Influência do agente de união na resistência ao cisalhamento da interface titânio/polímero de vidro

There is little information regarding bond strengths of polyglass to metal alloys. This study evaluated the influence of bonding system on shear bond strength of a composite resin (Artglass/Heraeus Kulzer) to cast titanium (Ti). Twenty metallic structures (4mm in diameter, 5mm thick) of titanium grade I were cast shaped and abraded with 250mm aluminum oxide and separated into two groups. For each group was applied one bonding system (Siloc or Retention Flow) before opaque and dentin polymer superposition. This procedure was managed using teflon matrices. They were manipulated and polymerized according to the manufacturer's recommendations. The samples were stored in distilled water for 24 hours at 37º and thermocycled (5º and 55ºC/500 cycles). Shear bond strength tests were performed by using an Instron Universal testing machine at a crosshead speed of 5mm/min. Results were analyzed statistically with one-way ANOVA (a=0,5) and they indicated that the Retention Flow system was statistically better than Siloc (20.74 MPa and 11.65 MPa , respectively). It was possible to conclude that the bonding agent influenced the adhesion between polymer and cast titanium.

Desenvolvimento e caracterização de dispositivos eletroluminescentes contendo uma blenda polimérica condutora e Zn2SiO4:Mn

Despite the great development of organic and polymeric electroluminescent materials, the large scale commercial application of devices made with these materials seems conditioned to specific cases, mainly due to the high cost and the low durability, in compared to conventional technologies. In this study was produced electroluminescent devices by a process simple, drop casting. Were produced electroluminescent films containing Zn2SiO4:Mn immersed in a conductive polymer blend with different thicknesses. The morphological characteristics of these films were studied by scanning electronic microscopy. These films were used in the manufacture of electroluminescent devices, in which the light emission properties of the developed material were evaluated. The blend was composed of the conductive polymer Poly(o-methoxyaniline), doped with p-toluene sulfonic acid, and an insulating polymer, Poly(vinylidene fluoride) and its copolymer Poly(vinylidene fluoride-cotrifluoroethylene). To this blend was added Zn2SiO4:Mn, thereby forming the composite. A first set of devices was obtained using composites with different weight fraction of polymeric and inorganic phases, which were deposited by drop casting over ITO substrates. Upper electrodes of aluminum were deposited by thermal evaporation. The resulting device architecture was a sandwich type structure ITO/ composite/ Al. A second set of devices was obtained as self-sustaining films using the best composite composition obtained for the device of the first set. ITO electrodes were deposited by RF-Sputtering, in both faces of these films. The AC electrical characterization of the devices was made with impedance spectroscopy measurements, and the DC electrical characterization was performed using a source/ meter unit Keithley 2410. The devices light emission was measured using a photodiode coupled to a digital electrometer, Keithley 6517A. The devices electrooptical characterization showed that the...

Estruturas de concreto reforçadas com PRFC parte II: análise dos modelos de cisalhamento

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Caracterização e reciclagem química via pirólise de resíduos da fabricação de pás eólicas

A energia eólica é uma forma de energia que seu uso encontra-se em expansão, e junto a esse crescimento, tem-se também o aumento da quantidade de resíduos gerados na fabricação das pás eólicas. Uma forma correta de destinação e aproveitamento desses resíduos é a reciclagem. Porém, esses são constituídos de materiais compósitos, geralmente a resina epóxi e a fibra de vidro; e por possuírem um polímero termofixo (a resina epóxi) na sua composição, a reciclagem convencional via fusão não é possível. Desta forma, a reciclagem química via pirólise apresenta-se como uma alternativa para o aproveitamento desses resíduos, em especial da fibra de vidro que o contém. Após caracterização do resíduo de uma indústria de pás eólicas, verificou-se que se tratava de um material com mais de 70% de fibra de vidro e muito densas. Foram realizados ensaios de pirólise a seco e com óleo de babaçu, considerado o mais interessante perante vários possíveis e no qual o resíduo fica totalmente imerso, facilitando o inchamento e a troca de calor. Em um sistema de aquecimento com vácuo, foram obtidas mais de 97% de fibras em 30 minutos a 310 oC, justamente a temperatura em que uma análise termogravimétrica apontou ser a de início de altas taxas de degradação térmica.

