An overview on armor research for the laser fusion project HiPER

During the current preparatory phase of the European laser fusion project HiPER, an intensive effort has being placed to identify an armour material able to protect the internal walls of the chamber against the high thermal loads and high fluxes of x-rays and ions produced during the fusion explosions. This poster addresses the different threats and limitations of a poly-crystalline Tungsten armour. The analysis is carried out under the conditions of an experimental chamber hypothetically constructed to demonstrate laser fusion in a repetitive mode, subjected to a few thousand 48MJ shock ignition shots during its entire lifetime. If compared to the literature, an extrapolation of the thermomechanical and atomistic effects obtained from the simulations of the experimental chamber to the conditions of a Demo reactor (working 24/7 at hundreds of MW) or a future power plant (producing GW) suggests that “standard” tungsten will not be a suitable armour. Thus, new materials based on nano-structured W and C are being investigated as possible candidates. The research programme launched by the HiPER material team is introduced.

Sub-bandgap spectral photo-response analysis of Ti supersaturated Si

We have analyzed the increase of the sheet conductance (ΔG□) under spectral illumination in high dose Ti implanted Si samples subsequently processed by pulsed-laser melting. Samples with Ti concentration clearly above the insulator-metal transition limit show a remarkably high ΔG□, even higher than that measured in a silicon reference sample. This increase in the ΔG□ magnitude is contrary to the classic understanding of recombination centers action and supports the lifetime recovery predicted for concentrations of deep levels above the insulator-metal transition.

Overall and local mechanical behaviour of dissimilar laser welded joints

The present investigation addresses the overall and local mechanical performance of dissimilar joints of low carbon steel (CS) and stainless steel (SS) thin sheets achieved by laser welding in case of heat source displacement from the weld gap centreline towards CS. Microstructure characterization and residua! strain scanning, carried out by neutron diffraction, were used to assess the joints features. It was found that the heat source position influences the base metals dilution and the residua! stress field associated to the welding process; the transverse residual stress is smaller than for the longitudinal component, of magnitudes close to the parent CS yield strength. Furthermore, compressive transverse residual stresses were encountered at the SS-weld interface. The tensile behavior of the joint different zones assessed by using a video-image based system (VIC-2D) reveals that the residual stress field, together with the positive difference in yield between the weld metal and the base materials protects the joint from being piastically deformed. The tensile loadings of flat transverse specimens generate the strain localization and failure in CS, far away from the weld.En este trabajo se exponen los resultados de una investigacion sobre el comportamiento mecanico de soldaduras disimiles acero inoxidable-acero al carbono, realizadas para unir chapas delgadas, desplazando la fuente de calor del eje longitudinal de la union soldada por laser sobre el acero al carbono. Se han determinado las caracteristicas microestructurales de la union soldada, las tensiones residuales generadas (mediante difraccion de neutrones) y las curvas tension-deformacion locales y globales, mediante medidas locales de deformacion empleando el sistema VIC-2D "video image correlation". El desplazamiento de la fuente de calor infiuye en la dilution de los metales base y el campo de tensiones residuales asociado al proceso de soldeo; las tensiones residuales medidas en direction longitudinal se aproximan al limite elastico del acero al carbono, mientras que las tensiones residuales transversales son menores, e incluso de compresion. El ensayo a traccion de la union soldada revela que las tensiones residuales y la diferencia de limite elastico entre los metales base y la soldadura propician que la rotura se produzca por inestabilidad plastica del acero al carbono, lejos de la soldadura, sin que la union plastifique.