Structure and properties of Brazilian peat: Analysis by spectroscopy and microscopy

Peat was taken from the Sergipe State, Brazil and characterized by several techniques: elemental and thermal analyses; Fourier infrared (FTIR) and solid state 13C nuclear magnetic resonance (NMR) spectroscopies; scanning electron microscopy (SEM), environmental scanning electron microscopy (ESEM) and X-ray diffractometry (XRD). Also, the Sergipe State peat samples were compared with other peat sample from later from Sao Paulo State, Brazil. The lowest O/C and E 4/E 6 ratios and differential thermal analysis (DTA) curves of the Santo Amaro (SAO) sample indicated that this sample had the highest degree of decomposition. FTIR results showed that Itabaiana (ITA) and São Paulo (SAP) samples presented more prominent peak at 1086 cm -1 attributed the presence of Si-O than SAO sample spectra. The SAO sample showed two more intense peaks at 2920 cm -1 and 2850 cm -1. These results were corroborated by 13C NMR and thermal gravimetric (TG) where the relative abundance of the alkyl-C groups was greater in the SAO sample. The X-ray diffractometry (XRD) of SAO sample is characteristic of amorphous matter however, the SAP and ITA samples revealed the large presence of quartz mineral. The scanning electron microscopy (SEM) and environmental scanning electron microscopy (ESEM) showed that the surface of peat samples have porous granules of organic material. The ITA and SAP peat samples are alike while SAO peat sample is richer in organic material. Only the SAO sample has truthful characteristics of peat. The results of this study showed that the samples are very different due to variable inorganic and organic material contents. ©2007 Sociedade Brasileira de Química.

Determination of atenolol in pharmaceutical formulations by diffuse reflectance spectroscopy

A simple analytical method for quantification of atenolol in pharmaceutical formulations by diffuse reflectance spectroscopy is described. The method is based on the reaction, on the filter paper surface, between the drug and p-chloranil producing a colored compound. The best reaction conditions were obtained with 20 μL of atenolol solution and 20 μL of p-chloranil. All reflectance measurements were carried out at 550 nm and the linear range was from 1.13×10-2 to 7.88×10-2 mol L-1 (r = 0.9992). The limit of detection was 2.80 × 10-3 mol L-1. The proposed method was successfully applied to analysis of different commercial brands of pharmaceutical formulations and the results obtained by the proposed method were in good agreement with those obtained using the British Pharmacopoeia method.

Structural and optical properties of Eu3+ and Mg2+ doped LiTaO3 obtained via the polymeric precursor method

This work reports on the pure lithium tantalate (LiTaO3), europium (III)-doped LiTaO3 and magnesium (II)-europium (III)-doped LiTaO3 preparared by the polymeric precursor method, using four different powered samples of Eu3+ ion concentrations 0.1 to 1at %. Structural and optical properties of powders have been studied. The different possible sites occupied by the rare earth were examined. The phase contents and lattice parameters were studied by the Rietveld method and the structural disorder in the LiTaO3 host caused by Eu3+ ions was analyzed. Results indicated LiTaO3 free of secondary phases at 650°C and the photoluminescence (PL) emission spectra showed the characteristic sharp emission bands given by Eu3+ ions when they are excited at a wavelength of 399 nm. An increase of dopants contents caused a non-homogeneous broadening and showed a slightly larger one when Mg was added. A displacement of the transition 5D0-7F0 to shorter wavelengths as function of Eu3+ concentration was also noticed.

