Production of Iron-Tin Compacts by Powder Metallurgy and a Synopsis of their Principle Properties

This thesis is concerned primarily with the production of metal powder compacts of iron and tin. In producing these compacts, the effects of process­ing variables on some of the essential properties of the pellets made were investigated.

The Corrosion Resistance of Iron-Tin Compacts as Produced by Powder Metallurgy

The art of Powder Metallurgy deals with the preparation of metal powders and their utilization. As a more pertinent definition, the following has been suggest­ed: "Powder Metallurgy is the art of producing metal powders and shaped objects from individual, mixed, or alloyed metal powders, with or without the inclusion of non-metallic consti­tuents".

Corrosion Testing of Iron-Tin Alloys by the Salt Spray Method

The purpose of this study was to determine the rela­tive rate of corrosion of iron-tin alloys containing low percentages of tin. Since in the world today, a great deal of work is being done to develop large tin deposits and new methods devised to treat these ores, it is possible that the metal will become abundant and will obtain a more important position in the metal industry.

A Study of the Physical Properties of Low Tin Solders

In 1947, out of the 100,000 long tons of tin con­sumed in the United States, 25,000 tons went into solder. Tin plate took 39,000 tons while babbit, bronze and coll­apsible tubes accounted for approximately 17,000 tons. Solder ranked second to tin plate and required more than the next three major uses combined.

Looking at Chemistry in Hard to See Places: Understanding Energy Conversion at 1400° Celsius

Solid oxide fuel cells (SOFCs) are promising devices for stationary and portable power and heat generation, because they can use complex fuels such as hydro-carbons, CO, and alcohols. Extreme, non-equilibrium conditions and high tem-peratures (≥ 700 ˚C) required for SOFC operation hamper efforts to understand the mechanisms of component degradation in SOFCs. This talk focuses on new insights into SOFC chemistry and the conversion of carbon-containing fuels (both hydrocarbons and oxygenated) into electricity, carbon dioxide and water, gleaned from a combination of techniques including electrochemical impedance spectroscopy, voltammetry, and vibrational Raman scattering.

A Study of the Transformation of a Twenty-Eight Per Cent Tin Bronze

In this investigation, attention is directed to the phases covered by a 28 per cent tin alloy. When the investigation was started, consideration was given to the possibility of making a Time - Temperature - Transformation curve for this parti­cular alloy. As the work progressed and further research was carried on, this phase of the work was abandoned.

Tin-containing fluoride solutions as anti-erosive agents in enamel: an in vitro tin-uptake, tissue-loss, and scanning electron micrograph study

Tin-containing fluoride solutions can reduce erosive tissue loss, but the effects of the reaction between tin and enamel are still not clear. During a 10-d period, enamel specimens were cyclically demineralized (0.05 M citric acid, pH 2.3, 6 x 5 min d(-1)) and remineralized (between the demineralization cycles and overnight). In the negative-control group, no further treatment was performed. Three groups were treated (2 x 2 min d(-1)) with tin-containing fluoride solutions (400, 1,400 or 2,100 ppm Sn2+, all 1,500 ppm F-, pH 4.5). Three additional groups were treated with test solutions twice daily, but without demineralization. Tissue loss was determined profilometrically. Energy-dispersive X-ray spectroscopy was used to measure the tin content on and within three layers (10 mum each) beneath the surface. In addition, scanning electron microscopy was conducted. All test preparations significantly reduced tissue loss. Deposition of tin on surfaces was higher without erosion than with erosion, but no incorporation of tin into enamel was found without demineralization. Under erosive conditions, both highly concentrated solutions led to the incorporation of tin up to a depth of 20 mum; the less-concentrated solution led to small amounts of tin in the outer 10 mum. The efficacy of tin-containing solutions seems to depend mainly on the incorporation of tin into enamel.

Convenient synthesis of substituted α-methylene--valerolactones in aqueous medium using Baylis-Hillman chemistry

A mild and convenient synthesis of substituted α-methylene--valerolactones was achieved by SN2 nucleophilic substitution of the acetates of the Baylis-Hillman adducts with acetyl acetone followed by one-pot saponification of the ester, reduction of the keto group and subsequent intramolecular ring closure in aqueous medium.

An alternate approach to quinoline architecture via Baylis-Hillman chemistry: SnCl2-mediated tandem reaction toward synthesis of 4-(substituted vinyl)-quinolines

An alternate approach to densely substituted quinolines from the products of SN2 nucleophilic substitution reaction between the acetyl derivatives of the Baylis-Hillman adducts obtained from 2-nitrobenzaldehydes and the carbonyl group containing carbon nucleophiles is described. Treatment of these compounds with SnCl2, trigger a tandem reaction wherein reduction of the nitro group is followed by a remarkably regioselective intramolecular cyclization and subsequent dehydrogenation to afford 4-(substituted vinyl)-quinolines.