Dense SnO2-based ceramics (relative density >95%) have been obtained by natural sintering at a moderate temperature (less than or equal to 1300 degrees C) with the help of a small amount of manganese, Further thermal treatments above 1500 degrees C result in grain growth and transport of manganese toward the sample surface. If the ceramic is embedded inside alumina powder, the diffusion of Mn out of the sample and into alumina during such heat treatments leads to a manganese-free body (<40 ppm) which is translucent. The transmission in the visible region depends on sample thickness; 61% was achieved for a 0.05 mm thick sample.
Resumo:
The present work aims to study the microstructure and mechanical properties of titanium alloys, widely used in the manufacture of orthopedic implants in order to compare a new manufacturing technology of implants, rapid prototyping in metals with conventional manufacturing processes. Rapid prototyping is being used in many areas of human knowledge to assist in the study and often in the manufacture of components for their own use. Nowadays with the advancement of software and equipment such as computed tomography and magnetic resonance imaging, we can reproduce any part of the human body in three-dimensional images with great perfection and it is used in the reproduction of implants, scaffolds, material aid and preparation in surgery. This work aims to do: A comparison between the microstructure of the alloy in the two manufacturing processes (prototyping and conventional), showing the grain size, the nature, form, quantity, and distribution of various ingredients or certain inclusions and study of mechanical properties of titanium in both cases.
Resumo:
A shift of the photoluminescence (PL) emission was observed in ZnS prepared by microwave assisted solvothermal method with the increase of the time in microwave. In this work we reported a study of the optical behavior linking with the structural disorder according to XRD and FEG-TEM results. The reduction of intrinsic defects in the lattice is responsible for the decrease of electronic levels in the band gap changing the PL profile. This effect was confirmed by electronic structure calculations.
Resumo:
In the work presented here, Ce0.97Cu0.03O2 nanoparticles were synthesized by a microwave-assisted hydrothermal method under different synthesis temperatures. The obtained nanoparticles were tested as catalysts in preferential oxidation of CO to obtain CO-free H2 (PROX reaction). The samples were characterized by X-ray diffraction, transmission electron microscopy (TEM), electron paramagnetic resonance spectroscopy (EPR) and temperature-programmed reduction (TPR). X-ray diffraction measurements detected the presence of pure cubic CeO2 for all synthesized samples. TEM images of the Ce0.97Cu0.03O2 nanoparticles revealed that samples synthesized at 80°C are composed mainly of nanospheres with an average size of 20 nm. The formation of some nanorods with an average diameter of 8 nm and 40 nm in length, and the size reduction of the nanoparticles from 20 to approximately 15 nm is observed with increasing synthesis temperature. EPR spectra indicated that copper is found well dispersed in sample synthesized at 160°C, located predominant in surface sites of ceria. For samples synthesized at 80 and 120°C, the species are less dispersed than in the other one, resulting in the formation of Cu2+−Cu2+ dimmers at the surface of ceria. TPR profiles presented two reduction peaks, one below 400°C attributed to the reduction of different copper species and a second peak around 800°C attributed to the reduction of Ce4+→ Ce3+ species located in the volume of the nanoparticles. The peak related to the reduction of copper species shifts to lower temperatures with increasing synthesis temperature, i.e., the sample synthesized at 160°C is more easily reduced than the ones synthesized at 120 and 80°C. The nanoparticles showed active as catalysts for the CO-PROX reaction. The microwave-assisted method revealed efficient for the synthesis of Ce0.97Cu0.03O2 nanoparticles with copper species selective for the CO-PROX reaction, which reaches CO conversions up to 92% for the sample synthesized at 160°C.