Diffusion phenomena of the oxygen and nitrogen in niobium by mechanical spectroscopy

The short-range diffusion phenomenon (Snoek Effect) was investigated by mechanical spectroscopy measurements between 300 K and 650 K, in a polycrystalline niobium sample, containing oxygen and nitrogen, using a torsion pendulum. Experimental spectra of anelastic relaxation were obtained under three conditions: as-received sample; annealed sample and subsequently annealed in an oxygen atmosphere for three hours at 1170 K in partial pressure of 5°10 -5mbar. The experimental spectra obtained were decomposed in elementary Debye peaks and the anelastic relaxation processes were identified. With anelastic relaxation parameters and the lattice parameters, the interstitial diffusion coefficients of the oxygen and nitrogen in niobium were calculated for each kind of preferential occupation (octahedral and tetrahedral). The results were compared with the literature data, and confirmed that the best adjustment is for the preferential occupation octahedral model for low concentrations of interstitial solutes, but at higher concentration of oxygen were observed deviations of experimental data for the interstitial diffusion coefficients of oxygen in niobium when compared with the literature data, this could be related to the possible occurrence of a double occupation of interstitial sites in the niobium lattice by oxygen interstitials. © (2010) Trans Tech Publications.

Impedance spectroscopy study of solid-state dye-sensitized solar cells with varying Spiro-OMeTAD concentration

This work reports on the changes of performance of solid-state cells dye-sensitized solar cells with the variation of concentration of spiro-OMeTAD between 5% and 25% in the fabrication of the cell. Variations of charge recombination and capacitance correlate with the improvement of current-potential characteristics at increasing spiro-OMeTAD content, which is explained by reduction of transport resistance for hole transport, the increase of charge separation in the dye molecules, and importantly, with the increase of the β-factor in the recombination resistance, that causes a reduction of the diode ideality factor. © 2010 Materials Research Society.

Determination of saturates, aromatics and ethanol in Brazilian commercial gasoline with low olefin content using 1 H NMR spectroscopy

In this work, a Hydrogen Nuclear Magnetic Resonance (1H NMR) method has been developed to determine aromatics and ethanol in Brazilian commercial gasoline with low olefin content. The proposed method involves subdividing an 1H NMR spectrum into regions, each of which is assumed to be associated with a specific type of structural group (OH, CH, CH2 and CH3). The method is based on the assignment of overlapping regions of 1H NMR spectra due to the signals of naphthene (N), iso and normal paraffins (P) and ethanol (E). Each 1H NMR spectrum was divided into 8 regions and the integration was correlated to the percentage of the substances to be determined. The results of the analysis by 1H NMR were compared with analysis of GC-FID obtained with the PONA system. The proposed technique of 1H NMR was shown to be an appropriate method for this sample type.

β-lactam antibiotics epitope mapping with STD NMR spectroscopy: A study of drug-human serum albumin interaction

Molecular recognition events are key issues in many biological processes. STD NMR (saturation transfer difference nuclear magnetic resonance spectroscopy) is one of the techniques used to understand such biological interactions. Herein, we have investigated the interactions of four β-lactam antibiotics belonging to two classes (cephalosporins and penicillins) with human serum albumin (HSA) by 1H STD NMR revealing that the interaction between the aromatic moiety and HSA is responsible for the binding efficiency. Thus, the structural differences from the five to six-membered thio ring in penicillins and cephalosporins do not seem to influence antibiotic-albumin interactions. © 2012 Sociedade Brasileira de Química.

Structural refinement and photoluminescence properties of cube-like (Ca 1-xCu x)TiO 3 crystals synthesized by the microwave-hydrothermal method

In this work, (Ca 1-xCu x)TiO 3 crystals with (x = 0, 0.01 and 0.02), labeled as CTO, CCTO1 and CCTO2, were synthesized by the microwave-hydrothermal method at 140°C for 32 min. XRD patterns (Fig. 1), Rietveld refinement and FT-Raman spectroscopy indicated that these crystals present orthorhombic structure Pbnm. Micro-Raman and XANES spectra suggested that the substitution of Ca by Cu in A-site promoted a displacement of the [TiO6]-[TiO6] clusters adjacent from its symmetric center, which leads distortions on the [CaO 12] clusters neighboring and consequently cause the strains into the CaTiO3 lattice. FE-SEM images showed that these crystals have an irregular shape as cube like probably indicating an Ostwald-ripening and self-assemble as dominant mechanisms to crystals growth. The powders presented an intense PL blue-emission.

