Melt crystallization of poly(ether ether ketone ketone) under strong electric field

In this paper, melt crystallization of poly(ether ether ketone ketone) (PEEKK) under strong electric field was investigated. In the crystal structure of PEEKK, the length of c axis was found to he 1.075 nm, increasing by 7% compared to that of PEEKK crystallized without strong electric field. The molecule chains might take a more extended conformation through the opening of the bridge bond angles by increasing from 124 degrees to 144 degrees under strong electric field in the crystal structure.

Photoluminescent properties of dye-doped poly(N-vinyleabzole) (PVK) in microcavity

A surface emitting microcavity was formed by sandwiching a polymer film containing poly(N-vinyleabzole) (PVK). 8-hydroxyquinoline aluminium (Alq(3)) and 4-(Dicyanome thylene)-2-methyl-6-(4-dimethylaminostyryl)-4H-Pyran(DCM) between a distributed Bragg reflector (DBR) with a reflectivity of 99% and a silver film. The sample was optically pumped with 250 ps pulses at 2 Hz repetition rate by a 355 nm line of the third harmonic of a mode-lock Nd:YAG laser. The lasing phenomenon was observed in DCM-doped PVK microcavity. The full width at half maximum (FWHM) was 3 nm with the peak wavelength at 602 nm. The threshold energy for lasing was estimated to be about 3 mu J. (C) 2000 Elsevier Science S.A. All rights reserved.

Gas and water vapor transport through a series of novel poly(aryl ether sulfone) membranes

The permeation behavior of water vapor, H-2, CO2, O-2, N-2, and CH4 gases in a series of novel poly(aryl ether sulfone)s has been examined over a temperature range of 30-100 degreesC. These polymers include four alkyl-substituted cardo poly(aryl ether sulfone)s and four intermolecular interaction enhanced poly(aryl ether sulfone)s. Their water vapor and gas transport properties were compared to the unmodified cardo poly(aryl ether sulfone) (PES-C). It was found that the bulky alkyl substituents on the phenylene rings were advantageous for gas permeability, while the intermolecular hydrogen bonds and ionic bonds resulted in a considerable increase in gas permselectivity. The causes of the trend were interpreted according to free volume, interchain distance, and glass transition temperature, together with the respective contribution of gas solubility and diffusivity to the overall permeability. Of interest was the observation that IMPES-L, which simultaneously bears bulky isopropyl substituent and pendant carboxylic groups, displayed 377% higher O-2 permeability and 5.3% higher O-2/N-2 permselectivity than PES-C. Furthermore, sodium salt form PES-Na+ and potassium salt form PES-K+ exhibited water vapor permeability twice as high as PES-C and H2O/N-2 selectivity in 10(5) order of magnitude.

Electroluminescent properties of the Tris-(acetylsalicylate)-terbium (Tb(AS)(3))

The solubility of [Tris-(acetylsalicylate)-terbium] [Tb(AS)(3)] is improved to a greater extent than [Tris-(salicylate)-terbium] [Tb(Sal)(3)] following introduction of a flexible acetyl group. Th3+ binds with acetylsalicylate in solution at low pH value and the resultant Tb(AS)(3) has good solubility in chloroform. A Green EL device with the structure ITO/PVK/PVB:PBD: Tb(AS)(3)/ PBD/Al has been fabricated based on soluble Tb(AS)(3), in which Tb(AS)(3) was first used as an emissive center doped with PVK and PBD. The hole-transporting layer and the emissive layer were formed by spin coating. The device exhibited a highly pure characteristic green light of Tb3+. (C) 2001 Elsevier Science B.V. All rights reserved.

Isothermal and nonisothermal crystallization of poly(aryl ether ketone ketone) with all-para phenylene linkage

Isothermal and nonisothermal crystallization behavior for PEKK(T) was studied using differential scanning calorimetry (DSC), transmission electron microscopy (TEM), and electron diffraction (ED). In the isothermal crystallization process, the Avrami parameters obtained were n = 2.33-2.69, which shows crystal growth of two-dimensional extensions consistent with our observations by TEM. The lamellar thickness increases with the crystallization temperature of PEKK(T) crystallized isothermally from the melt. However, for the nonisothermal crystallization of PEKK(T), the results from the modified Avrami analysis show two different crystallization processes. Avrami exponents n(1) = 3.61-5.30, obtained from the primary crystallization process, are much bigger than are the secondary n(2) = 2.26-3.04 and confirmed by the observation of the spherulite morphology. PEKK(T) crystallized isothermally from the melt possesses the same crystal structure (Form I) as that from nonisothermal melt crystallization. The results from TEM observation show that the spherulite radius decreases with an increasing cooling rate. (C) 2001 John Wiley & Sons, Inc.

