Hybrid permeable metal-base transistor with large common-emitter current gain and low operational voltage

We demonstrate the suitability of N,N'-diphenyl-N,N'-bis(1-naphthylphenyl)-1,1'-biphenyl-4,4'-diamine (NPB), an organic semiconductor widely used in organic light-emitting diodes (OLEDs), for high-gain, low operational voltage nanostructured vertical-architecture transistors, which operate as permeable-base transistors. By introducing vanadium oxide (V2O5) between the injecting metal and NPB layer at the transistor emitter, we reduced the emitter operational voltage.

Self-assembly of a hydrophobic polypeptide containing a short hydrophilic middle segment: Vesicles to large compound micelles

This report describes a facile route to prepare the vesicles and large compound micelles (LCMs) from a series of poly(epsilon-benzyloxycarbonyl L-lysine)-block-poly[diethylene glycol bis(3-amino propyl) ether]-block-poly(epsilon-benzyloxycarbonyl L-lySine) (PZLL-DGBE-PZLL) in their water solution, depending on molecular weight of the polypeptides. A pyrene probe is used to demonstrate the aggregate formation of PZLL-DGBE-PZLL in solution, and also to measure their critical micelle concentration as a function of molecular weight of the polymer.

草乌与诃子配伍前后醚提液中生物碱类成分的质谱研究

ESI-MS was adopted to detect the difference of alkaloids compounds between root of Kusnezoffii Monkshood(RKM) and the compatibility of RKM and Fructus Chebulae(FC). Contrast to the diethyl ether extract of RKM, the relative abundance of diester-alkaloids decreased significantly when Fructus Chebulae was added, whereas it of lipo-alkaloids increased markedly. The results indicated that the acid components of Fructus Chebulae reduced the dissolvability of diester-alkaloids in diethyl ether

Novel Sulfonated Polyimide Ionomers by Incorporating Pyridine Functional Group in the Polymer Backbone

A series of sulfonated polyimides (SPIs) containing pyridine ring in the polymer backbone were synthesized by the polycondensation of 1,4,5,8-naphthalene-tetracarboxylic dianhydride (NTDA), 5-(2,6-bis(4-arninophenyl)pyridin-4-yl)-2-methoxy benzene sulfonic acid (SDAM), and 4,4'-diaminodiphenyl ether (ODA). Flexible, transparent, and tough membranes were obtained. Property study revealed that all the membranes displayed high thermal stability with the desulfonation and decomposition temperature higher than 290 and 540 degrees C, respectively, as well as good mechanical property with Young's modulus larger than 1.0 GPa, maximum strength (MS) on a scale of 60-80 MPa, and elongation at break (EB) ranged from 41.79 to 75.17%.

Syndiotactically enriched 1,2-selective polymerization of 1,3-butadiene initiated by iron catalysts based on a new class of donors

A series of phosphoryl (P=O) contained compounds: triethylphosphate (a), diethyl phenyl phosphate (b), ethyldiphenylphosphate (c) triarylphosphates (d and h-m), triphenylphosphine oxide (e), phenyl diphenylphosphinate (f) and diphenyl phenylphosphonate (g) have been prepared. Iron catalysts, which are generated in situ by mixing the compounds with Fe(2-EHA)(3) and (AlBu3)-Bu-i in hexane, are tested for butadiene polymerization at 50 degrees C. Phosphates donated catalysts have been, unprecedently, found to conduct extremely high syndiotactically (pentad, rrrr=46.1-94.5%) enriched 1,2-selective (1,2-structure content=56.2-94.3%) polymerization of butadiene.

Synthesis, photoluminescence, and theoretical studies of novel Cu(I) complex

A novel diimine Cu(I)complex [Cu(ABPQ)(DPEphos)]BF4 [ABPQ and DPEphos are acenaphtho[1,2-b]bipyrido[2,3-h:3,2-f]quinoxaline and bis(2-(diphenylphosphanyl)phenyl) ether, respectively] is synthesized, and its photophysical properties are experimentally and theoretically characterized. The emission bands centered at ca. 400/470 and 550 nm of [Cu(ABPQ)(DPEphos)]BF4 are attributed to the ligand-centered pi -> pi* transition and the metal-to-ligand charge transfer d pi(Cu) -> pi*(N-N) transition, respectively. The luminescence quantum yield of [Cu(ABPQ)(DPEphos)]BF4 in CHCl3 is found to be about five times higher than that of [Cu(Phen)(DPEphos)]BF4.

