Effect of Ce and MgO on NO decomposition over La1-x-Ce-x-Sr-Ni-O/MgO

Ce and MgO were added simultaneously to La-Sr-Ni-O catalyst and a substantial enhancement of activity for NO decomposition was observed, which may be attributed to the formation of a new highly active site caused by the addition of Ce and MgO.

Cyanex923-H_2SO_4体系萃取第3相的形成和应用

考察了Cyanex 92 3 H2 SO4体系中稀释剂、萃取剂浓度、温度等对形成萃取第 3相的影响以及三相体系中的相行为 ,发现直链烷烃稀释剂的碳链越长体系越易出现第 3相 ,而稀释剂越易极化 ,体系越难形成第3相 ;萃取剂浓度和体系温度升高不利于出现第 3相 ,且萃取剂富集在第 3相中 ;利用形成的三相体系对萃取剂Cyanex 92 3进行了纯化。

VUV excited luminescence of europium activated calcium borophosphate prepared in air

XAFS (EXAFS and XANES) at Eu-L-3 edge were used to determine the local structure and the valences of europium in CaBPO5:Eu prepared in air. The results of EXAFS showed that the doped europium atoms were nine-coordinated by oxygen atoms and the distances of bond Eu-O were 2.39 Angstrom in the host lattice. XANES at Eu-L-3 edge exhibited that Eu2+ and Eu3+ coexisted in the matrix. The luminescent spectrum of the material excited by VUV at 147 nm presented a similar spectrum with that excited by f-f transition of Eu2+ at 396 nm and f-d transition of Eu2+ at 312 nm. The broad emission band due to both 4f(6)5d - 4f(7) transition of EU2+ and f - f transition of Eu3+ could be observed in emission spectra, which indicated that the trivalent europium ions were reduced in air in the matrix at high temperature by the defects [V-Cn]" formed by aliovalent substitution between Ca2+ and Eu3+ ions. The UV excitation spectrum showed the typical f-f transition of Eu3+ and f-d transition of Eu2+. The bands with the maxima at about 113 and 158 nm in VUV excitation spectrum were assigned to originate from the absorption of the host lattice.

Study of color centers and trace oxygen in KMgF3 : Eu single crystal

Using the Bridgeman-Stockbarger method, the KMgF3:EU2+ single crystal was grown. The color centers in unirradiated KMgF3:Eu crystal were studied. By thermal annealing, we confirmed the 422-nm emission resulted from color centers and oxygen centers, and we proved the energy transfer from EU2+ to color centers. From spectra, the relative oxygen content in crystal was calculated, and the relationships of oxygen displacing fluorine were studied.

Studies on the adduct reaction of disubstituted benzenes with ion system of acetone in gas phase

Ion - molecule reactions of disubstituted benzene with ion system of acetone and deuterium - labelled acetone under chemical ionization conditions were examined and the fragmentation reactions of the adduct ions formed by the ion - molecule reactions were studied using collision - induced dissociation (CID) technique. It was found that the electron - releasing groups favored the adduct reactions, whereas the electron - withdrawing groups did not. The position and properties of substituted groups affected the relative abundance of the adduct ions. The fragmentation reaction of the adduct ion formed by ortho - phenylenediamine with acetyl ion was similar to the reductive alkylation reaction of amine in condensed phase.

Charge transport in a blue-emitting alternating block copolymer with a small spacer to conjugated segment length ratio

We analyze current versus voltage data obtained using single carrier injection in several metal/polymer/metal sandwich structures. The polymer used in each case is a soluble blue-emitting alternating block copolymer. Our experimental results demonstrate that the electron transport is space-charge limited by the high density of traps having an exponential energy distribution (temperature dependent characteristic energy) in the copolymer. The electron mobility of 8x10(-10) cm(2)/V s is directly determined using space-charge-limited current analytical expressions. Hole transport is also space-charge limited, with a mobility of 2x10(-6) cm(2)/V s. A hole trap with energy 0.17 eV is observed. We compare these results with those obtained for related block copolymers with different spacer and conjugated segment lengths and discuss the influence of spacer length and conjugated segment length on the charge transport properties. (C) 2000 American Institute of Physics. [S0021-8979(00)04501-1].

气相中双取代苯在丙酮离子体系中的加合反应研究

研究了11组双取代苯在丙酮离子体系中的离子-分子反应特性及加合离子的碎裂反应特性,发现推电子基有利于加合反应的发生而吸电子基不利于加合反应的发生.双取代异构体的加合产物相对强度可以反映出它们取代基的位置及其性质的差异.邻苯二胺与乙酰基离子形成的加合离子在碎裂反应过程中可以发生与液相中胺的还原烷基化反应相类似的碎裂反应.