Saberes docentes, sistema de avaliação de rendimento escolar do Estado de São Paulo e ensino de Ciências: um estudo de caso a partir de situações de ensino-aprendizagem

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Efeito de diferentes cargas orgânicas em cimentos resinosos experimentais

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Obtenção de nanofibras de carbono a partir do processo de eletrofiação

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Novos materiais multifuncionais para aplicação em fotocatálise

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Síntese, caracterização e aplicação de hidrogéis nanoestruturados contendo nanoargila para melhorar a germinação e qualidade de muda de hortaliça

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Morfofisiologia de rastros branquiais de Prochilodus lineatus (Curimbatá) criados em ambientes perturbados

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Morfofisiologia de rastros branquiais de Prochilodus lineatus (Curimbatá) criados em ambientes perturbados

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Avaliação da mucosa sinusal do coelho à presença de implante biodegradável

Pensando em melhorar a qualidade de vida dos pacientes com doenças do humor vítreo, os oftalmologistas começaram a utilizar recentemente implantes biodegradáveis com corticoide. Estes mesmos implantes podem ser uma alternativa no tratamento da RSC e, para isso, realizamos um estudo experimental em seios maxilares de coelhos. OBJETIVO: Avaliar histologicamente a mucosa de seio maxilar de coelhos após a colocação de implante biodegradável de prednisolona. MÉTODO: Dezoito coelhos foram divididos aleatoriamente em dois grupos: Grupo 1: no seio maxilar esquerdo foi inserido um implante biodegradável com prednisolona; Grupo 2: No seio maxilar esquerdo foi inserido um implante biodegradável sem medicação. Os seios maxilares do lado direito serviram como controle. Após 7, 14 e 28 dias foram escolhidos aleatoriamente três coelhos de cada grupo e a resposta tecidual inflamatória foi avaliada. RESULTADOS: Foi encontrada diferença não significativa de inflamação na mucosa, quando comparamos o grupo de coelhos que receberam implantes com e sem medicação com o grupo controle; ou quando comparamos o grupo que recebeu implante com prednisolona com o grupo que recebeu implante sem medicação. CONCLUSÃO: Não foram observados sinais de toxicidade ou inflamação na mucosa do seio maxilar do coelho à presença do implante com ou sem prednisolona.

Characterization and use of swine deep bedding ashes in cementitious composites

The deep bedding is a swine alternative production, especially in the finishing phase, whose byproduct can be recycled, reducing the environmental impact. The objectives of this study were to characterize the ash coming from the controlled burning of the swine deep bedding (SDBA) based on rice husk, and to evaluate their performance in composites as a partial substitute for Portland cement (PC). To measure the differences between SDBA and rice husk ash (RHA) as a reference, we have characterized: particle size distribution, real specific density, x-ray diffraction, electrical conductivity, scanning electron microscopy, chemical analysis and loss on ignition. Samples were prepared for two experimental series: control, and another one with the partial replacement of 30% of SDBA in relation to the mass of the Portland cement. According to the results obtained for physical and mechanical characterization, the composites with SDBA can be used as a constructive element in the rural construction.

Caracterização da farinha e do amido isolado da semente de jaca e comportamento reológico de dispersões de amido