Resumo:
Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)
Microwave-assisted hydrothermal synthesis of NiO-Ce1-XEuxO2-δ powders for fuel cell catalytic anodes
Resumo:
CeO2-based materials doped with rare earth (TR +3) can be used as alternative to traditional NiO-YSZ anodes in solid oxide fuel cells as they have higher ionic conductivity and lower ohmic losses compared to YSZ. Moreover, they allow fuel cell operation at lower temperatures (500-800°C). In the anode composition, the concentration of NiO acting as catalyst in YSZ provides high electrical conductivity and high electrochemical activity of reactions, promoting internal reform in the cell. In this work, NiO - Ce1-xEuxO2-δ compounds (x = 0.1, 0.2 and 0.3) have been synthesized by microwave-assisted hydrothermal method. The materials were characterized by TG, XRD, TPR and SEM-FEG techniques. The refinement of data obtained by X-ray diffraction showed the presence of ceria doped with europium crystallized in a cubic phase with fluorite structure, in addition to the presence of NiO. The microwave-assisted hydrothermal method showed significant reduction in the average particle size and good mass control of phase compositions compared to other chemical synthesis techniques.
Resumo:
In the present work, we report the synthesis and characterization of NaNbO3 particles obtained by microwave-assisted hydrothermal method from Nb2O5 and NaOH. The synthesis was made at different periods at 180 °C and 300W. The crystallization of NaNbO3 structures produced Na2Nb2O6.H2O in the intermediate phase with fiber-like morphology, and this is associated with the synthesis time. Pure orthorhombic NaNbO3 with cube-like morphology originates after synthesizing for 240 minutes. To verify the remnant polarization of particles, films were obtained by electrophoresis process and sintered at 800°C for 10 minutes in a microwave furnace. The films characterization indicated that films of niobate with fiber-like morphology present remaining polarization, and the morphology of cubes did not show remaining polarization. Considering these results, it can be concluded that the morphology implemented ferroelectric property of NaNbO3.
Resumo:
Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)
Resumo:
We propose and experimentally demonstrate a simple and accurate technique for measuring differential mode group delay (DMGD) in few mode fibers (FMF). A frequency-swept microwave signal is modulated on a filtered optical incoherent source. The microwave signals carried on different fiber modes experience different time delays and interfere with each other in the photodetector. Optical interference between propagating fiber modes is avoided by the use of an incoherent optical source. A mathematical model is established to analyze the interference pattern and extract the DMGD values. A 456-m two-mode fiber and a 981-m FMF, which supports four LP modes, are measured. The measurement covers the whole C-band and the results coincide well with those obtained by the time-of-flight method and the numerical simulations. A precision of ±0.002 ps/m is achieved.
Resumo:
SnO2-based varistors are strong candidates to replace the ZnO-based varistors due to ordering fewer additives to improve its electrical behavior as well as by showing similar nonlinear characteristics of ZnO varistors. In this work, SnO2-nanoparticles based-varistors with addition of 1.0 %mol of ZnO and 0.05 %mol of Nb2O5 were synthesized by chemical route. SnO2.ZnO.Nb2O5-films with 5 μm of thickness were obtained by electrophoretic deposition (EPD) of the nanoparticles on Si/Pt substrate from alcoholic suspension of SnO2-based powder. The sintering step was carried out in a microwave oven at 1000 °C for 40 minutes. Then, Cr3+ ions were deposited on the films surface by EPD after the sintering step. Each sample was submitted to different thermal treatments to improve the varistor behavior by diffusion of ions in the samples. The films showed a nonlinear coefficient (α) greater than 9, breakdown voltage (VR) around 60 V, low leakage current (IF ≈ 10-6 A), height potential barrier above 0.5 eV and grain boundary resistivity upward of 107 Ω.cm.
