Effect of eicosapentaenoic acid, protein and amino acids on protein synthesis and degradation in skeletal muscle of cachectic mice

Atrophy of skeletal muscle reduces both the quality and quantity of life of patients with cancer cachexia. Loss of muscle mass is thought to arise from a reduction in protein synthesis combined with an enhanced rate of protein degradation, and few treatments are available to counteract this process. Eicosapentaenoic acid (EPA) has been shown to attenuate the enhanced protein degradation, but to have no effect on protein synthesis. This study examines the effect of EPA combined with a protein and amino-acid supplementation on protein synthesis and degradation in gastrocnemius muscle of mice bearing the cachexia-inducing MAC16 tumour. Muscles from cachectic mice showed an 80% reduction in protein synthesis and about a 50-fold increase in protein degradation compared with muscles from nontumour-bearing mice of the same age and weight. Treatment with EPA (1 g kg-1) daily reduced protein degradation by 88%, but had no effect on protein synthesis. Combination of EPA with casein (5.35 g kg-1) also had no effect on protein synthesis, but when combined with the amino acids leucine, arginine and methionine there was almost a doubling of protein synthesis. The addition of carbohydrate (10.7 g kg-1) to stimulate insulin release had no additional effect. The combination involving the amino acids produced almost a doubling of the ratio of protein synthesis to protein degradation in gastrocnemius muscle over that of EPA alone. No treatment had a significant effect on tumour growth rate, but the inclusion of amino acids had a more significant effect on weight loss induced by the MAC16 tumour than that of EPA alone. The results suggest that combination therapy of cancer cachexia involving both inhibition of the enhanced protein degradation and stimulation of the reduced protein synthesis may be more effective than either treatment alone. © 2004 Cancer Research UK.

Design and synthesis of proteoglycan analogues for tissue repair and regeneration

This thesis is concerned with the design and synthesis of a novel, injectable proteoglycan analogue for tissue repair. This is of particular relevance to the restoration of disc height to a degraded nucleus pulposus of the intervertebral disc. The focus is on the use of sulfonate monomers as proteoglycan analogues, in particular sodium 2-acrylamido-2-methylpropane sulfonic acid and the potassium salt of 3-sulfopropyl acrylate. For most biomedical applications, synthetic hydrogels need to show dimensional stability to changes in pH, osmolarity, and temperature. This is readily achieved by neutral structures however ionic sulfonate containing hydrogels are responsive to environmental change which renders them difficult to manage in most tissue replacement applications. In this case osmotic responsiveness rather than stability is desirable. Therefore sulfonate based materials possess advantageous properties. This is a result of the sulfonate becoming an ideal surrogate for the sulfate group present within the structure of natural proteoglycans. This thesis reports polymerisation studies based on the production of a redox initiated copolymer system capable of polymerising in situ within a timescale of circa. 5-7 minutes. The rheological properties, osmotic drive, and residual monomer content of successful compositions is analysed. Properties are adapted to mimic those of the target natural tissue. The adaptation of the material for use as an injectable intra-ocular lens, with hyaluronic acid as an interpenetrate is reported. The synthesis of a radiopaque macromer to allow visibility of the repair system once in situ is investigated and discussed. The results presented in this thesis describe a suitable proteoglycan tissue analogue which is injectable, biomimetic, osmotically responsive and mechanically stable in its desired application.

