Effect of Surface Conditioning Modalities on the Repair Bond Strength of Resin Composite to the Zirconia Core / Veneering Ceramic Complex

Purpose: This study evaluated the effect of different surface conditioning protocols on the repair strength of resin composite to the zirconia core / veneering ceramic complex, simulating the clinical chipping phenomenon.Materials and Methods: Forty disk-shaped zirconia core (Lava Zirconia, 3M ESPE) (diameter: 3 mm) specimens were veneered circumferentially with a feldspathic veneering ceramic (VM7, Vita Zahnfabrik) (thickness: 2 mm) using a split metal mold. They were then embedded in autopolymerizing acrylic with the bonding surfaces exposed. Specimens were randomly assigned to one of the following surface conditioning protocols (n = 10 per group): group 1, veneer: 4% hydrofluoric acid (HF) (Porcelain Etch) + core: aluminum trioxide (50-mu m Al2O3) + core + veneer: silane (ESPE-Sil); group 2: core: Al2O3 (50 mu m) + veneer: HF + core + veneer: silane; group 3: veneer: HF + core: 30 mu m aluminum trioxide particles coated with silica (30 mu m SiO2) + core + veneer: silane; group 4: core: 30 mu m SiO2 + veneer: HF + core + veneer: silane. Core and veneer ceramic were conditioned individually but no attempt was made to avoid cross contamination of conditioning, simulating the clinical intraoral repair situation. Adhesive resin (VisioBond) was applied to both the core and the veneer ceramic, and resin composite (Quadrant Posterior) was bonded onto both substrates using polyethylene molds and photopolymerized. After thermocycling (6000 cycles, 5 degrees C-55 degrees C), the specimens were subjected to shear bond testing using a universal testing machine (1 mm/min). Failure modes were identified using an optical microscope, and scanning electron microscope images were obtained. Bond strength data (MPa) were analyzed statistically using the non-parametric Kruskal-Wallis test followed by the Wilcoxon rank-sum test and the Bonferroni Holm correction (alpha = 0.05).Results: Group 3 demonstrated significantly higher values (MPa) (8.6 +/- 2.7) than those of the other groups (3.2 +/- 3.1, 3.2 +/- 3, and 3.1 +/- 3.5 for groups 1, 2, and 4, respectively) (p < 0.001). All groups showed exclusively adhesive failure between the repair resin and the core zirconia. The incidence of cohesive failure in the ceramic was highest in group 3 (8 out of 10) compared to the other groups (0/10, 2/10, and 2/10, in groups 1, 2, and 4, respectively). SEM images showed that air abrasion on the zirconia core only also impinged on the veneering ceramic where the etching pattern was affected.Conclusion: Etching the veneer ceramic with HF gel and silica coating of the zirconia core followed by silanization of both substrates could be advised for the repair of the zirconia core / veneering ceramic complex.

Influence of air-particle deposition protocols on the surface topography and adhesion of resin cement to zirconia

Objectives: This study evaluated the influence of air-particle abrasion protocols on the surface roughness (SR) of zirconia and the shear bond strength (SBS) of dual-polymerized resin cement to this ceramic. Materials and methods. Sintered zirconia blocks (n = 115) (Lava, 3M ESPE) were embedded in acrylic resin and polished. The specimens were divided according to the 'particle type' (Al: 110 mu m Al2O3; Si: 110 mu m SiO2) and 'pressure' factors (2.5 or 3.5 bar) (n = 3 per group): (a) Control (no air-abrasion); (b) Al2.5; (c) Si2.5; (d) Al3.5; (e) Si3.5. SR (Ra) was measured 3-times from each specimen after 20 s of air-abrasion (distance: 10 mm) using a digital optical profilometer. Surface topography was evaluated under SEM analyses. For the SBS test, 'particle type', 'pressure' and 'thermocycling' (TC) factors were considered (n = 10; n = 10 per group): Control (no air-abrasion); Al2.5; Si2.5; Al3.5; Si3.5; Control(TC); Al2.5(TC); Si2.5(TC); Al3.5(TC); Si3.5(TC). After silane application, resin cement (Panavia F2.0) was bonded and polymerized. Specimens were thermocycled (6.000 cycles, 5-55 degrees C) and subjected to SBS (1 mm/min). Data were analyzed using ANOVA, Tukey's and Dunnett tests (5%). Results. 'Particle' (p = 0.0001) and 'pressure' (p = 0.0001) factors significantly affected the SR. All protocols significantly increased the SR (Al2.5: 0.45 +/- 0.02; Si2.5: 0.39 +/- 0.01; Al3.5: 0.80 +/- 0.01; Si3.5: 0.64 +/- 0.01 mu m) compared to the control group (0.16 +/- 0.01 mu m). For SBS, only 'particle' factor significantly affected the results (p = 0.015). The SiO2 groups presented significantly higher SBS results than Al2O3 (Al2.5: 4.78 +/- 1.86; Si2.5: 7.17 +/- 2.62; Al3.5: 4.97 +/- 3.74; Si3.5: 9.14 +/- 4.09 MPa) and the control group (3.67 +/- 3.0 MPa). All TC specimens presented spontaneous debondings. SEM analysis showed that Al2O3 created damage in zirconia in the form of grooves, different from those observed with SiO2 groups. Conclusions. Air-abrasion with 110 mu m Al2O3 resulted in higher roughness, but air-abrasion protocols with SiO2 promoted better adhesion.