Simulation of Banded Spherulite Patterns by Coupled Logistic Map Lattice Model in Three Dimensions

Banded spherulite patterns are simulated in three dimensions by means of a Coupled Logistic map lattice model. The patterns obtained by numerical calculation are consistent with those in experiments. The simulation results also indicate that the hand spacing is decreased with the increase of parameter mu in the Logistic map and increased with the increase of the coupling parameter e for cube lattices, and increased with the increase of the thickness of the lattice for polymer film, which is quite similar to the results in some experiments. Spiral pattern in three dimensions is also shown in this paper, which helps us understand the form of banded spherulite in polymers.

Five supramolecular compounds of water-soluble sulfonylcalix[4]arenetetrasulfonate showing two calixarene conformations

Five new compounds of sulfonylcalix[4]arenetetrasulfonate (SC4AS), [H7Na(H2O)(3)(SC4AS)(phen)(5)](H2O)(11.9) (1), [H6Mn(H2O)(4)(SC4AS)(phen)(5)] (H2O)(12.7) (2), [Cu-4(SC4AS) (phen)(6)] (H2O)(4.5) (3), {[Cu (2)(SC4AS) (bpy)(2)][Cu(bpy)(2)(H2O)](2)} (H2O)(6.6) (4), and {[Zn-2(SC4AS) (phen)(2)][Zn(phen)(2)(H2O)(2)](2)} (H2O)(7) (5) (where phen 1,10-phenanthroline and bpy = 2,2'-bipyridine), were synthesized by a hydrothermal method and structurally determined by single crystal X-ray diffraction. The SC4AS ligand adopts partial cone conformation in compounds 1 and 2 and 1,2-alternate form in compounds 3-5. According to the structural analysis and density functional theory (DFT) calculations, we suggest that the metal can affect the conformation of SC4AS.

Synthesis and properties of soluble poly[bis(benzimidazobenzisoquinolinones)] based on novel aromatic tetraamine monomers

Four aromatic tetraamine monomers possessing flexible ether linkages were successfully synthesized by nucleophilic aromatic substitution of hydroquinone, 4,4'-dihydroxybiphenyl, 2,2'-bis(4-hydroxyphenyl)propane, and 2,7-dihydroxynaphthalene with 5-chloro-2-nitroaniline, followed by reduction, respectively. With these monomers, a new class of soluble poly[ bis(benzimidazobenzisoquinolinones)] was prepared by a one-step, high-temperature solution polycondensation. The resulting polymers were completely soluble in phenolic solvents and had high inherent viscosities ranging from 1.2 to 1.5 g dL(-1). These polymers had glass transition temperatures in the range of 427-449 degrees C. Thermogravimetric analysis showed that all polymers were thermally stable, with 5% weight loss recorded above 510 degrees C in nitrogen.

Novel hydrophilic-hydrophobic multiblock copolyimides as proton exchange membranes: Enhancing the proton conductivity

A series of novel multiblock copolymers based on sulfonated copolyimides were developed and evaluated for use as proton exchange membranes (PEMs). In these multiblock copolyimides, the hydrophilic blocks were composed of the sulfonated dianhydride and the sulfonated diamine, with sulfonic acid groups on every aromatic ring (i.e., fully sulfonated). This molecular design was implemented to effectively enhance the proton conductivity. The properties of the multiblock copolyimides with varying IEC values or block lengths were investigated to obtain a better understanding of the relationship between molecular structure and properties of proton exchange membranes. The water uptake and proton conductivity were found to be highly dependent upon their structure. The block copolymers displayed significantly higher proton conductivities, especially at low relative humidity than the random copolymers with a similar IEC.