Synthesis and characterization of aromatic dianhydrides and polyesterimides derived from 4-hydroxyphthalic anhydride

4-Hydroxyphthalic anhydride, prepared from 4-chlorophthalic anhydride, was reacted with trimellitic anhydride monoacid chloride or arylene diacid chloride to give aromatic ester-containing dianhydrides (EDAs). These dianhydrides were characterized by element analysis, melt point, FTIR and H-1-NMR. A series of aromatic poly (amic ester acid)s was synthesized by polycondensation of these EDAs and various diamines in polar organic solvent. The inherent viscosity of poly (amic ester acid)s ranged from 0.55 to 0.89 dL/g, indicating the intermediate to higher molecular weight. Polyesterimides having glass transition temperatures between 184-219degreesC were produced by thermal imidization of corresponding poly (amic ester acid)s. These polymers were fairly resistant to organic solvent, but some of them were soluble in phenol solvents. Thermogravimetric analyses revealed that these polyesterimides were stable up to 400degreesC, and the 5% weight loss temperatures were recorded in the range of 432-483degreesC in air atmosphers and 451-490degreesC in nitrogen.

Effect of FePc structure on the activity in the oxidation of cyclohexene catalyzed by pd (OAc)(2)/HQ/FePc

In an acidic aqueous solution of acetonitrile, the catalytic activity of the catalysts consisted of Pd(OAc)(2)/hydroquinone(HQ) with iron phthalocyanine (FePc) from various sources was obviously different in the oxidation of cyclohexene to cyclohexanone, The analysis of the FePc using IR spectroscopy, Mossbauer spectroscopy, X-ray photoelectron spectroscopy (XPS), X-ray powder diffraction (XRD), scanning electron microscopy(SEM) and BET surface area measurement indicated that the catalytic activity of the multicomponent catalytic system composed of iron phthalocyanines depends on the amount of mu -oxo FePc, the crystallinity and the surface structure of iron phthalocyanine.

Preparation of poly(4-vinylpyridine)/silica hybrids supported cyclopentadienyltitanium trichloride (CpTiCl3) catalyst and styrene polymerization

Poly(4 - vinylpyridine)/silica( PVP/SiO2) organic - inorganic nanoscale hybrid was prepared using sol - gel method, in which PVP was used as an organic component and TEOS as a SiO2 precusor, This hybrid was used as CpTiCl3 support. The XPS and IR measurements showed that two kinds of catalytic active site were formed through analyzing the interaction mode between support and CpTiCl3. The results of styrene polymerization showed that syndiotactic was the highest at 50 degreesC. The catalytic activity was 1.09 x 10(6) g PS/ (mol Ti . h) at 70 degreesC when n(Al)/n(Ti) = 1500. GPC results showed a bimodal molecular weight distribution.

FePc结构对Pd(OAc)_2/HQ/FePc催化环己烯氧化活性的影响

在乙腈酸性水溶液中 ,不同来源酞菁铁 (FePc)和 Pd(OAc)2/HQ（氢醌）组成的催化体系在环己烯氧化反应中有明显不同的催化活性 .通过 IR、 M ssbauer、 XPS、 XRD、 SEM、 BET等技术对酞菁铁的分析表明 ,由酞菁铁组成的多组份催化体系的催化活性与酞菁铁中的μ-氧酞菁铁含量、酞菁铁结晶度和表面形态有关.

主链含有β-二酮结构聚酰亚胺的合成与表征

采用传统的“二步法”合成了5种主链含有β-二酮结构的聚酰亚胺（PI）.所得聚酰酸（PAA）的特性粘度值在0.31～1.00dL／g之间、热分析结果给出5种PI的玻璃化转变温度在296～312℃之间,10％热失重温度均在428℃以上.

Synthesis and characterization of poly(amide imide)s containing cyclohexylidene moieties with bulky substituents

Novel poly(amide imide)s (PAI) containing alkyl-substituted cyclohexylidene moieties were synthesized by conventional polycondensation of trimellitic anhydride chloride with novel aromatic diamines followed by chemical imidization using acetic anhydride and pyridine. The inherent viscosities of the resulting PAIs are relatively high and range from 71 to 112 mt g(-1). The prepared PAIs show excellent thermal stability and good solubility. The glass transition temperatures (T-g) measured by DSC are observed in the range of 312-342 degrees C. Furthermore, all the polymers are readily soluble in less hygroscopic organic solvents like cyclohexanone, gamma-butyrolactone as well as aprotic polar solvents.

The reduction of Eu3+ in SrB6O10 prepared in air and the luminescence of SrB6O10 : Eu

The reduction of Eu3+ to Eu2+ in SrB6O10 prepared in air by a high-temperature solid state reaction was studied. The luminescent properties of Eu2+ in this matrix show f-d broad band emission peaking at about 386 and 432 nm at room temperature. A charge compensation mechanism is proposed as a possible explanation. The luminescence of Eu3+ with f-f transitions was studied in this sample and reflected that the Eu3+ ion occupied a site with non-centro-symmetry. The ESR spectrum was used to detect the existence of Eu2+ in the samples. (C) 1998 Elsevier Science S.A.

Transport property of polyaniline and its molecular weight dependence

The electrical conductivity of polyaniline doped with camphor sulfonic acid (PAn-CSA) was studied. The results indicate that there is a critical temperature (T-c) and the temperature dependence of PAn-CSA conductivity shows metallic and semiconductor characteristics above and below T-c, respectively. The higher the molecular weight of PAn, the lower the T-c. The conductivity was enhanced remarkably when PAn-CSA film was stretched, its room temperature conductivity is up to 750 S/cm when elogonation is 60%; however, T-c was independent of elongation.