The synthesis of a ferromagnetic polymer

The aim of this study was to prepare a ferromagnetic polymer using the design elements of molecular magnets. This involved the preparation of co-polyradicals of phenylacetylenes bearing nitronyl nitroxides and nitro/cyano groups. The magnetic properties of the materials were determined using a SQUID magnetometer. A novel rhodium catalyst, Rh(NBD)(NH3)Cl, was prepared in order to obtain good yields of polymerisation. A wide range of substituted phenylacetylenes were first homopolymerised in order to assess the efficiency of the catalyst. Yields were generally high, between 75% and 98%, and the time of polymerisation was short (one hour). SEC analysis revealed that the Mw of the polymers were in the range of 200,000 and 250,000. The discovery that phenylboronic acid acts a co-catalyst for the polymerisation served to increase the yields by 10% to 20% but the Mw of the polymers was reduced to approximately 100,000. Co-polyradicals were prepared in good to excellent yield using the new catalyst. The magnetic properties in the temperature range of 300K to 1.8K were investigated by SQUID, which revealed a spin glass system, antiferromagnets and possible dipolar magnets. Short-range ferromagnetic interactions between 300K and 100K were found in a co-polyradical containing nitronyl nitroxide and cyano substituted monomers. The magnetic properties were dependent upon both the type of monomers utilised and the ratio between them. The effects of ring substituents on the terminal alkyne have been studied by carbon-13 NMR. There was no correlation however, between the chemical shift of terminal alkyne and the polymerisability of the monomer.

Synthesis and characterisation of pillared clay catalysts for hydro-cracking of heavy liquid fuels

A range of chromia pillared montmorillonite and tin oxide pillared laponite clay catalysts, as well as new pillared clay materials such as cerium and europium oxide pillared montmorillonites were synthesised. Methods included both conventional ion exchange techniques and microwave enhanced methods to improve performance and/or reduce preparation time. These catalytic materials were characterised in detail both before and after use in order to study the effect of the preparation parameters (starting material, preparation method, pillaring species, hydroxyl to metal ratio etc.) and the hydro cracking procedure on their properties. This led to a better understanding of the nature of their structure and catalytic operation. These catalysts were evaluated with regards to their performance in hydrocracking coal derived liquids in a conventional microbomb reactor (carried out at Imperial College). Nearly all catalysts displayed better conversions when reused. The chromia pillared montmorillonite CM3 and the tin oxide pillared laponite SL2a showed the best "conversions". The intercalation of chromium in the form of chromia (Cr203) in the interlayer clearly increased conversion. This was attributed to the redox activity of the chromia pillar. However, this increase was not proportional to the increase in chromium content or basal spacing. In the case of tin oxide pillared laponite, the catalytic activity might have been a result of better access to the acid sites due to the delaminated nature of laponite, whose activity was promoted by the presence of tin oxide. The manipulation of the structural properties of the catalysts via pillaring did not seem to have any effect on the catalysts' activity. This was probably due to the collapse of the pillars under hydrocracking conditions as indicated by the similar basal spacing of the catalysts after use. However, the type of the pillaring species had a significant effect on conversion. Whereas pillaring with chromium and tin oxides increased the conversion exhibited by the parent clays, pillaring with cerium and europium oxides appeared to have a detrimental effect. The relatively good performance of the parent clays was attributed to their acid sites, coupled with their macropores which are able to accommodate the very high molecular mass of coal derived liquids. A microwave reactor operating at moderate conditions was modified for hydro cracking coal derived liquids and tested with the conventional catalyst NiMo on alumina. It was thought that microwave irradiation could enable conversion to occur at milder conditions than those conventionally used, coupled with a more effective use of hydrogen. The latter could lead to lower operating costs making the process cost effective. However, in practice excessive coke deposition took place leading to negative total conversion. This was probably due to a very low hydrogen pressure, unable to have any hydro cracking effect even under microwave irradiation. The decomposition of bio-oil under microwave irradiation was studied, aiming to identify the extent to which the properties of bio-oil change as a function of time, temperature, mode of heating, presence of char and catalyst. This information would be helpful not only for upgrading bio-oil to transport fuels, but also for any potential fuel application. During this study the rate constants of bio-oil's decomposition were calculated assuming first order kinetics.