Blends based on sulfonated poly[bis(benzimidazobenzisoquinolinones)] and poly(vinylidene fluoride) for polymer electrolyte membrane fuel cell

A new blend system consisting of an amorphous sulfonated poly[bis(benzimidazobenzisoquinolinones)] (SPBIBI) and the semi-crystalline poly(vinylidene fluoride) (PVDF) was prepared for proton exchange membranes. The miscibility behavior of a series of blends of SPBIBI with PVDF at various weight ratios was studied by WXRD, DSC and FTIR. The properties of the blend membranes were investigated, and it was found that the introduction of PVDF in the SPBIBI matrix altered the morphological structure of the blend membranes, which led to the formation of improved connectivity channels. For instance, the conductivity of the blend membrane containing 10 wt% PVDF displayed the highest proton conductivity (i.e., 0.086 S cm(-1)) at room temperature, a value almost twofold that of the pristine SPBIBI membranes (i.e., 0.054S cm(-1)) under identical conditions.

Novel proton exchange membranes based on water resistant sulfonated poly[bis(benzimidazobenzisoquinolinones)]

Novel water resistant sulfonated poly[bis(benzimidazobenzisoquinolinones)] (SPBIBIs) were synthesized from 6,6'-disulfonic-4,4'-binaphthy]-1,1',8,8'-tetracarboxylic dianhydride (SBTDA) and various aromatic ether tetraamines. The resulting polymers with IEC in the range of 2.17-2.87 mequiv g(-1) have a combination of desired properties such as high solubility in common organic solvents, film-forming ability, and excellent thermal and mechanical properties. Flexible and tough membranes, obtained by casting from m-cresol solution, had tensile strength, elongation at break, and tensile modulus values in the range of 87.6-98.4 MPa, 35.8-52.8%, and 0.94-1.07 GPa. SPBIBI membranes with a high degree of sulfonation displayed high proton conductivity and a good resistance to water swelling as well. SPBIBI-b with IEC of 2.80 mequiv g(-1) displayed the conductivity of 1.74 x 10(-1) S cm(-1) at 100 degrees C, which was comparable to that of Nafion (R) 117 (1.78 x 10(-1) S cm(-1), at 100 degrees C).

Implantation of Nafion (R) ionomer into polyvinyl alcohol/chitosan composites to form novel proton-conducting membranes for direct methanol fuel cells

A series of cost-effective, proton-conducting composite membranes, comprising of Nafion (R) ionomer, chitosan (CS). and polyvinyl alcohol (PVA), is successfully prepared. By taking advantage of the strong electrostatic interactions between Nafion (R) ionomer and CS component, Nafion ionomer is effectively implanted into the PVA/CS composite membranes, and improves proton conductivity of the PVA/CS composite membranes. Furthermore, this effect dramatically depends on the composition ratio of PVA/CS, and the optimum conductivity is obtained at the PVA/CS ratio of 1:1. The developed composite membranes exhibit much lower methanol permeability compared with the widely used Nafion (R) membrane, indicating that these novel membranes have great potential for direct methanol fuel cells (DMFCs).

High proton conductive advanced hybrid membrane based on sulfonated Si-SBA-15

Composite membranes based on Sulfonated poly(ether ether ketone) (SPEEK) and sulfonated organically modified Si-SBA-15 (S-SBA-15) were investigated with the purpose of increasing the proton conductivity. The novelty of the composite membranes was attributed to two special structures and different ion exchange capacities (IEC) of S-SBA-15 fillers, which were embedded in membranes. The typical hexagonal channels array of S-SBA-15 was confirmed by XRD and TEM. The regular vermiculate and amorphous structures of the inorganic fillers were proved by SEM. Composite membranes were prepared through common solvent casting method. SEM images indicated that the inorganic filler with regular structure dispersed homogeneously in the composite membranes, but the amorphous filler caused an agglomeration phenomenon at the same loading content.

Highly conductive, methanol resistant fuel cell membranes fabricated by layer-by-layer self-assembly of inorganic heteropolyacid

Layer-by-layer (LBL) self-assembly is a simple and elegant method of constructing organic-inorganic composite thin films from environmentally benign aqueous solutions. In this paper, we utilize this method to develop proton-exchange membranes for fuel cells. The multilayer film is constructed onto the surface of sulfonated poly(arylene ether ketone) (SPAEK-COOH) membrane by LBL self-assembly of polycation chitosan (CTS) and negatively charged inorganic particle phosphotungstic acid (VIA). The highly conductive inorganic nanoparticles ensure SPAEK-COOH-(CTS/PTA)(n) membranes to maintain high proton conductivity values up to 0.086 S cm(-1) at 25 degrees C and 0.24S cm(-1) at 80 degrees C, which are superior than previous LBL assembled electrolyte systems.