Zirconia-Porcelain Bonding: Effect of Multiple Firings on Microtensile Bond Strength

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Bonding of Y-TZP to Dentin: Effects of Y-TZP Surface Conditioning, Resin Cement Type, and Aging

Purpose: To evaluate the effects of two surface treatments, aging, and two resin cements on shear bond strength between dentin and yttrium-stabilized tetragonal zirconia polycrystal ceramic (Y-TZP).Materials and Methods: Eighty human molars were embedded in acrylic resin and sectioned 3 mm below the occlusal plane. These teeth and 80 cylindrical Y-TZP specimens (height, 4 mm; diameter, 3.4 mm) were divided into eight groups (n=10) using the following factors: Y-TZP surface treatment (Vi: low-fusing porcelain [vitrification] + hydrofluoric acid etching + silanization or Si: tribochemical silicatization); cementation strategies (PF: Pan avia or CC: Clearfil); and storage (nonaging or aging). Bonding surfaces of 40 Y-TZP specimens received Vi treatment, and the rest received Si treatment. Half of the ceramic-tooth assemblies were cemented with Panavia, the rest with Clearfil. Shear tests were executed using 0.4-mm-thick wire at 0.5 mm/min. Data were analyzed by three-way analysis of variance and Tukey test (alpha=0.05). Fractures were analyzed.Results: Y-TZP surface treatments did not affect bond strength (p=0.762, Vi = Si), while resin cements (p<0.001, Panavia > Clearfil) and aging (p=0.006, nonaging > aging) showed a significant effect. Most failures were in adhesive at dentin-cement interfaces; no failure occurred between zirconia and cement.Conclusion: When Y-TZP ceramic is bonded to dentin, the weakest interface is that between dentin and resin cement. The resin cement/Y-TZP interface was less susceptible to failures, owing to Y-TZP surface treatments.

Implant-retained finger prosthesis with modified retention system

Background: Amputations affect both the physical and the psychological aspects of an individual, causing significant impact on self-esteem. The main causes of finger amputations are work-related accidents with dangerous machinery, road traffic accidents, and animal bites, as well as systemic diseases such as diabetes. This report aims to describe a simple technique for fabrication of implant-retained finger prosthesis with a modified base of the retention system.Case Description and Methods: The O-Ring retention system was used with a modified hexagon-shaped base and a metallic capsule adapted to the acrylic resin to attach the prosthesis to the implant.Findings and Outcomes: The prosthesis was made with silicone, and after osseointegration, it was installed without complications, leading to a patient satisfied with the end result and encouraged to return to social life.

Application of acoustoelasticity to measure the stress generated by milling in ASTM A36 steel plates

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Avaliação da reação tecidual de uma resina termoplástica em tecido subcutâneo de ratos

Pós-graduação em Odontologia - ICT

Avaliação in vitro da resistência estrutural em dentes fragilizados utilizando reforços intra-radiculares

Pós-graduação em Odontologia Restauradora - ICT

Avaliação dos ciclos de polimerização da resina acrílica para base de prótese total

In the present work it was studied the behavior of four water bath curing cycles of heat activated acrylic resin considered as long duration (I – 65ºC for 30 min;50ºC for 23h and 30min; and 100º C for 1h; II- 50ºC for 24h and the rapid cycle), compared to the known long time curing cycle (9 hours for 72ºC) and short curing cycle (1 h for 65ºC; 30 min to elevate at 100º C and 1:00 to 100º C). Analysis consisted of observations and verification of the residual monomer, weight alterations, dimensional, dimensional lineal, porosity and hardness to determine material performance. The results pointed out that residual monomer presented statistical significant differences in the factor storage and interaction among the factors cycle X storage for weight alteration; statistical significant differences for the factor storage for lineal dimensional alterations, without significant differences for hardness. Porosity was verified in minimum degree in the cycle III and in appreciable amount in the cycle IV

