Analysis of failed commercially pure titanium dental implants: A scanning electron microscopy and energy-dispersive spectrometer X-ray study

Background: the failure of osseointegration in oral rehabilitation has gained importance in current literature and in clinical practice. The integration of titanium dental implants in alveolar bone has been partly ascribed to the biocompatibility of the implant surface oxide layer. The aim of this investigation was to analyze the surface topography and composition of failed titanium dental implants in order to determine possible causes of failure.Methods: Twenty-one commercially pure titanium (cpTi) implants were retrieved from 16 patients (mean age of 50.33 +/- 11.81 years). Fourteen implants were retrieved before loading (early failures), six after loading (late failures), and one because of mandibular canal damage. The failure criterion was lack of osseointegration characterized as dental implant mobility. Two unused implants were used as a control group. All implant surfaces were examined by scanning electron microscopy (SEM) and energy-dispersive spectrometer x-ray (EDS) to element analysis. Evaluations were performed on several locations of the same implant.Results: SEM showed that the surface of all retrieved implants consisted of different degrees of organic residues, appearing mainly as dark stains. The surface topography presented as grooves and ridges along the machined surface similar to control group. Overall, foreign elements such as carbon, oxygen, sodium, calcium, silicon, and aluminum were detected in failed implants. The implants from control group presented no macroscopic contamination and clear signs of titanium.Conclusion: These preliminary results do not suggest any material-related cause for implant failures, although different element composition was assessed between failed implants and control implants.

Influence of cyclosporin A on quality of bone around integrated dental implants: a radiographic study in rabbits

To evaluate the influence of cyclosporin A (CsA) administration on bone around integrated dental implants assessed by a bone quality index and by quantitative subtraction radiography.A total of 36 machine surface commercial implants were placed in 18 adult rabbits. After a 3-month healing period without any disturbance, the animals were randomly divided into three groups of six animals each. Group A was sacrificed at this time. CsA was injected subcutaneously in an immunosuppressive dose of 10 mg/kg/day in a test group (Group T), and a Group B served as a control, receiving only vehicle. After 3 months of cyclosporin administration, the animals of both Groups B and T were sacrificed. Radiographs were obtained at implant surgery and at the day of sacrifice with a CMOS sensor. Bone quality around the implants was compared between the groups using a bone quality index and quantitative subtraction radiography.The bone analysis showed that in Group T, the bone quality changed dramatically from a dense cortical to a loose trabecular bone structure (P < 0.0001, chi(2) test) while in Groups A and B there were no significant differences. Quantitative digital subtraction radiography showed significantly (P < 0.05) lower gray shade values (radiographic density) in a region of bone formation around the implants in Group T (118 +/- 12) than in Groups A (161 +/- 6) and B (186 +/- 10).Within the limits of this study, CsA administration has a negative effect on the quality of bone around integrated dental implant.

Clinical and radiographic changes around dental implants inserted in different levels in relation to the crestal bone, under different restoration protocols, in the dog model

Background: The aim of the present study was to evaluate clinical and radiographic changes that occur around dental implants inserted in different levels in relation to crestal bone under different restoration protocols.Methods: Thirty-six implants were inserted in the edentulous mandible of six mongrel dogs. Each implant was assigned to an experimental group according to the distance from the top of the implant to the crestal bone: Bone Level (at crestal bone level), Minus 1 (1 mm below crestal bone), or Minus 2 (2 mm below crestal bone). Each hemimandible was submitted to a restoration protocol: conventional (prosthesis was installed 120 days after implant placement, including 30 days with healing cap) or immediate (prosthesis was installed 24 hours after implant placement). Fixed partial prostheses were installed bilaterally in the same day. After 90 days, clinical and radiographic parameters were evaluated.Results: As long as the implants were inserted in more apical positions, the first bone-to-implant contact (fBIC) was positioned more apically (P<0.05). However, the apical positioning of the implants did not influence the ridge loss or the position of the soft tissue margin (PSTM) (P>0.05). In addition, in immediately restored sites, the PSTM was located significantly more coronally than that in conventionally restored sites (P=0.02).Conclusions: Despite the more apical positioning of the fBIC, the height of the peri-implant soft tissues and ridge was not jeopardized. Moreover, the immediate restoration protocol was beneficial to the maintenance of the PSTM. Further studies are suggested to evaluate the significance of these results in longer healing periods.