Design and synthesis of novel hydrogels for biological applications

The aims of this project were:1) the synthesis of a range of new polyether-based vinylic monomers and their incorporation into poly(2-hydroxyethyl methacrylate) (poly(HEMA)) based hydrogel networks, of interest to the contact lens industry.2) the synthesis of a range of alkyltartronic acids, and their derivatives. These molecules may ultimately be used to produce functionalised poly(-hydroxy acids) of potential interest in either drug delivery or surgical suture applications. The novel syntheses of a range of both methoxy poly(ethylene glycol) acrylates (MPEGAs) and poly(ethylene glycol) acrylates (PEGAs) are described. Products were obtained in very good yields. These new polyether-based vinylic monomers were copolymerised with 2-hydroxyethyl methacrylate (HEMA) to produce a range of hydrogels. The equilibrium water contents (EWC) and surface properties of these copolymers containing linear polyethers were examined. It was found that the EWC was enhanced by the presence of the hydrophilic polyether chains.Results suggest that the polyether side chains express themselves at the polymer surface, thus dictating the surface properties of the gels. Consequentially, this leads to an advantageous reduction in the surface adhesion of biological species. A synthesis of a range of alkyltartronic acids is also described. The acids prepared were obtained in very good yields using a novel four-stage synthesis. These acids were modified to give potassium monoethyl alkyltartronates. Although no polyesterification is described in this thesis, these modified alkyltartronic acid derivatives are considered to be potentially excellent starting materials for poly (alkyltartronic acid) synthesis via anhydrocarboxylate or anhydrosulphite cyclic monomers.

Synthesis of peptide nucleic acid (PNA) and entrapment of PNA into liposomes

DUE TO COPYRIGHT RESTRICTIONS ONLY AVAILABLE FOR CONSULTATION AT ASTON UNIVERSITY LIBRARY AND INFORMATION SERVICES WITH PRIOR ARRANGEMENT

On the active site in H3PW12O40/SiO2 catalysts for fine chemical synthesis

The surface environment and structural evolution of silica supported phosphotungstic acid (H3PW12O40) catalysts have been investigated as a function of acid loading. H3PW12O40 clusters are deposited intact upon the silica surface, adopting a Stranksi-Krastanov growth mode forming a two-dimensional adlayer which saturates at 45wt% acid. Intimate contact with the silica support perturbs the local chemical environment of three tungstate centres, which become inequivalent with those in the remaining cluster, suggesting an adsorption mode involving three terminal W==O groups. Above the monolayer, H3PW12O40 clusters form three-dimensional crystallites with physico-chemical properties indistinguishable from those in the bulk heteropoly acid. These H3PW12O40/SiO2 materials are efficient for the solventless isomerisation of α-pinene under mild reaction conditions. Activity scales directly with the number of accessible perturbed tungstate sites at the silica interface; these are the active species.

Synthesis, characterisation and applications of diamond materials

This thesis presented a detailed research work on diamond materials. Chapter 1 is an overall introduction of the thesis. In the Chapter 2, the literature review on the physical, chemical, optical, mechanical, as well as other properties of diamond materials are summarised. Followed by this chapter, several advanced diamond growth and characterisation techniques used in experimental work are also introduced. Then, the successful installation and applications of chemical vapour deposition system was demonstrated in Chapter 4. Diamond growth on a variety of different substrates has been investigated such as on silicon, diamond-like carbon or silica fibres. In Chapter 5, the single crystalline diamond substrate was used as the substrate to perform femtosecond laser inscription. The results proved the potentially feasibility of this technique, which could be utilised in fabricating future biochemistry microfluidic channels on diamond substrates. In Chapter 6, the hydrogen-terminated nanodiamond powder was studied using impedance spectroscopy. Its intrinsic electrical properties and its thermal stability were presented and analysed in details. As the first PhD student within Nanoscience Research Group at Aston, my initial research work was focused on the installation and testing of the microwave plasma enhanced chemical vapour deposition system (MPECVD), which will be beneficial to all the future researchers in the group. The fundamental of the on MPECVD system will be introduced in details. After optimisation of the growth parameters, the uniform diamond deposition has been achieved with a good surface coverage and uniformity. Furthermore, one of the most significant contributions of this work is the successful pattern inscription on diamond substrates by femtosecond laser system. Previous research of femtosecond laser inscription on diamond was simple lines or dots, with little characterisation techniques were used. In my research work, the femtosecond laser has been successfully used to inscribe patterns on diamond substrate and fully characterisation techniques, e.g. by SEM, Raman, XPS, as well as AFM, have been carried out. After the femtosecond laser inscription, the depth of microfluidic channels on diamond film has been found to be 300~400 nm, with a graphitic layer thickness of 165~190 nm. Another important outcome of this work is the first time to characterise the electrical properties of hydrogenterminated nanodiamond with impedance spectroscopy. Based on the experimental evaluation and mathematic fitting, the resistance of hydrogen-terminated nanodiamond reduced to 0.25 MO, which were four orders of magnitude lower than untreated nanodiamond. Meanwhile, a theoretical equivalent circuit has been proposed to fit the results. Furthermore, the hydrogenterminated nanodiamond samples were annealed at different temperature to study its thermal stability. The XPS and FTIR results indicate that hydrogen-terminated nanodiamond will start to oxidize over 100ºC and the C-H bonds can survive up to 400ºC. This research work reports the fundamental electrical properties of hydrogen-terminated nanodiamond, which can be used in future applications in physical or chemical area.