Electrochemiluminescence of tris(2,2 '-bipyridine)ruthenium(II) immobilized in poly(p-styrenesulfonate)-silica-Triton X-100 composite thin-films

The electrochemiluminescence (ECL) of tris(2,2'-bipyridine)ruthenium(ii) [Ru(bpy)(3)(2+)] immobilized in poly(p-styrenesulfonate) (PSS)-silica-Triton X-100 composite films was investigated. The cooperative action of PSS, sol-gel and Triton X-100 attached Ru(bpy)(3)(2+) to the electrode strongly, and the presence of Triton X-100 prevented drying fractures of the sol-gel films during gelation and even on repeated wet-dry cycles. The modified electrode was used for the ECL detection of oxalate, tripropylamine (TPA) and NADH in a flow injection analysis (FIA) system with a newly designed flow cell. The detection scheme exhibited good stability, short response time and high sensitivity. Detection limits were 0.1, 0.1 and 0.5 mu mol L-1 for oxalate, TPA and NADH, respectively, and the linear concentration range extended from 0.001 to 1 mmol L-1 for the three analytes. Applications of the flow cell in ECL and electrochemical detection, as well as the immobilization of reagents based on the cooperative action, are suggested.

Synthesis of poly(ether ether ketone)s with high content of sodium sulfonate groups as gas dehumidification membrane materials

Sodium sulfonate-functionalized polyether ether ketone)s derived from Bisphenol A with a degree of sulfonation up to 2.0 were synthesized by aromatic nucleophilic polycondensation of various amounts of 5,5-carbonylbis(2-fluorobenzenesulfonate) (1), 4,4'-diflurobenzophenone (2) and Bisphenol A (2). Copolymers showed excellent thermal stability and good mechanical properties. The selectivity of water vapor over nitrogen of membranes prepared from copolymers 3a and 3h was determined to be 3.43 x 10(6) and 1.05 x 10(7), respectively.

Synthesis and characterization of a series of high sulfonated poly(ether ether ketone)s

A series of high sulfonated poly(ether ether ketone)s were prepared by copolymerization of sodium 5,5 ' -carbonylbis (2-fluorobenzenesulfonate)(2),4,4 ' -difluorobenzophenone (1) and bisphenol A(3) in the presence of potassium carbonate in dimethylsulfoxide. The copolymers were characterized by IR and DSC, The influence of degree of sulfonation on the properties of copolymers, such as component, thermal stability, solubility and filming ability, was studied.

Preparation of poly(4-vinylpyridine)/silica hybrids supported cyclopentadienyltitanium trichloride (CpTiCl3) catalyst and styrene polymerization

Poly(4 - vinylpyridine)/silica( PVP/SiO2) organic - inorganic nanoscale hybrid was prepared using sol - gel method, in which PVP was used as an organic component and TEOS as a SiO2 precusor, This hybrid was used as CpTiCl3 support. The XPS and IR measurements showed that two kinds of catalytic active site were formed through analyzing the interaction mode between support and CpTiCl3. The results of styrene polymerization showed that syndiotactic was the highest at 50 degreesC. The catalytic activity was 1.09 x 10(6) g PS/ (mol Ti . h) at 70 degreesC when n(Al)/n(Ti) = 1500. GPC results showed a bimodal molecular weight distribution.