Incisive Canal Deflation for Correct Implant Placement: Case Report

Aim: This article is a case report of a patient in whom the prosthetic planning indicated the necessity of an incisive canal deflation for the correct installation of all implant that is to be osseointegrated.Case Report. In the reopening phase after the bone graft installation, the incisive canal deflation (biopsy of its content) was done and titanium implants were installed with one of them invading the anatomical space occupied previously by the incisive canal. The biopsy analysis showed fragments of the incisive artery and nerve., which are responsible for the anterior upper-tooth pulp, the periodontium vascularization. and the innervation. Front the anastomosis present along with other structures allied with the absence of teeth in the region, there was no detriment to the patient caused by the deflation.Conclusion: Incisive canal deflation is a viable technique in implantology. It can permit ideal prosthetic planning with no detriment to the patient. (Implant Dent 2009;18:473-479)

Effect of diabetes mellitus and insulin therapy on bone density around osseointegrated dental implants: a digital subtraction radiography study in rats

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

The antibacterial effect of photodynamic therapy in dental plaque-derived biofilms

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Genetic Responses to Nanostructured Calcium-phosphate-coated Implants

Nanostructured calcium phosphate (CaP) has been histologically and biomechanically proven to enhance osseointegration of implants; however, conventional techniques were not sufficiently sensitive to capture its biological effects fully. Here, we compared the conventional removal torque (RTQ) evaluation and gene expression in tissues around nanostructured CaP-coated implants, using real-time RT-PCR, with those of uncoated implants, in a rabbit model. At 2 wks, RTQ values were significantly higher, alkaline phosphatase (ALP) expression was significantly higher, and runt-related transcription factor 2 and tumor necrosis factor-alpha expressions were significantly lower in the coated than in the uncoated implants. This indicates that inflammatory responses were suppressed and osteoprogenitor activity increased around the CaP-coated surface. At 4 wks, although RTQ values did not significantly differ between the 2 groups, ALP and osteocalcin (OCN) were significantly up-regulated in the coated group, indicating progressive mineralization of the bone around the implant. Moreover, an osteoclast marker, adenosine triphosphatase, which indicates acidification of the resorption lacunae, was significantly higher for the coated implants, suggesting gradual resorption of the CaP coating. This study reveals detailed genetic responses to nanostructured CaP-coated implants and provides evidence that the effect of nanotopography is significant during the osseointegration cascade.

Antigenic Activity of Bacterial Endodontic Contents from Primary Root Canal Infection with Periapical Lesions against Macrophage in the Release of Interleukin-1 beta and Tumor Necrosis Factor alpha

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Evaluation of the RB-RB/LB-LB mnemonic rule for recording optimally projected intraoral images of dental implants: an in vitro study

Objective: The aim of this study was to evaluate a simple mnemonic rule (the RB-RB/LB-LB rule) for recording intra-oral radiographs with optimal projection for the control of dental implants.Methods: 30 third-year dental students received a short lesson in the RB-RB/LB-LB mnemonic rule. The rule is as follows: if right blur then raise beam (RB-RB), i.e. if implant threads are blurred at the right side of the implant, the X-ray beam direction must be raised towards the ceiling to obtain sharp threads on both implant sides; if left blur then lower beam (LB-LB), i.e. if implant threads are blurred at the left side of the implant, the X-ray beam direction must be lowered towards the floor to obtain sharp threads on both implant sides. Intra-oral radiographs of four screw-type implants placed with different inclination in a Frasaco upper or lower jaw dental model (Frasaco GmbH, Tettnang, Germany) were recorded. The students were unaware of the inclination of the implants and were instructed to re-expose each implant, implementing the mnemonic rule, until an image of the implant with acceptable quality (subjectively judged by the instructor) was obtained. Subsequently, each radiograph was blindly assessed with respect to sharpness of the implant threads and assigned to one of four quality categories: (1) perfect, (2) not perfect, but clinically acceptable, (3) not acceptable and (4) hopeless.Results: For all implants, from one non-perfect exposure to the following, a higher score was obtained in 64% of the cases, 28% received the same score and 8% obtained a lower score. Only a small variation was observed among exposures of implants with different inclination. on average, two exposures per implant (range: one to eight exposures) were needed to obtain a clinically acceptable image.Conclusion: The RB-RB/LB-LB mnemonic rule for recording intra-oral radiographs of dental implants with a correct projection was easy to implement by inexperienced examiners. Dentomaxillofacial Radiology (2012) 41, 298-304. doi: 10.1259/dmfr/20861598