Resumo:
The purpose of this in vitro study was to evaluate the effect of air-abrasion/zirconia sintering order on the yttria partially stabilized tetragonal zirconia polycrystal (Y-TZP) surface characterization (roughness, morphology, and phase transformation), flexural strength (FS), and shear bond strength (SBS) to a resin cement. Y-TZP specimens were air abraded with 50-μm Al2O3 particles after (AS), before (BS), or before and after zirconia sintering (BAS). For roughness (Ra), 30 block specimens (12×12×3.0 mm; n=10) had their surfaces analyzed by a profilometer. Next, on the air-abraded surfaces of these specimens, composite resin discs (n=30) were bonded with RelyX ARC. The bonded specimens were stored for 24 hours in distilled water at 37°C before shear testing. Failure mode was determined with a stereomicroscope (20×). The surface morphology (n=2) was evaluated by SEM (500×). For the four-point flexural strength test (EMIC DL2000), 39 bar-shaped specimens (20×4.0×1.2 mm; n=13) were air abraded according to the three conditions proposed, and an additional group (nonabraded) was evaluated (n=13). The quantitative analysis of phase transformation (n=1) was completed with Rietveld refinement with X-ray diffraction data. Ra (μm) and SBS (MPa) data were analyzed by one-way analysis of variance (ANOVA) and the Tukey test (α=0.05). Pearson correlation analysis was used to determine if there was a correlation between roughness and SBS. For FS (MPa) data, one-way ANOVA and the Dunnett C-test (α=0.05) were used. The air-abrasion/zirconia sintering order influenced significantly (p<0.001) Ra, SBS, and FS. The BS and AS groups presented the highest (1.3 μm) and the lowest (0.7 μm) Ra. The highest SBS (7.0 MPa) was exhibited by the BAS group, followed by the AS group (5.4 MPa) and finally by the BS group (2.6 MPa). All groups presented 100% adhesive failure. A weak correlation (r=−0.45, p<0.05) was found between roughness and SBS. The air-abrasion/zirconia sintering order provided differences in the surface morphology. The nonabraded (926.8 MPa) and BS (816.3 MPa) groups exhibited statistically similar FS values but lower values than the AS (1249.1 MPa) and BAS (1181.4 MPa) groups, with no significant difference between them. The nonabraded, AS, BS, and BAS groups exhibited, respectively, percentages of monoclinic phase of 0.0 wt%, 12.2 wt%, 0.0 wt%, and 8.6 wt%. The rougher surface provided by the air-abrasion before zirconia sintering may have impaired the bonding with the resin cement. The morphological patterns were consistent with the surface roughness. Considering the short-term SBS and FS, the BAS group exhibited the best performance. Air abrasion, regardless of its performance order, provides tetragonal to monoclinic transformation, while sintering tends to zero the monoclinic phase content.
Resumo:
To evaluate the ability of low time microwaveexposureto inactivate and damage cell membrane integrity of C. albicans. Materials and Methods: Two 200ml C. albicans suspensions were obtained. Sterile dentures were placed in a beaker containing Experimental (ES) or Control suspensions (CS). ES was microwaved at 650 W for 1, 2, 3, 4 or 5 min. Suspensions were optically counted using Methylene blue dye as indicative of membrane-damaged cells; spread on Agar Sabouraud dextrose (ASD) for viability assay; or spectrophotometrically measured at 550nm. Cell-free solutions were submitted to content analyses of protein (Bradford and Pyrogallol red methods); Ca++ (Cresolphthalein Complexone method); DNA (spectrophotometer measurements at 260nm) and K+ (selective electrode technique). Data were analyzed by Student-t test and linear regression (α=0.05). In addition, flowcytometry analysis of Candida cells in suspensionwas performed using propidium iodide. Results: All ES cells demonstrated cell membrane damage at 3, 4 and 5 min,viable cells were nonexistent at 3, 4 and 5 min ES ASD plates and optical density of ES and CS was not significantly differentfor all exposition times. ES cells released highcontents of protein, K+ , Ca++ and DNA after 2 min exposition when compared to that of the CSs. Similar results were observed with flow cytometry analysiswith regard to the periodsof microwave exposure. Conclusions: Microwave irradiation inactivated C. albicansafter 3min and damaged cell membrane integrity after 2 min exposition.
Resumo:
A pretreatment with microwave irradiation was applied to enhance enzyme hydrolysis of corn straw and rice husk immersed in water, aqueous glycerol or alkaline glycerol. Native and pretreated solids underwent enzyme hydrolysis using the extract obtained from the fermentation of Myceliophthora heterothallica, comparing its efficiency with that of the commercial cellulose cocktail Celluclast (R). The highest saccharification yields, for both corn straw and rice husk, were attained when biomass was pretreated in alkaline glycerol, method that has not been previously reported in literature. Moreover, FTIR, TG and SEM analysis revealed a more significant modification in the structure of corn straw subjected to this pretreatment.Highest global yields were attained with the crude enzyme extract, which might be the result of its content in a great variety of hydrolytic enzymes, as revealed zymogram analysis. Moreover, its hydrolysis efficiency can be improved by its supplementation with commercial beta-glucosidase.