CdMoO 4 synthesized by a microwave-assisted hydrothermal method and their photoluminescence and photocatality properties

In this work CdMoO 4 nanoparticles were obtained under hydrothermal conditions using microwave radiation (2.45 GHz) (MH) at 100°C for different times. These powders were analyzed by X-ray diffraction (XRD), Field-emisson gum scanning electron microscopy (FEG-SEM), Ultraviolet-visible (UV-vis) absorption spectroscopy and photoluminescence (PL) measurements. XRD pattern confirmed that the pure CdMoO 4 phases were obtained. FEG-SEM powders present large-scale and homogeneous particles with microspheres-like morphology. UV-vis results were employed to determine the optical band gap these materials. Also, it showed existence of photoluminescence (PL) emission in the green wavelength range of 540-546 nm. Photocatalytic activity of CdMoO 4 nanocrystals was examined by monitoring the degradation of rhodamine B dye.

Microwave-assisted hydrothermal synthesis of ZnO powders with different reagents

In this work, zinc oxide powders were synthesized by microwave-assisted hydrothermal method in basic medium. These powders were analyzed by X-ray diffraction (XRD), Field-emisson gum scanning electron microscopy (FEG-SEM), Ultraviolet-visible (UV-vis) absorption spectroscopy and photoluminescence (PL) measurements. XRD pattern confirmed that the pure ZnO phases were obtained after MH processing performed at 130°C/ 1h. FEG-SEM micrographs reveals that these nanostructures are made up of ZnO plates. UV-vis results were employed to determine the optical band gap these materials. Also, it showed existence of photoluminescence (PL) in the different zinc powders. An orange PL emission when excited by 350 nm wavelength at room temperature was observad in the different powders.

Using the electrochemical impedance spectroscopy to characterize carbon steel in biodiesel medium

Electrochemical impedance spectroscopy measurements using two carbon steel electrodes in soybean biodiesel medium, produced by methylic route, were performed in an electrochemical cell that allows positioning the two electrodes face-to-face. To retain the biodiesel between the electrodes and prevent its leakage a porous membrane soaked in biodiesel was used. The amplitude of the AC potential and the area of the electrodes were varied. The linearity between disturbance and response signals was observed for tests when the amplitude of the AC potential was lower than 1500 mV (rms). The electrical resistance of biodiesel dominates the global response and carbon steel presents low corrosion, which is observed only at low frequency, and was confirmed by chemical tests performed in the membrane. In conclusion the electrical resistance of biodiesel can be estimated using electrochemical impedance spectroscopy with two electrodes set up. ©The Electrochemical Society.

Broadband NIR emission in novel sol-gel Er3+-doped SiO 2-Nb2O5 glass ceramic planar waveguides for photonic applications

This paper reports on the sol-gel preparation and structural and optical characterization of new Er3+-doped SiO2-Nb 2O5 nanocomposite planar waveguides. Erbium-doped (100-x)SiO2-xNb2O5 waveguides were deposited on silica-on-silicon substrates and Si(1 0 0) by the dip-coating technique. The waveguides exhibited uniform refractive index distribution across the thickness, efficient light injection at 1538 nm, and low losses at 632 and 1538 nm. The band-gap values lied between 4.12 eV and 3.55 eV for W1-W5, respectively, showing an excellent transparency in the visible and near infrared region for the waveguides. Fourier Transform Infrared (FTIR) Spectroscopy analysis evidenced SiO2-Nb2O5 nanocomposite formation with controlled phase separation in the films. The HRTEM and XRD analyses revealed Nb2O5 orthorhombic T-phase nanocrystals dispersed in a silica-based host. Photoluminescence (PL) analysis showed a broad band emission at 1531 nm, assigned to the 4I13/2 → 4I15/2 transition of the Er3+ ions present in the nanocomposite, with a full-width at half medium of 48-68 nm, depending on the niobium content and annealing. Hence, these waveguides are excellent candidates for application in integrated optics, especially in EDWA and WDM devices. © 2012 Elsevier B.V. All rights reserved.