Studies on the structure and properties of thermotropic liquid crystalline poly(aryl ether ketone)s

Series of thermotropic liquid crystalline poly (aryl ether ketone) s were synthesized by mucleophilic substitution reactions of 4,4'-biphenol and substituted hydroquinone with different difluoromonomers, The relationship between structure and properties of the novel copolymers was investigated. For the copolymers with liquid crystalline properties, their melting transition temperatures show no great change with increase the content of the crystal-disrupting unit. The reason is that the crystal phase is directly transformed from the ordered liquid crystal phase. Side-groups have important effect on mesophase stability, The temperature range of mesophase stability for the chloro-polymers is smaller than those of other series of copolymers (P-phenyl, t-butyl, methoxy, 3-trifluoromethylbenzene). This behavior indicates that the effect of geometric repulsive factor on the thermodynamic stability of the mesophase is much larger than that of the polarizability attractive factor. Different ordered liquid crystal phases are observed in the polymers with different molecular weights. At low molecular weight, highly ordered smectic liquid crystal phases form. With increasing the molecular weight, the ordered degree of the liquid crystals decreases, and only the nematic liquid crystal phase is observed in the polymer with higher molecular weight.

Novel sodium sulfonate-functionalized poly(ether ether ketone)s derived from 4,4 '-thiodiphenol

Novel sodium sulfonate-functionalized poly(ether ether ketone)s derived from 4,4'-thiodiphenol with degree of sulfonation up to 2.0 were synthesized by nucleophilic polycondensation of various amount of 5,5 '-carbonylbis(2-fluorobenzenesulfonate) (1) and 4,4'-difluorobenzophenone (2) with 4,4'-thiodipheno (3). Component and structure of the polymers were confirmed by TR, NMR and elemental analysis. Wide angle X-ray diffraction patterns indicated an amorphous structure of the polymers. All the polymers showed excellent thermal stability and poor solubility in water. (C) 2001 Elsevier Science Ltd. All rights reserved.

Phase structure and transitions in a poly(methyloctadecylsilane) oligomer

A poly(methyloctadecylsilane) oligomer was synthesized by a typical Wurtz coupling reaction. Upon cooling, three transitions were observed at temperatures of 39.9, 37.5 and 33.9 degreesC at a rate of 2.5 degreesC/min in differential scanning calorimetry (DSC). The first transition, with enthalpy change of 0.47 kT/mol and supercooling of 0.2 degreesC, was characteristic of the conformational change in the Si-Si backbone into an all-trans conformation, which was detected by temperature-dependent Fourier transform infrared (FT-FR) spectroscopy. The second and the third transitions with large supercooling were identified as the formation of two-dimensional hexagonal crystal packing and three-dimensional two-chain orthorhombic crystal packing, respectively. The crystal structure was determined by the combination of WAXD and transmission electron microscopy (TEM) experiments. (C) 2000 Elsevier Science Ltd. All rights reserved.

Miscibility and crystallization behavior of poly(beta-hydroxybutyrate)/poly(ethylene oxide) blends

The miscibility and crystallization behavior of poly(beta-hydroxybutyrate) (PHB)/poly(ethylene oxide) (PEO) blends were studied by differential scanning calorimetry(DSC) and polarizing microscopy (POM). It is found that the miscibility is related to the composition of the blends. When the PEO content is over 20 percent, the miscible blends turn into partially miscible and the phase separation can be observed with POM. The addition of the PEO influences not only the morphology of PHB crystals and the radial growth rate of spherulites, but also the cold crystallization temperature.

Stimulated emission in blue wavelength region from a copolymer

A dye laser based on the soluble conjugated polymer, Poly[1,8-octanedioxy-2,6-dimethoxy-1,4-phenylene-1,2-ethenylene-1, 4-phenylene-1,2-ethenylene-3,5-dimethoxy-1,4-phenylene], has been fabricated. The laser was pumped by light pulses from the third harmonic radiation of an Nd:YAG laser. The lasing was observed in the blue wavelength region with the peak at 450 nm. The threshold energy is about 19 mu J. The energy conversion yield of the laser is about 3.4%. The maximum peak power of the laser output pulse arrives at about 20 kW.

Disodium 4,4 '-difluoro-3,3 '-carbonyl-dibenzenesulfonate hydrofluoride tetrahydrate

The structure determination of the title compound, 2Na(+). C13H6F2O7S22-. HF . 4H(2)O, indicates that intermolecular physical crosslinking through Na+ ions exists in the crystal so that ionic aggregates are formed.