/- 0.02; 0.10 +/- 0.01; 023 +/- 0.02; 0.36 +/- 0.01 and 0.39 +/- 0.04, for HP16, AFC, WG, YW and MW, respectively. Maternal heritability estimate for WG was 0.07 +/- 0.01. Genetic correlations estimated between HP16 and WG, YW and MW were 0.19 +/- 0.04; 0.25 +/- 0.06 and 0.14 +/- 0.05, respectively. The genetic correlations of AFC with WG, YW and MW were low to moderate and negative, with values of -0.18 +/- 0.06; -0.22 +/- 0.05 and -0.12 +/- 0.05, respectively. The high heritability estimated for HP16 suggests that this trait seem to be a better selection criterion for females sexual precocity than AFC. Long-term selection for animals that are heavier at young ages tends to improve the heifers sexual precocity evaluated by HP16 or AFC. Predicted breeding values for HP16 can be used to select bulls and it can lead to an improvement in sexual precocity. The inclusion of HP16 in a selection index will result in small or no response for females mature weight. (C) 2011 Elsevier B.V. All rights reserved.

Metalização mecânica de ZrO2 com Ti para brasagem ZrO2/Aço com ligas de adição sem metal ativo

Metal/ceramic interfaces using zirconia have dominated the industrial applications in the last decade, due to the high mechanical strength and fracture toughness of zirconia, especially at temperatures below 300 ºC. Also noteworthy is the good ionic conductivity in high temperatures of this component. In this work joining between ZrO2 Y-TZP and ZrO2 Mg-PSZ with austenitic stainless steel was studied. These joints were brazed at high-vacuum after mechanical metallization with Ti using filler alloys composed by Ag-Cu and Ag-Cu-Ni. The influence of the metallization, and the affinity between the different groups (ceramic / filler alloys) was evaluated, in order to achieve strong metal/ceramic joints. Evaluation of joints and interfaces, also the characterization of base materials was implemented using various techniques, such as: x-ray diffraction, leak test, three-point flexural test and scanning electron microscopy with chemical analysis. The microstructural analysis revealed physical and chemical bonds in the metal/ceramic interfaces, providing superior leak proof joints and stress cracking, in order to a good joint in all brazed samples. Precipitation zones and reaction layers with eutetic characteristics were observed between the steel and the filler metal

Efficiency of intermittent exercise on adiposity and fatty liver in rats fed with high-fat diet

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Anelastic spectroscopy in a Ti alloy used as biomaterial

Ti and its alloys have been used thoroughly in the production of prostheses and dental implants due to their properties, such as high corrosion resistance, low elasticity modulus and high mechanical strength/density relation. Among the Ti-based alloys, the Ti-35Nb-7Zr-5Ta (TNZT) is one that presents the smallest elasticity modulus, making it an excellent alternative to be used as a biomaterial. In this paper, mechanical spectroscopy measurements were made in TNZT alloys containing several quantities of oxygen and nitrogen in solid solution. Mechanical spectroscopy measurements were made by using a torsion pendulum, operating at an oscillation frequency in the interval 4-30 Hz, temperature in the range 100-700 K, heating rate of about 1 K/min and vacuum lower than 10(-5) Torr. Complex relaxation structures and a reduction in the elasticity modulus were observed for the heat-treated and doped samples. The observed peaks were associated with the interactions of interstitial atoms and the alloy elements. (C) 2009 Elsevier B.V. All rights reserved.

Anelastic relaxation due to hydrogen in Ti-35Nb-7Zr-5Ta alloy

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Anelastic Relaxation Measurements in Nb-46wt%Ti Alloys with Interstitial Solutes in Solid Solution

Anelastic relaxation measurements were performed in a Nb-46wt%Ti alloy, in the temperature range of 300 to 700 K, using a torsion pendulum operating at an oscillating frequency near 2.0 Hz. The samples were measured in different conditions: cold worked, annealed in ultra-high vacuum and doped with several quantities of nitrogen. The relaxation spectra obtained were resolved into their component peaks, corresponding to the different kinds of interaction of the interstitial solutes with the metallic matrix. The relaxation parameters of each process were calculated using Debye's elementary peaks.