Correlation between photoluminescence and structural defects in Ca 1+x Cu 3 - X Ti 4 O 12 systems

Ca1+xCu3-xTi4O12 powders were synthesized by a conventional solid-state reaction. X-ray diffraction (XRD) was performed to verify the formation of cubic CaCu3Ti4O 12 (CCTO) and orthorhombic CaTiO3 (CTO) phases at long range. Rietveld refinements indicate that excess Ca atoms added to the Ca 1-xCu3-xTi4O12 (x = 1.0) composition segregated in a CaTiO3 secondary phase suggesting that solubility limit of Ca atoms in the CaCu3Ti4O12 lattice was reached for this system. The FE-SEM images show that the Ca 1+xCu3-xTi4O12 (0 < x < 3) powders are composed of several agglomerated particles with irregular morphology. X-ray absorption near-edge structure spectroscopy (XANES) spectra indicated [TiO5Vo z]-[TiO6] complex clusters in the CaCu3Ti4O12 structure which can be associated with oxygen vacancies (Vo z = V o x, Vo •, and Vo ••) whereas in the CaTiO3 powder, this analysis indicated [TiO6]-[TiO6] complex clusters in the structure. Ultraviolet-visible (UV-vis) spectra and photoluminescence (PL) measurements for the analyzed systems revealed structural defects such as oxygen vacancies, distortions, and/or strains in CaCu3Ti4O12 and CaTiO3 lattices, respectively. © 2012 The American Ceramic Society.

Preparation and photoluminescence characteristics of In(OH) 3:xTb3+ obtained by Microwave-Assisted Hydrothermal method

Crystalline terbium-doped indium hydroxide structures were prepared by a rapid and efficient Microwave-Assisted Hydrothermal (MAH) method. Nanostructures were obtained at a low temperature. FE-SEM images confirm that these samples are composed of 3D nanostructures. XRD, optical diffuse reflectance and photoluminescence (PL) measurements were used to characterize the products. Emission spectra of terbium-doped indium hydroxide (In(OH)3:xTb 3+) samples under excitation (350.7 nm) presented broad band emission referent to the indium hydroxide matrix and 5D4 → 7F6, 5D4 → 7F 5, 5D4 → 7F4, and 5D4 → 7F3 terbium transitions at 495, 550, 590 and 627 nm, respectively. Relative intensities of the Tb 3+ emissions increased as the concentration of this ion increased from 0, 1, 2, 4 and 8 mol%, of Tb3+, but the luminescence is drastically quenched for the In(OH)3 matrix. © 2012 Elsevier B.V. All rights reserved.

Fe K-edge X-ray absorption spectroscopy study of Pb(Fe2/3W 1/3)O3-PbTiO3 multiferroic ceramics

The present paper is a comprehensive study concerning Fe K-edge X-ray absorption spectroscopy (XAS) measurements, which were performed to characterize the local structure of (1 - x)Pb(Fe2/3W1/3)O 3-xPbTiO3 samples as a function of temperature and PbTiO3 content. Results obtained by the fits of extended X-ray absorption fine structure consist with rhombohedral symmetry for Pb(Fe 2/3W1/3)O3 composition at temperatures lower than room temperature. This result is in apparent disagreement with X-ray and neutron diffraction characterization which have been reported. This apparent disagreement is related to the fact that XAS probes the short-range order, whereas X-ray diffraction provides structural information about the average structure. Moreover, as the PbTiO3 content increases, a disorder has been detected at local structure of the FeO6 octahedron. Analysis of X-ray absorption near edge structure spectra did not show modifications in intensity nor energy of transitions. © 2013 American Institute of Physics.