Resistência de união, índice de remanescente adesivo e avaliação da presença de esmalte sobre a base de braquetes após descolagem: estudo in vitro

Pós-graduação em Ciências Odontológicas - FOAR

Distribuição das tensões em próteses protocolo mandibulares com diferentes extensões de cantilever e material de revestimento oclusal

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influência da adição de nanopartículas na estabilidade de cor, microdureza e resistência à flexão de resina específica para confecção de próteses oculares

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Efeito do óleo essencial de Melaleuca alternifolia e de seu principal componente Terpinen-4-ol sobre isolados clínicos de Candida albicans resistentes

Pós-graduação em Ciências Odontológicas - FOAR

Avaliação da eficácia de primers para metal na resistência ao cisalhamento da união entre cimentos resinosos e metais não nobres. Efeito do armazenamento em água

O sucesso das restaurações metálicas indiretas depende, dentre outros fatores, de uma união eficaz entre a estrutura metálica e o cimento dentário empregados. Sabe-se que os primers para metal atuam com comprovada eficácia na resistência adesiva dos cimentos resinosos às ligas nobres. Entretanto, pouco foi estudado sobre o efeito de tais materiais em ligas não nobres. O propósito deste estudo foi avaliar a eficácia de primers para metal na resistência ao cisalhamento da união entre cimentos resinosos e metais não nobres. Discos (9 mm de diâmetro e 3 mm de altura) foram fundidos em liga de NiCr (n=80) e em titânio comercialmente puro (Ti c.p.) (n=80) e foram incluídos em anel de PVC com resina acrílica quimicamente ativada. As superfícies dos discos foram regularizadas com lixas de carbeto de silício de granulação 320, 400 e 600 e jateadas com partículas de óxido de alumínio de 50 µm. Espécimes de cada metal foram divididos em quatro grupos (n=20). Uma matriz metálica bi-partida (5 mm de diâmetro interno e 2 mm de altura) foi posicionada na superfície do espécime. As áreas adesivas receberam um dos seguintes tratamentos: 1) Panavia F; 2) Alloy Primer e Panavia F; 3) Bistite DC e 4) Metaltite e Bistite DC. Para evitar a exposição dos cimentos à luz, estes foram espatulados e inseridos na matriz dentro de uma câmara de revelação radiográfica. Quarenta minutos após a confecção, os espécimes foram armazenados em água destilada a 37ºC por 24 horas e então termociclados (1.000 ciclos, 5ºC e 55ºC, 30 segundos cada banho). Após a termociclagem, os espécimes foram armazenados novamente nas mesmas condições descritas anteriormente por um período de 24 horas (n=10) ou de 6 meses (n=10) antes do ensaio de cisalhamento em uma máquina de ensaios mecânicos (Material Test System 810).

Dentina humana e bovina: estudo comparativo das propriedades físicas e características da hibridização de sistemas adesivos convencionais ou grander modificados: análise em mev

A adesão longitudinal continua a representar um dos maiores desafios da Odontologia moderna. Uma nova proposta para o estabelecimento do equilíbrio da adesão aos tecidos dentários surge, baseada na observação dos resultados obtidos com a tecnologia Grander para revitalização da água. Objetiva-se com o estudo verificar a influência dessa tecnologia nas propriedades físicas de dois sistemas adesivos (convencional e autocondicionante) à partir da medição da tensão superficial e do ângulo de contato; e avaliar a formação e a qualidade da camada híbrida em dentina humana e bovina. A tensão superficial de quatro diferentes líquidos (água, Single Bond- 3M, Primer do Clearfil SE Bond -Kuraray, e Bond do Clearfil SE-Kuraray), foi medida antes e após a modificação pelo procedimento Grander em aparelho goniômetro (Ramé-hart). O ângulo de contato com três substratos distintos (placa de titânio, dentina humana e dentina bovina), foi medido para os quatro líquidos também antes e após a modificação pelo procedimento Grander, também em goniômetro. A formação e qualidade da camada híbrida, foi avaliada em MEV, a partir da confecção de corpos de prova dos substratos humano e bovino, devidamente embutidos, preparados em lixas de variada granulação até a exposição de dentina, submetidos ao procedimento adesivo (SB ou CSEB) normal ou grander modificado, recebendo ao final dupla camada de resina composta Z250-3M, fotopolimerizada por 40s. Após armazenamento em estufa bacteriológica por 24h, os procedimentos para análise ao MEV foram realizados (fixação, desidratação, secagem e metalização). A estatística de Análise de Variância ANOVA e Teste de Tukey 5% revelou que: houve redução estatisticamente significante da tensão superficial para todos os líquidos Grander modificados; houve redução estatisticamente... (Resumo completo, clicar acesso eletrônico abaixo)