FeNbP in ultra-low carbon Nb-added steel containing high P

Precipitation of FeTiP is reported to occur in Ti-added IF steels containing high P during thermomechanical processing. An ultra-low carbon (ULC) Nb-added steel ingot containing a higher P content (< 0.8 wt-%) was produced via aluminothermic reduction of Fe2O3 followed by double electron beam melting (EBM). FeNbP coarse precipitates were observed in the as-cast microstructure. After soaking at 1050C for 1 h, the plate was hot rolled from 31 mm down to 7 mm in thickness (total reduction of 77%). During cold rolling of these hot bands we observed embrittlement. We believe that this embrittlement can be attributed to the presence of the FeNbP precipitates. Light optical and scanning electron microscopy (SEM/EDS) were used to characterize the microstructure of this ULC steel. (C) 2000 Elsevier B.V. All rights reserved.

Conventional and microwave sintering of CaCu(3)Ti(4)O(12)/CaTiO(3) ceramic composites: non-ohmic and dielectric properties

The non-ohmic and dielectric properties as well as the dependence on the microstructural features of CaCu(3)Ti(4)O(12)/CaTiO(3) ceramic composites obtained by conventional and microwave sintering were investigated. It was demonstrated that the non-ohmic and dielectric properties depend strongly on the sintering conditions. It was found that the non-linear coefficient reaches values of 65 for microwave-sintered samples and 42 for samples sintered in a conventional furnace when a current density interval of 1-10 mA cm(-2) is considered. The non-linear coefficient value of 65 is equivalent to 1500 for samples sintered in the microwave if a current interval of 5-30 mA is considered as is shortly discussed by Chung et al (2004 Nature Mater. 3 774). Due to a high non-linear coefficient and a low leakage current (90 mu A) under both processing conditions, these samples are promising for varistor applications. The conventionally sintered samples exhibit a higher relative dielectric constant at 1 kHz (2960) compared with the samples sintered in the microwave furnace (2100). At high frequencies, the dielectric constant is also larger in the samples sintered in the conventional furnace. Depending on the application, one or another synthesis methodology is recommended, that is, for varistor applications sintered in a microwave furnace and for dielectric application sintered in a conventional furnace.

Effect of WC-10%Co-4%Cr coating on the Ti-6Al-4V alloy fatigue strength

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Structural Evaluation of Mechanically Alloyed (67-x)Ti-xZr-22Si-11B Powders

The present work reports on the structural evaluation of mechanically alloyed Ti-xZr-22Si-11B (x = 5, 7, 10, 15 and 20 at-%) powders. Milled powders and hot-pressed alloys were characterized by X-ray diffraction, electron scanning microscopy, and electron dispersive spectrometry. The Si and B atoms were preferentially dissolved into the Ti and Zr lattices during ball milling of Ti-xZr-22Si-11B (x = 7, 10, 15 and 20 at-%) powders, and extended solid solutions were achieved. The displacement of Ti peaks was more pronounced to the direction of lower diffraction angles with increasing Zr amounts in mechanically alloyed Ti-Zr-Si-B powders, indicating that the Zr atoms were also dissolved into the Ti lattice.

Surface Corrosion of Ti-16Si-4B Powder Alloy Implanted With Nitrogen by Plasma-Based Technique

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Fatigue fracture behavior of Ti-6Al-4V PVD coated

Fatigue, corrosion and wear resistance are important parameters in aircraft components development as landing gear. High strength/weight ratio and effective corrosion resistance make of titanium alloys an alternative choice to replace steel and aluminum alloys. However, titanium alloys have poor tribological properties, which reduce devices performance under friction. PVD coatings tribological systems has been increased due to their attractive mechanical properties as low environmental impact, low friction coefficient, low wear rate and hardness up to 2000 HV.In this study the influence of TiN deposited by PVD on the fatigue strength of Ti-6Al-4V alloy was evaluated. Comparison of fatigue strength of coated specimens and base material shows also a decrease when parts are coated. It was observed that the influence is more significant in high cycle fatigue tests. Scanning electron microscopy technique (SEM) was used to observe crack origin sites and fracture features. (C) 2010 Published by Elsevier Ltd.