O amido é um ingrediente com grande versatilidade de aplicação, e as sementes de jaca, fruto bem difundido, porém pouco aproveitado no Brasil, contêm uma quantidade considerável de amido, sendo ainda fonte de ferro e proteínas. Dessa maneira, os objetivos desse projeto foram a obtenção da farinha de sementes de jaca das variedades mole e dura, a extração do amido utilizando diferentes solventes, e a caracterização de suas propriedades físico-químicas, estruturais e funcionais, bem como a caracterização reológica de dispersões/géis de amido em cisalhamento estacionário e oscilatório. A extração alcalina do amido, além de reduzir significativamente o conteúdo de lipídeos e proteínas, deixando o amido mais puro, promoveu um aumento no teor de amilose e influenciou diretamente as características de inchamento e solubilidade, que apresentaram aumento significativo a partir da temperatura de 70 °C. O aumento da temperatura ocasionou aumento no poder de inchamento e solubilidade, que foi mais pronunciado para a variedade dura, porém esses valores ainda foram considerados baixos (< 17%). Os amidos de sementes de jaca apresentaram grânulos lisos, arredondados e em forma de sino, com formato mais truncado para o amido extraído com hidróxido de sódio. O diâmetro médio dos grânulos de amido foi menor para a extração alcalina, mas sempre com comportamento monomodal. Foi observado um padrão de difração de Raios-X do tipo A para todas as amostras estudadas, e o índice de cristalinidade foi maior para os amidos de sementes de jaca dura, com uma redução estimada em 70% para os amidos obtidos por extração alcalina. A temperatura de gelatinização dos amidos de semente de jaca foi considerada alta (70-100 °C). Os amidos de sementes de jaca dura obtidos na extração com água apresentaram maiores valores de viscosidade de pico e de Breakdown, que representa menor resistência mecânica. A extração com solução de NaOH 0,1 M aumentou a tendência a retrogradação de ~36% (extração aquosa) para 64% e 45% dos amidos de sementes de jaca das variedades mole e dura, respectivamente. Todas as amostras apresentaram comportamento pseudoplástico (n < 1) nas concentrações e temperaturas estudadas, e as dispersões e/ou géis de amido obtidos pela extração alcalina com NaOH apresentaram menor tixotropia e maiores valores de viscosidade. Os modelos Lei da Potência e Herschel Bulkley apresentaram ótimos ajustes aos pontos experimentais (R² ~0,998) para as amostras com 2 e 6 % de amido, respectivamente, porém para a concentração de 5%, o melhor modelo foi função da variedade do fruto usado na obtenção do amido. A dependência das propriedades reológicas com a temperatura foi analisada pela equação de Arrhenius e a energia de ativação foi baixa (15-25 kJ/mol). Quanto ao comportamento viscoelástico, as amostras com 5 e 6% de amido apresentaram comportamento de gel fraco e o aumento da concentração desse polissacarídeo produziu um aumento na elasticidade do material. Os módulos de armazenamento (G\') associados à elasticidade do gel de amido aumentaram durante o seu resfriamento nos ensaios de varredura de temperatura, o que pode ser relacionado à recristalização da amilose durante esse processo e mantiveram-se praticamente constantes no aquecimento isotérmico a 80 °C, sugerindo boa estabilidade térmica do gel. A farinha isolada da semente de jaca pode ser considerada fonte de fibras e apresentou elevados teores de proteínas (~14-16%) e ferro (~85-150 mg/kg). A distribuição do tamanho de partículas da farinha apresentou comportamento bimodal, com grânulos arredondados, presença de fibras e uma matriz proteica envolvendo os grânulos de amido. As propriedades de pasta revelaram maior pico de viscosidade para a farinha de semente de jaca mole. As características encontradas sugerem que os amidos de semente de jaca poderiam ser aplicados na produção de filmes biodegradáveis, e a farinha da semente de jaca poderia ser utilizada em substituição parcial à farinha convencional na fabricação de bolos e biscoitos.

Resposta imune do antígeno de superfície de hepatite B administrado via nasal em nanopartículas de quitosana liofilizadas

A nanotecnologia tornou possível estruturar nanopartículas (NPs), utilizando-se polímeros biodegradáveis e atóxicos, como a quitosana (QS) - capaz de carrear e disponibilizar antígenos para a mucosa, devido sua propriedade mucoadesiva. Uma vacina liofilizada, em comparação a uma formulação líquida, possui inúmeras vantagens, tais como melhora na estabilidade do produto e melhor resistência às variações de temperatura, aumentando sua vida de prateleira e possibilitando melhor logística do produto aos locais onde o acesso à rede refrigerada é difícil; ademais, um produto liofilizado tem sua mucoadesividade aumentada, possibilitando maior tempo de permanência na mucosa. O presente trabalho teve como objetivo observar a resposta imune, em camundongos, de uma vacina desenvolvida por um mecanismo de entrega intranasal do HBsAg (Antígeno de superfície da Hepatite B) encapsulado pelo método de incorporação em nanopartículas de quitosana (NPs) liofilizadas. A formação das NPs foi realizada pela interação eletroestática da quitosana e do TPP (tripolifosfato de sódio), utilizando método de geleificação iônica. Formulações de NPs com glicina 5% apresentaram boas características após reconstituição, umidade residual inferior a 1% e processo de liofilização de 13 horas. Foi avaliada a imunogenicidade da inoculação do HBsAg em formulações de NPs de quitosana líquida e liofilizada, verificando-se que a forma líquida produziu anticorpos IgG contra HBsAg.