Implant image quality in dental radiographs recorded using a customized imaging guide or a standard film holder

Objective: To compare a customized imaging guide and a standard film holder for obtaining optimally projected intraoral radiographs of dental implants.Material and methods: Intraoral radiographs of four screw-type implants with different inclination placed in an upper or lower dental phantom model were recorded by 32 groups of examiners after a short instruction in the use of the RB-RB/LB-LB mnemonic rule. Half of the examiners recorded the images using a standard film holder and the other half used a customized imaging guide. Each radiograph was assessed under blinded conditions with regard to rendering of the implant threads and was assigned to one of four quality categories: (1) perfect, (2) not perfect, but clinically acceptable, (3) not acceptable, and (4) hopeless.Results: For the upper jaw, the same number of exposures per implant were made to achieve an acceptable image (P = 0.86) by the standard film holder method (median = 2) and the imaging guide method (median = 2). For the lower jaw, medians for the imaging guide method and the film holder method were 1 and 2, respectively (P = 0.004). For the imaging guide method, the first exposure was rated as perfect/acceptable in 62% of the cases and for the film holder method in 41% of the cases (P = 0.013). After <= 2 exposures, 78% (imaging guide method) and 69% (film holder method) of the implant images were perfect/acceptable (P=0.23). The implant inclination did not have a major influence on the outcomes.Conclusion: Perfect or acceptable images were achieved after two exposures with the same frequency either using a customized imaging guide method or a standard film holder method. However, the use of a customized imaging guide method was overall significantly superior to a standard film holder method in terms of obtaining perfect or acceptable images with only one exposure.

Tumor Necrosis Factor alpha and Interleukin-1 beta Modulate Calcium and Nitric Oxide Signaling in Mechanically Stimulated Osteocytes

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Comparison of Biomaterial Implants in the Dental Socket: Histological Analysis in Dogs

Background:Bone graft procedures have been used commonly in buco-maxillo-facial surgery. For this reason, many researchers have evaluated the bone substitutes.Purpose:The present study evaluated soft and hard tissue reactions to two different hydroxyapatites HAs (synthetic HA and natural HA) and bioactive glass implanted into the sockets immediately after extraction.Materials and Methods:First and third upper and lower premolars, on both sides, were extracted from six female dogs. The alveolar sockets were randomly assigned to four groups: Group 1 - control (unfilled), Group 2 - filled with synthetic hydroxyapatite, Group 3 - filled with bovine bone mineral (natural HA), and Group 4 - filled with bioactive glass. The animals were euthanized at 4 weeks (n = 2), 8 weeks (n = 2), and 28 weeks (n = 2) after extraction. The mandible and maxilla of each animal were removed for histological analysis to determine soft tissue reactions, newly formed bone, bone characteristics, and presence or absence of implanted materials.Results:Most particles of synthetic hydroxyapatite had bone formation on their surface, although some particles showed a layer of fibrous connective tissue. The bovine bone mineral group exhibited particles partially replaced with bone formation. The bioactive glass group showed particles with a thin layer of calcified tissue, but was absent in some specimens, suggesting complete resorption.Conclusion:All biomaterials had similar behavior. Bovine bone mineral, compared to synthetic hydroxyapatite and bioactive glass, showed a larger number of particles covered with osseous tissue. All biomaterials interfered with the socket repair process.