Alkali- and nitrate-free synthesis of highly active Mg-Al hydrotalcite-coated alumina for FAME production

Mg-Al hydrotalcite coatings have been grown on alumina via a novel alkali- and nitrate-free impregnation route and subsequent calcination and hydrothermal treatment. The resulting Mg-HT/AlO catalysts significantly outperform conventional bulk hydrotalcites prepared via co-precipitation in the transesterification of C-C triglycerides for fatty acid methyl ester (FAME) production, with rate enhancements increasing with alkyl chain length. This promotion is attributed to improved accessibility of bulky triglycerides to active surface base sites over the higher area alumina support compared to conventional hydrotalcites wherein many active sites are confined within the micropores. © 2014 The Royal Society of Chemistry.

Hierarchical macroporous-mesoporous SBA-15 sulfonic acid catalysts for biodiesel synthesis

Hierarchical macroporous-mesoporous SBA-15 silicas have been synthesised via dual-templating routes employing liquid crystalline surfactants and polystyrene beads. These offer high surface areas and well-defined, interconnecting macro- and mesopore networks with respective narrow size distributions around 300 nm and 3-5 nm for polystyrene:tetraethoxysilane ratios ≥2:1. Subsequent functionalisation with propylsulfonic acid yields the first organized, macro-mesoporous solid acid catalyst. The enhanced mass transport properties of these new bi-modal solid acid architectures confer significant rate enhancements in the transesterification of bulky glyceryl trioctanoate, and esterification of long chain palmitic acid, over pure mesoporous analogues. This paves the way to the wider application of hierarchical catalysts in biofuel synthesis and biomass conversion. © 2010 The Royal Society of Chemistry.

Optimising the nanoporous architecture of solid acid and base catalysts for biodiesel synthesis

Dwindling oil reserves and growing concerns over CO2 emissions and associated climate change are driving the utilisation of renewable feedstocks as alternative, sustainable fuel sources. While rising oil prices are improving the commercial feasibility of biodiesel production, many current processes still employ homogeneous acid and/or base catalysts to transform plant or algae oil into the fatty acid methyl ester (FAME) components of biodiesel. Fuel purification requires energy intensive aqueous quench and neutralization steps, thus the rational design of new high activity catalysts is required to deliver biodiesel as a major player in the 21st century sustainable energy portfolio. Advances in the development of heterogeneous catalysts for biodiesel synthesis require catalysts with pore architectures designed to improve the accessibility of bulky viscous reactants typical of plant oils. Here we discuss how improvements to active site accessibility and catalyst activity in transesterification or esterification reactions can be achieved either by designing hierarchical pore networks or by pore expansion and use of interconnected pore architectures.

Pore-expanded SBA-15 sulfonic acid silicas for biodiesel synthesis

Here we present the first application of pore-expanded SBA-15 in heterogeneous catalysis. Pore expansion over the range 6-14 nm confers a striking activity enhancement towards fatty acid methyl ester (FAME) synthesis from triglycerides (TAG), and free fatty acid (FFA), attributed to improved mass transport and acid site accessibility.